Correction

Correction: Boruah, D.; Zhang, X. Effect of Post-Deposition Solution Treatment and Ageing on Improving Interfacial Adhesion Strength of Cold Sprayed Ti6Al4V Coatings. Metals 2021, 11, 2038

1
Faculty of Engineering, Environment and Computing, Coventry University, Coventry CV1 5FB, UK
2
Department of Electromechanical, Systems and Metal Engineering, Faculty of Engineering and Architecture, Ghent University, 9052 Gent, Belgium
*
Author to whom correspondence should be addressed.
Submission received: 28 March 2022 / Accepted: 25 April 2022 / Published: 24 May 2022
The authors wish to make the following corrections to this paper [1]:
Figure 8 in Section 4 (Discussion) incorrectly cited data taken from the literature. The reference to the literature results should have been [13], as amended below in Figure 8:
We will update the article and the original version will remain available on the article webpage.

Reference

  1. Dibakor, B.; Zhang, X. Effect of Post-Deposition Solution Treatment and Ageing on Improving Interfacial Adhesion Strength of Cold Sprayed Ti6Al4V Coatings. Metals 2021, 11, 2038. [Google Scholar] [CrossRef]
Figure 8. Adhesion strength in terms of % of mill annealed Ti6Al4V’s ultimate tensile strength (UTS), before and after thermal treatments, and comparison with the literature. (Note: IF-Interface Failure, and CF-Cohesion Failure).
Figure 8. Adhesion strength in terms of % of mill annealed Ti6Al4V’s ultimate tensile strength (UTS), before and after thermal treatments, and comparison with the literature. (Note: IF-Interface Failure, and CF-Cohesion Failure).
Metals 12 00893 g001
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Boruah, D.; Zhang, X. Correction: Boruah, D.; Zhang, X. Effect of Post-Deposition Solution Treatment and Ageing on Improving Interfacial Adhesion Strength of Cold Sprayed Ti6Al4V Coatings. Metals 2021, 11, 2038. Metals 2022, 12, 893. https://0-doi-org.brum.beds.ac.uk/10.3390/met12060893

AMA Style

Boruah D, Zhang X. Correction: Boruah, D.; Zhang, X. Effect of Post-Deposition Solution Treatment and Ageing on Improving Interfacial Adhesion Strength of Cold Sprayed Ti6Al4V Coatings. Metals 2021, 11, 2038. Metals. 2022; 12(6):893. https://0-doi-org.brum.beds.ac.uk/10.3390/met12060893

Chicago/Turabian Style

Boruah, Dibakor, and Xiang Zhang. 2022. "Correction: Boruah, D.; Zhang, X. Effect of Post-Deposition Solution Treatment and Ageing on Improving Interfacial Adhesion Strength of Cold Sprayed Ti6Al4V Coatings. Metals 2021, 11, 2038" Metals 12, no. 6: 893. https://0-doi-org.brum.beds.ac.uk/10.3390/met12060893

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop