Next Article in Journal
Reduced Dislocation Density of an InP/GaAs Virtual Substrate Grown by Metalorganic Chemical Vapor Deposition
Previous Article in Journal
Evaluation of the Effect of Varying the Angle of Asphaltic Concrete Core on the Behavior of the Meijaran Rockfill Dam
Previous Article in Special Issue
Friction and Wear Properties of Cr-Nx Coatings for Nuclear Fuel Cladding
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Effects of Laser-Remelting on the Microstructure, Hardness and Oscillating Wear Resistance of Atmospheric Plasma Sprayed Alumina-Rich Coatings

Materials and Surface Engineering Group, Institute of Materials Science and Engineering, Chemnitz University of Technology, 09107 Chemnitz, Germany
*
Author to whom correspondence should be addressed.
Submission received: 29 April 2022 / Revised: 12 May 2022 / Accepted: 17 May 2022 / Published: 24 May 2022
(This article belongs to the Special Issue Friction, Wear Properties and Applications of Coatings)

Abstract

:
Thermally sprayed ceramic coatings such as alumina have a specific microstructure characterized by porosity and microcracks. In addition, a process-related phase transformation from α-Al2O3 to γ-Al2O3 typically occurs, which affects the properties of the coatings compared to sintered alumina. In a previous study, simultaneous additions of Cr2O3 and TiO2 have already extended and improved the property profile of pure alumina coating (i.e., sliding wear resistance and corrosion resistance against 1N H2SO4). Depending on the powder material used, the phase composition of the coatings differs considerably, influencing the property profile. Chemical integration through reactive bonding promises a previously untapped potential for improvement. In this study, these alumina-rich ternary oxide coatings are remelted by laser, and the effect of different parameters such as speed, laser power or distance on the macro- and microstructure of the coatings is investigated. For this purpose, both light microscopic and SEM examinations are used as well as the determination of the phase composition by XRD and element distribution by EDS. The created coating microstructures are studied with respect to hardness and oscillation wear resistance.

1. Introduction

Thermally sprayed alumina coatings are used in a wide variety of applications, such as wear protection and electrical insulation, due to their high hardness and excellent dielectric strength [1,2,3,4]. The high melting temperature and low thermal conductivity of alumina result in a high difficulty of melting factor (DMF) [5,6]. Therefore, atmospheric plasma spraying process (APS) is most commonly utilized for deposition. Other thermal spray processes with lower amounts of thermal energy used for manufacturing alumina coatings are flame spraying, high velocity oxy-fuel (HVOF) spraying and detonation gun spraying (DGS) [7,8,9,10]. In all spraying processes, pure alumina shows a specific material behavior. Caused by the high cooling rates of the particles and a lower nucleation energy, a phase transformation takes place. While α-Al2O3 (corundum) is present in the powdered feedstock, the thermal sprayed coating consists predominantly of the metastable γ-Al2O3 phase [11,12,13,14]. The presence of γ-Al2O3 is generally assumed as the main reason that some alumina coating properties, such as corrosion resistance or electrical insulation, are noticeably worse than the properties of sintered alumina [1,15,16]. Retransformation of metastable γ-Al2O3 to favored α-Al2O3 can be reached through heat treatment or service temperature above 900 °C, with complete transformation occurring at 1200 °C [17,18,19]. Due to the density differences between γ-Al2O3 and α-Al2O3 as well as the large thermal stress caused by the high temperatures required, this phase retransformation is often related to extensive formation of defects in the coating, deterioration of the substrate properties or damage to the coating–substrate interface due to different thermal expansion coefficients [17,18,20].
Laser-remelting is a promising approach to realize the retransformation of α-Al2O3 and to improve the coating properties with a minimum of thermal stress on the coating–substrate composite [21,22,23,24]. In addition, in laser-remelted Al2O3-TiO2 coatings, the formation of Al2TiO5 was observed [22,23]. In general, APS coatings treated by laser-remelting show a dense and homogeneous zone but often also larger defects such as cracks as a result of the stresses [21,25,26,27,28]. After laser-remelting, the roughness of the coatings is reduced compared to the as-sprayed state [23]. Several studies show that laser-remelting can improve both the hardness and wear resistance of alumina coatings [23,24,26].
Additions of TiO2 or Cr2O3 can diversify the property profile and improve performance compared to plain alumina coatings. TiO2 additions lead to better melting behavior of the powder particles and thus improve the deposition efficiency and overall microstructure of the coating [29,30]. As a result of the reduced porosity and cracking of the coating, an increase in fracture toughness is often reported [31,32,33]. Both the lower defect level in the microstructure and the higher fracture toughness also enhance the wear resistance of Al2O3-TiO2 coatings under certain test conditions [30,33]. Cr2O3 additives, however, can improve wear resistance due to their extreme hardness. By forming an (Al,Cr)2O3 solid solution, depending on the chromium content, stabilization of the α-phase can be realized during the spraying process [13,14]. For both Cr2O3 and TiO2 additives, the effect on the actual property profile depends strongly on the type of feedstock powder used and the coating microstructure present. In a previous study, the influence of the simultaneous Cr2O3 and TiO2 additions on the microstructure and property profile of alumina-rich coatings was investigated in more detail [29]. Since these coating systems serve as the starting point for the present study, it is strongly recommended in order to achieve a better understanding.
The aim of the current study was to investigate the capability of laser-remelting to improve the wear properties of such multi-component coatings and to analyze the effects of different laser-remelting process parameters on the micro- and macrostructure of the coating. For this purpose, alumina-rich coatings (81.0 wt% Al2O3, 12.5 wt% Cr2O3, 6.5 wt% TiO2) are prepared using APS in the same way as in a previous study [29]. Despite the identical chemical composition, the coatings differ considerably in terms of their microstructure and properties. These coatings are remelted using a multi-diode laser, and the effect of different parameters of the laser process, such as power and velocity, on the macro- and microstructure and tribological properties of the coatings is investigated. Particular attention is also paid to the possibility of converting the multiphase coatings into single-phase coatings by reactions between the individual lamellae due to laser-remelting.

2. Materials and Methods

In this paper, three alumina-rich coatings are studied, having nominally the same chemical composition (81 wt% Al2O3, 12.5 wt% Cr2O3, 6.5 wt% TiO2), but differing in microstructure with regard to their porosity phase composition (i.e., blend so: multi-phase and as1: single-phase solid solution structure) and elemental distribution. For this purpose, two powder blends of fused and crushed powders were prepared, and one experimental powder feedstock was produced by agglomeration and sintering (hereinafter referred to as “as1”). The two powder blends consisted of the three single oxides (hereinafter referred to as “blend so”) and of an Al2O3-25 wt% Cr2O3 and an Al2O3-13 wt%TiO2 powder (hereinafter referred to as “blend bfc”). The feedstock powders used, the specification of the deposition by APS, and the microstructure and properties of the coatings are described in detail in a previous study [29]. In this study, these three coating systems were used to investigate the effect of laser-remelting on the microstructure and properties. Before laser-remelting, the coatings were ground and polished to produce a more comparable surface condition (roughness). A smooth surface is also essential for the determination of the vibration wear resistance. A multi-diode laser (Laserline, Lunovu, Herzogenrath, Germany) operating with a wavelength of 980 nm was used for laser-remelting. The working distance was constant at 20 mm, representing the focus spot of the laser, which has a diameter of 5 mm. The heat input into the coatings was varied by adjusting the laser power (150–450 W) and traverse speed (0.5–20 mm/s). Table 1 shows the parameter sets and the corresponding characteristic values used to obtain the best results without delamination for the respective coating types.
Cross sections were prepared using standard metallographic methods. For the evaluation of the laser-remelted tracks, images of the surface were taken using a stereo microscope MVX10 equipped with a UC90 camera (Olympus, Tokyo, Japan), and the microstructure was analyzed by scanning electron microscope (SEM) (LEO 1455VP, Zeiss, Oberkochen, Germany) using an acceleration voltage of 25 kV and backscattered electron detector (BSD). In addition, EDS analysis (GENESIS, EDAX, Mahwah, NJ, USA) was used to determine both the average chemical composition of the laser-remelted zone and the local chemical composition of the characteristic areas. To determine the average coating composition, large regions of the cross section (250 µm × 30 µm) were measured at three randomly selected locations. The local chemical composition of the characteristic areas was studied by five measuring points. The phase composition was studied by X-ray diffraction (XRD) using a D8 Discover diffractometer (Bruker AXS, Billerica, MA, USA) with a point focus (0.5 mm) operating with Co Kα radiation, a tube voltage of 35 kV, and a tube current of 40 mA. The diffraction patterns were measured for a 2θ range from 20° to 130° with a step size of 0.03° and a dwell time of 10.2 s/step.
The Vickers microhardness of the coatings was measured on the surface of the laser-remelted tracks by ten indentations with a test load of 2.94 N performed using a Wilson Tukon 1102 device (Buehler, Uzwil, Switzerland).
The wear resistance of the laser-remelted coatings was evaluated by an oscillating wear test according to ASTM G133, in which the counterbody (Al2O3 ball: 10 mm diameter, grade 10) was pushed against the oscillating moving sample with a defined test force. All test parameters are summarized in Table 2. Three repetitions were performed for each specimen. An optical 3D profilometer MikroCAS (LMI, Teltow, Germany) was used to determine the volume of the resulting wear marks.

3. Results

Figure 1 shows the images of surfaces of the laser-remelted tracks captured by a stereomicroscope. The tracks have a width of 5 mm, which corresponds to the diameter of the focus spot of the laser used. The red coloring of the laser-remelted track of the “as1” coating (Figure 1a) is particularly noticeable, whereas only a slight change in color can be observed for the laser-remelted tracks on the “blend bfc” (Figure 1b) and “blend so” (Figure 1c) coatings. Furthermore, it is noticeable that the coloring of the remelted tracks is not uniform but loses color intensity toward the edge. The transition to the initial thermally sprayed coating is clearly recognizable in all laser-remelted tracks by a thin, light coloration. In addition, severe cracks can be seen running parallel to the laser movement in the center of the track. Toward the edge, the cracks run increasingly perpendicular to the laser movement.
Figure 2 presents the SEM images of cross sections of the coatings before (a–c) and after laser-remelting (d–f). In the original state (Figure 2a–c), the coatings possess characteristics typical of thermally sprayed coatings, such as low porosity and some microcracks located along the splat boundaries or within the splats. Corresponding to the feedstock powder used, the coatings differ considerably in their phase composition. Whereas the “blend so” and “blend bfc” coatings, made from powder blends, are multiphase, the “as1” coating is largely single-phase due to the formation of an (Al,Cr,Ti)2O3 solid solution. Detailed analysis of the microstructures and properties of these coatings have already been presented in a previous study [29]. The present study is focused on the changes obtained by laser-remelting. Figure 2d–f shows the selected laser-remelted track of the respective coating system, and Figure 3 shows a detailed view of the laser-remelted zone. Significant differences can be observed, especially in the coatings made from powder blends (“blend bfc” and “blend so”).
Within the laser-remelted zone (green rectangles), the coatings no longer possess the characteristic lamellar structure, but have a relatively dense, dendritic microstructure (Figure 3b) in which boundaries of former particles/splats are no longer identifiable. In the laser-remelted zone, these coatings show a uniform shade of gray in BSD contrast. However, the laser-remelted coatings also contain defects, including small and medium pores (Figure 3a,c) and cavities (up to 30 µm) (Figure 2e, red arrow), which are mostly encapsulated in contrast to the as-sprayed state. In addition, the coatings show more severe and more frequently microcracks both in the laser-remelted zone (Figure 2f, red arrows) and in the surrounding coating (Figure 2d, cyan arrows). In addition, a transition zone (Figure 2d–f, blue rectangles) between the original coating and the laser-remelted zone can be recognized, especially in the coatings made from powder blends. This exhibits structural features that differ from both the original coating structure and the remelted edge of the coating. Furthermore, an accumulation of smaller pores (pore fringe) can be observed in the transition area (Figure 2e, white arrow).
The EDS analysis, shown in Figure 4, reveal a uniform distribution of chemical elements in the laser-remelted zone for all coatings. For the coatings made from powder blends (“blend bfc” and “blend so”), this is a particular change compared to the initial state, where the chemical composition of the individual splats differ according to the feedstock powders used. For the “as1” coating, a solid solution structure is already present in the initial state, as an experimental powder produced by agglomeration and sintering was used. Therefore, no significant differences in the chemical composition of the splats and the laser-remelted zone are detected. The average chemical composition of the coatings, as well as the chemical composition of the laser-remelted zones, are similar in the different coating systems. Only slight differences in the average chemical composition, especially with regard to the titanium content, occur in the coating and the laser-remelted zone (i.e., “as1”).
The XRD patterns, illustrated in Figure 5, show that the coatings have different phase compositions depending on the feedstock powder used. The coatings “as1” and “blend bfc” consist mainly of the differing solid solutions α- and γ-(Al,Cr,Ti)2O3. The “blend so” coatings do not contain such a solid solution and have only a small proportion of α-Al2O3. More detailed descriptions on the phase composition of the coatings as well as the changes compared to the feedstock powders due to the spraying process can be found in a previous study [29]. Conversely, the laser-remelted zones show similar XRD patterns among themselves, where the majority of the peaks can be assigned to an α-(Al,Cr,Ti)2O3 phase. What remains is a large peak at 2θ = 30.8° and smaller peaks at 2θ = 59.5°, 69.8° and 71.5°. In particular, the dominant peak at 2θ = 30.8° indicates an A2BO5 type phase with A as the trivalent element (Al3+, Cr3+ or Ti3+) and B as the tetravalent Ti4+. The structure of the A2BO5 phase is similar to phases Cr2TiO5, Al2TiO5 or Ti3O5.
From the shifted peak positions of the α- and γ-phases, the corresponding lattice parameters a and c, shown in Figure 6, were determined as an indicator of the incorporation of foreign atoms (exchange solid solution). The γ-phase in coatings “as1” and “blend bfc” show increased values for the lattice parameter a, while in the “blend so” coating, the lattice parameter a corresponds to the reference. Remarkably, the same values for lattice parameter a are determined for the “as1” and “blend bfc” coating. In the “blend so” coating, the lattice parameters a and c of the α-phase also correspond to the reference. The α-phase of the “as1” coating has larger lattice parameters a and c. In the “blend bfc” coating, two α-phases were detected in the XRD measurements. In one, the lattice parameters correspond to those of the reference, and in the other, much higher values were determined. In the laser-remelted tracks, only for the α-phase could the lattice parameters be determined, since too few other peaks were detected for the A2BO5-type phase, except for the dominant peak at 30.8°. The α-phase of the laser-remelted track on the “as1” coating has similar parameters as in the coating. In the “blend bfc” and “blend so” coatings, laser-remelting leads to an α-phase with lattice parameters significantly different from those of a-phases occurring in the coating. The α-phases in these laser-remelted zones (“blend bfc” and “blend so”) have a high similarity.
Figure 7 shows the microhardness and oscillating wear rate of the coatings and remelted tracks. All laser-remelted tracks possess an extremely high hardness on the surface on a comparable level of about 1800–1900 HV0.3. This marks a significant increase compared to the as-sprayed state and is in good agreement with other studies on laser-remelted alumina coatings [24,34]. Laser-remelting also has a positive effect on oscillating wear resistance, with a significant reduction in the wear rate compared to the as-sprayed state. The direct comparison with the literature is difficult due to the dependence of the wear rate on the tested tribological system (i.e., test parameters) and the lack of suitable references. However, studies on sliding wear already indicate an increase in wear resistance as a result of laser-remelting [24,28,35].

4. Discussion

Laser-remelting of alumina-rich multicomponent coatings using a multi-diode laser leads to a significant change in their microstructure. This becomes especially obvious in the disappearance of the typical lamellar structure of thermally sprayed coatings. As a result of the heat input, the individual lamellae/splats dissolve by reacting with each other, forming new phases that grow in dendritic structures. Despite the short process times, a largely homogeneous laser-remelted zone is formed from previously heterogeneous coating structures (e.g., “blend so”). The formation of these solid solutions can be traced by XRD measurements with determination of the lattice parameters as well as by EDS measurements. Due to the larger ionic radii of Cr3+ and Ti3+ (62 and 67 pm, respectively) compared to Al3+ (54 pm), the incorporation of these atoms into Al2O3 leads to an increase in the lattice parameters. Thus, the level of change of the lattice parameters indicates the amount of incorporated foreign atoms. Regardless of the phase composition of the coating, α-(Al,Cr,Ti)2O3 is mainly present after laser-remelting, which already existed in the homogeneous “as1“ coating. According to the determined lattice parameters, this phase is similar in all laser-remelted tracks. The slightly smaller lattice parameters for “as1” is a result of the lower proportion of atom replacement, as can be seen in the EDS measurements, which have already taken up a smaller proportion in the coating. Therefore, this lack of Cr and Ti is due to evaporation during powder production. Thus, the loss of an element because of laser-remelting can be excluded. The phase transformation of the γ-phase predominant in the coatings to the α-phase in the laser-remelted tracks reveals that the cooling rate during laser-remelting is considerably lower than during APS. Therefore, the results are consistent with previous works [21,23,24,27]. However, it has to be assumed that laser-remelting creates high residual stresses leading to defects such as cracks visible in the optical microscope. These residual stresses are likely caused by the high temperature gradient between the laser-remelted zone and the remaining coating. In addition, the residual stresses can be further increased by the volume increase induced by the γ → α phase transformation. In addition to the larger cracks, the laser-remelted zone shows other defects. Pores can either cluster as finely dispersed at the interface between the laser-remelted zone and the remaining coating, forming a pore fringe, accumulating into large cavities, forming pits at the surface, or remaining in the laser-remelted zone. When laser-remelting the “as1” coating, a network of cracks appeared in the surrounding coating as well as partial delamination at the coating–substrate interface, probably due to the defect-rich microstructure of the original coating (microcracks along the splat boundaries). A particularly thick and dense (except for large cavities) laser-remelted zone having a dendritic/columnar structure was obtained for the “blend bfc” coating. Despite the nominally identical chemical compositions, the coatings showed strongly different responses to laser treatment depending on their microstructure. All laser-remelted tracks consist of the same phase, but differ in their defect density. Despite the defects, all coatings exhibit superior microhardness, which ranks closer to the level of sintered ceramics than to that of thermally sprayed ceramic coatings. All laser-remelted tracks also show significantly enhanced resistance against oscillation wear compared to the coatings. Increased wear of the counterbody was not observed. Based on the microstructure, it is likely that the high hardness and compact microstructure of the laser-remelted coating contribute to the increase in wear behavior. Detachment or breaking out of individual splats, as occurs in the lamellar structure of thermally sprayed coatings, can be prevented by laser-remelting.

5. Conclusions

In this study, the effects of laser-remelting using a multi-diode laser on microstructure, hardness and oscillating wear of multicomponent alumina-rich coatings were investigated:
  • Laser-remelting provides a relatively dense and hard wear-resistant zone.
  • The laser-remelted zone has defects (pores), which differ depending on the laser parameters and phase composition of the initial coating.
  • In all coatings, the laser remelted zone has a compact structure that exhibits high homogeneity.
  • The lamellae/splats of the original coating react with each other and form a solid solution (α-(Al,Cr,Ti)2O3) independent of the initial phase composition. Both EDS and XRD measurements indicate the incorporation of the atoms.
  • The transformation from γ- (coating) to α-phase (laser-remelted zone) takes place.
  • Volume decrease (phase transformation) and temperature gradient result in high residual stresses, leading to cracks.
In further studies, the formation of defects and the influence of different phases on them have to be investigated in more detail in order to develop methods (such as preheating or using a pulsed CO2 laser) to reduce the defect density.

Author Contributions

Conceptualization, M.G., T.L. (Thomas Lindner) and T.L. (Thomas Lampke); investigation, M.G.; discussion, M.G., T.L. (Thomas Lindner) and T.L. (Thomas Lampke); writing—original draft preparation, M.G.; writing—review and editing, T.L. (Thomas Lindner) and T.L. (Thomas Lampke); supervision, T.L. (Thomas Lampke); project administration, T.L. (Thomas Lampke). All authors have read and agreed to the published version of the manuscript.

Funding

The APC was funded by the Deutsche Forschungsgemeinschaft (DFG, German Research Foundation) project number 491193532 and the Chemnitz University of Technology.

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

Not applicable.

Acknowledgments

The authors would like to specifically thank Robert Glaßmann, Marc Pügner, Christian Loos and Niclas Hanisch for their great assistance in the laser-remelting process, metallographic preparation, XRD measurement and wear testing.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Berger, L.-M. Tribology of Thermally Sprayed Coatings in the Al2O3-Cr2O3-TiO2 System. In Thermal Sprayed Coatings and Their Tribological Performances; Roy, M., Davim, J.P., Eds.; IGI Global: Hershey, PA, USA, 2015; pp. 227–267. ISBN 9781466674899. [Google Scholar]
  2. Sampath, S. Thermal Spray Applications in Electronics and Sensors: Past, Present, and Future. J. Therm. Spray Technol. 2010, 19, 921–949. [Google Scholar] [CrossRef] [Green Version]
  3. Toma, F.-L.; Scheitz, S.; Berger, L.-M.; Sauchuk, V.; Kusnezoff, M.; Thiele, S. Comparative Study of the Electrical Properties and Characteristics of Thermally Sprayed Alumina and Spinel Coatings. J. Therm. Spray Technol. 2011, 20, 195–204. [Google Scholar] [CrossRef]
  4. Mohammadian Bajgiran, M.; Rezvani Rad, M.; McDonald, A.; Moreau, C. Microstructure, phase and dielectric strength of thermally sprayed alumina layers in coating-based heating systems. Int. J. Appl. Ceram. Technol. 2021, 18, 1641–1656. [Google Scholar] [CrossRef]
  5. Grimm, M.; Conze, S.; Berger, L.-M.; Paczkowski, G.; Drehmann, R.; Lampke, T. Changes in the coating composition due to aps process conditions for Al2O3-Cr2O3-TiO2 ternary powder blends. J. Therm. Spray Technol. 2021, 30, 168–180. [Google Scholar] [CrossRef]
  6. McPherson, R. The relationship between the mechanism of formation, microstructure and properties of plasma-sprayed coatings. Thin Solid Films 1981, 83, 297–310. [Google Scholar] [CrossRef]
  7. Habib, K.A.; Saura, J.J.; Ferrer, C.; Damra, M.S.; Giménez, E.; Cabedo, L. Comparison of flame sprayed Al2O3/TiO2 coatings: Their microstructure, mechanical properties and tribology behavior. Surf. Coat. Technol. 2006, 201, 1436–1443. [Google Scholar] [CrossRef]
  8. Niemi, K.; Vuoristo, P.; Mäntylä, T. Properties of alumina-based coatings deposited by plasma spray and detonation gun spray processes. J. Therm. Spray Technol. 1994, 3, 199–203. [Google Scholar] [CrossRef]
  9. Shakhova, I.; Mironov, E.; Azarmi, F.; Safonov, A. Thermo-electrical properties of the alumina coatings deposited by different thermal spraying technologies. Ceram. Int. 2017, 43, 15392–15401. [Google Scholar] [CrossRef]
  10. Toma, F.-L.; Stahr, C.C.; Berger, L.-M.; Saaro, S.; Herrmann, M.; Deska, D.; Michael, G. Corrosion resistance of APS- and HVOF-sprayed coatings in the Al2O3-TiO2 system. J. Therm. Spray Technol. 2010, 19, 137–147. [Google Scholar] [CrossRef]
  11. McPherson, R. Formation of metastable phases in flame- and plasma-prepared alumina. J. Mater. Sci. 1973, 8, 851–858. [Google Scholar] [CrossRef]
  12. McPherson, R. On the formation of thermally sprayed alumina coatings. J. Mater. Sci. 1980, 15, 3141–3149. [Google Scholar] [CrossRef]
  13. Chráska, P.; Dubsky, J.; Neufuss, K.; Písacka, J. Alumina-base plasma-sprayed materials part I: Phase stability of alumina and alumina-chromia. J. Therm. Spray Technol. 1997, 6, 320–326. [Google Scholar] [CrossRef]
  14. Stahr, C.C.; Saaro, S.; Berger, L.-M.; Dubský, J.; Neufuss, K.; Herrmann, M. Dependence of the stabilization of α-alumina on the spray process. J. Therm. Spray Technol. 2007, 16, 822–830. [Google Scholar] [CrossRef]
  15. Gao, J.; Xiong, X.; Gao, Y. The effect of the α/γ phase on the dielectric properties of plasma sprayed Al2O3 coatings. J. Mater. Sci. Mater. Electron. 2017, 28, 12015–12020. [Google Scholar] [CrossRef]
  16. Herrmann, M.; Toma, F.-L.; Berger, L.-M.; Kaiser, G.; Stahr, C.C. Comparative study of the corrosion resistance of thermally sprayed ceramic coatings and their bulk ceramic counterparts. J. Eur. Ceram. Soc. 2014, 34, 493–504. [Google Scholar] [CrossRef]
  17. Thompson, V.S.; Whittemore, O.J. Structural changes on reheating plasma-sprayed alumina. Am. Ceram. Soc. Bull. 1967, 46, 637–641. [Google Scholar]
  18. Heintze, G.N.; Uematsu, S. Preparation and structures of plasma-sprayed γ- and α-Al2O3 coatings. Surf. Coat. Technol. 1992, 50, 213–222. [Google Scholar] [CrossRef]
  19. Dhakar, B.; Namdeo, A.; Chatterjee, S.; Sabiruddin, K. Heat treatment of plasma sprayed alumina-chromia composite coatings. Surf. Eng. 2018, 34, 737–746. [Google Scholar] [CrossRef]
  20. Caruso, K.S.; Drewry, D.G.; King, D.E.; Jones, J.S. Heat treatment of plasma-sprayed alumina: Evolution of microstructure and optical properties. In Advanced Ceramic Coatings and Interfaces II; Schulz, U., Lin, H.-T., Salem, J., Zhu, D., Eds.; John Wiley & Sons, Inc.: Hoboken, NJ, USA, 2007; pp. 175–192. ISBN 9780470339510. [Google Scholar]
  21. Das, B.; Nath, A.K.; Bandyopadhyay, P.P. Online monitoring of laser-remelting of plasma sprayed coatings to study the effect of cooling rate on residual stress and mechanical properties. Ceram. Int. 2018, 44, 7524–7534. [Google Scholar] [CrossRef]
  22. Li, C.G.; Yu, Z.S.; Zhang, Y.F.; Zhang, P.L.; Yan, H.; Lu, Q.H.; Li, W.G.; Wang, Y. Microstructure evolution of laser remelted Al2O3–13wt.%TiO2 coatings. J. Alloys Compd. 2013, 576, 187–194. [Google Scholar] [CrossRef]
  23. Wang, Y.; Li, C.G.; Tian, W.; Yang, Y. Laser surface remelting of plasma sprayed nanostructured Al2O3–13wt%TiO2 coatings on titanium alloy. Appl. Surf. Sci. 2009, 255, 8603–8610. [Google Scholar] [CrossRef]
  24. Yuanzheng, Y.; Youlan, Z.; Zhengyi, L.; Yuzhi, C. Laser-remelting of plasma sprayed Al2O3 ceramic coatings and subsequent wear resistance. Mater. Sci. Eng. A 2000, 291, 168–172. [Google Scholar] [CrossRef]
  25. Das, B.; Gopinath, M.; Nath, A.K.; Bandyopadhyay, P.P. Effect of cooling rate on residual stress and mechanical properties of laser remelted ceramic coating. J. Eur. Ceram. Soc. 2018, 38, 3932–3944. [Google Scholar] [CrossRef]
  26. Das, B.; Nath, A.; Bandyopadhyay, P.P. Scratch resistance and damage mechanism of laser remelted thermally sprayed ceramic coating. Surf. Coat. Technol. 2019, 364, 157–169. [Google Scholar] [CrossRef]
  27. Sivakumar, R.; Mordike, B.L. Laser melting of plasma sprayed ceramic coatings. Surf. Eng. 1988, 4, 127–140. [Google Scholar] [CrossRef]
  28. Szafarska, M.; Iwaszko, J. Laser-remelting treatment of plasma-sprayed Cr2O3 oxide coatings. Arch. Metall. Mater. 2012, 57, 215–221. [Google Scholar] [CrossRef]
  29. Conze, S.; Grimm, M.; Berger, L.-M.; Thiele, S.; Drehmann, R.; Lampke, T. Influence of simultaneous Cr2O3 and TiO2 additions on the microstructure and properties of APS alumina coatings. Surf. Coat. Technol. 2021, 405, 126702. [Google Scholar] [CrossRef]
  30. Grimm, M.; Conze, S.; Berger, L.-M.; Drehmann, R.; Lampke, T. Microstructure and properties of atmospheric plasma sprayed (Al,Cr)2O3–TiO2 coatings from blends. J. Therm. Spray Technol. 2022, 31, 256–268. [Google Scholar] [CrossRef]
  31. Ghazali, M.J.; Forghani, S.M.; Hassanuddin, N.; Muchtar, A.; Daud, A.R. Comparative wear study of plasma sprayed TiO2 and Al2O3–TiO2 on mild steels. Tribol. Int. 2016, 93, 681–686. [Google Scholar] [CrossRef]
  32. Yılmaz, R.; Kurt, A.O.; Demir, A.; Tatlı, Z. Effects of TiO2 on the mechanical properties of the Al2O3–TiO2 plasma sprayed coating. J. Eur. Ceram. Soc. 2007, 27, 1319–1323. [Google Scholar] [CrossRef]
  33. Fervel, V.; Normand, B.; Coddet, C. Tribological behavior of plasma sprayed Al2O3-based cermet coatings. Wear 1999, 230, 70–77. [Google Scholar] [CrossRef]
  34. Szkodo, M.; Bień, A.; Antoszkiewicz, M. Effect of plasma sprayed and laser re-melted Al2O3 coatings on hardness and wear properties of stainless steel. Ceram. Int. 2016, 42, 11275–11284. [Google Scholar] [CrossRef]
  35. Yang, K.; Li, J.; Wang, Q.; Li, Z.; Jiang, Y.; Bao, Y. Effect of laser-remelting on microstructure and wear resistance of plasma sprayed Al2O3-40%TiO2 coating. Wear 2019, 426–427, 314–318. [Google Scholar] [CrossRef]
Figure 1. Top-view images of the laser-remelted tracks of the coatings: (a) as1, (b) blend bfc, (c) blend so, with severe cracks in the direction of laser movement (black arrows).
Figure 1. Top-view images of the laser-remelted tracks of the coatings: (a) as1, (b) blend bfc, (c) blend so, with severe cracks in the direction of laser movement (black arrows).
Coatings 12 00721 g001
Figure 2. SEM images of the cross-sections of the coatings before (upper row) and after (lower row) laser-remelting treatment: (a,d) as1, (b,e) blend bfc and (c,f) blend so. After laser-remelting treatment, coatings show a laser-remelted zone (green rectangle), in which the original lamellar structure in no longer noticeable, and a transition zone (blue rectangle). In both zones and in the original coating underneath, numerous defects such as pores, microcracks or local delamination (marked by arrows) can be found.
Figure 2. SEM images of the cross-sections of the coatings before (upper row) and after (lower row) laser-remelting treatment: (a,d) as1, (b,e) blend bfc and (c,f) blend so. After laser-remelting treatment, coatings show a laser-remelted zone (green rectangle), in which the original lamellar structure in no longer noticeable, and a transition zone (blue rectangle). In both zones and in the original coating underneath, numerous defects such as pores, microcracks or local delamination (marked by arrows) can be found.
Coatings 12 00721 g002
Figure 3. SEM images (detailed view) of the laser-remelted zone of the coatings: (a) as1, (b) blend bfc and (c) blend so.
Figure 3. SEM images (detailed view) of the laser-remelted zone of the coatings: (a) as1, (b) blend bfc and (c) blend so.
Coatings 12 00721 g003
Figure 4. EDS analysis of the laser-remelted tracks compared to the initial state of the coatings described in more detail in a previous study [29]. Uniform element distribution and only a slight change in chemical composition (compared to average composition of the coating) due to dissolving and reaction of the individual splats.
Figure 4. EDS analysis of the laser-remelted tracks compared to the initial state of the coatings described in more detail in a previous study [29]. Uniform element distribution and only a slight change in chemical composition (compared to average composition of the coating) due to dissolving and reaction of the individual splats.
Coatings 12 00721 g004
Figure 5. Diffraction patterns of initial coating and respective laser-remelted track: (a) as1, (b) blend bfc and (c) blend so.
Figure 5. Diffraction patterns of initial coating and respective laser-remelted track: (a) as1, (b) blend bfc and (c) blend so.
Coatings 12 00721 g005
Figure 6. Lattice parameters of the γ- and α-phases of the coatings (left) and laser-remelted tracks (right). Shift of lattice parameters indicates incorporation of foreign atoms (exchange solid solution).
Figure 6. Lattice parameters of the γ- and α-phases of the coatings (left) and laser-remelted tracks (right). Shift of lattice parameters indicates incorporation of foreign atoms (exchange solid solution).
Coatings 12 00721 g006
Figure 7. Oscillating wear rate and microhardness of coatings and laser-remelted tracks. Significant improvements due to laser-remelting.
Figure 7. Oscillating wear rate and microhardness of coatings and laser-remelted tracks. Significant improvements due to laser-remelting.
Coatings 12 00721 g007
Table 1. Parameter sets used for laser-remelting of ternary oxide coatings.
Table 1. Parameter sets used for laser-remelting of ternary oxide coatings.
SystemLaser Power
Pel (W)
Traverse Speed
ν (mm/s)
Energy Density 1
(J/mm²)
as1 ((Al,Cr,Ti)2O3)225145
blend bfc ((Al,Cr)2O3 + Al2O3 − TiO2)200140
blend so (Al2O3 + Cr2O3 + TiO2)300106
1 Energy density J is calculated from J = Pel/(ν·D) [24]; D: diameter focus point.
Table 2. Parameters of oscillating wear test.
Table 2. Parameters of oscillating wear test.
Force
(N)
Frequency
(Hz)
Time
(s)
Amplitude
(mm)
Counterbody
MaterialDiameter (mm)
16406000.5Al2O310
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Grimm, M.; Lindner, T.; Lampke, T. Effects of Laser-Remelting on the Microstructure, Hardness and Oscillating Wear Resistance of Atmospheric Plasma Sprayed Alumina-Rich Coatings. Coatings 2022, 12, 721. https://0-doi-org.brum.beds.ac.uk/10.3390/coatings12060721

AMA Style

Grimm M, Lindner T, Lampke T. Effects of Laser-Remelting on the Microstructure, Hardness and Oscillating Wear Resistance of Atmospheric Plasma Sprayed Alumina-Rich Coatings. Coatings. 2022; 12(6):721. https://0-doi-org.brum.beds.ac.uk/10.3390/coatings12060721

Chicago/Turabian Style

Grimm, Maximilian, Thomas Lindner, and Thomas Lampke. 2022. "Effects of Laser-Remelting on the Microstructure, Hardness and Oscillating Wear Resistance of Atmospheric Plasma Sprayed Alumina-Rich Coatings" Coatings 12, no. 6: 721. https://0-doi-org.brum.beds.ac.uk/10.3390/coatings12060721

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.