Next Article in Journal
Tungsten–Gold Metallogenetic Potential of the Ziyunshan Pluton in Central Hunan, South China: Insights from Element Geochemistry of Granites
Next Article in Special Issue
Study on the Pb2+ Consolidation Mechanism of Gangue-Based Cemented Backfill
Previous Article in Journal
Comparative Analysis of Tunnel Plastic Zone Calculation and Engineering Measurement Based on Various Methods
Previous Article in Special Issue
Measuring Ultrasonic and Electrical Properties of Early-Age Cemented Tailings Backfill
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Minerals
Volume 13
Issue 2
10.3390/min13020142
minerals-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Effect of Content and Length of Polypropylene Fibers on Strength and Microstructure of Cementitious Tailings-Waste Rock Fill

by
Bo Gao
1,2,
Shuai Cao
1,2,* and
Erol Yilmaz
3,*
1
School of Civil and Resources Engineering, University of Science and Technology Beijing, Beijing 100083, China
2
State Key Laboratory of High-Efficient Mining and Safety of Metal Mines of Ministry of Education, University of Science and Technology Beijing, Beijing 100083, China
3
Department of Civil Engineering, Geotechnical Division, Recep Tayyip Erdogan University, Fener, Rize TR53100, Türkiye
*
Authors to whom correspondence should be addressed.
Minerals 2023, 13(2), 142; https://0-doi-org.brum.beds.ac.uk/10.3390/min13020142
Submission received: 18 December 2022 / Revised: 10 January 2023 / Accepted: 17 January 2023 / Published: 18 January 2023
(This article belongs to the Special Issue Backfilling Materials for Underground Mining, Volume III)
Browse Figures
Review Reports Versions Notes

Abstract

:
The mechanical strength properties of cemented tailings backfill are very important for the safe and environmentally friendly mining of mineral resources. To check the impact of polypropylene fiber on strength and microstructure of cementitious tailings waste rock fill (CTWRF), diverse fiber lengths (6 and 12 mm) and dosages (0-control specimen, 0.3, 0.6, and 0.9 wt.%) were considered to prepare fiber-reinforced CTWRF (FRCTWRF) matrices. Experiments such as UCS (uniaxial compressive strength), X-ray CT (computed tomography), and SEM (scanning electron microscopy) were implemented to better characterize the backfills studied. Results showed that UCS performance of FRCTWRF was the highest (0.93 MPa) value at 6 mm fiber long and 0.6 wt.% fiber content. The peak strain of FRCTWRF was the highest (2.88%) at 12 mm fiber long and 0.3 wt.% fiber content. Growing the length of fiber within FRCTWRF can reduce its fracture volume, enhancing the crack resistance of FRCTWRF. Fiber and FRCTWRF are closely linked to each other by the products of cement hydration. The findings of this work will offer the efficient use of FRCTWRF in mining practice, presenting diverse perspectives for mine operators and owners, since this newly formed cementitious fill quickens the strengths required for stope backfilling.

1. Introduction

To capably realize the green mining of underground ore resources [1], backfilling mining is one of the key mining techniques [2,3]. In recent years, scholars and engineers have commenced abundant researches on different subjects such as mining process [4], backfilling materials mechanics [5], and blasting parameter optimization [6]. During the mining and mineral processing sections, the two main types of solid wastes generated were waste rock [7] and minerals tailings [8], respectively. The storage of these wastes not only conquers large volumes of surface lands [9], but also leads to serious ecological hazards [10]. As the underground run of mine (ROM) ore was extracted, a large number of mined-out areas (i.e., stopes) were formed [11,12]. These stopes are essential for the overall stability of underground mining and must be managed well [13]. Hence, the ratio of the gap area created by the stopes to the total opening area in the underground mine should not be higher than 15% [14]. If these stopes are not backfilled in a timely manner [15], then stability problems, including local or regional collapses, may occur in mines [16], and even fatal mining accidents may occur [17]. The way to prevent all these bad consequences is to ensure the stability of each gap opened by backfilling without wasting time [18]. The most common type of the backfills used in mines is cementitious tailings/paste backfill (CTB/CPB: [19,20,21]) since it allows for fast settling [22], easy operation [23], offering local/regional support [24], and placing a key part of tailings underground [25], reducing the aboveground environmental problems [26]. Indeed, this is vital for sustainable/efficient mining [27]. The comprehensive utilization of both waste rock and processing tailings for back-filling the mined-out openings or stopes [28] could not only prevent the extraction area collapse [29] but also reduce the stockpiling of solid waste on the surface nearby the mine site [30,31].
CTB/CPB is a category of composites that is basically manufactured by a blend of mining waste, cement, and water [32,33,34,35]. The sums of these materials used in the matrix can vary significantly depending on the function of the backfill created for underground mines [36,37]. To attain the required mechanical strengths of CTB while maintaining its rheological properties [38], the proportion of each component must be determined [39]. Various extra materials such as sand [40,41], fiber [42,43], and pozzolans [44,45] have been recently used to reduce the backfill costs while increasing its strength behavior. Since ROM ore is also crushed into finer particles to boost ore recovery [46], the tailings employed for CTB making can easily cause low UCS values [47]. CTB with coarse-sized tailings has larger porosity than CTB with fine-sized tailings, resulting a major reduction in UCS [48]. Few studies are focused on CTB having other reinforcing materials such as fiber to improve their mechanical strengths [49,50,51]. Accordingly, improving the strength performance of CTB remains a chief research topic.
For filling materials, researchers have started important lab/field investigations on uniaxial-triaxial compression [52,53], Brazilian splitting [54], three-/four-point bending [55], and shearing [56] tests. The research materials involved CTB [57,58], cementitious coal fly ash/coal gangue backfill materials [59,60], and others [61]. In terms of research tools, many scholars also considered using acoustic emission (AE) system [62], industrial computed tomography (CT) scan [63], mercury intrusion porosimetry [64], and nuclear magnetic resonance system [65]. Yang et al. [66] examined the crack behavior of fiber-reinforced CTB by means of an AE system. Results showed that b-value and AE fractal aspect could assess the evolution of cracks. Mashifana and Sithole [67] assumed that the size distribution of the particles tested could govern the mechanical strength behavior of CTB specimens. Findings revealed that the slighter the grain size, the higher the strength of filling specimens. Xue and Yilmaz [68] found that polypropylene fibers were effective in improving CTB’s strength behavior. Sun et al. [69] observed that adding waste rock can develop the backfill’s strength. Results indicated that CTBs with 25–30% waste rock had better flowability than others. Some researchers [70,71] also quantified that fibers were able to importantly inhibit the rapid extension of the cracks observed within CTB specimens based on SEM micrograph observations.
This work firstly aims to investigate the impact of length and content of polypropylene fiber (PF) on quality and properties of fiber-reinforced cemented tailings-waste rock fill (FRCTWRF). Secondly, it aims to define the mechanical (uniaxial strength/peak strain) and microstructure (crack volume) behavior of FRCTWRF through UCS, X-ray CT, and SEM observations. Regarding the novelty of this work, it is significantly original, since it involved analyzing PF-reinforced CTWRF samples under elevated temperatures through SEM and micro-CT scan systems.

2. Materials and Methods

2.1. Materials

5–7 mm sized waste rock and gold tailings were utilized for making CTB samples. ordinary Portland cement (OPC) 42.5R was employed as a basic cementing source. Tap water in the lab was used as mixing water. A laser diffraction particle size analyzer was utilized to characterize specimens’ grain size distribution (GSD). GSD profiles of gold both tailings and cement are shown in Figure 1. Note that GSD plot of gold tailings was similar to that of cement. 10% of the tailings were less than 2 μm, and 50% of the tailings were less than 20 μm. The curvature coefficient of the tailings was 2.07, and the uniformity coefficient was 20.98.
It has been presented that polypropylene fibers can effectively prevent the crack expansion of the cementitious tailings backfill material [56]. Thus, different lengths of polypropylene fibers were selected to prepare FRCTWR in this section. Table 1 presents polypropylene fiber’s key properties.

2.2. Sample Preparation

To inspect the impact of longs/doses of PF fibers on CTWRF’s strength evolution, specimens were designed with diverse fiber longs (6/12 mm) and doses (0-control, 0.3, 0.6, and 0.9 wt.%). The solid content of FRCTWR was 72 wt.%. The proportion of cement mass to total mass of tailings and waste rock was 1:8. Table 2 shows the ratio of each composition of specimens. Fiber content is the fraction of solid mass in CTWRF. PP6-0.3 indicates polypropylene fibers of 6 mm in length and 0.3 wt.% CTWRF. N-PP was non-reinforced CTWRF. Backfills were cast into a 50 × 100 mm2 cylinder mold and then placed in a fixed temperature (19 ± 1 °C) and humidity (88 ± 2%) conditioning chamber. The mold was removed after 48 h. Figure 2 shows the CTWRF’s preparation processes.

2.3. Methods

2.3.1. UCS Test

After CTWRF sample was cured for 7-day, the UCS experiment was conducted by a fully automatic mechanical press which entirely meets national standard GB/T16491-2008. The instrument model used for UCS testing was WDW-200D (POPWIL, Jinan, Shandong, China) and the loading range was 0–200 kN, the accuracy of mechanical tests was ±0.5%, the displacement measurement resolution was 0.001 mm, the displacement error is not more than 0.02 mm. A rate of 1 mm/min was also implemented during loading. Strength and stress–strain plots were automatically collected by PC. To find the average UCS value, a total of 3 experiments were made from each backfill mixture recipe.

2.3.2. X-ray CT Scanning Test

After completing the UCS experiments, the CTWRF specimens with the optimum fiber content in each fiber length were selected for industrial CT scanning tests, which were performed by high-resolution test equipment manufactured by YXLON, Hamburg, Germany. To lessen the interference of various factors during testing, two specimens were scanned simultaneously. The image size was 1024 × 1024. The pixel size was 80 μm. A total of 1097 slices were obtained for experiments.

2.3.3. SEM-EDS Measurement

Samples were prepared by selecting the fiber-containing areas in CTWRF matrices. Sample size was 1 × 1 × 1 cm3. To interrupt the hydration reaction of cemented materials, samples were kept in ethanol for 1-day. To enhance samples’ electrical conductivity, samples dried for 12-h were sprayed with carbon twice by vacuum coating instrument. Specimens were kept motionless using conductive tin foil tape. CTWRF’s microstructure was observed by a Zeiss EVO 18 SEM (Zeiss, Oberkochen, Germany) which is used for imaging/analytical applications. The accelerating voltage was 20 kV. The hydration products within CTWRF specimens were also examined using an energy spectrometer.

3. Results and Discussion

3.1. Fiber Impact on FRCTWRF’s Strength/Peak Strain Behavior

Figure 3a presents an evolution of UCS recorded for different CTWRF ratios. Note that the UCS value of N-PP was 0.89 MPa. However, the UCS value of CTWRF ranges from 0.67 to 0.93 MPa. The blending of fiber led to a small fluctuation in the strength of CTWRF, ranging from +4.49% and −24.72%. This is due to variations in fiber content and length. Overall, adding fibers gave rise to a decrease in CTWRF’s strength. This is due to the higher aspect ratio and lower specific gravity of fiber, a property that contributes to the tendency of fibers to agglomerate and trapping of free water [55]. One can interpret that fibers can cause deterioration of pore structure in CTWRF, which was also a detrimental factor affecting the compressive strength of CTWRF [56]. UCS values of CTWRF were 0.77 to 0.93 MPa, and 0.83 to 0.67 MPa for a fiber long of 6 and 12 mm, respectively. CTWRF’s strength was enhanced by 6 mm fiber long for the same fiber content. It is contrary to the results of fiber-doped tailings fill (raw materials are fiber, tailings, and cement) studied by Xue et al. [57]. This suggests that the mixing of waste rock affects the interaction mechanism among fiber, cement, and tailings. For CTWRF specimens having the same length of fibers, a rise in the content of fiber caused a growth and then a drop in UCS. The maximum strength of FRCTWRF was found for a fiber content of 0.6 wt.%.
Figure 3b shows the impacts of length and content of polypropylene fiber on CTWRF’s peak strain. One can interpret that peak strain of N-PP is 1.31%. Adding fiber causes an increase in the peak strain of FRCTWRF by 16.03–119.85%, which is due to the good tensile properties of fibers. When exposed to external loading, fibers bonded between CTWRF matrix immersed more energy, which brings about a better deformability of CTWRF [58].
CTWRF’s peak strains were 1.99% (0.3 wt.%), 1.52% (0.6 wt.%), and 2.37% (0.9 wt.%) for 6 mm fiber long, respectively. A rise in the content of fiber led to a decrease and then an increase in the peak strain of CTWRF. CTWRF’s peak strains were 2.88% (0.3 wt.%), 2.53% (0.6 wt.%), and 2.23% (0.9 wt.%) for 12 mm fiber long. CTWRF’s peak strain drops with growing fiber dosage. Overall, increasing the fiber length can lead to an increase in CTWRF’s peak strain. Longer fibers have a larger contact area with CTWRF, resulting in a stronger bond. Longer fibers can boost the deformation capacity of CTWRF.

3.2. Fiber Effect on FRCTWRF’s Stress–Strain/Toughness Behavior

Figure 4a shows the deformation or stress–strain plots of FRCTWRF and CTWRF. Note that RCTWRF’s stress–strain plots are similar to those of CTWRF. The stress–strain curves are divided into four steps: (a) pore compacting step; (b) linear elastic step; (c) strain softening step; (d) crack extension step. It is easy to see that all curves have the same trend until the peak point. The influence of fibers on FRCTWRF’s stress–strain curve exists with the post-peak stage. The load-bearing capacity of CTWRF decreases after getting peak strength. However, FRCTWRF’s stress–strain plot declined in the level of post-peak, which indicated that fibers enlarged the post-peak load-carrying capacity and enhanced FRCTWRF’s ductility. FRCTWRF curves were smoother for 12 mm fiber length than 6 mm fiber one, showing that longer fibers are more conducive to FRCTWRF ductility enhancement than shorter fibers.
Researchers were more concerned with the ductility enhancement of FRCTWRF by fibers than the strength change. To scrutinize the impact of fiber long/content on ductility of FRCTWRF, slope K of post-peak curve was used as a parameter for the strength evaluation of FRCTWRF. Figure 4b shows the impact of fiber long/dose on slope K. One can interpret that; the K value of N-PP is the smallest at −0.20. Increasing the fiber length can lead to enhanced post-peak ductility of FRCTWRF at a certain fiber content. Let us say that the K value for 6-0.3 is −0.18 and for 12-0.3 is −0.09, which is a 50% increase in K value. FRCTWRF with 0.3 wt.% fiber content has the minimum K value and the worst ductility for a confident fiber length. The K values increased by 44.4% (6 mm) and 55.6% (12 mm) for fiber content increasing from 0.3 wt.% to 0.6 wt.%, respectively. As the content of fiber continued to increase, the K value remained constant.

3.3. Microstructures Analysis Based on 3D Reconstruction

To probe the impact of fiber long variation on spatial distribution of fibers, waste rock, and fractures, FRCTWRF samples (PP 6-0.6 and PP 12-0.6) after UCS tests were tested by industrial CT scan technique. Figure 5 and Figure 6 present the 2D slice images of 20 mm, 50 mm, and 80 mm from the bottom of the samples that were selected for comparative analysis. For visual observation, the 2D section images were pseudo-color enhanced using Image J software. Waste rock and fissures can be observed in 2D section images. Since the fiber gray values are similar to fissures, they can be distinguished by shape in the section images (filamentous structures are fibers in Figure 5 and Figure 6).
One can interpret from Figure 5 that 6 mm fiber lengths were distributed more uniformly in the FRCTWRF, and no fiber agglomeration was found. Some fibers penetrate both sides of the fissure and show an obvious bridging effect. The waste rock was not uniformly distributed in FRCTWRF, waste rock was less in the upper part of FRCTWRF (only one waste rock is found in Figure 5a), and waste rock was mostly focused on the middle/lower parts of FRCTWRF. Distribution of fissures and waste rocks was opposite, mainly distributed in the upper part of FRCTWRF. This may be related to the waste rock settlement [58].
One can interpret from Figure 6 that fibers of 12 mm in length are prone to agglomeration. Waste rocks are more abundant in Figure 6a,c and less abundant in Figure 6b. This shows that waste rocks are not uniformly distributed along the height. The section images also show a radially inhomogeneous distribution of waste rocks. This phenomenon is caused by the characteristics of waste rock itself. In Figure 6b, there is no waste rock distribution in the dense fiber region. This indicates that the inhomogeneous distribution of waste rocks is linked with fiber agglomeration. The fractures in PP12-0.6 specimen are only distributed at the edge of FRCTWRF composites due to the waste rock distribution. No cleavage similar to the one through the slice in Figure 5a was found.
To analyze the influence of fiber length variation on waste rock distribution, waste rock within FRCTWRF was extracted by the threshold segmentation. The percentage of waste rock area in the sliced images to the cross-sectional area of FRCTWRF was defined as waste rock percentage, and the waste rock percentage curve was used to quantitatively characterize the spatial distribution pattern of waste rock within FRCTWRF. Figure 7 and Figure 8 showed the three-dimensional images of waste rock, waste rock percentage curves, and slice images for PP6-0.6 and PP12-0.6.
One can deduce from Figure 7 that waste rock percentage is less than 2.47 in the upper part of PP6-0.6. However, in the middle and lower part, the waste rock percentage was between 26.09 and 36.25. This indicated that waste rock is distributed in the middle and lower part of FRCTWRF, which was similar to the distribution pattern of coarse particles in none-fiber cementitious materials [59]. Thus, 6 mm fiber length has no effect on waste rock distribution. One can deduce from Figure 8 that there are three main peaks in waste rock distribution curve in PP12-0.6, which were 36.32, 21.52, and 15.33, respectively. Waste rocks were highly concentrated in the peak distribution. Combined with the section images, it could also be found that fibers are mainly distributed in two regions, which were between three peak points. This indicates that fiber agglomerates affect the waste rock distribution.
Figure 9 and Figure 10 show 3D reconstructed images of cracks in PP6-0.6 and PP12-0.6, respectively. More tensile cracks are presented in PP6-0.6, which reveals tensile damage. The cracks are reduced in the bottom region, showing incomplete continuous sheet cracks. The crack structure is more complicated in PP12-0.6. The cracks showed discontinuous sheet shear cracks, and PP12-0.6 was shear damage. The crack volume was 4749.11 mm3 in PP6-0.6 and 3764.69 mm3 in PP12-0.6. One could say that increasing the fiber length resulted in a 20.73% drop in the crack volume. This shows that increasing fiber length can improve FRCTWRF’s cracking resistance.

3.4. SEM Characteristics and Element Distribution

Figure 11 showed the microstructure images of PP6-0.6 and PP12-0.9. Three microstructures, namely FRCTWRF matrix, fibers, and pores, could be seen in SEM images. The FRCTWRF matrix was much denser. The pore diameters were 29.4 μm and 102.2 μm within PP6-0.6 and PP12-0.9, respectively. The fibers were connected to FRCTWRF by hydration products. A large quantity of hydration materials was involved in the external part of visible fibers. The main consequences displayed that some of hydration products were separated from the FRCTWRF matrix and attached to the surface of PF fibers after FRCTWRF cracking. This clearly indicates that the influence of bonding is well-observed between fibers and FRCTWRF matrix from SEM micrographs, and 12 mm fiber length was also deformed after being pulled out. In contrast, the 6-mm-long fibers were not significantly deformed.
Figure 12 presents the morphological images of two extracted fibers in PP12-0.3. It could be observed that the pulled end of fiber was bent and deformed, while the other part was not deformed. A large number of neatly arranged scale-like FRCTWRF matrix were found on the surface of the extracted fibers. This was caused by the sliding of the fibers in the FRCTWRF matrix. This FRCTWRF matrix was not found on the surface of 6 mm long fibers. This may be due to the short sliding distance of 6 mm-long fibers in the FRCTWRF matrix.
Figure 13 showed the microscopic morphology and elemental distribution of hydration materials within FRCTWRF. One could deduce that the main hydration materials were CSH gels, and a slight quantity of needle-like Ca alumina (AFt). From elemental distribution results, it can be seen that O, C, Ca, Si, and Al are the chief features of cement hydration products. Figure 14 showed the mass percentages of each element in hydration products. One can also say that O and C have the highest content with 39.3 wt.% and 38.3 wt.%, respectively.

4. Conclusions

The impacts of fiber length/content on strength development of FRCTWRF were inspected by UCS tests. The internal fibers, waste rock, and fractures of FRCTWRF were visualized and analyzed by using a 3D reconstruction technique. The microstructure and element distribution of FRCTWRF were investigated by SEM observations. From the above experiments, the following conclusions were drawn:
(1)
Fiber incorporation can lead to changes in compressive strength of FRCTWRF. The changes in FRCTWRF’s strength were +4.49% and −24.72%. A rise in the content of fiber led to an increase and then a drop in FRCTWRF’s strength. The reinforcement effect of 6 mm long polypropylene fibers on FRCTWRF’s strength was better than 12 mm long fibers. FRCTWRF’s strength was maximum at 0.93 MPa for 6 mm long fiber and 0.6 wt.% fiber content.
(2)
FRCTWRF’s peak strains were all greater than those of CTWRF. The peak strains increased with rising fiber length. At 6 mm long fiber, a rise in the content of fiber led to a decrease and then an increase in peak strain. Peak strain decreases with growing fiber content for 6 mm long fiber. The maximum peak strain of FRCTWRF was 2.88% for 12 mm long fiber and 0.3 wt.% fiber content.
(3)
Fibers governs the post-peak step of the FRCTWRF’s stress–strain plot, and the post-peak ductility of FRCTWRF increases with increasing fiber length. 12 mm long fiber tends to agglomerate, and the fiber agglomeration affects the spatial distribution of waste stones. Waste rocks in PP6-0.6 are distributed in FRCTWRF’s middle and lower parts. Waste rocks are uniformly distributed along the radial direction. Waste rocks in PP12-0.6 are not uniformly distributed along the axial and radial directions.
(4)
Fibers have a bridging influence on cracks observed in FRCTWRF. The joint action of fibers and waste stones affects the damage mode of FRCTWRF, which is tensile damage in PP6-0.6 and shear damage in PP12-0.6. Increasing fiber long led to a drop of fracture body. FRCTWRF with 12 mm fibers is more resistant to cracking. Fibers and the FRCTWRF matrix were connected by hydration materials, which were typically CSH gel and needle-like Ca alumina. The key elements within the hydration products for filling specimens are O and C.
The present work offers the impact of fiber long/dose on strength and microstructure of cementitious backfills. It is thought that this new filling type, which is shaped by combining waste rock-fiber-tailings with different experimental methods, will be a trend research topic based on its cost-reducing and performance-enhancing properties. There is absolutely a need for more work in this area, but as such, the current work will contribute to other researchers by offering a diverse perspective and experimental methods. Some experiments are carried out by the same authors to examine the effect of some parameters on fresh/hardened performance of this fill type, and the results will be shared with the readers soon.

Author Contributions

Conceptualization, S.C.; methodology, B.G.; writing—original draft preparation, B.G.; writing—review and editing and supervision, E.Y. and S.C.; funding acquisition, S.C. All authors have read and agreed to the published version of the manuscript.

Funding

The writers frankly appreciate a generous fund granted from both the National Key Research and Development Program of China (No. 2022YFC2905004) and National Natural Science Foundation of China (No. 51804017).

Data Availability Statement

Not applicable.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Wang, Y.; Na, Q.; Zhang, L.F. Monitoring of in-situ properties for cemented tailings backfill that under drainage condition. Constr. Build. Mater. 2022, 356, 129254. [Google Scholar] [CrossRef]
  2. Du, X.J.; Feng, G.R.; Zhang, M.; Wang, Z.H.; Liu, W.H. Influence of backfilling rate on the stability of the “backfilling body-immediate roof” cooperative bearing structure. Int. J. Min. Sci. Technol. 2022, 32, 1197–1206. [Google Scholar] [CrossRef]
  3. Wang, Y.; Li, C.; Hou, Z.; Yi, X.; Wei, X. In vivo X-ray computed tomography investigations of crack damage evolution of cemented waste rock backfills (CWRB) under uniaxial deformation. Minerals 2018, 8, 539. [Google Scholar] [CrossRef] [Green Version]
  4. Ji, X.; Gu, X.; Wang, Z.; Xu, S.; Jiang, H.; Yilmaz, E. Admixture effects on rheological/mechanical behavior and microstructure evolution of alkali-activated slag backfills. Minerals 2023, 13, 30. [Google Scholar] [CrossRef]
  5. Lv, H.Y.; Chen, Y.L.; Xie, Q.; Wu, P.; Chen, Y.; Gu, J.; Wu, H.S. Performance optimization and characterization of loess-slag-based geopolymer composite: A new sustainable green material for backfill. Constr. Build. Mater. 2022, 354, 129103. [Google Scholar] [CrossRef]
  6. Yin, S.H.; Hou, Y.Q.; Yang, S.X.; Chen, X. Study on static and dynamic flocculation settlement characteristics of fine tailings slurry and influence of flocculant on strength of fine tailings backfill. Case Stud. Constr. Mater. 2022, 17, e01525. [Google Scholar] [CrossRef]
  7. Jian, S.W.; Cheng, C.; Lv, Y.; Wang, C.F.; Tan, H.B.; Li, B.D. Preparation and evaluation of high-fluid backfill materials from construction spoil. Constr. Build. Mater. 2022, 345, 128370. [Google Scholar] [CrossRef]
  8. Chiloane, N.M.; Mulenga, F.K. Revisiting factors contributing to the strength of cemented backfill support system: A review. J. Rock Mech. Geotech. Eng. 2022. [CrossRef]
  9. Tao, J.; Yang, X.G.; Ding, P.P.; Li, X.L.; Zhou, J.W.; Lu, G.D. A fully coupled thermo-hydro-mechanical-chemical model for cemented backfill application in geothermal conditions. Eng. Geol. 2022, 302, 106643. [Google Scholar] [CrossRef]
  10. Gao, Y.; Sui, H.; Yu, Z.X.; Wu, J.Y.; Chen, W.Q.; Jing, H.W.; Ding, M.J.; Liu, Y.M. Industrial graphene oxide-fly ash hybrid for high-performance cemented waste rock backfill. Constr. Build. Mater. 2022, 359, 129484. [Google Scholar] [CrossRef]
  11. Wang, Y.Y.; Yu, Z.Q.; Wang, H.W. Experimental investigation on some performance of rubber fiber modified cemented paste backfill. Constr. Build. Mater. 2021, 271, 121586. [Google Scholar]
  12. Yin, S.H.; Hou, Y.Q.; Chen, X.; Zhang, M.Z.; Du, H.H.; Gao, C. Mechanical behavior, failure pattern and damage evolution of fiber-reinforced cemented sulfur tailings backfill under uniaxial loading. Constr. Build. Mater. 2022, 332, 127248. [Google Scholar] [CrossRef]
  13. Chen, S.M.; Yilmaz, E.; Wang, W.; Wang, Y.M. Curing stress effect on stability, microstructure, matric suction and electrical conductivity of cementitious tailings backfills. Constr. Build. Mater. 2022, 360, 129601. [Google Scholar]
  14. Gao, T.; Sun, W.; Li, Z.; Fan, K.; Jiang, M.; Cheng, H. Study on shear characteristics and failure mechanism of inclined layered backfill in mining solid waste utilization. Minerals 2022, 12, 1540. [Google Scholar]
  15. Koohestani, B.; Mokhtari, P.; Yilmaz, E.; Mahdipour, F.; Darban, A.K. Geopolymerization mechanism of binder-free mine tailings by sodium silicate. Constr. Build. Mater. 2021, 268, 121217. [Google Scholar] [CrossRef]
  16. Béket Dalcé, J.; Li, L.; Yang, P. Experimental study of uniaxial compressive strength (UCS) distribution of hydraulic backfill associated with segregation. Minerals 2019, 9, 147. [Google Scholar]
  17. Yilmaz, E.; Belem, T.; Benzaazoua, M. One-dimensional consolidation parameters of cemented paste backfills. Gospod. Surowcami Miner./Miner. Resour. Manag. 2012, 28, 29–45. [Google Scholar]
  18. Tayebi-Khorami, M.; Edraki, M.; Corder, G.; Golev, A. Re-thinking mining waste through an integrative approach led by circular economy aspirations. Minerals 2019, 9, 286. [Google Scholar] [CrossRef] [Green Version]
  19. Chen, S.M.; Wang, W.; Yan, R.; Wu, A.; Wang, Y.; Yilmaz, E. A joint experiment and discussion for strength characteristics of cemented paste backfill considering curing conditions. Minerals 2022, 12, 211. [Google Scholar] [CrossRef]
  20. Sadrossadat, E.; Basarir, H.; Luo, G.; Karrech, A.; Durham, R.; Fourie, A.; Elchalakani, M. Multi-objective mixture design of cemented paste backfill using particle swarm optimisation algorithm. Miner. Eng. 2020, 153, 106385. [Google Scholar]
  21. Qiu, J.P.; Guo, Z.B.; Yang, L.; Jiang, H.Q.; Zhao, Y.L. Effect of tailings fineness on flow, strength, ultrasonic and microstructure characteristics of cemented paste backfill. Constr. Build. Mater. 2020, 263, 120645. [Google Scholar] [CrossRef]
  22. Yan, R.; Yin, S.; Zhang, H.; Wang, L.; Chen, D. Effect of superplasticizer on the setting behaviors and mechanical properties of tailings-waste rock cemented paste backfills. Case Stud. Constr. Mater. 2023, 18, e01714. [Google Scholar] [CrossRef]
  23. Zhao, Z.; Cao, S.; Yilmaz, E. Effect of layer thickness on flexural property and microstructure of 3D printed rhomboid polymer reinforced cemented tailings composites. Int. J. Miner. Metall. Mater. 2023, 30, 236–249. [Google Scholar] [CrossRef]
  24. Xu, X.; Fall, M.; Alainachi, I.; Fang, K. Characterisation of fibre-reinforced backfill/rock interface through direct shear tests. Geotech. Res. 2019, 7, 11–25. [Google Scholar] [CrossRef]
  25. Qin, S.W.; Cao, S.; Yilmaz, E. Employing U-shaped 3D printed polymer to improve flexural properties of cementitious tailings backfills. Constr. Build. Mater. 2022, 320, 126296. [Google Scholar] [CrossRef]
  26. Gorakhki, M.H.; Bareither, C.A. Sustainable reuse of mine tailings and waste rock as water-balance covers. Minerals 2017, 7, 128. [Google Scholar] [CrossRef]
  27. Yan, B.X.; Zhu, W.; Hou, C.; Yilmaz, E.; Saadat, M. Characterization of early age behavior of cemented paste backfill through the magnitude and frequency spectrum of ultrasonic P-wave. Constr. Build. Mater. 2020, 249, 118733. [Google Scholar] [CrossRef]
  28. Zhou, Y.B.; Fall, M.; Haruna, S. Flow ability of cemented paste backfill with chloride-free antifreeze additives in sub-zero environments. Cem. Concr. Compos. 2022, 126, 104359. [Google Scholar] [CrossRef]
  29. Huang, Z.; Yilmaz, E.; Cao, S. Analysis of strength and microstructural characteristics of mine backfills containing fly ash and desulfurized gypsum. Minerals 2021, 11, 409. [Google Scholar] [CrossRef]
  30. Yang, J.; Zhao, K.; Yu, X.; Yan, Y.J.; He, Z.W.; Lai, Y.; Zhou, Y. Crack classification of fiber-reinforced backfill based on Gaussian mixed moving average filtering method. Cem. Concr. Compos. 2022, 134, 104740. [Google Scholar] [CrossRef]
  31. Wang, S.; Song, X.P.; Chen, Q.S.; Wang, X.J.; Wei, M.L.; Ke, Y.X.; Luo, Z.H. Mechanical properties of cemented tailings backfill containing alkalized rice straw of various lengths. J. Environ. Manag. 2020, 276, 111124. [Google Scholar] [CrossRef]
  32. Xu, X.; Wu, W.; Xu, W. Sulfate-dependent shear behavior of cementing fiber-reinforced tailings and rock. Minerals 2020, 10, 1032. [Google Scholar] [CrossRef]
  33. Wang, Y.; Wang, H.; Zhou, X.; Yi, X.; Xiao, Y.; Wei, X. In situ X-ray CT investigations of meso-damage evolution of cemented waste rock-tailings backfill (CWRTB) during triaxial deformation. Minerals 2019, 9, 52. [Google Scholar] [CrossRef] [Green Version]
  34. Zhao, Y.L.; Wu, P.Q.; Qiu, J.P.; Guo, Z.B.; Tian, Y.S.; Sun, X.G.; Gu, X.W. Recycling hazardous steel slag after thermal treatment to produce a binder for cemented paste backfill. Powder Technol. 2022, 395, 652–662. [Google Scholar] [CrossRef]
  35. Qi, C.C.; Chen, Q.S.; Kim, S.S. Integrated and intelligent design framework for cemented paste backfill: A combination of robust machine learning modelling and multi-objective optimization. Miner. Eng. 2020, 155, 106422. [Google Scholar] [CrossRef]
  36. Hane, I.; Belem, T.; Benzaazoua, M.; Maqsoud, A. Laboratory characterization of cemented tailings paste containing crushed waste rocks for improved compressive strength development. Geotech. Geolog. Eng. 2017, 35, 645–662. [Google Scholar] [CrossRef]
  37. Solismaa, S.; Torppa, A.; Kuva, J.; Heikkilä, P.; Hyvönen, S.; Juntunen, P.; Benzaazoua, M.; Kauppila, T. Substitution of cement with granulated blast furnace slag in cemented paste backfill: Evaluation of technical and chemical properties. Minerals 2021, 11, 1068. [Google Scholar] [CrossRef]
  38. Li, J.J.; Yilmaz, E.; Cao, S. Influence of solid content, cement/tailings ratio and curing time on rheology and strength of cemented tailings backfill. Minerals 2020, 10, 922. [Google Scholar] [CrossRef]
  39. Li, J.J.; Cao, S.; Yilmaz, E. Characterization of macro mechanical properties and microstructures of cement-based composites prepared from fly ash, gypsum and steel slag. Minerals 2022, 12, 6. [Google Scholar] [CrossRef]
  40. Ouyang, S.Y.; Huang, Y.L.; Zhou, N. Experiment on hydration exothermic characteristics and hydration mechanism of sand-based cemented paste backfill materials. Constr. Build. Mater. 2022, 318, 125870. [Google Scholar] [CrossRef]
  41. Kasap, T.; Yilmaz, E.; Sari, M. Effects of mineral additives and age on microstructure evolution and durability properties of sand-reinforced cementitious mine backfills. Constr. Build. Mater. 2022, 352, 129079. [Google Scholar] [CrossRef]
  42. Chakilam, S.; Cui, L. Effect of polypropylene fiber content and fiber length on the saturated hydraulic conductivity of hydrating cemented paste backfill. Constr. Build. Mater. 2020, 262, 120854. [Google Scholar] [CrossRef]
  43. Cao, S.; Xue, G.L.; Yilmaz, E. Flexural behavior of fiber reinforced cemented tailings backfill under three-point bending. IEEE Access 2019, 7, 139317–139328. [Google Scholar] [CrossRef]
  44. Zhao, K.; He, Z.; Yang, J.; Yan, Y.; Yu, X.; Zhou, Y.; Zhang, X.; Wang, J. Investigation of failure mechanism of cement-fiber-tailings matrix composites using digital image correlation and acoustic emission. Constr. Build. Mater. 2022, 335, 127513. [Google Scholar] [CrossRef]
  45. Feng, Y.; Li, F.; Qi, W.; Ren, Q.; Qi, W.; Duan, G.; Zheng, K.; Han, Y.; Pang, H. Mechanical properties and microstructure of iron tailings cemented paste backfills using carbide slag-activated ground granulated blast furnace slag as alternative binder. Minerals 2022, 12, 1549. [Google Scholar] [CrossRef]
  46. Tan, Y.-y.; Zhang, K.; Yu, X.; Song, W.-d.; Wang, J.; Hai, C.-l. The mechanical and microstructural properties of composite structures made of a cement-tailing backfill and rock core. Minerals 2020, 10, 159. [Google Scholar] [CrossRef]
  47. Yi, X.; Ma, G.; Fourie, A. Compressive behaviour of fibre-reinforced cemented paste backfill. Geotext. Geomembr. 2015, 43, 207–215. [Google Scholar] [CrossRef]
  48. Yu, Z.; Shi, X.-Z.; Chen, X.; Zhou, J.; Qi, C.C.; Chen, Q.-S.; Rao, D.-J. Artificial intelligence model for studying unconfined compressive performance of fiber-reinforced cemented paste backfill. Trans. Nonferrous Met. Soc. China 2021, 31, 1087–1102. [Google Scholar] [CrossRef]
  49. He, W.; Liu, L.; Fang, Z.; Gao, Y.; Sun, W. Effect of polypropylene fiber on properties of modified magnesium coal-based solid waste backfill materials. Constr. Build. Mater. 2023, 362, 129695. [Google Scholar] [CrossRef]
  50. Chen, X.; Shi, X.Z.; Zhou, J.; Chen, Q.S.; Li, E.; Du, X.H. Compressive behavior and microstructural properties of tailings polypropylene fibre-reinforced cemented paste backfill. Constr. Build. Mater. 2018, 190, 211–221. [Google Scholar] [CrossRef]
  51. Xu, W.; Li, Q.; Zhang, Y. Influence of temperature on compressive strength, microstructure properties and failure pattern of fiber-reinforced cemented tailings backfill. Constr. Build. Mater. 2019, 222, 776–785. [Google Scholar] [CrossRef]
  52. Xue, G.L.; Yilmaz, E.; Feng, G.; Cao, S. Analysis of tensile mechanical characteristics of fiber reinforced backfill through splitting tensile and three-point bending tests. Int. J. Min. Reclam. Environ. 2022, 36, 218–234. [Google Scholar] [CrossRef]
  53. Wu, J.Y.; Jing, H.; Yin, Q.; Meng, B.; Han, G. Strength and ultrasonic properties of cemented waste rock backfill considering confining pressure, dosage and particle size effects. Constr. Build. Mater. 2020, 242, 118132. [Google Scholar] [CrossRef]
  54. Zhou, N.; Du, E.; Zhang, J.X.; Zhu, C.L.; Zhou, H. Mechanical properties improvement of sand-based cemented backfill body by adding glass fibers of different lengths and ratios. Constr. Build. Mater. 2021, 280, 122408. [Google Scholar] [CrossRef]
  55. Wang, Y.; Zhang, S.H.; Niu, D.T.; Fu, Q. Quantitative evaluation of the characteristics of air voids and their relationship with the permeability and salt freeze-thaw resistance of hybrid steel-polypropylene fiber-reinforced concrete composites. Cem. Concr. Compos. 2022, 125, 104292. [Google Scholar] [CrossRef]
  56. Cao, S.; Xue, G.L.; Yilmaz, E.; Yin, Z.Y. Assessment of rheological and sedimentation characteristics of cemented tailings backfill slurry. Int. J. Min. Reclam. Environ. 2021, 35, 319–335. [Google Scholar] [CrossRef]
  57. Xue, G.L.; Yilmaz, E.; Feng, G.R.; Cao, S. Bending behavior and failure mode of cemented tailings backfill composites incorporating different fibers for sustainable construction. Constr. Build. Mater. 2021, 289, 123163. [Google Scholar] [CrossRef]
  58. Li, J.J.; Cao, S.; Yilmaz, E. Compressive fatigue behavior and failure evolution of additive fiber-reinforced cemented tailings composites. Int. J. Miner. Metall. Mater. 2022, 29, 345–355. [Google Scholar] [CrossRef]
  59. Liu, Z.; Li, J.; Zhao, Q.; Wang, J.; Liu, T.; Zhang, Q. Gradation design of phosphorus tailing-graded waste rock subgrade filling using discrete element method. Minerals 2022, 12, 573. [Google Scholar] [CrossRef]
  60. Xin, L.W. Meso-scale modeling of the influence of waste rock content on mechanical behavior of cemented tailings backfill. Constr. Build. Mater. 2021, 307, 124473. [Google Scholar] [CrossRef]
  61. Yin, S.H.; Hou, Y.Q.; Chen, X.; Zhang, M.Z. Mechanical, flowing and microstructural properties of cemented sulfur tailings backfill: Effects of fiber lengths and dosage. Constr. Build. Mater. 2021, 309, 125058. [Google Scholar] [CrossRef]
  62. Libos, I.L.S.; Cui, L.; Liu, X.R. Effect of curing temperature on time-dependent shear behavior and properties of polypropylene fiber-reinforced cemented paste backfill. Constr. Build. Mater. 2021, 311, 125302. [Google Scholar] [CrossRef]
  63. Wang, A.A.; Cao, S.; Yilmaz, E. Effect of height to diameter ratio on dynamic characteristics of cemented tailings backfills with fiber reinforcement through impact loading. Constr. Build. Mater. 2022, 322, 126448. [Google Scholar] [CrossRef]
  64. Xu, X.Q.; An, N.; Fang, K. Experimental investigation into the temperature effect on the shear behavior of the fiber-reinforced interface between rock and cemented paste backfill. Constr. Build. Mater. 2022, 356, 129280. [Google Scholar] [CrossRef]
  65. Xue, G.L.; Yilmaz, E.; Feng, G.R.; Cao, S.; Sun, L.J. Reinforcement effect of polypropylene fiber on dynamic properties of cemented tailings backfill under SHPB impact loading. Constr. Build. Mater. 2021, 279, 122417. [Google Scholar] [CrossRef]
  66. Yang, J.; Zhao, K.; Yu, X.; Yan, Y.J.; He, Z.W.; Zhou, Y.; Lai, Y.M. Fracture evolution of fiber-reinforced backfill based on acoustic emission fractal dimension and b-value. Cem. Concr. Compos. 2022, 134, 104739. [Google Scholar] [CrossRef]
  67. Mashifana, T.; Sithole, T. Clean production of sustainable backfill material from waste gold tailings and slag. J. Clean. Prod. 2021, 308, 127357. [Google Scholar] [CrossRef]
  68. Xue, G.L.; Yilmaz, E. Strength, acoustic, and fractal behavior of fiber reinforced cemented tailings backfill subjected to triaxial compression loads. Constr. Build. Mater. 2022, 338, 127667. [Google Scholar] [CrossRef]
  69. Sun, W.; Wang, H.J.; Hou, K.P. Control of waste rock-tailings paste backfill for active mining subsidence areas. J. Clean. Prod. 2018, 171, 567–579. [Google Scholar] [CrossRef]
  70. Zhang, H.; Cao, S.; Yilmaz, E. Carbon nanotube reinforced cementitious tailings composites: Links to mechanical and microstructural characteristics. Constr. Build. Mater. 2023, 365, 130123. [Google Scholar] [CrossRef]
  71. Huang, Z.Q.; Cao, S.; Yilmaz, E. Investigation on the flexural strength, failure pattern and microstructural characteristics of combined fibers reinforced cemented tailings backfill. Constr. Build. Mater. 2021, 300, 124005. [Google Scholar] [CrossRef]
Minerals 13 00142 g001 550
Figure 1. GSD curves for cement and gold tailings.
Figure 1. GSD curves for cement and gold tailings.
Minerals 13 00142 g001
Minerals 13 00142 g002 550
Figure 2. A flow chart of specimen preparation processes, including innovative materials/methods.
Figure 2. A flow chart of specimen preparation processes, including innovative materials/methods.
Minerals 13 00142 g002
Minerals 13 00142 g003 550
Figure 3. UCS and peak strain of FRCTWRF samples: (a) UCS; (b) peak strain. Cyan means PP6; purple means PP12.
Figure 3. UCS and peak strain of FRCTWRF samples: (a) UCS; (b) peak strain. Cyan means PP6; purple means PP12.
Minerals 13 00142 g003
Minerals 13 00142 g004 550
Figure 4. Stress–strain curves and slopes of post-peak curves for FRCTWRF specimens: (a) stress–strain plots; (b) slopes of post-peak curves.
Figure 4. Stress–strain curves and slopes of post-peak curves for FRCTWRF specimens: (a) stress–strain plots; (b) slopes of post-peak curves.
Minerals 13 00142 g004
Minerals 13 00142 g005 550
Figure 5. 2D CT images of PP6-0.6: (a) Z = 80 mm; (b) Z = 50 mm; (c) Z = 20 mm.
Figure 5. 2D CT images of PP6-0.6: (a) Z = 80 mm; (b) Z = 50 mm; (c) Z = 20 mm.
Minerals 13 00142 g005
Minerals 13 00142 g006 550
Figure 6. 2D CT images of PP12-0.6: (a) Z = 80 mm; (b) Z = 50 mm; (c) Z = 20 mm.
Figure 6. 2D CT images of PP12-0.6: (a) Z = 80 mm; (b) Z = 50 mm; (c) Z = 20 mm.
Minerals 13 00142 g006
Minerals 13 00142 g007 550
Figure 7. Distribution pattern of waste rock within PP6-0.6.
Figure 7. Distribution pattern of waste rock within PP6-0.6.
Minerals 13 00142 g007
Minerals 13 00142 g008 550
Figure 8. Distribution pattern of waste rock within PP12-0.6.
Figure 8. Distribution pattern of waste rock within PP12-0.6.
Minerals 13 00142 g008
Minerals 13 00142 g009 550
Figure 9. 3D reconstructed image of the cracks in PP6-0.6.
Figure 9. 3D reconstructed image of the cracks in PP6-0.6.
Minerals 13 00142 g009
Minerals 13 00142 g010 550
Figure 10. 3D reconstructed image of the cracks in PP12-0.6.
Figure 10. 3D reconstructed image of the cracks in PP12-0.6.
Minerals 13 00142 g010
Minerals 13 00142 g011 550
Figure 11. Microstructure image of FRCTWRF: (a) PP6-0.6; (b) PP12-0.9.
Figure 11. Microstructure image of FRCTWRF: (a) PP6-0.6; (b) PP12-0.9.
Minerals 13 00142 g011
Minerals 13 00142 g012 550
Figure 12. Microscopic image of bent and deformed fibers in PP12-0.3. (a) Area 1; (b) Area 2.
Figure 12. Microscopic image of bent and deformed fibers in PP12-0.3. (a) Area 1; (b) Area 2.
Minerals 13 00142 g012
Minerals 13 00142 g013 550
Figure 13. The main element mapping distributions of FRCTWRF sample.
Figure 13. The main element mapping distributions of FRCTWRF sample.
Minerals 13 00142 g013
Minerals 13 00142 g014 550
Figure 14. EDS values for hydrated products of FRCTWRF sample.
Figure 14. EDS values for hydrated products of FRCTWRF sample.
Minerals 13 00142 g014
Table
Table 1. Key characteristics of polypropylene fiber employed in the backfill.
Table 1. Key characteristics of polypropylene fiber employed in the backfill.
Length (mm)Density (g/cm3)Tensile Strength (MPa)Elongation Rate (%)Elastic Modulus (GPa)
6.0/12.05.9386.03.827.2
Table
Table 2. The proportions of each component of each specimen.
Table 2. The proportions of each component of each specimen.
Sample IDFiber Length
(mm)		Fiber Content
(wt.%)		Tailings Content
(wt.%)		Waste Rock Content
(wt.%)
PP6-0.360.36040
PP6-0.660.66040
PP6-0.960.96040
PP12-0.3120.36040
PP12-0.6120.66040
PP12-0.9120.96040
N-PP 6040
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

Gao, B.; Cao, S.; Yilmaz, E. Effect of Content and Length of Polypropylene Fibers on Strength and Microstructure of Cementitious Tailings-Waste Rock Fill. Minerals 2023, 13, 142. https://0-doi-org.brum.beds.ac.uk/10.3390/min13020142

AMA Style

Gao B, Cao S, Yilmaz E. Effect of Content and Length of Polypropylene Fibers on Strength and Microstructure of Cementitious Tailings-Waste Rock Fill. Minerals. 2023; 13(2):142. https://0-doi-org.brum.beds.ac.uk/10.3390/min13020142

Chicago/Turabian Style

Gao, Bo, Shuai Cao, and Erol Yilmaz. 2023. "Effect of Content and Length of Polypropylene Fibers on Strength and Microstructure of Cementitious Tailings-Waste Rock Fill" Minerals 13, no. 2: 142. https://0-doi-org.brum.beds.ac.uk/10.3390/min13020142

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.