Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Mesoporous Organo-Silica Supported Chromium Oxide Catalyst for Oxidative Dehydrogenation of Ethane to Ethylene with CO2

1
Chemical Engineering Department, King Saud University, Riyadh 11421, Saudi Arabia
2
King Abdullah Institute for Nanotechnology, King Saud University, Riyadh 11451, Saudi Arabia
3
Department of Physics, College of Science, King Saud University, Riyadh 11451, Saudi Arabia
*
Author to whom correspondence should be addressed.
Submission received: 1 April 2021 / Revised: 3 May 2021 / Accepted: 12 May 2021 / Published: 18 May 2021
(This article belongs to the Special Issue Catalytic Applications of Metal or Metal Oxide Nanocomposites)

Abstract

:
Chromium oxide supported on mesoporous organo-silica (MOS) was synthesized with different Cr loading by an incipient method. The catalytic performance of a Cr(x)/MOS catalyst for CO2-based ethane dehydrogenation was investigated. The synthesized catalysts were characterized by XRD, BET, TEM, SEM, XPS, FTIR, and UV–Vis DR measurements. The textural properties of the prepared samples showed that the mesoporous nature of MOS sample was not disturbed by chromium impregnation. Among the prepared samples, Cr(8)/MOS catalyst exhibited good distribution of chromium species along with superior concentration of Cr6+ and the highest recorded Cr6+/Cr3+ ratio. The results revealed that the superior catalytic performance was reached at Cr(8)/MOS, with 50.4% and 90.1% of ethane conversion and ethylene selectivity, respectively. The catalytic activity decreased slowly over reaction time; it declined approximately 22% after 10 h of stream operation. The roles of CO2-based ethane dehydrogenation were also studied, where carbon dioxide can be a source of lattice oxygen and as a hydrogen consumer in reverse water–gas shift (RWGS) reaction. The effect of various catalytic factors, such as catalytic temperature, reaction time, space gas velocity, and CO2 partial pressure on the conversion of ethane, yield, and selectivity to ethylene, were investigated as well.

1. Introduction

Ethane to ethylene-based oxidative dehydrogenation (ODH) by implementing carbon dioxide as an oxidant has received much attention as a replacement to conventional thermal cracking processes and is a path for carbon dioxide utilization [1,2,3,4,5,6]. Among all investigated catalytic systems, chromium oxide supported over silica catalysts exhibits attractive catalytic performances for ODH of ethane with CO2. It has been found that an appropriate distribution of chromium species on the support surface is a basic ingredient to obtain a superior catalytic performance [7,8,9]. High dispersion of chromium species leads to high concentration of reducible Cr species which are supposed to be the active phases for the dehydrogenation of alkane with CO2 [9]. The highly dispersed Cr6+ species fully accessible to the reactant mixture have been recognized to be the active sites for light alkane dehydrogenation [10,11]. Therefore, more notice has been directed recently to siliceous mesoporous sieves, such as MCM-41 [12,13], SBA-15 [8], SBA-1 [7,10], and MSU-x [14,15] as supports for chromium-based catalytic systems. Due to their superior BET-surface areas with uniform pore structure, siliceous mesoporous materials have been extensively investigated as chromium-dispersed materials. MCM14-supported chromium oxide, for instance, has been extensively investigated in the dehydrogenation of alkanes, and it exhibited a high Cr dispersion which was reflected positively on their catalytic performance [12,13,16]. More recently, chromium supported on ZSM-5 was found to be more effective for ethane dehydrogenation. The excellent activity results from the high dispersity and stability of CrOx species on the surface of the investigated support [5].
In 1999, a novel class of siliceous mesoporous materials, known as mesoporous organo-silica (MOS), were developed independently by three research groups: Ozin et al. [17], Inagaki et al. [18], and Stein et al. [19]. MOS is an inorganic–organic hybrid that expands the potential of using regular mesoporous materials as catalysts, adsorbents, trapping agents, etc. [9,10,11,12]. Mesoporous organo-silica is classified according to the kinds of organic groups and their position in the matrix. Terminally bonded and bridge-bonded, and either mono-functional or bifunctional are examples for these kinds of mesoporous materials. The incorporation of organic moieties into mesoporous matrix greatly changes its surface properties, such as hydrophobicity, hydrophilicity, and surface reactivity, in addition to alterations of mechanical or optical properties of these materials [20,21].
The key step of typical MOS synthesis is through the utilization of hydrolysable bridged silsesquioxanes as precursors with the supramolecular templating approach (surfactants). The precursors undergo hydrolysis, followed by poly-condensation of the silica precursors around surfactant micelles, which lead to the formation of the pore wall. Subsequent thermal treatment or extraction of the surfactant liberates the pore voids. The consistent distribution of silicon and organic atoms in the organo-silica precursors is retained in the MOS matrix, so that each individual organic group is covalently bonded to two or more silicon atoms. These bridging organic functionalities are uniformly arranged into internal pore wall as well as their outer surface, which provides them thermal and mechanical stability.
Yamada and co-workers have loaded Au nanoparticles into mesoporous organo-silica, where the developed system revealed an effective catalytic activity towards CO oxidation [22]. Karimi et al. have prepared Pd loaded on mesoporous organo-silica that showed promising efficiency for the Suzuki cross-coupling reaction [23]. The results have shown that Pd/MOS exhibited high stabilization with good selectivity for alcohol oxidation. Additionally, Karimi et al. have utilized allyl imidazolium-based mesoporous organo-silica as supports of Rh metal nanoparticles. The developed catalyst converted the secondary alcohols to the corresponding aldehyde and ketones [24]. Shylesh et al. have prepared a Cr-containing mesoporous organo-silica catalyst that was utilized for the oxidation of cyclohexane [25]. However, to the best of our knowledge, Cr-supported mesoporous organo-silica systems have not been studied for the hydrogenation catalytic reactions so far.
In this work, we have investigated MOS as a support for a chromium-containing catalytic system for ethane dehydrogenation with CO2. A series of Cr(x)/MOS catalysts with different Cr content were synthesized and characterized with different physicochemical techniques. The catalyst behavior in the presence and absence of CO2, and the effect of CO2 partial pressure, were also investigated.

2. Results and Discussion

2.1. Catalyst Characterization

N2 physisorption isotherms, along with mesopore size distribution of the prepared MOS support and Cr(x)/MOS catalysts, are illustrated in Figure 1A,B. The textural properties of synthesized samples such as BET-surface area, pore volume, and size are presented in Table 1. The physisorption isotherms display IV type profile with an H1 hysteresis loop, according to the IUPAC classification, which is a common feature of mesoporous materials. Type H1 hysteresis is associated with porous materials exhibiting pore geometry of cylindrical shape, along with pore size uniformity which is distinguished for all synthesized samples (Figure 1A). The isotherms of Cr(x)/MOS (x = 2, 5, 8, and 11 Cr wt.%) catalysts showed that the nitrogen molecules formed multilayer adsorption. Then, capillary condensation took place in the pores of Cr(x)/MOS. As the relative pressure increases, the mesoporous nature of the MOS sample was not disturbed by chromium impregnation. Figure 1B exhibits the distribution of pore size computed by using the BJH method. All Cr(x)/MOS (x = 2, 5, 8, and 11 Cr wt.%) catalysts displayed a consistently narrowing pore size distribution that peaked at 3.5 nm. According to textural properties (Table 1), both BET-surface area and total pore volume of the Cr(x)/MOS samples were reduced slightly when compared to the MOS support. This means that impregnation of MOS with Cr species caused further filling of the MOS pores with chromium oxide species.
The XRD patterns of the Cr(x)/MOS catalysts are illustrated in Figure 2. The diffraction peaks at 2θ = 24.5°, 33.6°, 36.2°, 41.5°, 50.2°, 54.9°, 63.4°, and 65.18° confirmed the presence of rhombohedral Cr2O3 crystals (JCPDS 00-006-0504) [9,13]. The intensities of the feature peaks of 𝝰-Cr2O3 in all prepared samples increased with increasing chromium content from 2 to 11 wt.%. The small peak intensity, as in Cr(2)/MOS, and their broadness in Cr(5)/MOS and Cr(8)/MOS samples suggested a smaller size of Cr2O3 crystals in these catalysts. In contrast, the Cr(11)/MOS catalyst showed higher peak intensities that could indicate the agglomeration or formation of large Cr2O3 particles. Generally, 𝝰-Cr2O3 crystals are detected over silica support at quite low Cr loading in comparison to other support systems (i.e., ZrO2 and Al2O3) [11]. The low content of hydroxyl functionality within the surface of silica motivates the formation of Cr2O3 clusters, rather than a well-dispersed phase [11]. However, silica having a high surface area is essenti al in order to achieve a high dispersion of Cr species.
In order to establish more details on the surface topography of the prepared samples and to assess the dispersion of the Cr species over Cr(x)/MOS catalysts, TEM, SEM imaging, and EDX elemental mapping were obtained on MOS, Cr(2)/MOS, Cr(8)/MOS, and Cr(11)/MOS catalysts; the images are presented in Figure 3. TEM images of bare MOS (Figure 3a*) show the formation of the mesoporous organo-silica matrix. After loading of 2 wt.% of Cr (Figure 3b*), the Cr oxides had rod and cubic shapes, and their widths were in the range of 15–35 nm with good distribution onto the mesoporous organo-silica matrix. Increasing the Cr content to 8 wt.% (Figure 3c*) resulted in the formation of cubic Cr oxide nanoparticles with growth of their sizes to 50–100 nm. The state of distribution of the Cr oxide nanoparticles onto the organo-silica matrix was quite acceptable. However, increasing the loading content of Cr oxide nanoparticles to 11 wt.% (Figure 3d*) caused the formation of a mixture of rod and cubic nanoparticles with size range of 150–300 nm and poor distribution character onto the mesoporous organo-silica matrix. EDX elemental mapping also was used to investigate more about the state of distribution of CrOx onto the mesoporous organo-silica matrix. It could be clearly observed that CrOx species were well-dispersed on the surface of the mesoporous organo-silica support for all prepared catalysts (Figure 3a–d; CrOx can be seen as golden color dots), and the intensity of golden dots is increasing as the chromium content increased. The Cr(11)/MOS (Figure 3d, golden) catalyst show some agglomeration of Cr species of CrOx, as clearly seen from the larger golden dots, Cr(8)/MOS (Figure 4c, golden) possessed uniform distribution of Cr species at the catalyst surface with fine small particles. Good dispersity and the size of the metal particle are fundamental aspects governing the catalytic performance of metal-supported catalytic systems.
X-ray photoelectron measurement was employed to analyze the surface chemistry and to measure the concentration of each Cr species on the synthesized samples. The XPS spectra of the Cr(x)/MOS (x = 2, 5, 8 and 11 wt.% Cr) samples are presented in Figure 4A,B. In order to find the ratios of various oxidation states of Cr species, the Cr2p spectra were deconvoluted and the results are given in Table 2. According to the XPS survey spectrum of the Cr(8)/MOS catalyst (Figure 4A), Cr, O, Si and C elements are present on the surface of Cr(x)/MOS catalysts. Their peaks are located at 576 (Cr 2p), 529.6(O1s), 284.6(C1s), 153(Si2s) and 103.4(Si2p) electron volts. Figure 4B displays the finely scanned XPS spectra of Cr2p of the formed catalysts. It can be observed that two intensive peaks were detected in the Cr 2p3/2 spectrum for all prepared samples; one at around ~577 eV, whereas the other was at ~579 eV, which can be correlated to Cr3+ and Cr6+, respectively [26,27,28]. According the reported literature, the Cr species with high oxidation state are the main components responsible for the higher performance of Cr-based catalytic systems during the dehydrogenation of light alkanes [2,29,30]. Wang et al. suggested that the surface Cr3+ species and Cr6+/Cr3+ ratio is quite important in the ethane dehydrogenation [11], whereas Ge and his team found that the species with high oxidation states (Cr5+/Cr6+) are crucial for this reaction [31]. XPS peaks of Cr2p3/2 and Cr2p1/2 were further deconvoluted into two more peaks by using a Gaussian–Lorentzian–Voigt fitting method, considering the spin-orbit splitting of 9.3 eV and 2:1 height ratio. Based on the previous literature reports, the peaks at ~579 and ~589 eV are normally associated with the Cr6+ ions, while energies at 577, and 587 eV are ascribed to the Cr3+ [5,12,32,33]. It was observed that both Cr6+ and Cr3+ had existed on the surface of all prepared samples, but with changes in their Cr6+/Cr3+ ratio. Table 2 summarizes the ratios. According to the quantitative data (Table 2), the Cr6+/Cr3+ ratio increased with the increasing Cr content up to 8 wt.% Cr, but with further a Cr increase to 11 wt.%, the ratio dropped. The Cr(8)/MOS catalyst showed the highest Cr6+/Cr3+ ratio of ~0.66. The dominance of Cr6+ at the surface of the optimum catalyst proposes a superior catalytic conversion toward ODH of C2H6 with CO2.
The presence of Cr of different oxidation states was also illustrated with UV–Vis DR measurements, and the spectra are presented in Figure 5A. In all spectra, two main absorption peaks at 270 and 370 nm are detected. These two peaks are associated with charge transfer of O2−→ Cr6+ within chromate species with a tetrahedral structure [34,35,36]. An additional shoulder band is also observed at around 415 nm, which is attributed to dichromate or poly-chromates on the catalysts surface [26,37]. Contrastingly, the peaks at 470 and 600 nm are assigned to d-d transition of Cr3+ species within the octahedral structure [5,11,26,38,39,40]. It can be observed that the intensity of Cr6+ bands increased with increasing chromium loading up to 8 wt.%, and the Cr(8)/MOS catalyst had the highest Cr6+ bands and the lowest Cr3+ bands among all the prepared samples. Further increasing the chromium loading resulted in reducing the intensity of Cr6+ bands, as shown in Cr(11)/MOS catalyst, and increasing the Cr3+ intensities as results of Cr2O3 phase formation. Fourier-transform infrared spectroscopy measurements of Cr(x)/MOS catalysts were conducted in the 680–4000 cm−1 range, and spectra are illustrated in Figure 5B. Silica presence in the prepared samples was confirmed by the existence of 810 and 1090 cm−1 absorption bands that are assigned to symmetric vibrations of Si–O–Si bonding in the samples. Disappearance of chromium absorption bands at 905 cm−1 was due to overlapping with the SiO2 vibration band. The absorption band at about 1636 cm−1 is assigned to the adsorbed water [13]. The peak observed at 2360 cm−1 can be related to CO2 which is adsorbed from the air [41,42]. It can be seen that there is no noticeable difference for the synthesized samples with various Cr content, because similar FTIR bands were detected.

2.2. Catalytic Performance of Cr(x)/MOS Catalysts

The catalytic activity for the formed Cr(x)/MOS samples was tested for oxidative CO2 ethane dehydrogenation at various catalytic temperatures, and the results are displayed in Figure 6. It can be noticed that both the conversion of ethane and the yield of ethylene rapidly increased with catalytic temperature due to the endothermic character of the ODH reaction. Conversely, the selectivity of ethylene dropped slightly with catalytic temperature, suggesting that hydrocracking reactions are present at high catalytic temperatures. Moreover, the experimental results obviously showed that the Cr loading is a key element in the catalytic performance of Cr(x)/MOS catalysts. The ethane conversion as well as the ethylene yield increased significantly with increasing the chromium content of Cr(x)/MOS up to 8 wt.% Cr, and then gradually decreased with further increases in chromium content to the Cr(11)/MOS catalyst. However, this drop in activity at high Cr loading is mainly caused by the formation of less active chromium oxide crystals. The XRD, UV–Vis DRS of Cr(11)/MOS catalyst showed that the crystalline 𝝰-Cr2O3 is dominant in this sample. In contrast, the Cr(8)/MOS catalyst showed the highest catalytic activity for the CO2-based ODH of ethane over the tested range of temperatures. The high activity of this catalyst could be related to superior chromium species distribution with high concentrations of reducible Cr6+ on the surface of the Cr(8)/MOS sample. It has been reported that the high concentration of reducible Cr6+ species is significant for the dehydrogenation reaction [15,40].
The SEM and XPS measurements clearly show that the Cr species were highly dispersed and Cr6+ species predominated on the prepared Cr(8)/MOS catalyst. In addition, the XPS results illustrated that the superior number of Cr6+ species and subsequently the highest Cr6+/Cr3+ ratio were recorded for the Cr(8)/MOS sample, which was reflected in its activity. The catalyst displayed an ethane conversion of 50.4% at 700 °C after one hour on the reaction stream and an ethylene yield of 45.4%. Table 3 summarizes the performance of some Cr-supported catalytic systems tested in the ethane dehydrogenation with CO2, including Cr(8)/MOS prepared for this study. Although reaction conditions were diverse, Cr/MOS exhibited comparable ethane conversion and higher activity than some catalysts listed in the table, which is partly attributed to reaction conditions or the number of used catalysts. The results show that Cr/MOS is a promising active catalyst for the ODH of ethane.
In addition to catalytic temperature and chromium loading effects, stability of the prepared catalysts was also investigated at 700 °C for 10 h, and the results are shown in Figure 7. For all samples, the conversion of ethane and the yield of ethylene decreased slowly over catalytic time, proposing a slight de-activation of the tested catalysts. Unlike our previously [3,12,46] investigated catalytic systems, deactivation of the Cr(x)/MOS catalytic system declined approximately 22% after 10 h of on-stream operation. For instance, using large-pore mesoporous silica as a support for the chromium-based catalytic system led to the same catalytic activity (50.5% and 91.1% conversion of ethane and selectivity of ethylene, respectively), but with 39% declination in the catalytic activity for the same reaction conditions [43]. Additionally, the results of this work are comparable to those other researcher groups, indicating its importance. Shi et al., for example, tested Cr(5) /SBA-15 for ethane dehydrogenation and found that the ethane conversation dropped from 46.3 to 23.6% after reacting for 5 h [8]. In addition to coke formation, the catalyst deactivation took place basically due to the reduction of high valence states of CrOx species, whereas the numbers of re-oxidized Cr3+ species were reduced with the passage of reaction time while the non-redox agglomerated Cr sites were increased. However, enhancement of the stability of Cr(x)/MOS catalysts could partly be attributed to the presence of organic components on the wall pore which may resist the agglomeration of Cr sites and inhibit catalyst sintering.
Therefore, slight deactivation of the Cr(x)/MOS catalytic system happened mostly because of the reduction of high-valence Cr6+ of CrOx species along with coke formation. However, for better understanding of the reasons of deactivation after the reaction, characterizations of spent catalyst were compared with the fresh catalyst and the results are included as a supplementary file. Even after 10 h of on-stream operation, Cr(8)/MOS showed high catalytic activity, with 40.81% and 38.37% for the conversion of ethane and yield of ethylene, respectively.
CO2-based oxidative dehydrogenation of ethane over the Cr(8)/MOS catalyst was also studied at various gas hourly space velocities (GHSV), and the results are presented in Figure 8. The GHSV was altered by changing the reactant flow rate while maintaining the same reactant ratio. From the results, the conversion of ethane as well as yield of ethylene decreased, while ethylene selectivity’s increased by increasing the GHSV. These results were expected because increasing the space velocity will reduce the reactants’ residence time inside the catalytic system, which leads to decreases in ethane conversion. In order to clarify the role of carbon dioxide in the dehydrogenation of ethane, the catalytic reaction was conducted in the presence and absence of CO2 over the optimum catalyst (Cr(8)/MOS) at various temperatures, and the results are presented in Figure 9.
It can be observed that the catalytic performance of the Cr(8)/MOS sample increased with reaction temperature, regardless of the presence or absence of CO2 in the reaction. Moreover, the catalytic performance of Cr(8)/MOS in the presence of CO2 was clearly superior than that in the absence of it, revealing the enhancement effects of carbon dioxide for ethane dehydrogenation. Furthermore, ethylene selectivity was slightly improved in the presence of CO2 as an oxidation agent. In the presence of carbon dioxide, ethylene was simultaneously formed either by dehydrogenation or oxidative dehydrogenation reactions, and a high conversion of ethane and yield of ethylene could be obtained, while the dehydrogenation of ethane without of CO2 was thermodynamically limited [11,47]. Reaction mechanisms of ethane dehydrogenation with CO2 over Cr-based catalysts follow the Mars–van Krevelen redox-type mechanism. This mechanism has been proposed for chromium [14,16,48,49,50], vanadium [51,52], manganese [53], and iron [54] oxide-based catalysts. In our catalytic system, the mechanism suggests that ethylene is simultaneously produced by the dehydrogenation and oxidative dehydrogenation of ethane [9,29,33,43,55]. According to the mechanism, oxidative dehydrogenation of ethane in the presence of CO2 follows the following steps:
  • Ethane adsorbs on Cr-species active site and/or acidic site of support;
  • Adsorbed ethane reacts with lattice oxygen atoms of CrO3 to produce both ethylene and water, and Cr3+, as a result of Cr6+ reduction;
3C2H6 + 2CrO3⟷3C2H4 + Cr2O3 + 3H2O
  • Re-oxidation of Cr3+ by surface oxygen species formed by the dissociation of CO2
Cr2O3 + 3CO2⟷3CO +2CrO3
In addition to the above reactions, the following reactions occurred:
  • Dehydrogenation of ethane
C2H6⟷C2H4 + H2
  • Reverse water–gas shift (RWGS) reaction, which shifted ethane dehydrogenation towards increased ethylene production
H2 + CO2⟷CO + H2O
Another possible reaction is:
  • Hydrocracking of ethane to methane
C2H6+H2⟷CH4 + H2
However, carbon dioxide could contribute either directly, by supplying the lattice oxygen in the oxidative dehydrogenation reaction, or indirectly, by removing the produced hydrogen from the dehydrogenation reaction [9]. On the other hand, the catalyst stability could be enhanced when the dehydrogenation reaction was carried out in the presence of CO2, where it assists by removing the deposited carbon on the catalyst surface according the following equation [56]:
CO2 + C⟷2CO
Eventually, the catalytic performance of the Cr/MOS catalyst in the CO2 atmosphere was clearly higher than that in the absence of it, suggesting the stimulating role of CO2 for the oxidative dehydrogenation of ethane in the presence of CO2. These findings are consistent with previous studies of light alkane oxidative dehydrogenation over Cr-based catalysts [5,33,45].
Effects of the CO2/C2H6 ratio on C2H6 dehydrogenation over the most active catalyst at various reaction temperatures were investigated, and the results are shown in Figure 10. It can be seen that, for all temperatures, both ethane conversion and ethylene yield increased with increasing CO2/C2H6 ratio until it attained its peak at ratio equal to five, after which it was almost constant with further increases in the CO2/C2H6 ratio.

3. Materials and Methods

3.1. Materials

Compounds 1,4-bis (triethoxysilyl) benzene (BTEB), ammonium hydroxide solution NH4OH: 28.0–30.0%, and Cetyltrimethylammonium chloride (25 wt.%) were supplied from Sigma-Aldrich (Steinheim, Germany). Chromium nitrate nonahydrate was used as a Cr precursor, and it was bought from Alfa Aesar (Karlsruhe, Germany).All chemicals were utilized as received without performing any additional purification.

3.2. Catalyst Preparation

Mesoporous organo-silica (MOS) was prepared by using BTEB and CTAC as the organo-silica source and surfactant, respectively. In a typical procedure, 4.40 ml of CH3(CH2)15N(Cl)(CH3)3, 52.5 ml of H2O, and 4 ml of NH4OH were combined and stirred for 10 min, in which a homogeneous solution was formed. After that, 5 ml of C6H4 (Si (OC2H5)3)2 was added dropwise under vigorous stirring for 60 minutes. Then, the formed precipitate was filtered, washed, and dried overnight. The dried powder was then heat-treated at 550 °C for 12 h.
In the next step, a series of Cr(x)/MOS catalysts were prepared by the incipient wetness impregnation approach where the prepared MOS support was treated with an aqueous solution having the specific amount of Cr precursor. The concentration of chromium nitrate in solution was tuned so as to obtain 2, 5, 8, and 11 wt.% of total Cr content (Cr total) in the final catalysts. The prepared samples were dried, and then were calcined at 650 °C for 12 h in air. The catalysts are denoted as Cr(x)/MOS, where x stands for the nominal Cr total given in wt.% of Cr.

3.3. Catalyst Characterization

All synthesized Cr(x)/MOS samples were characterized using the same instruments mentioned in supplementary information, namely, X-ray diffraction (PANalytical X’Pert PRO MPD, PANalytical, Almelo, Netherlands), N2 adsorption isotherms (Micromeritics ASAP 2010, Micromeritics, Norcross, GA, USA), scanning electron microscopy, energy-dispersive X-ray elemental mapping (JEOL JEM-7500F and X-ray photoelectron spectroscopy (XPS 9030 JEOL), JEOL, Tokyo, JAPAN), Fourier-transform infrared spectroscopy (Unicam 4000), and diffuse reflectance UV–Vis spectroscopy (Shmadzu, Kyoto, Japan).

3.4. Catalyst Testing

Oxidative dehydrogenation ODH reactions were performed in a stainless-steel packed catalyst bed reactor (internal diameter, 6 mm) at 600–700 °C and one atmosphere. Samples of 300 mg of Cr(x)/MOS catalysts were packed in the reactor, and glass wool was put at both ends of the catalyst bed. Prior to starting the reaction, the catalyst samples were pre-treated at 600 °C in an air atmosphere for 60 minutes before switching to the reactant mixture. During the test, the feed mixture ratio was maintained at 1:5:4 for ethane, carbon dioxide and nitrogen gases, respectively. Additionally, the total flowrate was kept at 75 mL/min. Carbon dioxide was replaced with N2 when the experiments were implemented in the absence of CO2. The ODH reaction was performed within a 600–700 °C temperature range. The tested samples were maintained at the reaction conditions for 20 min before starting the analysis. Both the reactants and the reaction products were analyzed by on-line Agilent 6890 N gas chromatography (Agilent 6890N, Agilent, Santa Clara,
CA, USA) which was connected to the reactor outlet. The GC was equipped with TCD and FID detectors, and using hayesep Q, molecular sieve 5 Å, and gas pro-columns.
The ethane conversion, as well as ethylene yield and selectivity, were thus computed according to Equations (1)–(3), given below:
Ethane   Conversion   ( % ) = F C 2 H 6 in F C 2 H 6 out F C 2 H 6 in × 100
Ethylene   Yield   ( % ) = F C 2 H 4 F C 2 H 6 in × 100
Ethylene   Selectivity   ( % ) = F C 2 H 4 F C 2 H 4 +   F CH 4 × 100
where Fj is the number of moles of component j.

4. Conclusions

CO2-based ethane oxidative dehydrogenation was studied over supported chromium oxide on mesoporous organo-silica (MOS). The results show that the prepared Cr(x)/MOS catalysts possessed promising catalytic performance in the dehydrogenation of ethane, with a less than 23% drop of its activity after 600 min. A highly active and stable catalyst Cr(8)/MOS was obtained, with an conversion of ethane ~50.9% and selectivity of ethylene ~90.1%. TEM and elemental mapping showed a gradual increment of the size of CrOx species, along with their poor distribution with increasing the Cr content. EDX analysis revealed CrOx content close to the proposed added values during the impregnation step. XPS measurements revealed that Cr6+/Cr3+ ratio increased with increasing the Cr content up to 8 wt.% Cr, but with a further Cr increase to 11 wt.%, the ratio dropped. The high activity of this catalyst could be related to the superior chromium species distribution with high concentration of reducible Cr6+ on the surface of the Cr(8)/MOS sample. The deactivation of the catalyst was much improved as compared to previous reports, which can be correlated to enhancement of the redox Cr species stability due to the high surface area and stable structure supports, which we developed by using MOS as a support for our catalytic system.

Supplementary Materials

The following are available online at https://0-www-mdpi-com.brum.beds.ac.uk/article/10.3390/catal11050642/s1, Figure S1: (A) N2 sorption isotherms and (B) pore size distribution of Cr(8)/MOS catalysts before and after the reaction; Figure S2: (A) UV–Vis DR and (B) FTIR patterns of Cr(8)/MOS catalysts before and after the reaction; Figure S3: TEM images of Cr(8)/MOS catalysts (A) before and (B) after the reaction; Table S1: Textural properties of fresh and used Cr(8)/MOS catalysts.

Author Contributions

Conceptualization, writing-review editing: A.E.A. and S.M.A.-Z. Investigation, writing-original draft, and writing-review editing: A.S.A.-A., A.M.E.-T., and A.A.A.-Z. Methodology and formal analysis: A.S.A.-A., J.P.L., H.G., A.K. and A.M.E.-T. All authors have read and agreed to the published version of the manuscript.

Funding

Deanship of Scientific Research at King Saud University, Riyadh (RG-1438-094).

Data Availability Statement

The raw/processed data required to reproduce these findings cannot be shared at this time as the data also forms part of an ongoing study.

Acknowledgments

The authors extend their appreciation to the Deanship of Scientific Research at King Saud University, Riyadh for funding this work through Research Group (RG-1438-094).

Conflicts of Interest

The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.

References

  1. Wang, S.; Murata, K.; Hayakawa, T.; Hamakawa, S.; Suzuki, K. Effect of promoters on catalytic performance of Cr/SiO2 catalysts in oxidative dehydrogenation of ethane with carbon dioxide. Catal. Lett. 2001, 73, 107–111. [Google Scholar] [CrossRef]
  2. Mimura, N.; Okamoto, M.; Yamashita, H.; Oyama, S.T.; Murata, K. Oxidative Dehydrogenation of Ethane over Cr/ZSM-5 Catalysts Using CO2 as an Oxidant. J. Phys. Chem. B 2006, 110, 21764–21770. [Google Scholar] [CrossRef] [PubMed]
  3. Deng, S.; Li, S.; Li, H.; Zhang, Y. Oxidative Dehydrogenation of Ethane to Ethylene with CO2 over Fe−Cr/ZrO2 Catalysts. Ind. Eng. Chem. Res. 2009, 48, 7561–7566. [Google Scholar] [CrossRef]
  4. Xu, L.; Liu, J.; Yang, H.; Xu, Y.; Wang, Q.; Lin, L. Regeneration behaviors of Fe/SiO2 and Fe–Mn/SiO2 catalysts for C2H6 dehydrogenation with CO2 to C2H4. Catal. Lett. 1999, 62, 185–189. [Google Scholar] [CrossRef]
  5. Cheng, Y.; Zhang, F.; Zhang, Y.; Miao, C.; Hua, W.; Yue, Y.; Gao, Z. Oxidative dehydrogenation of ethane with CO2 over Cr supported on submicron ZSM-5 zeolite. Chin. J. Catal. 2015, 36, 1242–1248. [Google Scholar] [CrossRef]
  6. Shi, X.; Ji, S.; Wang, K.; Li, C. Oxidative Dehydrogenation of Ethane with CO2 over Novel Cr/SBA-15/Al2O3/FeCrAl Monolithic Catalysts. Energy Fuels 2008, 22, 3631–3638. [Google Scholar] [CrossRef]
  7. Michorczyk, P.; Pietrzyk, P.; Ogonowski, J. Preparation and characterization of SBA-1—Supported chromium oxide catalysts for CO2 assisted dehydrogenation of propane. Microporous Mesoporous Mater. 2012, 161, 56–66. [Google Scholar] [CrossRef]
  8. Shi, X.; Ji, S.; Wang, K. Oxidative Dehydrogenation of Ethane to Ethylene with Carbon dioxide over Cr–Ce/SBA-15 Catalysts. Catal. Lett. 2008, 125, 331–339. [Google Scholar] [CrossRef]
  9. Rahmani, F.; Haghighi, M.; Mahboob, S. CO2-enhanced dehydrogenation of ethane over sonochemically synthesized Cr/clinoptilolite-ZrO2 nanocatalyst: Effects of ultrasound irradiation and ZrO2 loading on catalytic activity and stability. Ultrason. Sonochem. 2016, 33, 150–163. [Google Scholar] [CrossRef]
  10. Michorczyk, P.; Ogonowski, J.; Niemczyk, M. Investigation of catalytic activity of CrSBA-1 materials obtained by direct method in the dehydrogenation of propane with CO2. Appl. Catal. A Gen. 2010, 374, 142–149. [Google Scholar] [CrossRef]
  11. Michorczyk, P.; Ogonowski, J.; Zeńczak, K. Activity of chromium oxide deposited on different silica supports in the dehydrogenation of propane with CO2—A comparative study. J. Mol. Catal. A Chem. 2011, 349, 1–12. [Google Scholar] [CrossRef]
  12. Al-Awadi, A.S.; El-Toni, A.M.; Alhoshan, M.; Khan, A.; Labis, J.P.; Al-Fatesh, A.; Abasaeed, A.E.; Al-Zahrani, S.M. Impact of precursor sequence of addition for one-pot synthesis of Cr-MCM-41 catalyst nanoparticles to enhance ethane oxidative dehydrogenation with carbon dioxide. Ceram. Int. 2019, 45, 1125–1134. [Google Scholar] [CrossRef]
  13. Asghari, E.; Haghighi, M.; Rahmani, F. CO2 Oxidative Dehydrogenation of Ethane to Ethylene over Cr/MCM-41 Nanocatalyst Synthesized via Hydrothermal/Impregnation Methods: Influence of Chromium Content on Catalytic Properties and Performance. J. Mol. Catal. A Chem. 2016, 418, 115–124. [Google Scholar] [CrossRef]
  14. Liu, L.; Li, H.; Zhang, Y. Mesoporous silica-supported chromium catalyst: Characterization and excellent performance in dehydrogenation of propane to propylene with carbon dioxide. Catal. Commun. 2007, 8, 565–570. [Google Scholar] [CrossRef]
  15. Baek, J.; Yun, H.J.; Yun, D.; Choi, Y.; Yi, J. Preparation of Highly Dispersed Chromium Oxide Catalysts Supported on Mesoporous Silica for the Oxidative Dehydrogenation of Propane Using CO2: Insight into the Nature of Catalytically Active Chromium Sites. ACS Catal. 2012, 2, 1893–1903. [Google Scholar] [CrossRef]
  16. Michorczyk, P.; Ogonowski, J.; Kuśtrowski, P.; Chmielarz, L. Chromium oxide supported on MCM-41 as a highly active and selective catalyst for dehydrogenation of propane with CO2. Appl. Catal. A Gen. 2008, 349, 62–69. [Google Scholar] [CrossRef]
  17. Asefa, T.; MacLachlan, M.J.; Coombs, N.; Ozin, G.A. Periodic mesoporous organosilicas with organic groups inside the channel walls. Nature 1999, 402, 867–871. [Google Scholar] [CrossRef]
  18. Inagaki, S.; Guan, S.; Fukushima, Y.; Ohsuna, T.; Terasaki, O. Novel mesoporous materials with a uniform distribution of organic groups and inorganic oxide in their frameworks. J. Am. Chem. Soc. 1999, 121, 9611–9614. [Google Scholar] [CrossRef]
  19. Melde, B.J.; Holland, B.T.; Blanford, C.F.; Stein, A. Mesoporous sieves with unified hybrid inorganic/organic frameworks. Chem. Mater. 1999, 11, 3302–3308. [Google Scholar] [CrossRef]
  20. Mizoshita, N.; Tani, T.; Inagaki, S. Syntheses, properties and applications of periodic mesoporous organosilicas prepared from bridged organosilane precursors. Chem. Soc. Rev. 2011, 40, 789–800. [Google Scholar] [CrossRef]
  21. Fujita, S.; Inagaki, S. Self-organization of organosilica solids with molecular-scale and mesoscale periodicities. Chem. Mater. 2008, 20, 891–908. [Google Scholar] [CrossRef]
  22. Masatake, H.; Tetsuhiko, K.; Hiroshi, S.; Nobumasa, Y. Novel Gold Catalysts for the Oxidation of Carbon Monoxide at a Temperature far Below 0 °C. Chem. Lett. 1987, 16, 405–408. [Google Scholar]
  23. Karimi, B.; Elhamifar, D.; Clark, J.H.; Hunt, A.J. Ordered Mesoporous Organosilica with Ionic-Liquid Framework: An Efficient and Reusable Support for the Palladium-Catalyzed Suzuki–Miyaura Coupling Reaction in Water. Chem.—Eur. J. 2010, 16, 8047–8053. [Google Scholar] [CrossRef] [PubMed]
  24. Karimi, B.; Elhamifar, D.; Yari, O.; Khorasani, M.; Vali, H.; Clark, J.H.; Hunt, A.J. Synthesis and Characterization of Alkyl-Imidazolium-Based Periodic Mesoporous Organosilicas: A Versatile Host for the Immobilization of Perruthenate (RuO4) in the Aerobic Oxidation of Alcohols. Chem.—Eur. J. 2012, 18, 13520–13530. [Google Scholar] [CrossRef] [PubMed]
  25. Shylesh, S.; Srilakshmi, C.; Singh, A.; Anderson, B. One step synthesis of chromium-containing periodic mesoporous organosilicas and their catalytic activity in the oxidation of cyclohexane. Microporous Mesoporous Mater. 2007, 99, 334–344. [Google Scholar] [CrossRef]
  26. Weckhuysen, B.M.; Wachs, I.E.; Schoonheydt, R.A. Surface Chemistry and Spectroscopy of Chromium in Inorganic Oxides. Chem. Rev. 1996, 96, 3327–3350. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  27. Grzybowska, B.; Słoczyński, J.; Grabowski, R.; Wcisło, K.; Kozłowska, A.; Stoch, J.; Zieliński, J. Chromium Oxide/Alumina Catalysts in Oxidative Dehydrogenation of Isobutane. J. Catal. 1998, 178, 687–700. [Google Scholar] [CrossRef]
  28. Hoang, M.; Mathews, J.F.; Pratt, K.C. Oxidative Dehydrogenation of Isobutane over Supported Chromium Oxide on Lanthanum Carbonate. J. Catal. 1997, 171, 320–324. [Google Scholar] [CrossRef]
  29. Wang, S.; Murata, K.; Hayakawa, T.; Hamakawa, S.; Suzuki, K. Dehydrogenation of ethane with carbon dioxide over supported chromium oxide catalysts. Appl. Catal. A Gen. 2000, 196, 1–8. [Google Scholar] [CrossRef]
  30. Weckhuysen, B.M.; Schoonheydt, R.A. Alkane dehydrogenation over supported chromium oxide catalysts. Catal. Today 1999, 51, 223–232. [Google Scholar] [CrossRef] [Green Version]
  31. Ge, X.; Zhu, M.; Shen, J. Catalytic performance of silica-supported chromium oxide catalysts in ethane dehydrogenation with carbon dioxide. React. Kinet. Catal. Lett. 2002, 77, 103–108. [Google Scholar] [CrossRef]
  32. Zhao, X.; Wang, X. Oxidative dehydrogenation of ethane to ethylene by carbon dioxide over Cr/TS-1 catalysts. Catal. Commun. 2006, 7, 633–638. [Google Scholar] [CrossRef]
  33. Wang, S.; Murata, K.; Hayakawa, T.; Hamakawa, S.; Suzuki, K. Oxidative dehydrogenation of ethane by carbon dioxide over sulfate-modified Cr2O3/SiO2 catalysts. Catal. Lett. 1999, 63, 59–64. [Google Scholar] [CrossRef]
  34. De Rossi, S.; Pia Casaletto, M.; Ferraris, G.; Cimino, A.; Minelli, G. Chromia/zirconia catalysts with Cr content exceeding the monolayer. A comparison with chromia/alumina and chromia/silica for isobutane dehydrogenation. Appl. Catal. A Gen. 1998, 167, 257–270. [Google Scholar] [CrossRef]
  35. Zhao, X.; Wang, X. Synthesis, characterization and catalytic application of Cr–SBA-1 mesoporous molecular sieves. J. Mol. Catal. A Chem. 2007, 261, 225–231. [Google Scholar] [CrossRef]
  36. Weckhuysen, B.M.; Verberckmoes, A.A.; Debaere, J.; Ooms, K.; Langhans, I.; Schoonheydt, R.A. In situ UV-Vis diffuse reflectance spectroscopy—on line activity measurements of supported chromium oxide catalysts: Relating isobutane dehydrogenation activity with Cr-speciation via experimental design. J. Mol. Catal. A Chem. 2000, 151, 115–131. [Google Scholar] [CrossRef] [Green Version]
  37. Weckhuysen, B.M.; Verberckmoes, A.A.; Baets, A.R.D.; Schoonheydt, R.A. Diffuse Reflectance Spectroscopy of Supported Chromium Oxide Catalysts: A Self-Modeling Mixture Analysis. J. Catal. 1997, 166, 160–171. [Google Scholar] [CrossRef] [Green Version]
  38. Ayari, F.; Mhamdi, M.; Álvarez-Rodríguez, J.; Ruiz, A.R.G.; Delahay, G.; Ghorbel, A. Selective catalytic reduction of NO with NH3 over Cr-ZSM-5 catalysts: General characterization and catalysts screening. Appl. Catal. B Environ. 2013, 367–380. [Google Scholar] [CrossRef]
  39. Cavani, F.; Koutyrev, M.; Trifirò, F.; Bartolini, A.; Ghisletti, D.; Iezzi, R.; Santucci, A.; Del Piero, G. Chemical and Physical Characterization of Alumina-Supported Chromia-Based Catalysts and Their Activity in Dehydrogenation of Isobutane. J. Catal. 1996, 158, 236–250. [Google Scholar] [CrossRef]
  40. Puurunen, R.L.; Weckhuysen, B.M. Spectroscopic Study on the Irreversible Deactivation of Chromia/Alumina Dehydrogenation Catalysts. J. Catal. 2002, 210, 418–430. [Google Scholar] [CrossRef]
  41. Abdollahifar, M.; Haghighi, M.; Babaluo, A.A. Syngas production via dry reforming of methane over Ni/Al2O3-MgO nanocatalyst synthesized using ultrasound energy. J. Ind. Eng. Chem. 2014, 20, 1845–1851. [Google Scholar] [CrossRef]
  42. Khoshbin, R.; Haghighi, M. Urea-nitrate combustion synthesis and physicochemical characterization of CuO-ZnO-Al2O3 nanoparticles over HZSM-5. Chin. J. Inorg. Chem. 2012, 28, 1967–1978. [Google Scholar]
  43. Al-Awadi, A.S.; Al-Zahrani, S.M.; El-Toni, A.M.; Abasaeed, A.E. Dehydrogenation of Ethane to Ethylene by CO2 over Highly Dispersed Cr on Large-Pore Mesoporous Silica Catalysts. Catalysts 2020, 10, 97. [Google Scholar] [CrossRef] [Green Version]
  44. Al-Awadi, A.S.; El-Toni, A.M.; Al-Zahrani, S.M.; Abasaeed, A.E.; Alhoshan, M.; Khan, A.; Labis, J.P.; Al-Fatesh, A. Role of TiO2 nanoparticle modification of Cr/MCM41 catalyst to enhance Cr-support interaction for oxidative dehydrogenation of ethane with carbon dioxide. Appl. Catal. A Gen. 2019, 584, 117114. [Google Scholar] [CrossRef]
  45. Rahmani, F.; Haghighi, M.; Amini, M. The beneficial utilization of natural zeolite in preparation of Cr/clinoptilolite nanocatalyst used in CO2-oxidative dehydrogenation of ethane to ethylene. J. Ind. Eng. Chem. 2015, 31, 142–155. [Google Scholar] [CrossRef]
  46. Al-Awadi, A.S.; El-Toni, A.M.; Alhoshan, M.; Khan, A.; Shar, M.A.; Abasaeed, A.E.; Al-Zahrani, S.M. Synergetic Impact of Secondary Metal Oxides of Cr-M/MCM41 Catalyst Nanoparticles for Ethane Oxidative Dehydrogenation Using Carbon Dioxide. Crystals 2019, 10, 7. [Google Scholar] [CrossRef] [Green Version]
  47. Shishido, T.; Shimamura, K.; Teramura, K.; Tanaka, T. Role of CO2 in dehydrogenation of propane over Cr-based catalysts. Catal. Today 2012, 185, 151–156. [Google Scholar] [CrossRef]
  48. Nakagawa, K.; Kajita, C.; Ikenaga, N.-o.; Nishitani-Gamo, M.; Ando, T.; Suzuki, T. Dehydrogenation of light alkanes over oxidized diamond-supported catalysts in the presence of carbon dioxide. Catal. Today 2003, 84, 149–157. [Google Scholar] [CrossRef]
  49. Zhang, X.; Yue, Y.; Gao, Z. Chromium Oxide Supported on Mesoporous SBA-15 as Propane Dehydrogenation and Oxidative Dehydrogenation Catalysts. Catal. Lett. 2002, 83, 19–25. [Google Scholar] [CrossRef]
  50. Takehira, K.; Ohishi, Y.; Shishido, T.; Kawabata, T.; Takaki, K.; Zhang, Q.; Wang, Y. Behavior of active sites on Cr-MCM-41 catalysts during the dehydrogenation of propane with CO2. J. Catal. 2004, 224, 404–416. [Google Scholar] [CrossRef]
  51. Santacesaria, E.; Cozzolino, M.; Di Serio, M.; Venezia, A.M.; Tesser, R. Vanadium based catalysts prepared by grafting: Preparation, properties and performances in the ODH of butane. Appl. Catal. A Gen. 2004, 270, 177–192. [Google Scholar] [CrossRef]
  52. Takahara, I.; Saito, M.; Inaba, M.; Murata, K. Dehydrogenation of propane over a silica-supported vanadium oxide catalyst. Catal. Lett. 2005, 102, 201–205. [Google Scholar] [CrossRef]
  53. Krylov, O.V.; Mamedov, A.K.; Mirzabekova, S.R. The regularities in the interaction of alkanes with CO2 on oxide catalysts. Catal. Today 1995, 24, 371–375. [Google Scholar] [CrossRef]
  54. Michorczyk, P.; Kuśtrowski, P.; Chmielarz, L.; Ogonowski, J. Influence of redox properties on the activity of iron oxide catalysts in dehydrogenation of propane with CO2. React. Kinet. Catal. Lett. 2004, 82, 121–130. [Google Scholar] [CrossRef]
  55. Mimura, N.; Takahara, I.; Inaba, M.; Okamoto, M.; Murata, K. High-performance Cr/H-ZSM-5 catalysts for oxidative dehydrogenation of ethane to ethylene with CO2 as an oxidant. Catal. Commun. 2002, 3, 257–262. [Google Scholar] [CrossRef]
  56. Nakagawa, K.; Kajita, C.; Okumura, K.; Ikenaga, N.-o.; Nishitani-Gamo, M.; Ando, T.; Kobayashi, T.; Suzuki, T. Role of Carbon Dioxide in the Dehydrogenation of Ethane over Gallium-Loaded Catalysts. J. Catal. 2001, 203, 87–93. [Google Scholar] [CrossRef]
Figure 1. (A) N2 sorption isotherms and (B) mesopore size distribution of Cr(x)/MOS catalysts prepared with varying Cr loading.
Figure 1. (A) N2 sorption isotherms and (B) mesopore size distribution of Cr(x)/MOS catalysts prepared with varying Cr loading.
Catalysts 11 00642 g001
Figure 2. XRD patterns of Cr(x)/MOS catalysts prepared with varying Cr loading (*Cr= Cr2O3).
Figure 2. XRD patterns of Cr(x)/MOS catalysts prepared with varying Cr loading (*Cr= Cr2O3).
Catalysts 11 00642 g002
Figure 3. TEM, SEM images, and EDX elemental mapping (Cr (golden); Si (blue)) of Cr(x)/MOS catalysts prepared at different chromium loadings (a*,a) MOS; (b*,b) Cr(2)/MOS; (c*,c) Cr(8)/MOS; and (d*,d) Cr(11)/MOS (white arrows refer to Cr species).
Figure 3. TEM, SEM images, and EDX elemental mapping (Cr (golden); Si (blue)) of Cr(x)/MOS catalysts prepared at different chromium loadings (a*,a) MOS; (b*,b) Cr(2)/MOS; (c*,c) Cr(8)/MOS; and (d*,d) Cr(11)/MOS (white arrows refer to Cr species).
Catalysts 11 00642 g003
Figure 4. (A) XPS survey scan of Cr(8)/MOS; (B) Cr2p XPS spectra of Cr(x)/MOS, formed with varying Cr loading, where x: (B-a) 2, (B-b) 5, (B-c) 8, and (B-d) 11 wt.% Cr.
Figure 4. (A) XPS survey scan of Cr(8)/MOS; (B) Cr2p XPS spectra of Cr(x)/MOS, formed with varying Cr loading, where x: (B-a) 2, (B-b) 5, (B-c) 8, and (B-d) 11 wt.% Cr.
Catalysts 11 00642 g004
Figure 5. UV–Vis DR spectrum (A) and FTIR patterns (B) of Cr(x)/MOS catalysts prepared with varying Cr loading.
Figure 5. UV–Vis DR spectrum (A) and FTIR patterns (B) of Cr(x)/MOS catalysts prepared with varying Cr loading.
Catalysts 11 00642 g005
Figure 6. Effects of Cr loading on ethane conversion (A) and ethylene selectivity (B) for Cr(x)/MOS catalysts at various reaction temperatures. Reaction conditions: temperature = 700 °C; feed composition C2H6/CO2/N2 = 1/5/4; catalyst weight = 300 mg; reaction time = 1.0 h.
Figure 6. Effects of Cr loading on ethane conversion (A) and ethylene selectivity (B) for Cr(x)/MOS catalysts at various reaction temperatures. Reaction conditions: temperature = 700 °C; feed composition C2H6/CO2/N2 = 1/5/4; catalyst weight = 300 mg; reaction time = 1.0 h.
Catalysts 11 00642 g006
Figure 7. Variation of ethane conversion (A) and ethylene selectivity (B) time-on-stream over Cr(x)/MOS catalysts.
Figure 7. Variation of ethane conversion (A) and ethylene selectivity (B) time-on-stream over Cr(x)/MOS catalysts.
Catalysts 11 00642 g007
Figure 8. Effects of GHSV on the conversion of ethane and selectivity of ethylene for the Cr(8)/MOS catalyst at different temperatures.
Figure 8. Effects of GHSV on the conversion of ethane and selectivity of ethylene for the Cr(8)/MOS catalyst at different temperatures.
Catalysts 11 00642 g008
Figure 9. Effects of CO2 addition on the conversion of ethane and selectivity of ethylene for the Cr(8)/MOS catalyst at different temperatures.
Figure 9. Effects of CO2 addition on the conversion of ethane and selectivity of ethylene for the Cr(8)/MOS catalyst at different temperatures.
Catalysts 11 00642 g009
Figure 10. Effects of partial pressure of CO2 on the conversion of ethane and selectivity of ethylene for the Cr(8)/MOS catalyst at different temperatures.
Figure 10. Effects of partial pressure of CO2 on the conversion of ethane and selectivity of ethylene for the Cr(8)/MOS catalyst at different temperatures.
Catalysts 11 00642 g010
Table 1. Textural properties of the MOS and Cr(x)/MOS prepared catalysts.
Table 1. Textural properties of the MOS and Cr(x)/MOS prepared catalysts.
Cr(x)/MOS
x =
Cr Content
wt.%
BET (m2/g)Pore Volume (cm3/g)Pore Size (nm)Cr content by EDX
wt.%
Cr surface Density (CrOX/nm2) a
MOS07940.614.03-
Cr(2)/MOS26950.493.502.550.33
Cr(5)/MOS56840.483.505.130.85
Cr(8)/MOS86730.473.517.771.38
Cr(11)/MOS116550.433.4410.542.37
a Chromium dispersion as calculated by considering the Cr content in the gel (surface density = NA*(CrWt. %/CrMwt)/SBET) [13].
Table 2. XPS data of Cr(x)/MOS (x = 2, 5, 8 and 11 wt.%) catalysts.
Table 2. XPS data of Cr(x)/MOS (x = 2, 5, 8 and 11 wt.%) catalysts.
Catalyst Cr 2p3/2 Binding Energy (eV)Cr6+/Cr3+
Cr3+Cr6+
Cr(2)/MOS577.32579.620.47
Cr(5)/MOS577.08579.310.54
Cr(8)/MOS577.31579.680.66
Cr(11)/MOS577.32579.620.55
Table 3. Comparison of different catalysts in the dehydrogenation of ethane with CO2.
Table 3. Comparison of different catalysts in the dehydrogenation of ethane with CO2.
CatalystReaction ConditionsCatalytic ActivityRef.
T (°C)Flow Rate (ml/min)Catalyst weight
(g)
Feed CompositionEthane Conversion (%)Ethylene Selectivity (%)
Cr(8)/MOS700450.3C2H6/CO2/N2 = 1/5/450.490.1Present study
Cr(5)/SBA-15700120.2C2H6/CO2 = 1/346.394.7[8]
Cr(5)/SiO2650601.0C2H6/CO2/N2 = 1/5/456.192.9[29]
Cr(5)/SiO2–(SO4)2-650151.0C2H6/CO2/N2 = 1/5/467.281.8[33]
Cr(4)/LPMS700450.3C2H6/CO2/N2 = 1/5/450.591.1[43]
Cr(8)/Ti(1.9)/MCM41700750.4C2H6/CO2/N2 = 1/5/451.992.8[44]
Cr(10)–Fe(5)/ZrO2650500.2C2H6/CO2/Ar = 1/3/149.090.0[3]
Cr(5)/CLT-IA650600.5C2H6/CO2/N2 = 1/5/418.999.5[45]
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Al-Awadi, A.S.; El-Toni, A.M.; Labis, J.P.; Khan, A.; Ghaithan, H.; Al-Zahrani, A.A.; Abasaeed, A.E.; Al-Zahrani, S.M. Mesoporous Organo-Silica Supported Chromium Oxide Catalyst for Oxidative Dehydrogenation of Ethane to Ethylene with CO2. Catalysts 2021, 11, 642. https://0-doi-org.brum.beds.ac.uk/10.3390/catal11050642

AMA Style

Al-Awadi AS, El-Toni AM, Labis JP, Khan A, Ghaithan H, Al-Zahrani AA, Abasaeed AE, Al-Zahrani SM. Mesoporous Organo-Silica Supported Chromium Oxide Catalyst for Oxidative Dehydrogenation of Ethane to Ethylene with CO2. Catalysts. 2021; 11(5):642. https://0-doi-org.brum.beds.ac.uk/10.3390/catal11050642

Chicago/Turabian Style

Al-Awadi, Abdulrhman S., Ahmed Mohamed El-Toni, Joselito P. Labis, Aslam Khan, Hamid Ghaithan, Attiyah A. Al-Zahrani, Ahmed E. Abasaeed, and Saeed M. Al-Zahrani. 2021. "Mesoporous Organo-Silica Supported Chromium Oxide Catalyst for Oxidative Dehydrogenation of Ethane to Ethylene with CO2" Catalysts 11, no. 5: 642. https://0-doi-org.brum.beds.ac.uk/10.3390/catal11050642

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop