Liquation Cracking Susceptibility and Mechanical Properties of 7075 Aluminum Alloy GTAW Joints

1
Institute of Light Alloy and Processing, Faculty of Materials and Manufacturing, Beijing University of Technology, Beijing 100124, China
2
School of Mechanical and Engineering, Tianjin Sino-German University of Applied Sciences, Tianjin 300350, China
*
Author to whom correspondence should be addressed.
Submission received: 14 April 2022 / Revised: 12 May 2022 / Accepted: 12 May 2022 / Published: 20 May 2022

Abstract

:
In this work, aluminum alloy 7075-T651 was welded by using customized Al-Cu-Si and Al-Cu-Mg-Zn filler wire during gas tungsten arc welding. The liquation cracking susceptibility of the joints was tested under a circular-patch welding experiment. Besides, the temperature vs. solid fraction curves (T-fS) was calculated for different samples to reveal the formation mechanism of liquation cracking. The joint was susceptible to liquation cracking if (fS)weld > (fS)workpiece during the cooling stage. The results of the circular-patch welding experiment show that the liquation cracking susceptibility of the joint by using ER5356, Al-Cu1.5-Si4.5, Al-Cu3.0-Si2.5, Al-Cu4.5-Si1.5, Al-Cu2.3-Mg2.3-Zn6.6 and Al-Cu2.2-Mg2.0-Zn7.8 filler metal is 22.8%, 8.3%, 2.8%, 2.8%, 3.3% and 1.4%, respectively. The mechanical test shows that the data dispersion of the 7075 gas tungsten arc welding joint can be decreased by eliminating the liquation crack.

1. Introduction

Aluminum alloy was characterized by low-density, corrosion-proof and high-impact energy absorptivity, which led to its extensive application in automotive, marine and aircraft industries [1,2,3]. The high thermal diffusion coefficient of the aluminum alloy makes it is difficult to be effectively heated during the fusion welding process in which case a concentrated heat source is required [4,5]. Besides, to meet the demands of effective heating and oxide film cleaning, an alternating or variable polarity power source is typically used in aluminum alloy arc welding [6,7].
Aluminum alloy 7075 (AA7075) is a kind of high-specific-strength light metal. AA7075 possesses high strength under a peak aged state due to its high mass fraction of the Cu-Mg-Zn alloying element [8]. However, the metallurgical characteristics of AA7075 lead to its high susceptibility to solidification cracking and liquation cracking [9,10]. Finding an optimal combination between the filler wire and base metal to prevent these defects is a major concern in the research field of aluminum alloy arc welding.
Both aluminum and magnesium alloy have a wide temperature gap between liquidus and solidus. During the fusion welding process, a partially melted zone (PMZ) forms adjacent to the fusion zone (FZ) [11,12]. Liquation cracking is a common defect in aluminum or magnesium alloy arc welding joints, which occurs within the PMZ. Kou et al. suggested an effective criterion to predict the liquation cracking susceptibility [10,13]. By considering the dilution rate, the solid fraction (fS)weld and (fS)workpiece evolution was calculated within each melting temperature range (T-fS curve). The joint was susceptible to liquation cracking if (fS)weld > (fS)workpiece when this local site was under tension. Adding alloying elements to adjust the T-fS curve of FZ is an effective method to restrain the liquation cracking susceptibility of a welding joint [14]. It is necessary to carry out fundamental research on the cracking phenomenon for metals likely to crack when a custom filler metal was used.
Typically, ER5356 or ER4043 is used as filler wire during the AA7075 arc welding process [10]. The Cu and Zn composition of the FZ is lower than the base metal. This would lead to a decrease in strength and an increase in the susceptibility to galvanic corrosion. Besides, the difference in composition between FZ and PMZ may lead to liquation cracking if (fS)weld > (fS)workpiece during the cooling period. It is necessary to develop a novel filler metal for AA7075 arc welding.
In this study, custom Al-Cu-Si and Al-Cu-Mg-Zn filler wires are used in AA7075 gas tungsten arc welding. The liquation cracking susceptibility and mechanical property of the joints are investigated.

2. Materials and Methods

2.1. Welding Test

Aluminum alloy 7075-T651 (the 0.2% yield strength is 470 MPa while the tensile strength is 540 MPa) was used as a base metal while a series of custom Al-Cu-Si and Al-Cu-Mg-Zn wire was used as filler metal in this study. The main alloying elements of each material are summarized in Table 1.
A 315P AC/DC gas tungsten arc welding machine was used for the welding test. The welding process was conducted under 99.99% high-purity argon shielding gas. The welding current was 85 A under AC mode while the traveling speed of the welding gun was 1 mm/s. The liquation cracking susceptibility for different combinations of the base metal and filler wire was tested by a circular-patch welding experiment of which the samples’ dimensions are shown in Figure 1. After testing, the liquation cracking susceptibility for each joint was recorded by counting the cracking percentage along the outer edge of the circular weld. Besides, the color metallography samples (CM samples) at the interface of FZ/PMZ were prepared to show the cracked or un-cracked morphology (prepared by anodizing using a solution of 25 mL fluoboric acid + 475 mL H2O). The anodizing voltage was 20 V, while the anodizing time was 120 s. The sampling position of the CM samples was near the crater of the weld.
Furthermore, butt-welding joints were prepared and cut for microstructural and tensile test samples, of which the dimensions are shown in Figure 2 (2 mm thickness). The welding parameters were the same as the samples in the circular-patch welding experiment. Moreover, CM samples of the interface of FZ/PMZ in different butt-welded samples were prepared. Electron probe microanalysis (EPMA) for welds using a filler metal of Al-Cu1.5-Si4.5, Al-Cu4.5-Si1.5 and Al-Cu2.3-Mg2.3-Zn6.6 was conducted by a Shimadzu EPMA-1720 device. The tensile tests were conducted on a CSS-44100 material test system (three samples repeated) at a tensile speed of 1 mm/min. The fracturing surface was observed by a scanning electron microscope (Hitachi S-3400N).

2.2. Liquation Cracking Susceptibility Analysis by T-fS Criterion

During AA7075 gas tungsten arc welding (GTAW) with filler wire, the solid–liquid phase transition pattern can be schematically illustrated in Figure 3. There is a thin layer of PMZ in the work piece surrounding the liquid welding pool, while a mushy zone (MZ) exists at the tail zone of the liquid welding pool. A rectangle located at the interface between the MZ and PMZ was enlarged in Figure 3b,c. There is no mass transfer between MZ and PMZ. It is considered that there is a small-volume element Ω within MZ and PMZ. The range of Ωweld was from the center line of a secondary dendritic arm to its boundary, while the range of Ωworkpiece was from the center line between two residual grains to the solid boundary. T-fS curves of Ωweld and Ωworkpiece were calculated. The liquation cracking is susceptible if (fS)weld > (fS)workpiece during the cooling stage.
In Figure 3c, the interface between FZ and PMZ can be observed. The MZ forms between the liquidus and solidus of the FZ. So, the MZ/PMZ interface is exhibited at the FZ/PMZ interface at room temperature.
The T-fS curves of Ωweld and Ωworkpiece were calculated using JMatPro with an aluminum alloy database. The Scheil–Gulliver solidification model was used. The T-fS curves could be obtained by using the following equations:
C i S ¯ C i L d f L = f L d C i L
C i S ¯ = f j f j C i j
d C i L d C i + 1 L = C i L C i S ¯ C i + 1 L C i + 1 S ¯
where fL is the liquid fraction while the solid fraction is given by fS = (1fL); C is the concentration of a specific element; the superscripts identify the phase, and the subscripts refer to a specific component. By solving the solid fraction evolution within the freezing temperature range of the target materials, the T-fS curves could be obtained.
The effect of each alloying element (Cu, Mg, Si and Zn) on the solidification path was assessed by calculating the T-fS curve within the corresponding binary system. The calculation range for each alloying element is from 1 to 10 wt.% with an interval of 1 wt.%. In order to determine the composition of the weld, the dilution of the workpiece is assumed to be 40%. The composition of the AA7075 base metal for T-fS calculation is 1.5Cu-2.2Mg-0.4Si-5.5Zn (wt.%). Besides, the phase transition of the typical welds during the solidification period was also calculated to aid in the analysis of the microstructure evolution of the AA7075 joint with different filler wires.

3. Results and Discussion

3.1. Liquation Cracking Susceptibility of Different Base Metal/Filler Wire Combination

By considering the schematic of an aluminum alloy GTAW joint in Figure 3, the relationship between the solidification path and the liquation cracking susceptibility can be illustrated: The temperature field distribution of the joint is continuous. The volume of Ω is infinitely small compared to the welds. So, the temperature of Ωweld and Ωworkpiece can be considered the same as each other where they are adjacent to the interface between MZ and PMZ. Besides, during the cooling stage, a similar level of tension is generated under both in Ωweld and Ωworkpiece. Experimental data show the semi-solid Al alloy’s strength increases with the increase in its solid fraction fS [15]. Under the same temperature and tension, if the fS in Ωweld was higher than that of Ωworkpiece, liquation cracking will take place within PMZ, where it is adjacent to MZ.
Figure 4 shows the effect of the alloying elements on the T-fS curves. It can be observed that fS is decreased under a specific temperature by increasing the content of each element. Besides, for Cu, Mg and Si, a eutectic reaction takes place at the end of the solidification process. Typically, the eutectic reaction with intermetallic compounds forms at the interdendritic zone of a weld [6]. This will decrease the ductility of the weld. The assessment of the effects of each alloying element on the solidification path shows that each alloying element shall be added under an appropriate mass fraction in the filler wire. If the content of a specific alloying element is too low, the joint is prone to cracking. If the content of a specific alloying element is too high, the ductility of the weld is compromised.
Table 2 shows the liquation cracking susceptibility of each joint, which is tested by a circular-patch welding experiment. Compared to the welds using ER5356, the liquation cracking susceptibility of welds using Al-Cu-Si and Al-Cu-Mg-Zn filler wire is obviously decreased.
Figure 5 shows the T-fS curves of Ωweld and Ωworkpiece under different base metal/filler wire combinations. During the entire cooling period, (fS)weld > (fS)workpiece for the weld with ER5356. For the weld with Al-Cu-Si wire, (fS)weld < (fS)workpiece within the high-temperature zone while (fS)weld > (fS)workpiece within the low-temperature zone. For those welds with Al-Cu-Mg-Zn wire, (fS)weld < (fS)workpiece within most of the semi-solid temperature range.
For the AA7075/ER5356 joint (Figure 5a), T-fS curves show that (fS)weld > (fS)workpiece at any temperature range, which means the liquation cracking sensibility is high under this base metal/filler wire combination. The literature on magnesium alloy hot cracking shows the crack forms initially at 500 °C [16]. For the AA7075/Al-Cu1.5-Si4.5 joint, (fS)weld < (fS)workpiece within the temperature range of 545~625 °C while (fS)weld > (fS)workpiece when the temperature is below 545 °C. So, it is possible that liquation cracking occurs when the FZ/PMZ interface’s temperature decreases below 545 °C. The temperature range of (fS)weld > (fS)workpiece for the AA7075/Al-Cu3.0-Si2.5 joint and the AA7075/Al-Cu4.5-Si1.5 joint is below 530 °C and 515 °C, respectively. The PMZ’s local strength increases when the local temperature is lowered, which can resist the occurrence of liquation cracking. In fact, the results of the circular-patch welding test in Table 2 show the liquation cracking susceptibility of the AA7075/Al-Cu1.5-Si4.5 joint is slightly higher than that of the AA7075/Al-Cu3.0-Si2.5 joint and the AA7075/Al-Cu4.5-Si1.5 joint. Besides, both T-fS curves and the circular-patch welding test show that the liquation cracking susceptibility of the AA7075/Al-Cu2.3-Mg2.3-Zn6.6 joint and the AA7075/Al-Cu2.2-Mg2.0-Zn7.8 joint is low.

3.2. Liquation Cracking Susceptibility of Different Base Metal/Filler Wire Combinations

Figure 6 shows the color metallography images of different joints in circular-patch welding tests. It can be observed that the liquation crack appears within the PMZ, adjacent to the FZ, in the AA7075/ER5356 and AA7075/Al-Cu1.5-Si4.5 joint. By contrast, no liquation crack was found in other samples (near the crater).
Furthermore, liquation cracks could also be observed in the butt-welded sample if the liquation cracking sensibility of the filler/workpiece combination is high (Figure 7). Note that the thermal stress distribution is fairly different between the circular-patch welding sample and the butt-welding sample [17,18]. In the former case, the liquation cracking is prone to occur. In the butt-welding sample, the liquation cracks present as tiny discontinuous cracks. The liquation crack can be observed at the FZ/PMZ interface of the weld with ER5356 filler wire. There is no sign of liquation cracking for other samples.
Figure 8 shows the phase evolution within FZ during the solidification process of the AA7075/Al-Cu4.5-Si1.5, AA7075/Al-Cu1.5-Si4.5 and AA7075/Al-Cu2.3-Mg2.3-Zn6.6 joints, respectively. It can be observed that, during the initial solidification stage, α-Al firstly crystallized from the liquid. Corresponding to the alloying elements, different secondary crystalline phases [19,20,21] such as Al2Cu, Al2CuMg, Al5Cu2Mg8Si6, Mg2Si, MgZn2 and Si form at the ending stage of solidification. This solidification path led to FZ presenting a dendrite-like microstructure with alloying elements segregating at the inter-dendrite zone.
FZ consists of a typical dendrite-like microstructure. Figure 9, Figure 10 and Figure 11 show the alloying element distributions of typical welds tested by EPMA. It can be observed that Cu, Mg, Si or Zn elements are segregated at the inter-dendrite zone, which supports the analysis result in Figure 8.

3.3. Mechanical Property of the Joints

The tensile test results are listed in Table 3. The data dispersion of the joints with the ER5356 filler wire occurs at a high degree. This is because liquation cracking exists within the joints. A previous work by the authors shows that the cracks within PMZ can increase the data dispersion of mechanical tests [22]. The fracture location shows that the joints with high liquation cracking susceptibility are prone to fracture in PMZ.
For all joints in the as-welded state, ductility is poor. This is because the alloying elements are segregated at the inter-granular zone, which forms a large number of IMCs. Besides, the fracturing location for joints with the ER5356 filler wire is the FZ/PMZ interface, while the other joints are fractured within FZ.
Figure 12 shows the fracturing surface of each sample. The dendritic feature on the fracturing surface suggests the liquation cracking takes place at the FZ/PMZ interface of the joint with the ER5356 filler wire.

4. Conclusions

In this study, the liquation cracking susceptibility and mechanical properties of 7075 aluminum alloy GTAW joints with different filler wires were investigated. The phase evolution data of different joints were calculated using a multi-alloying-elements thermodynamics database to reveal the mechanisms. The following conclusions can be drawn:
(1)
The effect of each alloying element on the solidification path was analyzed. The design principle of the Al-Cu-Si and Al-Cu-Mg-Zn filler wires in this work causes the fS of the weld to be a little higher than its counterpart of the workpiece under the specific temperature range.
(2)
During the whole cooling period, the solid fraction within the fusion zone is higher than that of the partial melting zone for the joint with ER5356. By using Al-Cu-Si and Al-Cu-Mg-Zn filler metal, the solid fraction within the fusion zone is lower than that of the partial melting zone during the cooling period. By using Al-Cu-Si and Al-Cu-Mg-Zn filler metal, the liquation crack within the partial melting zone is restrained.
(3)
The weld’s phase evolution data and the microstructure observation results indicate that α-Al firstly crystallized during the initial solidification stage to form the dendrite stem, while secondary crystalline phases at the inter-dendrite were generated during the ending solidification stage.
(4)
The existence of liquation cracks led to a high degree of dispersion of the testing data in the joints’ tensile test. Compared to the joint with ER5356, the joint with Al-Cu-Si and Al-Cu-Mg-Zn filler metal exhibits a lower degree of data dispersion in the tensile test.

Author Contributions

Conceptualization and writing—review and editing, Y.Z. (Yu Zhang); methodology and data curation, Y.Z. (Yulin Zhang); software and writing—original draft preparation, Z.L.; validation and resources, H.L.; formal analysis and resources, Y.W.; investigation and resources, L.W. All authors have read and agreed to the published version of the manuscript.

Funding

This research was supported by the National Natural Science Foundation of China (Grant Nos. 51905300 and 52074017), the Beijing Municipal Natural Science Foundation (No. 3202002), the 38th China-Poland intergovernmental Joint S&T Committee Meeting, Personal Exchange Project (2020-13), the China-CEEC Joint Education Project for Higher Education (No. 2021113) and the International Research Cooperation Seed Fund of Beijing University of Technology (2021B27 and 2021A14).

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

Not applicable.

Acknowledgments

The authors wish to acknowledge the Beijing International Science and Technology Cooperation Base of Carbon-based Nanomaterials.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Gong, B.; Zhang, Z.; Hou, J.; Duan, Q.; Wang, X. Effect of aging state on corrosion fatigue properties of 7075 aluminum alloy. Int. J. Fatigue 2022, 8, 106916. [Google Scholar] [CrossRef]
  2. Zhao, Q.; Guo, C.; Niu, K.; Zhao, J.; Huang, Y.; Li, X. Long-term corrosion behavior of the 7A85 aluminum alloy in an industrial-marine atmospheric environment. J. Mater. Res. Technol. 2021, 12, 1350–1359. [Google Scholar] [CrossRef]
  3. Egorkin, V.S.; Medvedev, I.M.; Sinebryukhov, S.L.; Vyaliy, I.E.; Gnedenkov, A.S.; Nadaraia, K.V.; Izotov, N.V.; Mashtalyar, D.V.; Gnedenkov, S.V. Atmospheric and Marine Corrosion of PEO and Composite Coatings Obtained on Al-Cu-Mg Aluminum Alloy. Materials 2020, 13, 2739. [Google Scholar] [CrossRef] [PubMed]
  4. Pan, J.; Hu, S.; Yang, L.; Li, H. Simulation and analysis of heat transfer and fluid flow characteristics of variable polarity GTAW process based on a tungsten–arc-specimen coupled model. Int. J. Heat Mass Transf. 2016, 5, 346–352. [Google Scholar] [CrossRef]
  5. Pujari, K.; Patil, D.; Mewundi, G. Selection of GTAW process parameter and optimizing the weld pool geometry for AA 7075-T6 Aluminium alloy. Mater. Today Proc. 2018, 5, 25045–25055. [Google Scholar] [CrossRef]
  6. Lin, Y.T.; Wang, M.C.; Zhang, Y.; He, Y.Z.; Wang, D.P. Investigation of microstructure evolution after post-weld heat treatment and cryogenic fracture toughness of the weld metal of AA2219 VPTIG joints. Mater. Des. 2017, 113, 54–59. [Google Scholar] [CrossRef]
  7. Lang, R.; Han, Y.; Bai, X.; Bao, X. Influence of the metal flow in the keyhole molten pool on the molten pool stability in continuous variable polarity plasma arc keyhole vertical-up welding. J. Manuf. Processes 2022, 4, 195–209. [Google Scholar] [CrossRef]
  8. Li, S.; Dong, H.; Shi, L.; Wang, X.; Liu, Z.; Shangguan, L.; Tian, Y. The Effects of Heat Straightening Temperature on the Microstructure and Properties of 7N01 Aluminum Alloy. Materials 2019, 12, 2949. [Google Scholar] [CrossRef] [Green Version]
  9. Li, G.; Jadhav, S.D.; Martín, A.; Montero-Sistiaga, M.L.; Soete, J.; Sebastian, M.S.; Cepeda-Jiménez, C.M.; Vanmeensel, K. Investigation of Solidification and Precipitation Behavior of Si-Modified 7075 Aluminum Alloy Fabricated by Laser-Based Powder Bed Fusion. Metall. Mater. Trans. A 2021, 52, 194–210. [Google Scholar] [CrossRef]
  10. Cao, B.G.; Kou, S. Predicting and Reducing Liquation-Cracking Susceptibility Based on Temperature vs. Fraction Solid. Weld. J. 2006, 1, 9s–18s. [Google Scholar]
  11. Łyczkowska, K.; Adamiec, J. The Phenomena and Criteria Determining the Cracking Susceptibility of Repair Padding Welds of the Inconel 713C Nickel Alloy. Materials 2022, 15, 634. [Google Scholar] [CrossRef] [PubMed]
  12. Luo, C.; Li, H.; Zhang, Y.; Li, J.; Wen, Y.; Yang, L. Microstructure and Mechanical Properties of Tungsten Inert Gas Weld Joints of Sprayed and Cast Aluminium–Lithium Alloy. Materials 2020, 13, 3787. [Google Scholar] [CrossRef] [PubMed]
  13. Yuan, T.; Chai, X.; Luo, Z.; Kou, S. Predicting susceptibility of magnesium alloys to weld-edge cracking. Acta Mater. 2015, 90, 242–251. [Google Scholar] [CrossRef]
  14. Zhang, Y.; Zhou, Z.; Fu, Y.; Li, H.; Li, Z.; Mariusz, B.; Senkara, J. Effects of Al/Zn interlayer on the solidification path and liquation cracking susceptibility of AZ31/ZK61 dissimilar magnesium alloy resistance spot welding joints. J. Manuf. Processes 2022, 75, 60–71. [Google Scholar] [CrossRef]
  15. Dahle, K.; Arnberg, L. Development of strength in solidifying aluminium alloys. Acta Mater. 1997, 45, 547–559. [Google Scholar] [CrossRef]
  16. Cao, G.; Kou, S. Hot tearing of ternary Mg-Al-Ca alloy castings. Metall. Mater. Trans. A 2006, 37, 3647–3663. [Google Scholar] [CrossRef]
  17. Chai, X.; Yuan, T.; Kou, S. Liquation and liquation cracking in partially melted zones of magnesium welds. Weld. J. 2016, 95, 57–67. [Google Scholar]
  18. Yuan, T.; Zhang, H.; Jiang, X.; Chen, S.; Xu, M.; Liu, X. Investigation on liquation cracks of dissimilar magnesium alloy welds using the circular-patch experiment and numerical simulation. J. Manuf. Processes 2022, 75, 49–59. [Google Scholar] [CrossRef]
  19. Zhang, Y.; Li, H.; Li, Z.; Mariusz, B.; Senkara, J. Quantitative analysis of the solute redistribution and precipitate of Al-Mg-Si series alloys re-sistance spot welds after post-weld heat treatment. J. Mater. Res. Technol. 2021, 15, 5906–5919. [Google Scholar] [CrossRef]
  20. Liu, J.; Kou, S. Susceptibility of ternary aluminum alloys to cracking during solidification. Acta Mater. 2017, 125, 513–523. [Google Scholar] [CrossRef] [Green Version]
  21. Liu, J.; Duarte, H.P.; Kou, S. Evidence of back diffusion reducing cracking during solidification. Acta Mater. 2017, 122, 47–59. [Google Scholar] [CrossRef] [Green Version]
  22. Li, H.; Yan, W.; Li, Z.; Mariusz, B.; Senkara, J.; Zhang, Y. Numerical and experimental study of the hot cracking phenomena in 6061/7075 dissimilar aluminum alloy resistance spot welding. J. Manuf. Processes 2022, 77, 794–808. [Google Scholar] [CrossRef]
Figure 1. Circular-patch welding experiment: (a) Assembly of the parts; (b) dimensions of the workpiece (unit: mm).
Figure 1. Circular-patch welding experiment: (a) Assembly of the parts; (b) dimensions of the workpiece (unit: mm).
Materials 15 03651 g001
Figure 2. Extracting CM and tensile test samples from the butt-welding joints (unit: mm).
Figure 2. Extracting CM and tensile test samples from the butt-welding joints (unit: mm).
Materials 15 03651 g002
Figure 3. Schematic of analyzing liquation cracking susceptibility by using volume elements Ω: (a) Sub-divisions of the welds; (b) magnification of the rectangle area in (a); (c) CM figure of AA7075 GTAW joint of corresponding area.
Figure 3. Schematic of analyzing liquation cracking susceptibility by using volume elements Ω: (a) Sub-divisions of the welds; (b) magnification of the rectangle area in (a); (c) CM figure of AA7075 GTAW joint of corresponding area.
Materials 15 03651 g003
Figure 4. Assessment of each alloying element on the solidification path: (a) Al-Cu binary system; (b) Al-Mg binary system; (c) Al-Si binary system; (d) Al-Zn binary system.
Figure 4. Assessment of each alloying element on the solidification path: (a) Al-Cu binary system; (b) Al-Mg binary system; (c) Al-Si binary system; (d) Al-Zn binary system.
Materials 15 03651 g004
Figure 5. T-fS curves of different joints: (a) The AA7075/ER5356 joint; (b) AA7075/Al-Cu1.5-Si4.5 joint; (c) the AA7075/Al-Cu3.0-Si2.5 joint; (d) the AA7075/Al-Cu4.5-Si1.5 joint; (e) the AA7075/Al-Cu2.3-Mg2.3-Zn6.6 joint; (f) the AA7075/Al-Cu2.2-Mg2.0-Zn7.8 joint.
Figure 5. T-fS curves of different joints: (a) The AA7075/ER5356 joint; (b) AA7075/Al-Cu1.5-Si4.5 joint; (c) the AA7075/Al-Cu3.0-Si2.5 joint; (d) the AA7075/Al-Cu4.5-Si1.5 joint; (e) the AA7075/Al-Cu2.3-Mg2.3-Zn6.6 joint; (f) the AA7075/Al-Cu2.2-Mg2.0-Zn7.8 joint.
Materials 15 03651 g005
Figure 6. Color metallography images of different joints (circular-patch welding): (a) The AA7075/ER5356 joint; (b) AA7075/Al-Cu1.5-Si4.5 joint; (c) the AA7075/Al-Cu3.0-Si2.5 joint; (d) the AA7075/Al-Cu4.5-Si1.5 joint; (e) the AA7075/Al-Cu2.3-Mg2.3-Zn6.6 joint; (f) the AA7075/Al-Cu2.2-Mg2.0-Zn7.8 joint.
Figure 6. Color metallography images of different joints (circular-patch welding): (a) The AA7075/ER5356 joint; (b) AA7075/Al-Cu1.5-Si4.5 joint; (c) the AA7075/Al-Cu3.0-Si2.5 joint; (d) the AA7075/Al-Cu4.5-Si1.5 joint; (e) the AA7075/Al-Cu2.3-Mg2.3-Zn6.6 joint; (f) the AA7075/Al-Cu2.2-Mg2.0-Zn7.8 joint.
Materials 15 03651 g006
Figure 7. Colur metallography images of different joints (butt-welding): (a) The AA7075/ER5356 joint; (b) AA7075/Al-Cu1.5-Si4.5 joint; (c) the AA7075/Al-Cu3.0-Si2.5 joint; (d) the AA7075/Al-Cu4.5-Si1.5 joint; (e) the AA7075/Al-Cu2.3-Mg2.3-Zn6.6 joint; (f) the AA7075/Al-Cu2.2-Mg2.0-Zn7.8 joint.
Figure 7. Colur metallography images of different joints (butt-welding): (a) The AA7075/ER5356 joint; (b) AA7075/Al-Cu1.5-Si4.5 joint; (c) the AA7075/Al-Cu3.0-Si2.5 joint; (d) the AA7075/Al-Cu4.5-Si1.5 joint; (e) the AA7075/Al-Cu2.3-Mg2.3-Zn6.6 joint; (f) the AA7075/Al-Cu2.2-Mg2.0-Zn7.8 joint.
Materials 15 03651 g007
Figure 8. The phase evolution data during solidification process of typical welds: (a) The AA7075/Al-Cu4.5-Si1.5 weld; (b) the magnification of (a); (c) the AA7075/Al-Cu1.5-Si4.5 weld; (d) the magnification of (c); (e) the AA7075/Al-Cu2.3-Mg2.3-Zn6.6 weld; (f) the magnification of (f).
Figure 8. The phase evolution data during solidification process of typical welds: (a) The AA7075/Al-Cu4.5-Si1.5 weld; (b) the magnification of (a); (c) the AA7075/Al-Cu1.5-Si4.5 weld; (d) the magnification of (c); (e) the AA7075/Al-Cu2.3-Mg2.3-Zn6.6 weld; (f) the magnification of (f).
Materials 15 03651 g008
Figure 9. The EPMA mapping results (the AA7075/Al-Cu1.5-Si4.5 weld): (a) Secondary electronic image; (b) Cu distribution; (c) Mg distribution; (d) Si distribution.
Figure 9. The EPMA mapping results (the AA7075/Al-Cu1.5-Si4.5 weld): (a) Secondary electronic image; (b) Cu distribution; (c) Mg distribution; (d) Si distribution.
Materials 15 03651 g009
Figure 10. The EPMA mapping results (the AA7075/Al-Cu4.5-Si1.5 weld): (a) Secondary electronic image; (b) Cu distribution; (c) Mg distribution; (d) Si distribution.
Figure 10. The EPMA mapping results (the AA7075/Al-Cu4.5-Si1.5 weld): (a) Secondary electronic image; (b) Cu distribution; (c) Mg distribution; (d) Si distribution.
Materials 15 03651 g010
Figure 11. The EPMA mapping results (the AA7075/Al-Cu2.3-Mg2.3-Zn6.6 weld): (a) Secondary electronic image; (b) Cu distribution; (c) Mg distribution; (d) Si distribution.
Figure 11. The EPMA mapping results (the AA7075/Al-Cu2.3-Mg2.3-Zn6.6 weld): (a) Secondary electronic image; (b) Cu distribution; (c) Mg distribution; (d) Si distribution.
Materials 15 03651 g011
Figure 12. Fracturing surface: (a) The AA7075/ER5356 joint; (b) AA7075/Al-Cu1.5-Si4.5 joint; (c) the AA7075/Al-Cu3.0-Si2.5 joint; (d) the AA7075/Al-Cu4.5-Si1.5 joint; (e) the AA7075/Al-Cu2.3-Mg2.3-Zn6.6 joint; (f) the AA7075/Al-Cu2.2-Mg2.0-Zn7.8 joint.
Figure 12. Fracturing surface: (a) The AA7075/ER5356 joint; (b) AA7075/Al-Cu1.5-Si4.5 joint; (c) the AA7075/Al-Cu3.0-Si2.5 joint; (d) the AA7075/Al-Cu4.5-Si1.5 joint; (e) the AA7075/Al-Cu2.3-Mg2.3-Zn6.6 joint; (f) the AA7075/Al-Cu2.2-Mg2.0-Zn7.8 joint.
Materials 15 03651 g012
Table 1. Chemical composition of filler and base metal (wt.%).
Table 1. Chemical composition of filler and base metal (wt.%).
Filler WireCuMgSiZnAl
ER5356-4.5--Bal.
Al-Cu1.5-Si4.51.5-4.5-Bal.
Al-Cu3.0-Si2.53-2.5-Bal.
Al-Cu4.5-Si1.54.5-1.5-Bal.
Al-Cu2.3-Mg2.3-Zn6.62.282.32-6.57Bal.
Al-Cu2.2-Mg2.0-Zn7.82.152.08-7.81Bal.
Table 2. Liquation cracking susceptibility and compositions of welds.
Table 2. Liquation cracking susceptibility and compositions of welds.
Filler WireCracking PercentageCu in Weld
(wt.%)
Mg in Weld
(wt.%)
Si in Weld
(wt.%)
Zn in Weld
(wt.%)
ER535622.8%0.63.580.162.2
Al-Cu1.5-Si4.58.3%1.50.882.862.2
Al-Cu3.0-Si2.52.8%2.40.881.662.2
Al-Cu4.5-Si1.52.8%3.30.881.062.2
Al-Cu2.3-Mg2.3-Zn6.63.3%1.892.130.226.14
Al-Cu2.2-Mg2.0-Zn7.81.4%1.972.270.226.89
Table 3. Tensile test results.
Table 3. Tensile test results.
Workpiece/Filler Wire0.2% Yield Strength (MPa)Average Tensile Strength (MPa)Standard Deviation of Tensile StrengthPercentage ElongationStandard Deviation of Percentage ElongationFracture Location
AA7075/ER535698.6193.8126.11.49%1.17%PMZ
AA7075/Al-Cu1.5-Si4.581.8154.332.40.9%0.2%PMZ
AA7075/Al-Cu3.0-Si2.5100.4181.954.81.2%0.3%FZ
AA7075/Al-Cu4.5-Si1.5157.8286.813.52.4%0.5%PMZ
AA7075/Al-Cu2.3-Mg2.3-Zn6.6153.8279.435.12.2%0.5%FZ
AA7075/Al-Cu2.2-Mg2.0-Zn7.8112.9194.333.51.3%0.2%FZ
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Li, Z.; Zhang, Y.; Li, H.; Wang, Y.; Wang, L.; Zhang, Y. Liquation Cracking Susceptibility and Mechanical Properties of 7075 Aluminum Alloy GTAW Joints. Materials 2022, 15, 3651. https://0-doi-org.brum.beds.ac.uk/10.3390/ma15103651

AMA Style

Li Z, Zhang Y, Li H, Wang Y, Wang L, Zhang Y. Liquation Cracking Susceptibility and Mechanical Properties of 7075 Aluminum Alloy GTAW Joints. Materials. 2022; 15(10):3651. https://0-doi-org.brum.beds.ac.uk/10.3390/ma15103651

Chicago/Turabian Style

Li, Zhuoxin, Yulin Zhang, Hong Li, Yipeng Wang, Lijuan Wang, and Yu Zhang. 2022. "Liquation Cracking Susceptibility and Mechanical Properties of 7075 Aluminum Alloy GTAW Joints" Materials 15, no. 10: 3651. https://0-doi-org.brum.beds.ac.uk/10.3390/ma15103651

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop