Article

Triple Perovskite Nd1.5Ba1.5CoFeMnO9−δ-Sm0.2Ce0.8O1.9 Composite as Cathodes for the Intermediate Temperature Solid Oxide Fuel Cells

College of Materials Science and Engineering, Nanjing Tech University, Nanjing 211816, China
*
Author to whom correspondence should be addressed.
Submission received: 28 April 2022 / Revised: 16 May 2022 / Accepted: 17 May 2022 / Published: 20 May 2022
(This article belongs to the Special Issue Cathode Materials for Solid Oxide Fuel Cells)

Abstract

:
Triple perovskite has been recently developed for the intermediate temperature solid oxide fuel cell (IT-SOFC). The performance of Nd1.5Ba1.5CoFeMnO9−δ (NBCFM) cathodes for IT-SOFC is investigated in this work. The interfacial polarization resistance (RP) of NBCFM is 1.1273 Ω cm2~0.1587 Ω cm2 in the range of 700–800 °C, showing good electrochemical performance. The linear thermal expansion coefficient of NBCFM is 17.40 × 10−6 K−1 at 40–800 °C, which is significantly higher than that of the electrolyte. In order to further improve the electrochemical performance and reduce the thermal expansion coefficient (TEC) of NBCFM, Ce0.8Sm0.2O2−δ (SDC) is mixed with NBCFM to prepare an NBCFM-xSDC composite cathode (x = 0, 10, 20, 30, 40 wt.%). The thermal expansion coefficient decreases monotonically from 17.40 × 10−6 K−1 to 15.25 × 10−6 K−1. The surface oxygen exchange coefficient of NBCFM-xSDC at a given temperature increases from 10−4 to 10−3 cm s−1 over the p o 2 range from 0.01 to 0.09 atm, exhibiting fast surface exchange kinetics. The area specific resistance (ASR) of NBCFM-30%SDC is 0.06575 Ω cm2 at 800 °C, which is only 41% of the ASR value of NBCFM (0.15872 Ω cm2). The outstanding performance indicates the feasibility of NBCFM-30% SDC as an IT-SOFC cathode material. This study provides a promising strategy for designing high-performance composite cathodes for SOFCs based on triple perovskite structures.

1. Introduction

The solid oxide fuel cell (SOFC) has attracted much attention for its low pollutant emission and fuel flexibility in an attempt to effectively solve the energy crisis and environmental problems [1,2,3,4]. However, the high operating temperature has restricted the choice of available materials and affects the chemical stability and durability of cell components. In the past decade, developing IT-SOFCs with high power density and long-term stability has become one of the main research directions of SOFC [5,6]. One of the critical challenges is to develop cell components with low ohmic and polarization losses to reduce the cell resistivity and enhance the electrochemical performance at relative lower temperature [7,8,9]. It is recognized that polarization losses of the cell mainly result from the cathode. The cathode material should have high oxygen transport capacity, high electro-catalytic activity, and good compatibility with the electrolyte.
Recently, a family of oxides such as AA’Co2O5+δ (A = RE and A’ = Ba, Sr) with layered or double perovskite-type structures has received widespread attention for its potential application in IT-SOFC cathodes [10]. In the A-site Ln3+ and Ba2+ cation-ordered LnBaCo2O5+δ, oxygen atoms can be partially or entirely removed from the lanthanide planes, significantly enhancing the diffusivity of oxide ions in the bulk and possibly supplying surface defect sites [11]. This family of oxides shows excellent ion transport properties and surface exchange kinetics and high electrical conductivity [12,13,14,15,16,17,18].
However, the thermal expansion coefficient (TEC) of LnBaCo2O5+δ is too high to match with that of YSZ ((Y2O3)0.08-(ZrO2)0.92) or CeO2-based electrolytes (10~12 × 10−6 K−1) [19]. The mismatch between the cathode and electrolyte may trigger the cracking and delamination of cathode in the thermal cycling process, which is detrimental to the properties of SOFCs. The high TEC of LnBaCo2O5+δ is related to the change of the electron-filling state of Co3+. This drawback can be minimized by substituting of the Co with transition-metal ions such as Fe, Mn, or Ni [20,21,22]. In addition, electrolyte materials as the second phase are often introduced to form composite cathodes, which can effectively reduce the TEC of the electrode, enlarge the electrochemically active area, and improve the electrode performance. For example, the area specific resistance (ASR) of LaBaCo2O5+δ-50%SDC was 0.052 Ω cm2 at 700 °C, which was less than the ASR of LBCO (0.3 Ω cm2 at 700 °C) [23]. The polarization resistance (RP) of SmBaCoCuO5+δ-50%GDC cathode was about seven times smaller than that of SmBaCoCuO5+δ at 750 °C [24]. The microtubular solid oxide fuel cells with a 50vol%NdSrCo2O5+δ-50vol%GDC composite cathode presented good electrochemical performances. The cell RP was 0.03 Ω cm2 at 800 °C, and the maximum power density was 0.67 W cm−2 [25].
The introduction of different cations and the ordering of the cations in the octahedral sites of the layered perovskite lead to a complex triple perovskite (A2A′B2B′O9) [26,27,28]. Nam-In Kim [29] studied Nd1.5Ba1.5CoFeMnO9−δ (NBCFM) as a highly active and durable oxygen electrode catalyst for the oxygen evolution reaction (OER) and the oxygen reduction reaction (ORR). The NBCFM structure is generated by stacking three single perovskites. The nonstoichiometry δ value for NBCFM is 0.495, calculated from the cobalt oxidation state by using the iodometric titration method. These characteristics thus inspired us to extend our work to the practical application of NBCFM for an SOFC cathode to promote the development of SOFC.
Herein, Nd1.5Ba1.5CoFeMnO9−δ (NBCFM) was synthesized by the glycine-nitrate process. The structure, thermal expansion behavior, and electrochemical performances of NBCFM were characterized. In order to overcome the thermal mismatching between the electrode and electrolyte and improve the electrochemical performance, SDC was added to NBCFM to prepare NBCFM-xSDC (x = 10, 20, 30 and 40 wt.%) composite cathodes. The structure, chemical compatibility, electrical conductivity, TEC, and oxygen surface exchange of these composite materials were investigated, and the electrochemical performance of NBCFM-xSDC as cathodes for IT-SOFC applications was evaluated.

2. Materials and Methods

2.1. Cathode Powder Synthesis

NBCFM powder was prepared by the glycine-nitrate process (GNP). A certain amount of metal nitrate precursors, Nd(NO3)3·6H2O (Aladdin Reagent Co., Ltd., AR., Shanghai, China), Ba(NO3)2 (China National Pharmaceutical Group Co., AR., Shenzhen, China), Co(NO3)3·6H2O (Aladdin Reagent Co., Ltd., AR. Shanghai, China), Fe(NO3)3·9H2O (Aladdin Reagent Co., Ltd., AR. Shanghai, China), Mn (NO3)3 (China National Pharmaceutical Group Co., AR. Shenzhen, China), and glycine (China National Pharmaceutical Group Co., AR. Shenzhen, China), were solubilized in deionized water. The molar ratio of metal ions to glycine was 1:2.5. The mixture solution was stirred and heated at 80 °C continuously until a homogeneous gel was formed. Then, the gel was heated continuously and ignited spontaneously. The precursor powder was calcined at 1200 °C for 2 h in the air. Ce0.8Sm0.2O1.9 (SDC) powder was also prepared by GNP with a molar ratio of metal ions to glycine of 1:1.8. The precursor powder was calcined at 700 °C for 2 h. The NBCFM-xSDC (x = 10, 20, 30 and 40 wt.%) powders were prepared by mixing SDC and NBCFM and grinding thoroughly for 2 h. The samples were denoted as NBCFM-10%SDC, NBCFM-20%SDC, NBCFM-30%SDC, and NBCFM-40%SDC, respectively.

2.2. Cell Fabrication

SDC electrolyte was prepared by pressing 0.6 g SDC powder into a pellet at 220 MPa. Then, the green pellet (φ = 10 mm) was calcined at 1400 °C for 6 h in air. The cathode slurry containing the prepared NBCFM-xSDC powder, terpineol, and ethyl cellulose was brushed on both sides of the SDC electrolyte and calcined at 1050 °C for 2 h. The final surface area of the symmetrical cell with the configuration of cathode/SDC/cathode was about 0.56 cm2. The half-cell with Ni-YSZ/YSZ/GDC was fabricated by the tape casting method, and the NBCFM-xSDC slurry was deposited onto the electrolyte film by a brush painting method, followed by firing at 1050 °C for 2 h. The anode-supported single cell with an active area of 0.28 cm2 for current-voltage (I-V) tests had the configuration of Ni-YSZ/YSZ/GDC/NBCFM-xSDC.

2.3. Characterization and Electrochemical Performance Test

The crystal structure was determined by X-ray diffraction (XRD, Rigaku Smartlab, Irvine, CA, USA) on Cu Kα radiation (λ = 1.5148 Å) with a step width of 0.02° and a scan range of 20°–80° at room temperature. The morphology of the sample and the interface contact between cathode and electrolyte were observed by a scanning electron microscope (SEM, ZEISS Sigma 300, Kino, Germany).
NBCFM and NBCFM-xSDC cathode powder were pressed into rods (64 mm × 3 mm × 5 mm) at the pressure of 100 MPa and sintered at 1150 °C for the measurement of the electrical conductivity and thermal expansion coefficient. The electrical conductivity was tested by a standard direct current (DC) four-terminal probe method in the temperature range of 450–800 °C in air. The oxygen diffusion behavior of NBCFM-xSDC was determined by the electrical conductivity relaxation (ECR) technique. When the oxygen pressure changed momentarily at a certain temperature, the corresponding conductivity of the material would also change to a new equilibrium. The oxygen partial pressure changed from 0.1 to 0.9 atm, and the flowing gas was kept at 50 mL min−1 for the ECR measurement. The data were recorded every three seconds and estimated by the least-squares model. TEC was measured in air from 40 to 800 °C by using a high-temperature thermal dilatometer (DIL 402PC NETZSCH, Selb, Germany). The electrochemical impedance spectroscopy was performed using an electrochemical analyzer (PARSTAT 227, AMETEK, Berwyn, IL, USA) in the temperature range of 500 °C–800 °C. Platinum wires were used to collect the current. The frequency range was 0.1 Hz–100 kHz, and the amplitude of the AC signal was 20 mV. The single cell performance was evaluated with hydrogen (97% H2/3% H2O) as fuel and ambient air as oxidant in 650–800 °C by an electrochemical workstation (RTS-8, Tianjin Nuoxinda Technology Co., Ltd., Tianjin, China).

3. Result and Discussion

3.1. Crystal Structure and Cathode Performance of NBCFM

NBCFM structure was determined by the X-ray powder diffraction technique. The XRD patterns of NBCFM and SDC can be indexed as perovskite and fluorite structures with a space group of P4/mmm and Fm–3m, respectively (Figure 1a). The visualized crystal structure of the triple perovskite NBCFM is shown in Figure 1b. The lattice parameters of NBCFM and SDC are listed in Table 1.
The thermal expansion coefficient is an essential parameter for SOFC components. The mismatch of TEC between cathode and electrolyte can induce obvious strain during thermal cycling and lead to the cracking and delamination of the components. Figure 1c shows the thermal expansion curves of NBCFM cathode. The TEC value of NBCFM is 17.40 × 10−6 K−1, which is different from the TEC values of common electrolytes for IT-SOFC.
The electrochemical properties of NBCFM are studied by Electrochemical Impedance Spectroscopy (EIS). The EIS results of NBCFM in the temperature range of 650–800 °C are shown in Figure 1d. To clearly display the electrode polarization response, the ohmic response of the electrolyte and wire is returned to zero. The difference between intercepts of the high-frequency arc and low-frequency arc with the real axis corresponds to the interfacial polarization resistance (RP), which reflects the rate of oxygen reduction reaction (ORR). The RP values of NBCFM are 0.1587 Ω cm2, 0.7239 Ω cm2, and 1.1273 Ω cm2 at 800 °C, 750 °C, and 700 °C, respectively. With the increase of temperature, the RP of NBCFM decreases and the oxygen reduction reaction accelerates. At 800 °C, NBCFM exhibits low polarization loss, which can be attributed to its oxygen vacancy-rich structure. At high temperature, the increase of oxygen vacancy concentration is beneficial for the oxygen ion transport. This leads to the reduction of the polarization loss.
According to the above study, triple perovskite NBCFM exhibited relatively excellent electrochemical performance, but it still has a certain gap with the TEC of SDC electrolyte. To surmount this limitation, SDC was introduced to the NBCFM cathode to improve the thermal suitability of the cell’s module and extend the triple phase boundary (TPB) length.

3.2. Chemical Compatibility and Thermal Expansion Matching

The NBCFM and SDC powers were mixed and co-calcined at 1000 °C for 4 h to identify the chemical compatibility. The phase composition of NBCFM-xSDC was analyzed by XRD. Figure 2a shows the XRD patterns of NBCFM, SDC, and NBCFM-xSDC. All diffraction peaks of the composite cathodes could be indexed well based on triple perovskite NBCFM and fluorite SDC phases, suggesting that no observable reaction is detected in the binary-mixed NBCFM-SDC systems.
Figure 2b shows the thermal expansion curves of NBCFM-xSDC composites and SDC between 40 and 750 °C. The TEC values are inserted in the figure. As expected, the TEC of the composite cathode decreases with the increasing of SDC content because of the lower TEC of SDC. The TEC values of NBCFM-30%SDC and NBCFM-40%SDC composite cathodes are 15.36 and 15.25 × 10−6 K−1, respectively, which are significantly lower than the TEC of NBCFM cathode. Despite the fact that the TEC value of NBCFM-xSDC is higher than that of SDC (~12.44 × 10−6 K−1), it is much lower than those of cobalt-containing cathodes, such as PrBa0.5Sr0.5Co2−xFexO5+δ (x = 0.5, 1.0, 1.5, TEC = 19.2~21.3 × 10−6 K−1) [30] and PrBaCo1.9Ni0.1O5+δ-xSDC (x = 0, 10, 20, 30, 40 wt.%, TEC = 17.5~22.63 × 10−6 K−1) [31]. The decreases in TEC values can enhance the interface compatibility between the cathode and electrolyte and consequently improve the long-term stability.

3.3. Electrical Conductivity

Figure 3a shows the temperature dependence of the electrical conductivity of NBCFM-xSDC composite cathodes in 450–800 °C. The Arrhenius plots of the total conductivity for NBCFM-xSDC are presented in Figure 3b, which shows a linear relationship between ln(σT) and 1000/T. Because the mobility of electrons is much faster than oxygen ions, the electrical conductivity of NBCFM and NBCFM-xSDC is mainly dominated by electronic conductivity. The conductivity of NBCFM increases with the rising temperature and reaches the maximum (36.51 S·cm−1) at 800 °C, indicating a typical semiconductor behavior. This behavior can be ascribed to electron hopping under thermal activation. For the perovskite materials containing cobalt, the electron conduction is mainly generated by electron hopping between Co3+/Co4+. The increase in temperature provides more energy for electron hopping and promotes carrier migration. However, the electrical conductivity of NBCFM-xSDC decreases with the increase of SDC content. In fluorite SDC, doping Ce4+ by Sm3+ leads to the formation of oxygen vacancies. The ions migrate rapidly via oxygen vacancies, meaning that the SDC exhibits high ionic conductivity. However, the oxygen vacancies take a disadvantage to the migration of carriers and disturb the (Co, Fe, Mn)-O-(Co, Fe, Mn) periodic potential, resulting in the localization of carriers and the decrease of electronic conductivity [32]. On the other hand, the conductivity of all NBCFM-xSDC is lower than that of NBCFM, related to the obstruction of contact between NBCFM particles by SDC particles. The path length of electron migration increases in the composite cathode, leading to a decrease in electron conductivity.
The activation energy for the migration of carrier (Ea) can be calculated by Arrhenius Equation (1):
σ = ( A T ) exp ( E a k T )
where A is the pre-exponential factor and k is the Boltzmann’s constant. The Ea values of NBCFM-xSDC are shown in Figure 3b. The activation energy increases with the increase of SDC content. With the addition of SDC, the conductivity activation energy of the NBCFM-xSDC cathodes increases from 1.55 to 3.18 eV. The conductivity activation energy of NBCFM-40%SDC is 1.7 times higher than that of NBCFM.

3.4. Oxygen Surface Exchange Process

The ORR catalytic activity of mixed ionic–electronic conductors depends on two oxygen diffusion kinetic processes: one is the surface oxygen exchange process, and the other is the oxygen ion diffusion process. Oxygen diffusion kinetics works like a key to the catalytic activity of ORR and the oxygen ionic conductivity. The electrical conductivity relaxation (ECR) technique was utilized to characterize the oxygen diffusion behavior. For the samples with dimensions 2l1 × 2l2 × 2l3 (6 mm × 2 mm × 64 mm), the length is far larger than the width and height. The relationship between relative conductivity f(t) and time (t) is given by Equation (2) [33]:
1 f ( t ) = 1 σ t σ 0 σ σ 0 = i = 1 n = 1 m = 1 2 C 1 2 exp ( β i 2 D 0 t l 1 2 ) β i 2 ( β i 2 + C 1 2 + C 1 ) × 2 C 2 2 exp ( γ n 2 D 0 t l 2 2 ) γ n 2 ( γ n 2 + C 2 2 + C 2 ) × 2 C 3 2 exp ( δ m 2 D 0 t l 3 2 ) δ m 2 ( δ m 2 + C 3 2 + C 3 ) ,
where σt, σ0, and σ represent the time-dependent, initial, and final conductivities, respectively. Cx is defined as the ratio of the half thickness to the characteristic length of the sample, ld.
C x = l x l d ,
l d = D 0 k c h e m ,
The coefficients βi, γn, and δm are the nonzero root of the transcendental equation:
β i tan β i = C 1 ,     γ n tan γ n = C 2 ,     δ m tan δ m = C 3 ,
The oxygen transport of the sample is entirely controlled by the surface exchange process when Cx in Equation (3) tends to zero. This indicates that the surface exchange process of the sample is much slower than the diffusion in the bulk phase. When the dimensions of the sample in one dimension (l3) are much longer than the other dimensions (l1, l2), the oxygen exchange process is mainly considered in the direction of the smaller dimension. In the smaller dimensional direction, the diffusion process can be ignored, and the oxygen exchange process is dominant since the diffusion path of oxygen is very short. At this time, Equation (2) can be simplified to an analytic function containing only the exchange coefficients:
1 σ t σ 0 σ σ 0 = exp ( k c h e m t ( l 1 1 + l 2 1 ) 1 ) ,
The changing of the external atmosphere has a specific effect on the concentration of internal oxygen vacancies for mixed conductor oxide. This change in the oxygen vacancy concentration will affect its electrical properties, which is the basis for the electrical conductivity relaxation test. Figure 4 shows the conductivity test results of NBCFM-10%SDC under nitrogen, air, and oxygen atmospheres. In the whole test temperature range, the conductivity in the nitrogen atmosphere is significantly lower than that in air and oxygen atmospheres. The defect response that occurs during the test can be described by Equation (7).
O O × + 2 h · 1 2 O 2 ( g ) + V O · · ,
The ambient oxygen partial pressures are different in the three test atmospheres. To balance the lower oxygen partial pressure in a nitrogen atmosphere, the reaction moves to the right. The surface oxygen escapes from the lattice with a decrease in electron holes and an increase in oxygen vacancies, resulting in the ionic conductivity increasing and the electronic conductivity decreasing. Similarly, the reaction moves to the left under the oxygen atmosphere. The increase of electron holes and the reduction of oxygen vacancies increase the electronic conductivity and decrease the ionic conductivity. Although the contribution of ionic conductivity increases in the medium and high temperature stages, the electronic conductance still dominates. The apparent total conductivity is σ(O2) > σ(Air) > σ(N2). Therefore, it can be seen that changes in the external environment of NBCFM-xSDC can certainly have some effect on its internal oxygen defect concentration.
In order to study the effect of SDC content on the surface kinetics process, the surface exchange coefficient (kchem) is measured by the ECR method. Figure 5 shows the conductivity relaxation plots for NBCFM-xSDC in the temperature range of 700–800 °C. It can be seen that the trend of the curve changes from steep to flat as the oxygen partial pressure changes from 0.1 to 0.9 atm. This dynamic equilibrium process reflects the change of the oxygen vacancy concentration. The equilibrium time gradually decreases with the increase of testing temperature because ions gain more energy to move by thermal excitation. The calculated kchem values of NBCFM-xSDC are presented in Figure 5, where the decrease of the surface exchange coefficient with increasing SDC content can be observed. NBCFM-10%SDC has a maximum kchem of 4.4507 × 10−3 cm s−1 at 800 °C, which is higher than that of other composite cathodes, as given in Figure 5e. The surface exchange process usually includes oxygen absorption, dissociation, and reduction at the surface, and oxygen ions move into the cathode. As the ionic conductor content increases, the electron transport distance becomes longer and the concentration of surface electron reduces, resulting in a slower oxygen reduction process on the surface. In addition, the ionic potentials of samarium (Sm3+~1.410) and cerium (Ce4+~1.608) ions are stronger than those of neodymium (Nd3+~1.382), Ba2+~1.126, Co2+~1.377 (LS), Fe2+~1.390 (LS), or Mn2+~1.343 (LS) [34] ions. Elements with higher ionic potential are more strongly bound to oxygen; thus, in NBCFM-xSDC with higher SDC content, oxygen escape is more difficult, and a lower surface exchange coefficient kchem is exhibited. In addition, more energy is required for the ions to jump between the two-phase interfaces in the composite cathode. As the second phase content increases, the ion transport distance becomes longer and the concentration of surface oxygen reduces, leading to a slower overall oxygen surface exchange process.

3.5. Electrochemical Performance and the Microstructure

The ORR rate of MIEC materials is affected by the concentration of oxygen vacancies and microstructure. A high vacancy concentration provides more sites for the oxygen incorporation, and the microstructure reflects the length of the TPB. To obtain further information on the ORR catalytic activity of NBCFM-xSDC, the Electrochemical Impedance Spectroscopy (EIS) is fitted by the Zview software using the equivalent circuit L-RΩ (RP1-CPER1)-(RP2-CPER2) [35]. L is the high frequency inductance, which is caused by the cathode system and the lead wire. RΩ is related to the ohmic resistance of the electrolyte. To clearly show the differences in the cathodic polarization behavior, the ohmic resistances measured in this study are normalized to 0 when the electronic conduction in the electrolyte is negligible. RP1-CPER1 and RP2-CPER2 correspond to a high frequency arc and a low frequency arc, respectively. The higher frequency RP1 and the lower frequency RP2 are related to the processes of charge transfer and oxygen diffusion, respectively [36,37]. CPERi is a constant phase component. The total polarization resistance RP is the sum of RP1 and RP2. The area specific resistance (ASR) can be determined by the following relationship: ASR = RP × S/2 [38,39], where S is the electrode surface area.
The impedance spectra for NBCFM-xSDC are shown in Figure 6. The ASR values significantly depend on the relative mass ratio of SDC and NBCFM (Table 2). The NBCFM-30%SDC sample exhibits the lowest ASR values of 0.06575 Ω cm2 at 800 °C. Under SOFC operating conditions, the highly ionic conductive SDC is known to have a good ability to store, release, and transport oxygen. The appropriate amount of SDC can greatly improve the oxygen catalytic activity. The ASR value of NBCFM-30%SDC is only 41% of that of NBCFM. The better performance for NBCFM-xSDC is believed to be due to the good adhesion between the cathode and electrolyte and the faster charge transfer. By introducing SDC as a second phase, the ion diffusion path in the cathodes is shortened, and the TPB areas of the composite electrode are extended. As a result, the distance between oxygen vacancies is reduced and the ionic conductivity is enhanced, thereby increasing the oxygen ion transport capacity. The thermal expansion mismatch of NBCFM-xSDC is also weakened with the increase of SDC content. In conclusion, the improvement in thermal expansion properties and the increase in ionic conductivity enhance the electrochemical properties of NBCFM-xSDC. The ASR value of NBCFM-30%SDC is lower than that of Gd0.8Sr0.2CoO3−δ-20 Sm0.1Ce0.9O1.95 (0.16 Ω cm2 at 750 °C) [38] and YBa0.5Sr0.5Co1.4Cu0.6O5+δ-30%SDC composite cathode (0.034 Ω cm2 at 800 °C) [40]. However, the RP increases when the SDC content is higher than 30 wt.%. The increase of RP can be ascribed to the enlarged electronic transport path and slow surface exchange kinetics. As the SDC content increases, the connectivity of NBCFM particle decreases. The path of electronic transport may be obstructed and the rate of electrochemical reaction decrease, resulting in an increase of RP.
Figure 7a displays the ASR values of NBCFM-xSDC with the temperature, while the ASR values of NBCFM-xSDC as a function of the SDC contents at 750 and 800 °C are also shown in the inset of Figure 7. This shows clearly that the content of SDC has a significant effect on ASR. The ASR values of NBCFM-xSDC composite cathodes decrease at first and then begin to increase with increasing SDC content. Figure 7b shows the Arrhenius plots of RP values as a function of temperature, and the activation energy is calculated from the slope of the curves. It can be observed that RP of NBCFM-xSDC has a linear behavior with temperature. All the composites have a lower activation energy than NBCFM, suggesting that the incorporation of SDC into NBCFM can effectively lower the barrier for cathode reaction and improve the electrochemical performance of the cells. The result also shows that the composite incorporated with 30 wt.% SDC exhibits optimal performance in the present experiment. In order to examine NBCFM-30%SDC stability in operating conditions, the ASRs of a symmetric cell were periodically measured at 750 °C in air. As can be seen in Figure 8, the cell shows a fairly stable performance without any detectable degradation for 33 h.
NBCFM-30%SDC composite oxide is evaluated as a cathode material due to its relatively lower TEC values and polarization resistance. The anode-supported single cell with the configuration of Ni-YSZ/YSZ/GDC/NBCFM-30%SDC (or NBCFM) is constructed, and the cell performance is shown in Figure 9. The power density increases with the increase of operating temperature. The peak power densities (PPDs) of the cell using NBCFM as a cathode were 451.03 mW cm−2, 570.34 mW cm−2, and 757.79 mW cm−2 at 700 °C, 750 °C, and 800 °C, respectively. Furthermore, the PPDs of the single cells using NBCFM-30%SDC as a cathode were 556.76 mW cm−2, 670.75 mW cm−2, and 792.56 mW cm−2 at 700 °C, 750 °C, and 800 °C, respectively. The NBCFM-30%SDC cathode showed better cell performance, which is consistent with the ASR results. It is believed that the SDC-matched TEC and low ASR value of NBCFM-30%SDC make a great contribution to high power density.
The SEM images of NBCFM-30%SDC are shown in Figure 10. The coarse and fine particles can be observed in the cross-sectional images of the composite cathodes, where the smaller particles are in the SDC phase. It can be seen that the good contact between the porous NBCFM-30%SDC cathodes and the dense SDC electrolyte layers ensures the low cathode/electrolyte interface resistances in the NBCFM-30%SDC/SDC/NBCFM-30%SDC symmetrical cell. The uniform and continuous distribution of ionic conductors leads to better oxygen ions diffusion for the ORR, resulting in the good electrochemical performance of NBCFM-30%SDC cells.

4. Conclusions

In this work, triple perovskite Nd1.5Ba1.5CoFeMnO9−δ and a series of NBCFM-xSDC composite cathodes were successfully prepared, and their feasibility as SOFC cathodes was evaluated. The NBCFM with high oxygen vacancies had low polarization impedance, exhibiting good electrochemical catalytic performance. The power density of a single cell using NBCFM as a cathode was 757.79 mW cm−2 at 800 °C. NBCFM-xSDC had good chemical stability because NBCFM oxide had good chemical compatibility with SDC. Electrical conductivities and TECs decreased monotonously with increasing SDC content. The TEC decreased from 17.40 × 10−6 K−1 for NBCFM to 15.25 × 10−6 K−1 for NBCFM-40%SDC. However, the conductivity values of the NBCFM-xSDC cathode are not extraordinary and still need to be improved. The ECR results showed that the oxygen surface exchange rate of NBCFM-xSDC slowed down with increasing SDC content, and its surface oxygen exchange coefficients were within the range of 10−4 to 10−3 cm s−1 at the tested temperature. Among composite cathodes, the NBCFM-30%SDC exhibited the lowest polarization resistance. The maximum power density of NBCFM-30%SDC based on an anode-supported single cell achieved 792.56 mW cm−2 at 800 °C. The result indicates that NBCFM-30%SDC is a promising cathode material for SOFC application.

Author Contributions

Conceptualization, H.Z.; methodology, Y.C.; software, Y.C.; validation, Y.C. and T.Y.; formal analysis, T.Y. and J.J.; investigation, Y.C.; resources, J.J.; data curation, Y.C. and T.Y.; writing—original draft preparation, Y.C.; writing—review and editing, H.Z.; visualization, J.J.; supervision, J.J. and H.Z.; project administration, J.J. and H.Z.; funding acquisition, J.J. and H.Z. All authors have read and agreed to the published version of the manuscript.

Funding

This work has received financial support from Priority Academic Program Development of Jiangsu Higher Education Institutions (PAPD).

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

All data that support the findings of this study are included within the article.

Acknowledgments

This work was financially supported by Priority Academic Program Development of Jiangsu Higher Education Institutions (PAPD).

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Ndubuisi, A.; Abouali, S.; Singh, K.; Thangadurai, V. Recent advances, practical challenges, and perspectives of intermediate temperature solid oxide fuel cell cathodes. J. Mater. Chem. A 2022, 10, 2196–2227. [Google Scholar] [CrossRef]
  2. Abd Aziz, A.J.; Baharuddin, N.A.; Somalu, M.R.; Muchtar, A. Review of composite cathodes for intermediate-temperature solid oxide fuel cell applications. Ceram. Int. 2020, 46, 23314–23325. [Google Scholar] [CrossRef]
  3. Eftekhari, A.; Fang, B. Electrochemical hydrogen storage: Opportunities for fuel storage, batteries, fuel cells, and supercapacitors. Int. J. Hydrogen Energy 2017, 42, 25143–25165. [Google Scholar] [CrossRef]
  4. Shen, M.; Ai, F.; Ma, H.; Xu, H.; Zhang, Y. Progress and prospects of reversible solid oxide fuel cell materials. iScience 2021, 24, 103464. [Google Scholar] [CrossRef]
  5. Fallah Vostakola, M.; Amini Horri, B. Progress in material development for low-temperature solid oxide fuel cells: A review. Energies 2021, 14, 1280. [Google Scholar] [CrossRef]
  6. Bello, I.T.; Zhai, S.; He, Q.; Xu, Q.; Ni, M. Scientometric review of advancements in the development of high-performance cathode for low and intermediate temperature solid oxide fuel cells: Three decades in retrospect. Int. J. Hydrogen Energy 2021, 46, 26518–26536. [Google Scholar] [CrossRef]
  7. Kaur, P.; Singh, K. Review of perovskite-structure related cathode materials for solid oxide fuel cells. Ceram. Int. 2020, 46, 5521–5535. [Google Scholar] [CrossRef]
  8. Azad, A.K.; Kim, J.H.; Irvine, J.T.S. Structural, electrochemical and magnetic characterization of the layered-type PrBa0.5Sr0.5Co2O5+δ perovskite. J. Solid State Chem. 2014, 213, 268–274. [Google Scholar] [CrossRef] [Green Version]
  9. Shao, Z.; Tade, M.O. Intermediate-temperature solid oxide fuel cells. Chem. Soc. Rev. 2016, 37, 1568. [Google Scholar]
  10. Klyndyuk, A.I.; Chizhova, E.A.; Kharytonau, D.S.; Medvedev, D.A. Layered oxygen-deficient double perovskites as promising cathode materials for solid oxide fuel cells. Materials 2021, 15, 141. [Google Scholar] [CrossRef]
  11. Maignan, A.; Martin, C.; Pelloquin, D.; Nguyen, N.; Raveau, B. Structural and magnetic studies of ordered oxygen-deficient perovskites LnBaCo2O5+δ, closely related to the “112” structure. J. Solid State Chem. 1999, 142, 247–260. [Google Scholar] [CrossRef]
  12. Kim, J.H.; Mogni, L.; Prado, F.; Caneiro, A.; Alonso, J.A.; Manthiram, A. High temperature crystal chemistry and oxygen permeation properties of the mixed ionic–electronic conductors LnBaCo2O5+δ(Ln=Lanthanide). J. Electrochem. Soc. 2009, 156, B1376–B1382. [Google Scholar] [CrossRef]
  13. Wang, H.; Lei, Z.; Jing, J.; Xu, X.; Jiang, W.; Yang, Z.; Peng, S. Evaluation of NdBaCo2O5+δ oxygen electrode combined with negative expansion material for reversible solid oxide cells. J. Eur. Ceram. Soc. 2022, 42, 4259–4265. [Google Scholar] [CrossRef]
  14. Zhao, L.; Shen, J.; He, B.; Chen, F.; Xia, C. Synthesis, characterization and evaluation of PrBaCo2−xFexO5+δ as cathodes for intermediate-temperature solid oxide fuel cells. Int. J. Hydrogen Energy 2011, 36, 3658–3665. [Google Scholar] [CrossRef]
  15. Seymour, I.D.; Tarancón, A.; Chroneos, A.; Parfitt, D.; Kilner, J.A.; Grimes, R.W. Anisotropic oxygen diffusion in PrBaCo2O5.5 double perovskites. Solid State Commun. 2012, 216, 41–43. [Google Scholar] [CrossRef]
  16. Parfitt, D.; Chroneos, A.; Tarancón, A.; Kilner, J.A. Oxygen ion diffusion in cation ordered/disordered GdBaCo2O5+δ. J. Mater. Chem. 2011, 21, 2183–2186. [Google Scholar] [CrossRef]
  17. Anjum, U.; Agarwal, M.; Khan, T.S.; Prateek; Gupta, R.K.; Haider, M.A. Controlling surface cation segregation in a nanostructured double perovskite GdBaCo2O5+δ electrode for solid oxide fuel cells. Nanoscale 2019, 11, 21404–21418. [Google Scholar] [CrossRef]
  18. Wei, B.; Schroeder, M.; Martin, M. Surface cation segregation and chromium deposition on the double-perovskite oxide PrBaCo2O5+δ. ACS Appl. Mater. Inter. 2018, 10, 8621–8629. [Google Scholar] [CrossRef]
  19. Jun, A.; Kim, J.; Shin, J.; Kim, G. Perovskite as a cathode material: A review of its role in solid-oxide fuel cell technology. ChemElectroChem 2016, 3, 511–530. [Google Scholar] [CrossRef]
  20. Kim, Y.N.; Kim, J.H.; Manthiram, A. Effect of Fe substitution on the structure and properties of LnBaCo2−xFexO5+δ (Ln=Nd and Gd) cathodes. J. Power Sources 2010, 195, 6411–6419. [Google Scholar] [CrossRef]
  21. Che, X.; Shen, Y.; Li, H.; He, T. Assessment of LnBaCo1.6Ni0.4O5+δ (Ln=Pr, Nd, and Sm) double-perovskites as cathodes for intermediate-temperature solid-oxide fuel cells. J. Power Sources 2013, 222, 288–293. [Google Scholar] [CrossRef]
  22. Zhang, L.; Chen, G.; Dai, R.; Lv, X.; Yang, D.; Geng, S. A review of the chemical compatibility between oxide electrodes and electrolytes in solid oxide fuel cells. J. Power Sources 2021, 492, 229630. [Google Scholar] [CrossRef]
  23. Gu, H.; Chen, H.; Gao, L.; Guo, L. Electrochemical properties of LaBaCo2O5+δ–Sm0.2Ce0.8O1.9 composite cathodes for intermediate-temperature solid oxide fuel cells. Electrochim. Acta 2009, 54, 7094–7098. [Google Scholar] [CrossRef]
  24. Lü, S.; Meng, X.; Zhang, Y.; Yang, J.; Wei, M.; Liu, Y.; Li, X.; Fu, C.; Ji, Y. Performances of SmBaCoCuO5+δ–Ce0.9Gd0.1O1.95 composite cathodes for intermediate-temperature solid oxide fuel cells. Int. J. Hydrogen Energy 2012, 37, 18319–18325. [Google Scholar] [CrossRef]
  25. Wang, S.-F.; Hsu, Y.-F.; Liao, Y.-L.; Huang, S.-T.; Jasinski, P. High-performance NdSrCo2O5+δ–Ce0.8Gd0.2O2−δ composite cathodes for electrolyte-supported microtubular solid oxide fuel cells. Int. J. Hydrogen Energy 2021, 46, 31778–31787. [Google Scholar] [CrossRef]
  26. Casallas-Caicedo, F.M.; Vera-López, E.; Roa-Rojas, J. Impedance spectroscopy study of electrical response and correlation with structural properties in the La2SrFe2CoO9 triple complex perovskite. Phys. B 2021, 607, 412865. [Google Scholar] [CrossRef]
  27. Hodgkins, T.L.; Savory, C.N.; Bass, K.K.; Seckman, B.L.; Scanlon, D.O.; Djurovich, P.I.; Thompson, M.E.; Melot, B.C. Anionic order and band gap engineering in vacancy ordered triple perovskites. Chem. Commun. 2019, 55, 3164–3167. [Google Scholar] [CrossRef] [Green Version]
  28. Tomar, A.K.; Joshi, A.; Singh, G.; Sharma, R.K. Triple perovskite oxide as an advanced pseudocapacitive material: Multifarious element approach with an ordered structure. J. Mater. Chem. A 2020, 8, 24013–24023. [Google Scholar] [CrossRef]
  29. Kim, N.-I.; Sa Young, J.; Yoo Tae, S.; Choi Sung, R.; Afzal Rana, A.; Choi, T.; Seo, Y.-S.; Lee, K.-S.; Hwang Jun, Y.; Choi Woo, S.; et al. Oxygen-deficient triple perovskites as highly active and durable bifunctional electrocatalysts for oxygen electrode reactions. Sci. Adv. 2018, 4, eaap9360. [Google Scholar] [CrossRef] [Green Version]
  30. Jiang, L.; Wei, T.; Zeng, R.; Zhang, W.-X.; Huang, Y.-H. Thermal and electrochemical properties of PrBa0.5Sr0.5Co2−xFexO5+δ (x=0.5, 1.0, 1.5) cathode materials for solid-oxide fuel cells. J. Power Sources 2013, 232, 279–285. [Google Scholar] [CrossRef]
  31. Guo, W.; Guo, R.; Cai, G.; Wu, C.; Liu, Z. Preparation and characterization of PrBaCo1.9Ni0.1O5–Ce0.8Sm0.2O1.9 composite cathodes for intermediate temperature solid oxide fuel cells. Solid State Ion. 2015, 283, 10–15. [Google Scholar] [CrossRef]
  32. Lee, K.T.; Manthiram, A. Comparison of Ln0.6Sr0.4CoO3−δ (Ln=La, Pr, Nd, Sm, and Gd) as Cathode Materials for Intermediate Temperature Solid Oxide Fuel Cells. J. Electrochem. Soc. 2006, 153, A794. [Google Scholar] [CrossRef]
  33. Zhang, H.; Zhao, L.; Jian, B.; Jin, J.; Zhang, H. Oxygen diffusion and electrochemical performance of La0.6−xSr0.4BaxCo1−yFeyO3−δ. J. Mater. Sci. Mater. Electron. 2019, 30, 20050–20057. [Google Scholar] [CrossRef]
  34. Li, K.; Xue, D. Estimation of electronegativity values of elements in different valence states. J. Phys. Chem. A 2006, 110, 11332–11337. [Google Scholar] [CrossRef] [PubMed]
  35. Jørgensen, M.; Primdahl, S.; Mogensen, M. Characterisation of Composite SOFC Cathodes Using Electrochemical Impedance Spectroscopy. Electrochim. Acta 1999, 44, 4195–4201. [Google Scholar] [CrossRef]
  36. Kawada, T.; Suzuki, J.; Sase, M.; Kaimai, A.; Yashiro, K.; Nigara, Y.; Mizusaki, J.; Kawamura, K.; Yugami, H. Determination of Oxygen Vacancy Concentration in a Thin Film of La0.6Sr0.4CoO3−δ by an Electrochemical Method. J. Electrochem. Soc. 2002, 149, E252. [Google Scholar] [CrossRef]
  37. Baumann, F.S.; Fleig, J.r.; Konuma, M.; Starke, U.; Habermeier, H.-U.; Maier, J. Strong Performance Improvement of La0.6Sr0.4Co0.8Fe0.2O3−δ SOFC Cathodes by Electrochemical Activation. J. Electrochem. Soc. 2005, 152, A2074. [Google Scholar] [CrossRef]
  38. Ji, Y.; Wang, H.; Zhang, H. Gd0.8Sr0.2CoO3−δ–Sm0.1Ce0.9O1.95 composite cathode for intermediate temperature solid oxide fuel cells. Mater. Res. Bull. 2017, 85, 30–34. [Google Scholar] [CrossRef]
  39. Li, S.; Xia, T.; Li, Q.; Sun, L.; Huo, L.; Zhao, H. A-site Ba-deficiency layered perovskite EuBa1−xCo2O6−δ cathodes for intermediate-temperature solid oxide fuel cells: Electrochemical properties and oxygen reduction reaction kinetics. Int. J. Hydrogen Energy 2017, 42, 24412–24425. [Google Scholar] [CrossRef]
  40. Liu, M.; Fu, X.; Meng, X.; Lü, S.; Ren, S.; Liu, X.; Wang, F.; Fan, H.; Chen, Y.; Wang, L. Enhanced electrochemical performance of the YBa0.5Sr0.5Co1.4Cu0.6O5+δ cathode material by Sm0.2Ce0.8O1.9 incorporation for solid oxide fuel cells application. J. Solgel Sci. Technol. 2020, 96, 742–752. [Google Scholar] [CrossRef]
Figure 1. (a) X-ray patterns of SDC and NBCFM; (b) NBCFM crystal structure, (c) thermal expansion curves, and (d) impedance spectra at 650–800 °C of NBCFM; inset is the enlarged impedance spectra at 750 °C and 800 °C.
Figure 1. (a) X-ray patterns of SDC and NBCFM; (b) NBCFM crystal structure, (c) thermal expansion curves, and (d) impedance spectra at 650–800 °C of NBCFM; inset is the enlarged impedance spectra at 750 °C and 800 °C.
Materials 15 03663 g001
Figure 2. (a) The XRD profiles of the SDC, NBCFM, and NBCFM-xSDC powders after calcination at 1000 °C; (b) thermal expansion curves of SDC, NBCFM, and composite cathodes.
Figure 2. (a) The XRD profiles of the SDC, NBCFM, and NBCFM-xSDC powders after calcination at 1000 °C; (b) thermal expansion curves of SDC, NBCFM, and composite cathodes.
Materials 15 03663 g002
Figure 3. (a) Temperature dependence and (b) Arrhenius plots of the electrical conductivity for NBCFM and NBCFM-xSDC.
Figure 3. (a) Temperature dependence and (b) Arrhenius plots of the electrical conductivity for NBCFM and NBCFM-xSDC.
Materials 15 03663 g003
Figure 4. (a) Conductivity and (b) Arrhenius plots of the electrical conductivity for NBCFM-10%SDC at different temperatures (500–800 °C) in different atmospheres.
Figure 4. (a) Conductivity and (b) Arrhenius plots of the electrical conductivity for NBCFM-10%SDC at different temperatures (500–800 °C) in different atmospheres.
Materials 15 03663 g004
Figure 5. Conductivity relaxation plots of (a) NBCFM-10%SDC, (b) NBCFM-20%SDC, (c) NBCFM-30%SDC and (d) NBCFM-40%SDC at 700 °C, 750 °C and 800 °C; variation of (e) kchem of NBCFM-xSDC with SDC content.
Figure 5. Conductivity relaxation plots of (a) NBCFM-10%SDC, (b) NBCFM-20%SDC, (c) NBCFM-30%SDC and (d) NBCFM-40%SDC at 700 °C, 750 °C and 800 °C; variation of (e) kchem of NBCFM-xSDC with SDC content.
Materials 15 03663 g005
Figure 6. Impedance spectra of the NBCFM and composite electrodes at (a) 800 °C and (b) 750 °C.
Figure 6. Impedance spectra of the NBCFM and composite electrodes at (a) 800 °C and (b) 750 °C.
Materials 15 03663 g006
Figure 7. (a) ASR values for NBCFM-xSDC composite cathodes at 600–800 °C in air; inset shows dependence of ASR for NBCFM-xSDC composite cathodes with different SDC contents at 750 °C and 800 °C; (b) Arrhenius plots of the polarization resistance of the NBCFM-xSDC composite cathode materials.
Figure 7. (a) ASR values for NBCFM-xSDC composite cathodes at 600–800 °C in air; inset shows dependence of ASR for NBCFM-xSDC composite cathodes with different SDC contents at 750 °C and 800 °C; (b) Arrhenius plots of the polarization resistance of the NBCFM-xSDC composite cathode materials.
Materials 15 03663 g007
Figure 8. Short-term stability of a symmetric cell at 750 °C in air.
Figure 8. Short-term stability of a symmetric cell at 750 °C in air.
Materials 15 03663 g008
Figure 9. I-V and I-P curves of single cells at different temperatures (700–800 °C) for cathode (a) NBCFM and (b) NBCFM-30%SDC.
Figure 9. I-V and I-P curves of single cells at different temperatures (700–800 °C) for cathode (a) NBCFM and (b) NBCFM-30%SDC.
Materials 15 03663 g009
Figure 10. SEM micrograph interface-view for (a,b) NBCFM-30%SDC/SDC cathodes, and (c) Ni-YSZ/YSZ/GDC/NBCFM-30%SDC single cell after cell test.
Figure 10. SEM micrograph interface-view for (a,b) NBCFM-30%SDC/SDC cathodes, and (c) Ni-YSZ/YSZ/GDC/NBCFM-30%SDC single cell after cell test.
Materials 15 03663 g010
Table 1. The lattice parameters and the unit cell volume.
Table 1. The lattice parameters and the unit cell volume.
NBCFMSDC
Phase structure TetragonalCubic
Space group P4/mmmFm–3m
Lattice parametera (Å)3.88555.411
b (Å)3.88555.411
c (Å)11.68975.411
Unit cell volume (Å3) 176.4807158.428
Table 2. The fitted results of ASR for NBCFM-xSDC composite cathodes measured at 800 °C in air.
Table 2. The fitted results of ASR for NBCFM-xSDC composite cathodes measured at 800 °C in air.
SamplesRP1 (Ω cm2)RP2 (Ω cm2)ASR (Ω cm2)
NBCFM0.10730.05140.1587
NBCFM-10%SDC0.06150.04870.1102
NBCFM-20%SDC0.03230.06400.0963
NBCFM-30%SDC0.02340.04220.0656
NBCFM-40%SDC0.06670.02520.0919
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Chen, Y.; Yu, T.; Jin, J.; Zhang, H. Triple Perovskite Nd1.5Ba1.5CoFeMnO9−δ-Sm0.2Ce0.8O1.9 Composite as Cathodes for the Intermediate Temperature Solid Oxide Fuel Cells. Materials 2022, 15, 3663. https://0-doi-org.brum.beds.ac.uk/10.3390/ma15103663

AMA Style

Chen Y, Yu T, Jin J, Zhang H. Triple Perovskite Nd1.5Ba1.5CoFeMnO9−δ-Sm0.2Ce0.8O1.9 Composite as Cathodes for the Intermediate Temperature Solid Oxide Fuel Cells. Materials. 2022; 15(10):3663. https://0-doi-org.brum.beds.ac.uk/10.3390/ma15103663

Chicago/Turabian Style

Chen, Yunru, Tao Yu, Jiang Jin, and Hua Zhang. 2022. "Triple Perovskite Nd1.5Ba1.5CoFeMnO9−δ-Sm0.2Ce0.8O1.9 Composite as Cathodes for the Intermediate Temperature Solid Oxide Fuel Cells" Materials 15, no. 10: 3663. https://0-doi-org.brum.beds.ac.uk/10.3390/ma15103663

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop