Next Article in Journal
Use of Ferritin-Based Metal-Encapsulated Nanocarriers as Anticancer Agents
Next Article in Special Issue
Thermo-Responsive Shape-Memory Effect and Surface Features in Polycarbonate (PC)
Previous Article in Journal
Nonlinear Silicon Photonic Signal Processing Devices for Future Optical Networks
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Thermal Sensitive Shape Memory Behavior of Epoxy Composites Reinforced with Silicon Carbide Whiskers

Key Laboratory of Ministry of Education for Electronic Equipment Structure Design, Xidian University, Xi’an 710071, China
*
Author to whom correspondence should be addressed.
Submission received: 5 December 2016 / Revised: 13 January 2017 / Accepted: 16 January 2017 / Published: 21 January 2017
(This article belongs to the Special Issue Shape Memory Polymers)

Abstract

:
A novel shape memory polymer composite was fabricated by introducing various amounts of silicon carbide whiskers (SiCws) into a shape memory epoxy. The relationship between the thermomechanical properties of the system and structural changes were investigated via dynamic mechanical analysis, scanning electron microscopy, and bending tests. The results show that the bend strength of composites can improve by 64.1% when SiCw content reaches 12 wt %. The shape transition temperatures of SiCw/epoxy composites decreased slightly with the increase in SiCw content, but it was noted that all of the composites showed excellent shape memory properties. The shape fixity ratio increased as SiCw content increased (>99%), and the shape recovery ratio slightly decreased as SiCw content increased (>95%). All of the composites nearly recovered to their original shape within 2 min (not 100%), and the shape recovery speed significantly improved at a higher temperature. It is anticipated that tagging products will be used in the aerospace industry.

1. Introduction

Shape memory polymers (SMPs) are stimuli-responsive materials that can assume a temporary shape and recover their original shape when triggered through an external stimulation such as thermal stimulus, electric current, light, magnetic field, moisture, and pH value [1,2,3,4,5,6,7,8]. Thermally induced SMPs are the most common type of SMP. Compared to shape memory alloys and shape memory ceramics, SMPs have been widely researched due to their facile processability, low cost, appreciable shape recovery, and broad range of shape recovery temperatures [9,10,11,12]. Therefore, they are ideal candidates for potential applications in intelligent biomedical materials, heat shrinkable packaging, smart textile, aeronautics, astronautics, sensors and actuators, information carriers, disassembly concepts, and supervision technologies for cooling chains [13,14,15,16,17,18,19,20,21].
Though outstanding in some aspects compared with shape memory alloys and shape memory ceremics, SMPs have obvious shortcomings: low mechanical strength and shape recovery stress. The recovery stress of shape memory alloys can reach as high as 800 megapascals, but the recovery stress of SMPs is usually from a few tenths of a megapascal to a few tens of megapascals. In order to solve this problem, considerable efforts have been made. However, until today, the immediate method has been using high modulus inorganic or organic fillers to reinforce the pristine SMPs. In the past few years, carbon materials, including carbon black, carbon fiber, carbon nanotubes, and graphene, have been widely applied in polymer composites. Ma et al. [22] filled shape memory polyethylene with carbon black to prepare two-way reversible shape memory polymer composites. In the composites, the additional of carbon black nanoparticles has had a beneficial effect on performance in the two-way shape memory effect, and carbon black increased the tensile modulus in the rubbery. Park et al. [23] reinforced shape memory polyurethane with graphene and found that graphene effectively reinforced polyurethane and improved the shape recovery of an SMP composite.
In general, there are two types of SMPs: thermoplastic and thermoset SMPs. Compared with thermoplastic SMPs, thermoset SMPs exhibit a much higher stiffness and dimensional stability, and have better environmental durability. Therefore, thermosetting SMPs have received much of the attention among researchers and are commonly used as matrix materials in structural composites for their high stiffness and shape recovery force. However, the studies have been mostly conducted in tension mode. In the current work, silicon carbide whiskers (SiCws) were used to fill a hydro-epoxy resin to prepare a shape memory polymer composite. SiCws usually act as reinforcement phases to improve the property of a polymer-matrix due to their exceptional mechanical properties, low weight, high aspect ratio, high elastic modulus, chemical stability, and high thermal shock resistance [24,25,26]. Moreover, epoxy resins have been associated with a high modulus and strength, and have been widely studied and used in many kinds of structural composites [27]. Therefore, SiCws were chosen as the reinforcing phase to fill the shape memory epoxy resin. The effect of the SiCws on the mechanical properties, thermal properties, and shape memory performance of SiCw/hydro-epoxy composites were investigated.

2. Experimental

2.1. Materials

The hydro-epoxy (AL3040, epoxy value is 0.43 eq/100g) was produced by Yantai Aolifu Chemical Industry Co., Ltd. (Yantai, China). The curing agent methyl tetrahydro-phthalic anhydride (MeTHPA, molecular weight is 166.181 Da) was purchased from Xi’an Hangang Chemical Co., Ltd. (Xi’an, China). The accelerant agent 2,4,6-tris(dimethylaminomethyl) phenol (DMP-30, Molecular weight is 265.4 Da) was provided by Guangzhou Kay Trade Co., Ltd. (Guangzhou, China). Silicon carbide whiskers (SiCws, β-SiC whisker, 0.05–2.5 μm, length: diameter ≥20, purity ≥99%) were supplied by Xuzhou Hong Wu Nanomaterials Co., Ltd. (Xuzhou, China). These materials were used without further purification.

2.2. Preparation of Shape Memory SiCw/Hydro-Epoxy Composites

The samples were fabricated by incorporating different contents of high purity SiCws (4, 8, 12, and 16 wt %) into hydro-epoxy resin. Firstly, the SiCws were treated with a silane coupling agent KH-560 for surface treatment. Secondly, a certain proportion of hydro-epoxy and SiCws was stirred evenly at 80 °C, MeTHPA and DMP-30 (the weight ratio of hydro-epoxy/MeTHPA/DMP-30 = 100:80:0.8) were mixed in, and the mixture was then stirred with a magnetic stirrer until the mixture was evenly mixed. After that, the mixtures were sonicated by an ultrasonic dispersion instrument for 20 min. Finally, the mixture was poured into a glass mold for curing, and the curing temperature process was 80 °C/1 h + 110 °C/3 h + 150 °C/2 h.

2.3. Experimental Methods

In order to investigate the influence of SiCw content on the mechanical properties of SiCw/hydro-epoxy composites, blend tests at room temperature were performed with a SANS tester (Shenzhen SANS Material Test Instrument Co. Ltd., Shenzhen, China) according to ASTM D7264.
The SiCw/hydro-epoxy composites were cut into pieces of 4 × 20 × 20 mm3 and tested with a thermal constant analyzer (Hot-Disk, AB Company, Bern, Switzerland).
The SiCw/hydro-epoxy composites were cut into 5 × 10 × 30 mm3, and the samples were sanded with 800 grit sandpaper (Shandong Lianjie Engineering Materials Co., Ltd., Jinan, China). DMA was performed in a single cantilever clamping fixture and carried out using a Q800 (TA instruments company, New Castle, DE, USA). The temperature was increased to 180 °C from 20 °C at a rate of 5 °C/min, and the amplitude and dynamic load were 10 um and 1 Hz, respectively.
The specimens were frozen in liquid nitrogen and then brittle-fractured. The broken surfaces were sputter-coated with gold and observed with a SEM (INCA X-ACT, Tescan, Brno, Czech Republic).
Rectangular samples (100 × 10 × 3 mm3) were cut to investigate the thermo-active shape memory effect of the SiCw/hydro-epoxy composites. Shape memory performance of the composites were tested as follows: (i) in an oven, the samples were heated to the glass transition temperature (Tg) and held for 5 min; (ii) the samples were bent into a “U” shape and then quickly dipped into ice water, the angle recovery of the “U” shape was measured, and the shape fixity ratio (Rf) was tested; (iii) the “U”-shaped samples were placed into the oven, and the temperature of the oven was set to Tg, Tg + 10 °C, and Tg + 20 °C of the composites; (iv) the shape recovery process of the composites was observed, and, when the shape of the samples did not change, the recovery time was recorded. Figure 1 shows the shape memory model. The shape memory recovery speed is defined as θi/t, and the shape recovery ratio (Rr) is defined as (θi − θf)/θi × 100% [28], where θi is the deformation angle (°), t is the recovery time, and θf is the angle of recovery after deformation.

3. Results and Discussions

3.1. Mechanical Properties

The bending strength and tensile strength are the most important indicators revealing the mechanical property of SiCw/hydro-epoxy composites. The relationship between mechanical properties and SiCw content is shown in Figure 2 and Figure 3. From Figure 2, it can be found that, with the increase in SiCw content, the bending strength of the SiCw/hydro-epoxy composites increases when the SiCw content is less than 12 wt %. The bending strength of the bulk specimen is 72.2 MPa, and the bending strength of sample with 12 wt % SiCw increases by 64.1% compared to the 0 wt %. Figure 3 reveals that the tensile strength of SiCw /hydro-epoxy composites increases first and then decreases with the increase in SiCw content. When the content of the SiCw content is less than 8 wt %, the tensile strength of the SiCw/hydro-epoxy composites increases linearly with the increase in SiCw content. However, the tensile strength increases significantly when the SiCw content rises to 12 wt %, and the tensile strength increases about 77.16% compared with the bulk specimen. However, the tensile strength decreases when the SiCw content increases to 16 wt %. This shows that the SiCw content should be such that the mechanical properties of the SiCw/hydro-epoxy composites are improved.
Considering the effect of SiCw reinforment, the bending strength of the composites will increase [29]. However, it was noted that the bending strength of the sample with 16 wt % SiCw decreased significantly; this is due to the proper amount of SiCw can not only strengthen the matrix but also make up the micro defects present in the pure epoxy resin, which can effectively transfer the stress, prevent the crack growth, and improve the mechanical properties of the pure epoxy resin. However, too many SiCws will increase the viscosity of epoxy resin. It is easy to produce bubbles and other defects and destroy the continuous structure of epoxy resin matrix.

3.2. Thermal Properties Analyses and SEM

Thermal conductivity is one of the key factors for shape memory composites, and the high thermal conductivity favors a reduction in the shape recovery time of the SiCw/hydro-epoxy composites. Figure 4 reveals that the thermal conductivity of the composites was improved with the addition of SiCw filler, and the thermal conductivity increased with increasing SiCw content. This is because, when SiCw content is low, few SiCws are in contact with each other, and thermal conductivity is slightly improved [30]. However, with an increase in SiCw content (>12 wt %), the probability of the thermal conductivity chain and thermal conductivity network increased. Thus, the thermal conductivity increased significantly.
Dynamic mechanical analysis (DMA) is can not only be used to characterize the mechanical properties of polymers in different temperature fields, but also characterize the glass transition temperature of Tg. The Tgs of the SiCw/hydro-epoxy composites are the peaks of the tan δ curves, as shown in Figure 5. The storage modulus of the SiCw/hydro-epoxy composites are shown in Figure 6. Tg is an important parameter of the themomechanical properties and the shape memory effect of shape memory polymer composites. In this work, the shape memory transition temperature is glass transition temperature (Tg). From Figure 5, it can be found that the Tg values of the SiCw/hydro-epoxy composites slightly decrease with increasing SiCw content. This phenomenon is due to the addition of the whiskers, reducing the crosslinking density of the epoxy resin, and increasing the peristalsis ability of the molecular chain in the curing network, which leads to the decrease in the Tg values of the SiCw/hydro-epoxy composite.
The storage modulus below the shape memory transition temperature is related to the shape fixity ratio of the composites, and the storage modulus above the shape memory transition temperature is related to the shape recovery ratio [31]. It also can be found in Figure 6 that the storage modulus increases with the increase in SiCw content but decreases when SiCw content rises to 16 wt %. For further analysis, the SEM images of the samples were observed. Figure 7 indicates that, when SiCw content is lower than 12 wt %, the whiskers are dispersed in the matrix, and the whiskers cannot contact each other. The interface between the SiCws and the hydro-epoxy resin is smooth, and the fracture surface is ductile fracture. Therefore, the mechanical properties and thermal conductivity of the composites insignificantly improved. When the whisker content increased to 12 wt %, the SiCw network structure was formed in the composites, which can be useful in improving the mechanical properties and thermal conductivity of composites; however, higher SiCw content (w ≥ 16 wt %) caused a serious aggregation that resulted in bubbles in the matrix, which destroy the continuous structure of the resin. Thus, the mechanical properites of the composites decreased.

3.3. Shape Memory Property Analysis

Through the DMA analysis, it can found that the SiCw has a passive effect on the shape fixity ratio. However, because the SiCw does not have shape memory behavior, there is no doubt that the SiCw has a negative effect on the shape recovery ratio of the SiCw/hydro-epoxy composite. In order to analyze the effect of SiCw content on the shape memory properties of the hydro-epoxy system, we tested the shape memory performance of the SiCw/hydro-epoxy composite. The results are shown in Table 1, revealing that, with the increase in SiCw content in the shape memory composites, the shape recovery speed slightly decreased, the shape fixity ratio improved, and the shape recovery ratio significantly decreased. However, the shape recovery ratio of all samples was more than 95%, which indicates that the SiCw/hydro-epoxy composite is an excellent shape memory polymer composite. Figure 8 shows the shape memory process of a specimen with 8 wt % SiCw. Starting from the original shape, the specimen is deformed into a U shape in the oven. Upon cooling under load, the deformed temporary shape is fixed. Then, placing the specimen in the 56 °C oven, full recovery was observed after only 75 s.
In fact, the shape memory effect of the polymer composite is determined by two factors. One is the external condition [32]. These external conditions include the deformation amplitude, the velocity of deformation, deformation temperature, temporary fixed time, cooling rate, and deformation response times. Different conditions cause different shape memory effects. The other is the structure of the polymer composite [33]. Therefore, it is very important to control the external conditions of the shape memory polymer composites when the polymer has the same structures. In this work, we mainly analyzed the effect of the deformation temperature and cycle times on the shape memory performance of the SiCw/hydro-epoxy composites.
The sample with 12 wt % SiCw was used to investigate the effect of the deformation temperature on the shape memory effect of the SiCw/hydro-epoxy composite, as shown in Figure 9. According to the results, the slope of the curves is generally larger from 60° to 120°. This indicates that the shape recovery rate is high. However, the specimens have a relative low recovery rate at the initial and final stages. This increase is because, during the initial stage, the specimen needs time to increase temperature to that of the shape memory transition. The molecular chain slowly begins to creep, and the frozen stress begins to release gradually. After that, the frozen stress releases rapidly, and the shape recovery speed significantly increases. However, during the final stage, there is little frozen stress in the specimen, and the recovery rate thus becomes slow again.
Figure 10 shows the effect of the cycling number on the recovery ratio of SiCw/hydro-epoxy composites. It can be found that the shape recovery ratio of composites slightly decreases with increasing cycling number. However, the shape recovery ratio was gradually balanced when the cycling number was higher than 5. This phenomenon is attributed to the accumulation of plastic deformations in the composites, which inevitably occurs during the recovery process. Moreover, when the deformation occurs more than 5 times, the change in the shape recovery ratio is small, which is due to the stability of the molecular chain and plastic deformations.

4. Conclusions

A series of thermo-induced shape memory SiCw/hydro-epoxy composites were fabricated. Due to the reinforcement of the SiCws, the mechanical properties of the SiCw/hydro-epoxy composites were improved by 64.1% when SiCw content was 12 wt %. With increasing SiCw content, the shape memory transition temperatures of the SiCw/hydro-epoxy composites slightly decreased, but thermal conductivity increased. The additional SiCws improved the shape fixity ratio of SiCw/hydro-epoxy composites, but the shape recovery ratio significantly decreased because the SiCws do not have shape memory effect. The shape recovery speed increased with the increase in test temperature. Though the cycling times have a disadvantageous effect on shape memory behavior, the shape recovery ratio of the composites is higher than 90%.

Acknowledgments

This work supported by Research Program supported by the National Natural Science Foundation of China (61176130, 51305320 and 51675397), the Ningbo Natural Science Foundation (2016A610030), the 60 class General Financial Grant from the China Postdoctoral Science Foundation (2016M600765), and the Fundamental Research Funds for the Central Universities of China (JB150408 and K5051304003).

Author Contributions

Yongkun Wang and Junjie Ye conceived and designed the experiments; Yongkun Wang and Xiaohan Liu performed the experiments; Yongkun Wang and Wen Chao Tian analyzed the data; Yongkun Wang wrote the paper.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Zhao, Q.; Qi, H.J.; Xie, T. Recent progress in shape memory polymer: New behavior, enabling materials, and mechanistic understanding. Prog. Polym. Sci. 2015, 49, 79–102. [Google Scholar] [CrossRef]
  2. Michal, B.T.; Spencer, E.J.; Rowan, S.J. Stimuli-responsive reversible two-level adesion from structural dynamic shpe memory polymer. ACS Appl. Mater. Inters. 2016, 8, 11041–11049. [Google Scholar] [CrossRef] [PubMed]
  3. Meng, H.; Li, G.Q. A review of stimuli-responsive shape memory polymer composites. Polymer 2013, 54, 2199–2221. [Google Scholar] [CrossRef]
  4. Liu, Y.J.; Du, H.Y.; Liu, L.W.; Leng, J.S. Shape memory polymers and their composites in aerospace applications: A review. Smart Mater. Struct. 2014, 23, 023001. [Google Scholar] [CrossRef]
  5. Sun, L.; Huang, W.M.; Ding, Z.; Zhao, Y.; Wang, C.C.; Purnawali, H.; Tang, C. Stimulus-responsive shape memory materials: A review. Mater. Des. 2012, 33, 577–640. [Google Scholar] [CrossRef]
  6. Wang, Y.K.; Tian, W.C.; Xie, J.Q.; Liu, Y. Thermoelectric responsive shape memory graphene/hydro-epoxy composites for actuators. Micromachines 2016, 7, 145. [Google Scholar] [CrossRef]
  7. Zhao, Q.; Marc, B.; Lendlein, A. Shape-memory polymers with multiple transitions: Complex actively moving polymers. Soft Matter. 2013, 6, 1744–1755. [Google Scholar] [CrossRef]
  8. Pan, L.; Zhu, X.D.; Xie, X.M.; Liu, Y.T. Smart Hybridization of TiO2 Nanorods and Fe3O4 Nanoparticles with Pristine Graphene Nanosheets: Hierarchically Nanoengineered Ternary Heterostructures for High-Rate Lithium Storage. Adv. Funct. Mater. 2015, 25, 3341–3350. [Google Scholar] [CrossRef]
  9. Wang, Y.K.; Zhu, G.M.; Xie, J.Q.; Meng, Q.N.; Liu, T.T.; Ren, F. Mechanical and shape memory behavior of chemically cross-linked SBS/LDPE blends. J. Polym. Res. 2014, 21, 3. [Google Scholar] [CrossRef]
  10. Lv, H.B.; Yao, Y.T.; Huang, W.M.; Leng, L.S.; Hui, D. Significantly improving infrared light-induced shape recovery behavior of shape memory polymeric nanocomposite via a synergistic effect of carbon nanotube and boron nitride. Compos. Part B Eng. 2014, 62, 256–261. [Google Scholar]
  11. Jiang, Y.; Fang, L.; Kratz, K.; Lendlein, A. Influence of Compression Direction on the Shape-Memory Effect of Micro-Cylinder Arrays Prepared from Semi-Crystalline Polymer Networks. MRS Adv. 2016, 27, 1985–1993. [Google Scholar] [CrossRef]
  12. Wang, Y.K.; Zhu, G.M.; Cui, X.P.; Liu, T.T.; Liu, Z.; Wang, K. Electroactive shape memory effect of radiation cross-linked SBS/LLDPE composites filled with carbon black. Colloid Polym. Sci. 2014, 292, 2311–2317. [Google Scholar] [CrossRef]
  13. Ghosh, P.; Rao, A.; Srinivasa, A.R. Design of multi-state and smart-bias components using shape memory alloy and shape memory polymer composites. Mater. Design 2013, 44, 164. [Google Scholar] [CrossRef]
  14. Li, G.Q.; Ajisafe, O.; Meng, H. Effect of strain hardening of shape memory polymer fibers on healing efficiency of thermosetting polymer composites. Polymer 2013, 54, 920–928. [Google Scholar] [CrossRef]
  15. Fang, L.; Fang, T.Y.; Liu, X.X.; Chen, S.P.; Lu, C.H.; Xu, Z.Z. Near-Infrared Light Triggered Soft Actuators in Aqueous Media Prepared from Shape-Memory Polymer Composites. Macromol. Mater. Eng. 2016, 301, 1111. [Google Scholar] [CrossRef]
  16. Wang, Y.K.; Tian, W.C.; Zhu, G.M.; Xie, J.Q. Thermomechanical and shape memory properties of SCF/SBS/LLDPE composites. Chin. J. Polym. Sci. 2016, 34, 1354–1362. [Google Scholar]
  17. Ecker, M.; Pretsch, T. Multifunctional poly (ester urethane) laminates with encoded information. RSC Adv. 2014, 4, 286. [Google Scholar] [CrossRef]
  18. Ecker, M.; Pretsch, T. Novel design approaches for multifunctional information carriers. RSC Adv. 2014, 4, 46680. [Google Scholar] [CrossRef]
  19. Ecker, M.; Pretsch, T. Durability of switchable QR code carriers under hydrolytic and photolytic conditions. Smart Mater. Struct. 2013, 22, 094005. [Google Scholar] [CrossRef]
  20. Purnwali, H.; Xu, W.W.; Zhao, Y.; Ding, Z.; Wang, C.C.; Huang, W.M.; Fan, H. Poly (methyl methacrylate) for active disassembly. Smart Mater. Struct. 2012, 21, 075006. [Google Scholar] [CrossRef]
  21. Fritzsche, N.; Pretsch, T. Programming of temperature-memory onsets in a semicrystalline polyurethane elastomer. Macromolecules 2014, 47, 5952–5959. [Google Scholar] [CrossRef]
  22. Ma, L.; Zhao, J.; Wang, X.Y.; Chen, M.; Liang, Y.R.; Wang, Z.W.; Yu, Z.N.; Hedden, R.C. Effects of carbon black nanoparticles on two-way reversible shape memory in crosslinked polyethylene. Polymer 2015, 56, 490–497. [Google Scholar] [CrossRef]
  23. Park, J.H.; Dao, T.D.; Lee, H.; Jeong, H.M.; Kim, B.K. Properties of graphene/shape memory thermoplastic polyurethane composites actuating by various methods. Materials 2014, 7, 1520–1538. [Google Scholar] [CrossRef]
  24. Wang, M.C.; Miao, R.; He, J.K.; Xu, X.Q.; Liu, J.C.; Du, H.Y. Silicon Carbide whiskers reinforced polymer-based adhesive for joining C/C composites. Mater. Des. 2016, 99, 293–302. [Google Scholar] [CrossRef]
  25. Wang, Q.H.; Li, Y.W.; Jin, S.L.; Sang, S.B. Catalyst-free hybridization of silicon carbide whiskers and expanded graphite by vapor deposition method. Ceram. Int. 2015, 41, 14359–14366. [Google Scholar] [CrossRef]
  26. Yuan, Z.K.; Yu, J.H.; Rao, B.L.; Jiang, N.; Gao, J.; Lu, S.R. Enhanced Thermal Properties of Epoxy Composites by Using Hyperbranched Aromatic Polyamide Grafted Silicon Carbide Whiskers. Macromol. Res. 2014, 22, 405–411. [Google Scholar] [CrossRef]
  27. Kumar, K.S.S.; Biju, R.; Nair, C.P.R. Progress in shape memory epoxy resins. React. Funct. Polym. 2013, 73, 421. [Google Scholar] [CrossRef]
  28. Wang, Y.K.; Zhu, G.M.; Tang, Y.S.; Liu, T.T.; Xie, J.Q.; Ren, F. Short glass fiber reinforced radiation crosslinked shape memory SBS/LLDPE blends. J. Appl. Polym. Sci. 2014, 131, 40691. [Google Scholar]
  29. Suchanek, W.; Yashima, M.; Kakihana, M.; Yoshimura, M. Hydroxyapatite/hydroxyapatite-whisker composites without sintering additives: Mechanical properties and microstructural evolution. J. Am. Ceram. Soc. 1997, 80, 2805. [Google Scholar] [CrossRef]
  30. Gu, J.W.; Meng, X.D.; Tang, Y.S.; Li, Y.; Zhuang, Q.; Kong, J. Hexagonal boron nitride/silicone rubber dielectric thermally conductive composites with excellent thermal stabilities. Compos. Part A Appl. Sci. Manuf. 2017, 92, 27–32. [Google Scholar] [CrossRef]
  31. Wen, L.Z.; Xiao, P.; Li, Z.; Yu, X.Y.; Li, Y. Thermal cycling behavior and oxidation resistance of SiC whisker-toughened-mullite/SiC coated carbon/carbon composites in burner rig tests. Corros. Sci. 2016, 106, 179. [Google Scholar]
  32. Sabbaghianrad, S.; Langdon, T.G. Developing superplasticity in an aluminum matrix composite processed by high-pressure torsion. Mater. Sci. Eng. A Struct. 2016, 655, 36–43. [Google Scholar] [CrossRef]
  33. Wang, K.; Zhu, G.M.; Ren, F.; Yan, X.G.; Cui, X.P. The effect of carbon fiber on electroactive shape memory behaviors of cyanate-polybutadiene epoxy-carbon black composites. J. Reinf. Plast. Comp. 2016, 35, 556. [Google Scholar] [CrossRef]
Figure 1. Shape memory model.
Figure 1. Shape memory model.
Applsci 07 00108 g001
Figure 2. Bending strength of the SiCw/hydro-epoxy composites.
Figure 2. Bending strength of the SiCw/hydro-epoxy composites.
Applsci 07 00108 g002
Figure 3. Tensile strength of the SiCw/hydro-epoxy composites.
Figure 3. Tensile strength of the SiCw/hydro-epoxy composites.
Applsci 07 00108 g003
Figure 4. Thermal conductivity of SiCw/hydro-epoxy composites with different SiCw amounts.
Figure 4. Thermal conductivity of SiCw/hydro-epoxy composites with different SiCw amounts.
Applsci 07 00108 g004
Figure 5. Tan δ curves of SiCw/hydro-epoxy composites.
Figure 5. Tan δ curves of SiCw/hydro-epoxy composites.
Applsci 07 00108 g005
Figure 6. Storage modulus of SiCw/hydro-epoxy composites.
Figure 6. Storage modulus of SiCw/hydro-epoxy composites.
Applsci 07 00108 g006
Figure 7. SEM of the SiCw/hydro-epoxy composites.
Figure 7. SEM of the SiCw/hydro-epoxy composites.
Applsci 07 00108 g007
Figure 8. Shape memory process of the hydro-epoxy composites with 8 wt % SiCw at 56 °C.
Figure 8. Shape memory process of the hydro-epoxy composites with 8 wt % SiCw at 56 °C.
Applsci 07 00108 g008
Figure 9. Relationship between recovering angle and recovering time of 12 wt % SiCw/hydro-epoxy composite at different temperatures.
Figure 9. Relationship between recovering angle and recovering time of 12 wt % SiCw/hydro-epoxy composite at different temperatures.
Applsci 07 00108 g009
Figure 10. Effects of cycling number on recovery ratio of SiCw/hydro-epoxy composites.
Figure 10. Effects of cycling number on recovery ratio of SiCw/hydro-epoxy composites.
Applsci 07 00108 g010
Table 1. Effect of SiCw content on the shape memory properties of the hydro-epoxy system.
Table 1. Effect of SiCw content on the shape memory properties of the hydro-epoxy system.
SampleBulk4 wt %8 wt %12 wt %16 wt %
Vr °/s3.212.652.42.071.82
Rf/%98.599.399.8100100
Rr/%99.799.298.497.695.7

Share and Cite

MDPI and ACS Style

Wang, Y.; Tian, W.; Liu, X.; Ye, J. Thermal Sensitive Shape Memory Behavior of Epoxy Composites Reinforced with Silicon Carbide Whiskers. Appl. Sci. 2017, 7, 108. https://0-doi-org.brum.beds.ac.uk/10.3390/app7010108

AMA Style

Wang Y, Tian W, Liu X, Ye J. Thermal Sensitive Shape Memory Behavior of Epoxy Composites Reinforced with Silicon Carbide Whiskers. Applied Sciences. 2017; 7(1):108. https://0-doi-org.brum.beds.ac.uk/10.3390/app7010108

Chicago/Turabian Style

Wang, Yongkun, Wenchao Tian, Xiaohan Liu, and Junjie Ye. 2017. "Thermal Sensitive Shape Memory Behavior of Epoxy Composites Reinforced with Silicon Carbide Whiskers" Applied Sciences 7, no. 1: 108. https://0-doi-org.brum.beds.ac.uk/10.3390/app7010108

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop