Next Article in Journal
Asymmetric Michael Addition of Malononitrile with Chalcones via Rosin-Derived Bifunctional Squaramide
Next Article in Special Issue
Hydrotreating of Methyl Esters to Produce Green Diesel over Co- and Ni-Containing Zr-SBA-15 Catalysts
Previous Article in Journal
Structural Evolution of Ni-Based Co-Catalysts on [Ca2Nb3O10]− Nanosheets during Heating and Their Photocatalytic Properties
Previous Article in Special Issue
SBA-15 Anchored Metal Containing Catalysts in the Oxidative Desulfurization Process
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Catalysts
Volume 10
Issue 1
10.3390/catal10010012
catalysts-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Mesoporous Silica Nanosheets with Tunable Pore Lengths Supporting Metal Nanoparticles for Enhanced Hydrogenation Reactions

by
Xiaohui Wang
1,*,
Xin Ding
1 and
Houbing Zou
2,*
1
College of Chemistry and Chemical Engineering, Inner Mongolia University for the Nationalities, Tongliao 028000, China
2
School of Chemistry and Chemical Engineering, Shanxi University, Taiyuan 030006, China
*
Authors to whom correspondence should be addressed.
Catalysts 2020, 10(1), 12; https://0-doi-org.brum.beds.ac.uk/10.3390/catal10010012
Submission received: 2 December 2019 / Revised: 18 December 2019 / Accepted: 18 December 2019 / Published: 20 December 2019
(This article belongs to the Special Issue SBA-15 and Catalysis)
Browse Figures
Versions Notes

Abstract

:
The channel lengths of mesoporous materials have a crucial impact on the catalytic performances of as-loaded active components. However, it remains a challenge to precisely tune the mesochannel length in a wide range from ≤50 nm to 200 nm. In this paper, we developed a top-down strategy, that is to say, crushing hollow microspheres, for preparing mesoporous silica nanosheets (MSSs) with perpendicular mesochannels and tunable thicknesses. Owing to the heterogeneous growth of the mesoporous silica layer on the surfaces of polystyrene microspheres (hard template), it was achieved to regulate the mesochannel length continuously in the range of 20–200 nm. The obtained materials were characterized by X-ray diffraction (XRD), nitrogen sorption, scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The effect of channel lengths on the catalytic activity of metal nanoparticles was then investigated in the selective hydrogenation reaction of nitroarenes. It was found that a short channel not only favored dispersing metal nanoparticles uniformly and then avoiding pore blocking, but also improved the accessibility of metal nanoparticles largely during reactions.

Graphical Abstract

1. Introduction

Owing to the high surface area, tunable pore structures and diverse surface functionalization, mesoporous silicas have been widely employed as a solid support to immobilize catalytic active metal nanoparticles for heterogeneous catalysis [1,2,3,4,5,6]. Their uniform mesochannels can not only provide a confined nanospace for protecting the metal nanoparticles from sintering and leaching out, but also afford an efficient mass transport for reactants and intermediates as well as products [7,8,9]. Over the past decades, a variety of metal nanoparticles, including bimetallic and even multimetallic catalysts, have been loaded inside mesoporous silicas for improving their catalytic performances largely [10,11,12,13,14,15,16,17,18,19]. However, for the conventional order mesoporous silicas such as MCM-41 and SBA-15, their micrometer-sized bulk morphology and parallel channels often lead to limited pore accessibility [20]. This lowers the molecular diffusion rate significantly and produces an issue of pore blocking during the process of loading metal nanoparticles. Therefore, designing new mesoporous materials with short mesochannels is desirable to optimize the diffusion process and the pore accessibility, and then to further enhance the catalytic properties of metal nanoparticles.
An alternative strategy to shorten the mesochannel lengths is to prepare mesoporous materials with two-dimensional (2D) morphologies of platelet/sheet and perpendicular mesochannels [21,22,23]. In 2004, Chen and co-workers reported the fabrication of SBA-15 platelets with vertical channels via using a ternary surfactant system as the structure-directing agent [24]. Inspired by their success, different surfactants and additives were attempted to prepare mesoporous silica platelets with uniform morphology and tunable channel length. For example, Tomczk et al. reported a biomimetic approach for synthesizing hexagonal silica platelets [25], in which a polypeptide was employed as the soft template. NH4F and Zr(IV) ions were also used as the additive to tailor the coassembly process of surfactants and inorganic precursors, then guiding the formation of SBA-15 platelets [26]. Although great progress has been achieved, however, the mesoporous silica platelets prepared via aforementioned bottom-up methods still showed a mesochannel length of ≥150 nm. More importantly, it is still very difficult for these bottom-up approaches to precisely adjust the channel length from ≤50 nm to 200 nm due to the limit in tuning the coassembly between the surfactants and the inorganic precursors in nanoscale.
In comparison to the bottom-up approaches, top-down routes often show advantages in simplifying the fabrication procedures and tailoring the structure parameters of as-obtained materials [27,28,29,30]. Very recently, we reported Janus mesoporous silica nanosheets with two distinct surfaces via a top-down strategy of crushing hollow microspheres [31]. In this work, such a simple strategy was extended to precisely tune the channel lengths of mesoporous silica nanosheets (MSSs) and the effect of channel lengths on the catalytic performance of as-loaded active components was investigated. Because the co-assembly process of the surfactants and the inorganic precursors occurred on the surfaces of polystyrene microspheres (hard template), the thickness of the formed mesoporous silica layer could be easily adjusted in the range of 20–200 nm. Then a precise modulation can be achieved on the mesochannel length. The obtained materials were characterized by X-ray diffraction (XRD), nitrogen sorption, scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Finally, the Pd nanoparticles were introduced into MSSs and the effect of the channel lengths was studied on the catalytic performance of Pd nanoparticles in the selective hydrogenation reaction of nitroarenes.

2. Results and Discussions

The synthetic route for the mesoporous silica nanosheets (MSSs) with tunable thicknesses is shown in the Figure 1a. Firstly, mesoporous silica with vertical channels was coated on the surfaces of polystyrene microspheres via a well-defined, wet-chemistry method (Figure 1b,c), in which hexadecyltrimethylammonium bromide (CTAB) and ammonia were respectively used as the surfactant and the base catalyst. Then a calcination process was performed to remove the surfactant molecule (CTAB) and the hard template (polystyrene), presenting mesoporous silica hollow microspheres with open mesochannels. Figure 1d shows the SEM image of broken hollow microspheres. Finally, a simple grinding results in the formation of MSSs. Because the thickness of the mesoporous silica layer on the polystyrene microspheres is highly controllable due to its heterogeneous growth, the channel length of MSSs can be facilely tailored. As shown in Figure 1e, the as-obtained sample (denoted as MSSs-40) has a morphology of an irregular nanosheet. The diameter of these nanosheets broadly distributes in the range of 200–800 nm. The irregular morphology and the broad particle size distribution are the typical feature of top-down strategy for preparing nanomaterials. The cross-sectional SEM image further indicates that the nanosheet thickness is nearly 40 nm (the inset in Figure 1e), in good agreement with the shell thickness of the hollow microsphere. Moreover, the TEM image confirms the morphology of irregular nanosheet, and reveals that a uniform mesoporous structure appears in these nanosheets (Figure 1f). The HRTEM image further indicates that the mesochannels are perpendicular to the nanosheets, as evidenced by the distinct hexagonal pattern (indicated by a white box in Figure 1g), which is similar to the (110) direction of MCM-41 materials [32]. In addition, it must be noted that these nanosheets also possess many defect structures (indicated by a yellow cycle in Figure 1g), which are likely resulted from the drastic grinding process. Such a defect structure is expected to assist the mesochannels to further improve the molecule diffusion.
Figure 2 shows the SEM and TEM images of the sample MSSs with a bigger thickness (denoted as MSSs-75 and MSSs-120) prepared via increasing the amount of tetraethylorthosilicate from 0.3 mL to 0.5 mL and 0.8 mL under the same conditions. It is clear that both of these samples show a morphology of an irregular nanosheet with a broad particle size distribution (Figure 2a,d), which is identical to that of MSSs-40. Whereas, the cross-sectional SEM images show that their thicknesses are respectively 75 nm and 120 nm (the inset in Figure 2a,d). The TEM and HRTEM images further confirm the uniform mesoporous structures of MSSs-75 and MSSs-120. Their mesochannels are also perpendicular to the nanosheets, keeping consistent with that of MSSs-40. Additionally, it is worth mentioning that the defect structures of MSSs-75 and MSSs-120 are less than that of MSSs-40. This is likely due to their bigger thicknesses that can avoid beingdestroyed during the drastic grinding process. All these results demonstrate that we have successfully obtained mesoporous silica nanosheets with tunable channel lengths via a facile top-down strategy.
The mesoporous structure of three MSSs samples were further characterized by X-ray diffraction (XRD) and nitrogen sorption. As shown in the Figure 3a, the small-angle XRD patterns of three MSSs samples all display one sharp diffraction peak and one weak diffraction peak at 2θ values of approximately 2.2 and 4.0 degrees, which can be indexed as the (100) and (110) reflections of a hexagonal mesophase (space group p6mm). This suggests that they have a partly ordered mesopore array. Moreover, a gradually increased structure order can be seen along with the increase of nanosheet thickness, which may be caused by the domain-size increase of the ordered mesostructure [33]. The nitrogen adsorption–desorption isotherms of three MSSs samples show a type IV curve according to the IUPAC classification (Figure 3b). A sharp capillary condensation step can also be clearly observed in the P/P0 range of 0.1–0.4. These results indicate that three MSSs samples have a uniform mesoporous structure. Furthermore, their corresponding Barrett–Joyner–Halenda (BJH (1951)) pore size distribution curves reveal a sharp distribution (Figure 3b), suggesting a uniform mesoporous structure. The average pore diameter is approximately 2.54 nm. Meanwhile, the sample MSSs-40 distinctly shows a secondary mesopore centered at 4.2 nm, which could be assigned to the defect structure of nanosheets. This mesopore is gradually disappeared in the pore size distribution curves along with the increase of the nanosheet thickness, indicating that the defect structure is gradually decreased and even disappeared. The Brunauer–Emmett–Teller (BET (1938)) surface areas of MSSs-40, MSSs-75 and MSSs-120 are 927.2 m2 g−1, 923.9 m2 g−1 and 1016.1 m2 g−1 (Table 1), respectively. Their total pore volumes are 0.75 cm3 g−1, 0.68 cm3 g−1 and 0.66 cm3 g−1, respectively. These results further confirm the partly ordered mesoporous structures of MSSs samples, keeping highly consistent with the results of the TEM images.
The metal Pd nanoparticles were introduced into the mesochannels of MSSs via a simple impregnation–reduction route. In order to anchor the Pd nanoparticles uniformly inside the channels, the –NH2 group was modified on the mesopore surfaces by a post-grafting process. From the TEM images in Figure 4a,b, we can see that the Pd nanoparticles are uniformly loaded in the sample MSSs, and the metal loading process has no obvious influence upon the morphology of MSSs. The HRTEM image further reveals that the particle size of Pd nanoparticles distributes in the range from 1–6 nm with an average size of 3.0 nm (Figure 4b). It is distinct that there is no aggregation of metal nanoparticles occurring on the mesochannels of MSSs, which should be attributed to the short pore channels and as-provided fast molecule diffusion. Although the large Pd nanoparticles (e.g. ≥5 nm) cannot be immobilized inside the mesochannels of MSSs, their defect structures are big enough to accommodate the large Pd nanoparticles, as indicated by the white box (Figure 4a). The high-angle, annular dark-field scanning TEM (HAADF-STEM) image confirms that the ultrafine Pd nanoparticles are uniformly distributed in the vertical mesochannels (Figure 4c). Furthermore, elemental mapping obtained using energy-dispersive X-ray spectroscopy (EDX) shows a homogeneous distribution of Si, O, C and Pd elements throughout the nanosheet (Figure 4d–g). The loading amount of Pd was further identified to be 2.0 wt% by inductively coupled plasma mass spectrometry (ICP). These results clearly indicate that the short mesochannels of MSSs are very beneficial to uniformly dispersing ultrafine metal nanoparticles in the mesoporous materials. For comparison, the Pd nanoparticles were also supported in the conventional MCM-41 under the same conditions.
Selective hydrogenation of nitroarenes is an environmentally benign and highly efficient process for producing anilines which are key intermediates for the manufacture of fine chemicals, pharmaceuticals and agrochemicals [34,35,36,37]. In the current study, the catalytic performances of Pd-loaded MSSs with different pore lengths were evaluated in the selective transformation of nitrobenzene to aniline. As shown in Figure 5a, the sample Pd/MSSs-40 presents a conversion of nearly 100% within 2 h. Whereas, the sample Pd/MSSs-75 and Pd/MSSs-120 with a longer channel length can only give a conversion of 57.6% and 38.4% under the same conditions, respectively. Pd/MSSs-75 needs 5 h to full convert the substrate, and Pd/MSSs-120 obtains a conversion of only 83.8% within 5 h. Moreover, using the conventional Pd/MCM-41 as the catalyst, a conversion of only 55.5% is obtained under the same conditions, which is much lower than those of the Pd/MSSs samples. This result indicates that the morphology of mesoporous materials indeed has an important influence on the catalytic activity of as-supported metal nanoparticles. In order to compare their catalytic activities more distinctly, the turnover frequencies (TOFs) of the catalysts were calculated according to the conversion of nearly 30%. It can be clearly seen that the TOF of Pd/MSSs-40 is much higher than those of other catalysts (Figure 5b), which is 2.18-fold, 3.53-fold and 6.0-fold higher than that of Pd/MSSs-75, Pd/MSSs-120 and Pd/MCM-41, respectively.
These results reveal that the channel length of mesoporous materials plays a critical role in improving the catalytic activities of the as-supported metal nanoparticles. The shorter is the channel length, the higher is the catalytic activity. Considering the similar BET surface area and pore volume (Table 1), this is likely due to the fact that a short mesochannel can largely enhance the reactants and products to diffuse into and out from the channel [38,39], thus presenting a higher accessibility towards metal nanoparticles. In addition, it is interesting to observe that a significant activity enhancement is realized once the channel length is decreased to below 50 nm (comparing the activity of Pd/MSSs-40 and Pd/MSSs-75). This suggests that a mesochannel with a length of ≤50 nm can promote the molecule diffusion rate largely.
Considering the largely improved catalytic activity, the substrate scope and the catalytic stability were then examined. As shown in the Table 2, we can see that a conversion of nearly 99% can be always obtained in selectively hydrogenating nitrobenzene with different substituted groups including –CH3, –C2H5, –OH, –OCH3 and –NH2 (1a, 1e–1h). Multi-groups substituted nitrobenzene can also be efficiently converted into corresponding aniline (1d). It is also found that the substituted position of nitroarenes has no influence on the catalytic activity (1a–1c). These results clearly reveal a high versatility of the catalyst Pd/MSSs-40. Moreover, we found that the catalyst Pd/MSSs-40 had a good reusability. After being used for five times continually, Pd/MSSs-40 still showed a conversion of ≥ 97% with an aniline selectivity of ≥ 98% (Figure 5c). We characterized the recovered catalysts after the fifth reaction and the TEM image indicates that there is no distinct aggregation in the metal nanoparticles (Figure 5d). This should be attributed to the anchoring effect of –NH2 and the confinement effect of the mesochannels, resulting in the superior catalytic stability of Pd/MSSs-40.

3. Experimental Section

3.1. Chemicals

Tetraethylorthosilicate (TEOS, 98%), aqueous ammonia (NH3·H2O, 28%) and cetyltrimethylammonium bromide (CTAB, 99.0%), styrene (>99%) were purchased from Sinopharm Chemical Reagent (Shanghai, China). 3-aminopropyltriethyoxylsilane (APTES, 96%) was obtained from Meryer. Poly(vinyl pyrrolidone) (PVP, MW = 40000) and 2,2-azobis(2-methylpropionitrile) (AIBN) were obtained from Beijing Solarbio Science and Technology Co., Ltd (Beijing, China). Sodium tetrachloropalladate (II) (Na2PdCl4, 98%) and all nitroaromatics were purchased from Aladdin(Shanghai, China). All chemicals were used as received without any further purification.

3.2. Synthesis of Mesoporous Silica Nanosheets with Tunable Thickness

Firstly, we prepared polystyrene microspheres via a previous publication. Typically, styrene (30 mL), PVP (2.25 g), AIBN (0.5 g), ethanol (95 mL), and water (3 mL) were added to a 250-mL single bottle with a reflux condenser and a nitrogen gas inlet. The air in the flask was replaced by a stream of nitrogen, and the mixture was kept under nitrogen until the polymerization was finished. The polymerization was carried out at 70 °C for 24 h with a low stirring rate. The product was collected by filtration and washed with ethanol. Then, 0.96 g of polystyrene microspheres was dispersed in a mixture of ethanol (60 mL), water (50 mL) and NH3·H2O (0.4 mL, 28 wt%). A solution of CTAB (0.48 g) dissolved in a mixture containing water (8 mL) and ethanol (4 mL) was then added. After the mixture was stirred for 30 min, TEOS (0.3 mL) was quickly added. The obtained mixture was thereafter stirred at 25 °C for 6 h. After that, temperature was increased to 80 °C, and the mixture was kept undisturbed overnight. The resulting solid PS@mSiO2 were collected by centrifugation and washed with deionized water. The surfactant CTAB and polystyrene were subsequently removed via a simple calcination at 550 °C for 6 h, presenting mesoporous silica hollow microspheres. Finally, the mesosilica nanosheets were obtained by a simple grind. Generally, 20 min was essential to crushing the hollow microspheres. Adjusting the amount of TEOS leaded to the formation of mesosilica nanosheets with tunable thickness.

3.3. LoadingPd Nanoparticles in Mesoporous Silica Nanosheets with Tunable Thickness

Before loading Pd nanoparticles, the –NH2 group was grafted on the mesopore surfaces of mesosilica nanosheets by a simple process of surface modification. Typically, 200 mg of mesosilica nanosheets were dispersed in 20 mL of toluene containing APTES (0.1 mL) and triethylamine (0.05 mL). The mixture was refluxed for 4 h at 120 °C. The solid was recovered by centrifugation and washed with ethanol and deionized water. Then the Pd nanoparticles were introduced into the mesochannels of the mesosilica nanosheet via a simple impregnation–reduction route. Specifically, 200 mg of NH2-modified mesosilica nanosheets were dispersed in 50 mL of deionized water via sonication. After the fresh Na2PdCl4 aqueous solution (20 mm, 1.9 mL) was added dropwise, the mixture was stirred for 4 h at 30 °C. Then 0.1 M fresh NaBH4 solution (2.0 mL) was added dropwise, and the mixture was aged at the same temperature for 24 h. The solid was isolated by centrifugation and washed four times with ethanol. Finally, we obtained the catalyst after drying at 80 °C under vacuum for 6 h.

3.4. Catalytic Test

0.5 mmol of nitroarene, Pd catalysts (0.2 mol%), and 4.0 mL of ethanol were mixed in a 25 mL round-bottomed flask equipped with a reflux condenser. The solution was sealed and purged three times with hydrogen to remove the air at room temperature. The reaction was then performed at 80 °C in an oil bath under magnetic stirring. After the completion of the reaction, the solid catalyst was isolated by centrifugation. The obtained liquid phase was subsequently analyzed by Agilent 7890A gas chromatograph with a flame ionization detector (FID) (Beijing, China), and dodecane was used as the internal standard. For the recycling test, the catalyst was collected using centrifugation. The residual catalyst was washed with water and ethanol for several times and used directly for the next catalytic reaction. The loading amount of Pd was identified to be 2.0 wt% by inductively coupled plasma mass spectrometry (ICP).

3.5. Materials Characterization

Scanning electron microscopy (SEM) was performed on a JEOL JSM-6700F field-emission electron microscope (Tokyo, Japan). Transmission electron microscope (TEM) images were obtained on an FEI Tecnai G2 F20s-twin D573 field emission transmission electron microscope with an accelerating voltage of 200kV. Powder X-ray diffractometry (XRD) patterns were obtained by using a Rigaku 2550 diffractometer (Tokyo, Japan) with Cu Ka radiation (λ = 1.5418 Å). N2 adsorption–desorption isotherms were obtained at −196 °C on a Micromeritics ASAP 2010 sorptometer (Shanghai, China). Samples were degassed at 120 °C for a minimum of 12 h prior to analysis. Brunauer–Emmett–Teller (BET) surface areas were calculated from the linear part of the BET plot. Pore size distribution was estimated from the adsorption branch of the isotherm by the Barrett–Joyner–Halenda (BJH) method. The total pore volume was estimated from the adsorbed amount at P/P0 = 0.995. Inductively coupled plasma mass spectrometry (ICP) analyses were carried out on a NexION 350 ICP-MS instrument (Shanghai, China).

4. Conclusions

In summary, we have prepared MSSs with perpendicular mesochannels and tunable channel lengths by crushing corresponding hollow microspheres and then studied the effect of channel lengths on the catalytic activities of as-loaded metal nanoparticles. In comparison to the conventional Pd/MCM-41, MSSs loaded Pd nanoparticles presented an up to 6-fold activity enhancement in the selective hydrogenation reaction of nitroarenes. Superior substrate applicability and good catalytic stability were also realized. Importantly, it was found that the catalytic activities were highly dependent on the channel length of mesoporous materials and the shorter was the channel length the higher was the catalytic activity.
It was proposed that a short mesochannel, particularly for a channel of less than 50 nm, can largely accelerate the molecule diffuse process and promote the accessibility of metal nanoparticles inside channels, thus presenting a much higher catalytic activity. We expect that the structure–performance relationship established in this work will provide some insights for designing and preparing advanced heterogeneous catalysts.

Author Contributions

X.W. and X.D. performed the experiments, analyzed the experimental data and wrote the manuscript. H.Z. designed the experiments and revised the paper. All authors have read and agreed to the published version of the manuscript.

Funding

This research was supported by PhD early development program of Inner Mongolia University for the Nationalities (BS431).

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Wan, Y.; Zhao, D. On the Controllable Soft-Templating Approach to Mesoporous Silicates. Chem. Rev. 2007, 107, 2821–2860. [Google Scholar] [CrossRef] [PubMed]
  2. Bayne, L.; Ulijn, R.V.; Halling, P.J. Effect of Pore Size on the Performance of Immobilised Enzymes. Chem. Soc. Rev. 2013, 42, 9000–9010. [Google Scholar] [CrossRef] [PubMed]
  3. Diaz, U.; Brunel, D.; Corma, A. Catalysis Using Multifunctional Organosiliceous Hybrid Materials. Chem. Soc. Rev. 2013, 42, 4083–4097. [Google Scholar] [CrossRef] [PubMed]
  4. Li, W.; Yue, Q.; Deng, Y.H.; Zhao, D.Y. Ordered Mesoporous Materials Based on Interfacial Assembly and Engineering. Adv. Mater. 2013, 25, 5129–5152. [Google Scholar] [CrossRef] [PubMed]
  5. Prieto, G.; Tuysuz, H.; Duyckaerts, N.; Knossalla, J.; Wang, G.H.; Schuth, F. Hollow Nano- and Microstructures as Catalysts. Chem. Rev. 2016, 116, 14056–14119. [Google Scholar] [CrossRef]
  6. Li, B.W.; Zeng, H.C. Architecture and Preparation of Hollow Catalytic Devices. Adv. Mater. 2019, 1801104. [Google Scholar] [CrossRef]
  7. Wang, S.; Zhao, Q.F.; Wei, H.M.; Wang, J.Q.; Cho, M.Y.; Cho, H.S.; Terasaki, O.; Wan, Y. Aggregation-Free Gold Nanoparticles in Ordered Mesoporous Carbons: Toward Highly Active and Stable Heterogeneous Catalysts. J. Am. Chem. Soc. 2013, 135, 11849–11860. [Google Scholar] [CrossRef]
  8. Prieto, G.; Shakeri, M.; de Jong, K.P.; de Jongh, P.E. Quantitative Relationship between Support Porosity and the Stability of Pore-confined Metal Nanoparticles Studied on CuZnO/SiO2 Methanol Synthesis Catalysts. ACS Nano 2014, 8, 2522–2531. [Google Scholar] [CrossRef]
  9. Parlett, C.M.A.; Bruce, D.W.; Hondow, N.S.; Lee, A.F.; Wilson, K. Support-Enhanced Selective Aerobic Alcohol Oxidation over Pd/Mesoporous Silicas. ACS Catal. 2011, 1, 636–640. [Google Scholar] [CrossRef]
  10. Yang, Q.H.; Liu, J.; Zhang, L.; Li, C. Functionalized Periodic Mesoporous Organosilicas for Catalysis. J. Mater. Chem. 2009, 19, 1945–1955. [Google Scholar] [CrossRef]
  11. Yang, H.Q.; Zhang, L.; Zhong, L.; Yang, Q.H.; Li, C. Enhanced Cooperative Activation Effect in the Hydrolytic Kinetic Resolution of Epoxides on [Co(salen)] Catalysts Confined in Nanocages. Angew. Chem. Int. Ed. 2007, 46, 6861–6865. [Google Scholar] [CrossRef] [PubMed]
  12. Chen, Z.J.; Guan, Z.H.; Li, M.R.; Yang, Q.H.; Li, C. Enhancement of the Performance of a Platinum Nanocatalyst Confined within Carbon Nanotubes for Asymmetric Hydrogenation. Angew. Chem. Int. Ed. 2011, 50, 4913–4917. [Google Scholar] [CrossRef] [PubMed]
  13. Zou, H.B.; Wang, R.W.; Dai, J.Y.; Wang, Y.; Wang, X.; Zhang, Z.T.; Qiu, S.L. Amphiphilic Hollow Porous Shell Encapsulated Au@Pd Bimetal Nanoparticles for Aerobic Oxidation of Alcohols in Water. Chem. Commun. 2015, 51, 14601–14604. [Google Scholar] [CrossRef] [PubMed]
  14. Zou, H.B.; Dai, J.Y. Encapsulating Mesoporous Metal Nanoparticles: Towards a Highly Active and Stable Nanoreactor for Oxidative Coupling Reactions in Water. Chem. Commun. 2019, 55, 5898–5901. [Google Scholar] [CrossRef] [PubMed]
  15. Wan, Y.; Wang, H.Y.; Zhao, Q.F.; Klingstedt, M.; Terasaki, O.; Zhao, D.Y. Ordered Mesoporous Pd/Silica-Carbon as a Highly Active Heterogeneous Catalyst for Coupling Reaction of Chlorobenzene in Aqueous Media. J. Am. Chem. Soc. 2009, 131, 4541–4550. [Google Scholar] [CrossRef] [PubMed]
  16. Duan, L.L.; Fu, R.; Zhang, B.S.; Shi, W.; Chen, S.J.; Wan, Y. An Efficient Reusable Mesoporous Solid-Based Pd Catalyst for Selective C2 Arylation of Indoles in Water. ACS Catal. 2016, 6, 1062–1074. [Google Scholar] [CrossRef]
  17. Datta, K.K.R.; Reddy, B.V.S.; Ariga, K.; Vinu, A. Gold Nanoparticles Embedded in a Mesoporous Carbon Nitride Stabilizer for Highly Efficient Three-Component Coupling Reaction. Angew. Chem. Int. Ed. 2010, 49, 5961–5965. [Google Scholar] [CrossRef]
  18. Zhu, J.; Kónya, Z.; Puntes, V.F.; Kiricsi, I.; Miao, C.X.; Ager, J.W.; Alivisatos, A.P.; Somorjai, G.A. Encapsulation of Metal (Au, Ag, Pt) Nanoparticles into the Mesoporous SBA-15 Structure. Langmuir 2003, 19, 4396–4401. [Google Scholar] [CrossRef]
  19. Ma, C.Y.; Dou, B.J.; Li, J.J.; Cheng, J.; Hu, Q.; Hao, Z.P.; Qiao, S.Z. Catalytic Oxidation of Benzyl Alcohol on Au or Au-Pd Nanoparticles Confined in Mesoporous Silica. Appl. Catal. B 2009, 92, 202–208. [Google Scholar] [CrossRef]
  20. Shen, D.; Chen, L.; Yang, J.; Zhang, R.; Wei, Y.; Li, X.; Li, W.; Sun, Z.; Zhu, H.; Abdullah, A.M.; et al. Ultradispersed Palladium Nanoparticles in Three-Dimensional Dendritic Mesoporous Silica Nanospheres: Toward Active and Stable Heterogeneous Catalysts. ACS Appl. Mater. Interfaces 2015, 7, 17450–17459. [Google Scholar] [CrossRef]
  21. Zhang, H.; Sun, J.; Ma, D.; Bao, X.; Klein-Hoffmann, A.; Weinberg, G.; Su, D.; Schlogl, R. Unusual Mesoporous SBA-15 with Parallel Channels Running along the Short Axis. J. Am. Chem. Soc. 2004, 126, 7440–7441. [Google Scholar] [CrossRef] [PubMed]
  22. Han, Y.; Ying, J.Y. Generalized Fluorocarbon-Surfactant-Mediated Synthesis of Nanoparticles with Various Mesoporous Structures. Angew. Chem. Int. Ed. 2005, 44, 288–292. [Google Scholar] [CrossRef] [PubMed]
  23. Sujandi, L.O.; Park, S.E.; Han, D.S.; Han, S.C.; Jin, M.J.; Ohsuna, T. Amino-functionalized SBA-15 Type Mesoporous Silica Having Nanostructured Hexagonal Platelet Morphology. Chem. Commun. 2006, 2006, 4131–4133. [Google Scholar] [CrossRef] [PubMed]
  24. Chen, B.C.; Lin, H.P.; Chao, M.C.; Mou, C.Y.; Tang, C.Y. Mesoporous Silica Platelets with Perpendicular Nanochannels via a Ternary Surfactant System. Adv. Mater. 2004, 16, 1657–1661. [Google Scholar] [CrossRef]
  25. Tomczak, M.M.; Glawe, D.D.; Drummy, L.F.; Lawrence, C.G.; Stone, M.O.; Perry, C.C.; Pochan, D.J.; Deming, T.J.; Naik, R.R. Polypeptide-Templated Synthesis of Hexagonal Silica Platelets. J. Am. Chem. Soc. 2005, 127, 12577–12582. [Google Scholar] [CrossRef] [PubMed]
  26. Chen, S.Y.; Tang, C.Y.; Chuang, W.T.; Lee, J.J.; Tsai, Y.L.; Chan, J.C.C.; Lin, C.Y.; Liu, Y.C.; Cheng, S. A Facile Route to Synthesizing Functionalized Mesoporous SBA-15 Materials with Platelet Morphology and Short Mesochannels. Chem. Mater. 2008, 20, 3906–3916. [Google Scholar] [CrossRef]
  27. Yang, J.; Ling, T.; Wu, W.T.; Liu, H.; Gao, M.R.; Ling, C.; Li, L.; Du, X.W. A Top-Down Strategy Towards Monodisperse Colloidal Lead Sulphide Quantum Dots. Nat. Commun. 2013, 4, 1695. [Google Scholar] [CrossRef] [PubMed]
  28. Dong, Y.F.; Yu, M.L.; Wang, Z.Y.; Liu, Y.; Wang, X.Z.; Zhao, Z.B.; Qiu, J.S. A Top-Down Strategy toward 3D Carbon Nanosheet Frameworks Decorated with Hollow Nanostructures for Superior Lithium Storage. Adv. Funct. Mater. 2016, 26, 7590–7598. [Google Scholar] [CrossRef]
  29. Liang, F.X.; Shen, K.; Qu, X.Z.; Zhang, C.L.; Wang, Q.; Li, J.L.; Liu, J.G.; Yang, Z.Z. Inorganic Janus Nanosheets. Angew. Chem. Int. Ed. 2011, 50, 2379–2382. [Google Scholar] [CrossRef]
  30. Liu, X.F.; Cui, X.R.; Liu, Y.D.; Yin, Y.D. Stabilization of Ultrafine Metal Nanocatalysts on Thin Carbon Sheets. Nanoscale 2015, 7, 18320–18326. [Google Scholar] [CrossRef]
  31. Yan, S.; Zou, H.B.; Chen, S.; Xue, N.; Yang, H.Q. Janus Mesoporous Silica Nanosheets with Perpendicular Mesochannels: Affording Highly Accessible Reaction Interfaces for Enhanced Biphasic Catalysis. Chem. Commun. 2018, 54, 10455–10458. [Google Scholar] [CrossRef] [PubMed]
  32. Zou, H.B.; Wang, R.W.; Li, X.X.; Wang, X.; Zeng, S.J.; Ding, S.; Lu, L.; Zhang, Z.T.; Qiu, S.L. An Organosilane-directed Growth induced Etching Strategy for Preparing Hollow/Yolk−shell Mesoporous Organosilica Nanospheres with Perpendicular Mesochannels and Amphiphilic Frameworks. J. Mater. Chem. A 2014, 2, 12403–12412. [Google Scholar] [CrossRef]
  33. Qian, X.; Li, B.; Hu, Y.; Niu, G.; Zhang, D.; Che, R.; Tang, Y.; Su, D.; Asiri, A.; Zhao, D. Exploring Meso-/Microporous Composite Molecular Sieves with Core-Shell Structures. Chem. Eur. J. 2012, 18, 931–939. [Google Scholar] [CrossRef] [PubMed]
  34. Zhang, S.; Chang, C.R.; Huang, Z.Q.; Li, J.; Wu, Z.M.; Ma, Y.Y.; Zhang, Z.Y.; Wang, Y.; Qu, Y.Q. High Catalytic Activity and Chemoselectivity of Sub-nanometric Pd Clusters on Porous Nanorods of CeO2 for Hydrogenation of Nitroarenes. J. Am. Chem. Soc. 2016, 138, 2629–2637. [Google Scholar] [CrossRef] [PubMed]
  35. Cui, X.L.; Long, Y.; Zhou, X.; Yu, G.Q.; Yang, J.; Yuan, M.; Ma, J.T.; Dong, Z.P. Pd-doped Ni Nanoparticle-Modified N-Doped Carbon Nanocatalyst with High Pd Atom Utilization for the Transfer Hydrogenation of Nitroarenes. Green Chem. 2018, 20, 1121–1130. [Google Scholar] [CrossRef]
  36. Hu, X.W.; Long, Y.; Fan, M.Y.; Yuan, M.; Zhao, H.; Ma, J.T.; Dong, Z.P. Two-Dimensional Covalent Organic Frameworks as Self-Template Derived Nitrogen-Doped Carbon Nanosheets for Eco-friendly Metal-Free Catalysis. Appl. Catal. B 2019, 244, 25–35. [Google Scholar] [CrossRef]
  37. Pérez-Mayoral, E.; Matos, I.; Bernardo, M.; Fonseca, I.M. New and Advanced Porous Carbon Materials in Fine Chemical Synthesis. Emerging Precursors of Porous Carbons. Catalysts 2019, 9, 133. [Google Scholar] [CrossRef] [Green Version]
  38. Zurner, A.; Kirstein, J.; Doblinger, M.; Brauchle, C.; Bein, T. Visualizing Single-molecule Diffusion in Mesoporous Materials. Nature 2007, 450, 705–708. [Google Scholar] [CrossRef]
  39. Karger, J.; Valiullin, R. Mass Transfer in Mesoporous Materials: The Benefit of Microscopic Diffusion Measurement. Chem. Soc. Rev. 2013, 42, 4172–4197. [Google Scholar] [CrossRef]
Catalysts 10 00012 g001 550
Figure 1. (a) Schematic illustration for the preparation of mesoporous silica nanosheets with tunable channel lengths. Scanning electron microscopy (SEM) images of the sample polystyrene microspheres (b), polystyrene@mesosilica microspheres (c) and mesosilica hollow microspheres (d). SEM (e) and transmission electron microscopy (TEM) (f,g) images of mesoporous silica nanosheets with a channel length of 40 nm. The inset in SEM images (e) is the corresponding cross-sectional SEM image.
Figure 1. (a) Schematic illustration for the preparation of mesoporous silica nanosheets with tunable channel lengths. Scanning electron microscopy (SEM) images of the sample polystyrene microspheres (b), polystyrene@mesosilica microspheres (c) and mesosilica hollow microspheres (d). SEM (e) and transmission electron microscopy (TEM) (f,g) images of mesoporous silica nanosheets with a channel length of 40 nm. The inset in SEM images (e) is the corresponding cross-sectional SEM image.
Catalysts 10 00012 g001
Catalysts 10 00012 g002 550
Figure 2. SEM (a,d) and TEM (b,c,e,f) images of mesoporous silica nanosheets with different channel lengths: 75 nm (a–c) and 120 nm (d–f). The inset in SEM images (a,d) is their corresponding cross-sectional SEM image.
Figure 2. SEM (a,d) and TEM (b,c,e,f) images of mesoporous silica nanosheets with different channel lengths: 75 nm (a–c) and 120 nm (d–f). The inset in SEM images (a,d) is their corresponding cross-sectional SEM image.
Catalysts 10 00012 g002
Catalysts 10 00012 g003 550
Figure 3. Small angle X-ray diffraction (XRD) patterns (a), nitrogen adsorption–desorption isotherms (b) and Barrett–Joyner–Halenda (BJH) pore size distribution curves (c) of mesoporous silica nanosheets with different channel lengths: 40 nm (black line), 75 nm (red line) and 120 nm (blue line).
Figure 3. Small angle X-ray diffraction (XRD) patterns (a), nitrogen adsorption–desorption isotherms (b) and Barrett–Joyner–Halenda (BJH) pore size distribution curves (c) of mesoporous silica nanosheets with different channel lengths: 40 nm (black line), 75 nm (red line) and 120 nm (blue line).
Catalysts 10 00012 g003
Catalysts 10 00012 g004 550
Figure 4. Low-magnification TEM (a), high-magnification TEM (b), high-angle, annular dark-field scanning transmission electron microscopy (HAADF-STEM) (c) and energy-dispersive X-ray spectroscopy (EDX) element mapping (d–g) of the catalyst Pd/mesosilica nanosheet.
Figure 4. Low-magnification TEM (a), high-magnification TEM (b), high-angle, annular dark-field scanning transmission electron microscopy (HAADF-STEM) (c) and energy-dispersive X-ray spectroscopy (EDX) element mapping (d–g) of the catalyst Pd/mesosilica nanosheet.
Catalysts 10 00012 g004
Catalysts 10 00012 g005 550
Figure 5. (a) Kinetic plots of selective hydrogenation of nitrobenzene over different catalysts. (b) Turnover frequencies (TOFs) for different catalysts identified from a conversion of approximately 30%. (c) Recyclability test of Pd/MSSs-40 in selective hydrogenation of nitrobenzene. (d) TEM image of recovered catalyst Pd/MSSs-40 after five cycles. Reaction conditions: nitrobenzene (0.5 mmol), 4.0 mL of ethanol, catalyst (Pd, 0.376 mol%), H2 (1 atm), 80 °C.
Figure 5. (a) Kinetic plots of selective hydrogenation of nitrobenzene over different catalysts. (b) Turnover frequencies (TOFs) for different catalysts identified from a conversion of approximately 30%. (c) Recyclability test of Pd/MSSs-40 in selective hydrogenation of nitrobenzene. (d) TEM image of recovered catalyst Pd/MSSs-40 after five cycles. Reaction conditions: nitrobenzene (0.5 mmol), 4.0 mL of ethanol, catalyst (Pd, 0.376 mol%), H2 (1 atm), 80 °C.
Catalysts 10 00012 g005
Table
Table 1. Textural Properties of the sample MSSs-40, MSSs-75 and MSSs-120.
Table 1. Textural Properties of the sample MSSs-40, MSSs-75 and MSSs-120.
SampleSBET a (m2 g−1)Vt b (cm3 g−1)Dp c (nm)
MSSs-40927.20.752.54, 4.2
MSSs-75923.90.682.68, 4.2
MSSs-1201016.10.662.53
a Brunauer–Emmett–Teller (BET) specific surface areas evaluated in P/P0 from 0.05 to 0.25. b Total pore volumes estimated based on the volume adsorbed at P/P0 of ∼0.995. c Pore sizes derived from the adsorption branches of the isotherms by using the BJH method.
Table
Table 2. Selective hydrogenation of different nitroarenes over the catalyst Pd/MSSs-40 a.
Table 2. Selective hydrogenation of different nitroarenes over the catalyst Pd/MSSs-40 a.
Catalysts 10 00012 i001
Catalysts 10 00012 i002 Catalysts 10 00012 i003 Catalysts 10 00012 i004 Catalysts 10 00012 i005
1a, 2h, 99.2%1b, 2h, 99.6%1c, 2h, 99.8%1d, 2h, 98.8%
Catalysts 10 00012 i006 Catalysts 10 00012 i007 Catalysts 10 00012 i008 Catalysts 10 00012 i009
1e, 2h, 99.1%1f, 3h, 99.9%1g, 3h, 99.9%1h, 4h, 99.8%
a Reaction conditions: nitroarene (0.5 mmol), 4.0 mL of ethanol, catalyst (Pd, 0.376 mol%), H2 (1 atm), 80 °C.

Share and Cite

MDPI and ACS Style

Wang, X.; Ding, X.; Zou, H. Mesoporous Silica Nanosheets with Tunable Pore Lengths Supporting Metal Nanoparticles for Enhanced Hydrogenation Reactions. Catalysts 2020, 10, 12. https://0-doi-org.brum.beds.ac.uk/10.3390/catal10010012

AMA Style

Wang X, Ding X, Zou H. Mesoporous Silica Nanosheets with Tunable Pore Lengths Supporting Metal Nanoparticles for Enhanced Hydrogenation Reactions. Catalysts. 2020; 10(1):12. https://0-doi-org.brum.beds.ac.uk/10.3390/catal10010012

Chicago/Turabian Style

Wang, Xiaohui, Xin Ding, and Houbing Zou. 2020. "Mesoporous Silica Nanosheets with Tunable Pore Lengths Supporting Metal Nanoparticles for Enhanced Hydrogenation Reactions" Catalysts 10, no. 1: 12. https://0-doi-org.brum.beds.ac.uk/10.3390/catal10010012

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop