Next Article in Journal
Towards Universal Stimuli-Responsive Drug Delivery Systems: Pillar[5]arenes Synthesis and Self-Assembly into Nanocontainers with Tetrazole Polymers
Next Article in Special Issue
Dendritic Forest-Like Ag Nanostructures Prepared Using Fluoride-Assisted Galvanic Replacement Reaction for SERS Applications
Previous Article in Journal
Li2(BH4)(NH2) Nanoconfined in SBA-15 as Solid-State Electrolyte for Lithium Batteries
Previous Article in Special Issue
Doubly-Resonant Photonic Crystal Cavities for Efficient Second-Harmonic Generation in III–V Semiconductors
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Nanomaterials
Volume 11
Issue 4
10.3390/nano11040948
nanomaterials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Glucose Detection of 4-Mercaptophenylboronic Acid-Immobilized Gold-Silver Core-Shell Assembled Silica Nanostructure by Surface Enhanced Raman Scattering

by
Xuan-Hung Pham
1,
Bomi Seong
1,
Eunil Hahm
1,
Kim-Hung Huynh
1,
Yoon-Hee Kim
1,
Jaehi Kim
1,
Sang Hun Lee
2 and
Bong-Hyun Jun
1,*
1
Department of Bioscience and Biotechnology, Konkuk University, Seoul 143-701, Korea
2
Department of Chemical and Biological Engineering, Hanbat National University, Daejeon 34158, Korea
*
Author to whom correspondence should be addressed.
Nanomaterials 2021, 11(4), 948; https://0-doi-org.brum.beds.ac.uk/10.3390/nano11040948
Submission received: 27 February 2021 / Revised: 2 April 2021 / Accepted: 4 April 2021 / Published: 8 April 2021
(This article belongs to the Special Issue Nanostructured Materials for Photonics and Plasmonics)
Browse Figures
Review Reports Versions Notes

Abstract

:
The importance of glucose in many biological processes continues to garner increasing research interest in the design and development of efficient biotechnology for the sensitive and selective monitoring of glucose. Here we report on a surface-enhanced Raman scattering (SERS) detection of 4-mercaptophenyl boronic acid (4-MPBA)-immobilized gold-silver core-shell assembled silica nanostructure (SiO2@Au@Ag@4-MPBA) for quantitative, selective detection of glucose in physiologically relevant concentration. This work confirmed that 4-MPBA converted to 4-mercaptophenol (4-MPhOH) in the presence of H2O2. In addition, a calibration curve for H2O2 detection of 0.3 µg/mL was successfully detected in the range of 1.0 to 1000 µg/mL. Moreover, the SiO2@Au@Ag@4-MPBA for glucose detection was developed in the presence of glucose oxidase (GOx) at the optimized condition of 100 µg/mL GOx with 1-h incubation time using 20 µg/mL SiO2@Au@Ag@4-MPBA and measuring Raman signal at 67 µg/mL SiO2@Au@Ag. At the optimized condition, the calibration curve in the range of 0.5 to 8.0 mM was successfully developed with an LOD of 0.15 mM. Based on those strategies, the SERS detection of glucose can be achieved in the physiologically relevant concentration range and opened a great promise to develop a SERS-based biosensor for a variety of biomedicine applications.

1. Introduction

Today, diabetes mellitus is a global problem issue with approximately 200 million people worldwide. It is of the principal causes of morbidity and disability and is largely responsible for kidney failure, heart disease, and so on [1]. A monitoring of blood glucose is of important for diabetes care [2]. Therefore, the development of a simple, rapid, and accurate method for glucose detection is highly essential, because blood glucose level is closely associated with diabetes, and hypoglycemia [3,4]. Various methods for glucose detection have been reported, including high-performance liquid chromatography (HPLC) [5], colorimetric detection [6,7,8,9,10], electrochemical detection [11,12,13], fluorescence detection [14,15,16], and surface enhanced Raman scattering (SERS) [17,18,19,20,21,22,23]. Compared with HPLC, SERS exhibited significant advantages, such as rapid, non-destructive, molecular fingerprinting, ultrasensitive, and selectivity [24,25,26,27]. Therefore, various nanoparticles (NPs) such as silver and gold nanostructures have been developed as SERS substrates for glucose detection [17,18,19,20,21].
However, a low affinity with metal surface and Raman scattering cross-section of polarizability limited the detection of glucose by SERS [17,22,28,29]. To achieve a high affinity and selectivity for glucose, a various boronic acid-based Raman reporter have been used to capture glucose selectively on the substrate [17,19,28,29,30,31,32,33]. Most of those studies mainly focused on the specific binding of glucose with the boronic acid motif in 4-MPBA, leading to a significant increase in the absolute intensity of the SERS signal of 4-MPBA, which was ascribed to the orientation change and the charge transfer effect [17,18,19,21,34]. An active SERS substrate based on Ag@4-MPBA nanorod was reported for quantitative detection of glucose [17]. However, the Ag nanorods preparation can sometimes be complicated. On the other hand, the self-condensation of 4-MPBA in order to form anhydride due to the association of OH− with 4-MPBA in various pH media affects the binding of glucose through the formation of esters, which may lead to the properties of the functional molecules being different from those in a solution [18]. Furthermore, the calculation of the peak area of SERS band was so complicated, resulting in a narrow dynamic linear range of glucose concentration. Furthermore, the composite of Au nanoparticles and Porphyrin-Based Metal-Organic Framework for SERS was used to detect glucose with high selectivity and sensitivity [35]. However, the Porphyrin-Based Metal-Organic Framework (Cu-TCPP(Fe) MOF using surfactant caused the binding of surfactant on the surface of MOF nanosheet and blocked some the actives sites of MOFs [36]. It results in the difficulty in synthesizing well-dispersed 2D-MOF nanosheets without blocking their active sites.
Recently, our group developed a gold-silver core-shell assembled silica nanostructure (SiO2@Au@Ag) based on the Au-seed-mediated growth of Ag on the surface of a SiO2 NP template. The presence of Au seeds facilitates and allows for the precise control of the distance and uniform of the Ag shell on SiO2 NPs as well as tuning the optical property of SiO2@Au@Ag in the visible to near IR region [37,38,39]. The presence of the silica template facilitates the density, size, and shape, and the nanogap of Au-Au on the SiO2 surface was easily controlled by SiO2 core, and generating a homogenous SERS substrate of SiO2@Au@Ag [39]. As a result, a high-strength and reliable SiO2@Au@Ag based-SERS substrates with high reproducibility and 4.2 × 106 fold-enhancement as compared to without the nanomaterial was developed for the enzyme-linked immunosorbent assay (ELISA) [40,41]. Simultaneously, a Raman reporter was also immobilized between the Au and Ag layer to play the role of an internal standard for the accurate detection of the pesticide thiram [42,43,44]. However, their use in SERS detection for glucose requires further investigation. In this study, a sensitive and selective analytical method using the basic structure of SiO2@Au@Ag NPs incubated in 4-MPBA and enzyme glucose oxidase was developed for glucose detection using SERS. The evaluation of the SERS band toward glucose level was calculated by the ratio of SERS intensity of intrinsic internal standard 4-MPBA, which was simpler than that based on the peak area of SERS bands.

2. Materials and Methods

2.1. Chemicals and Reagents

Tetraethylorthosilicate (TEOS), 3-aminopropyltriethoxysilane (APTS), silver nitrate (AgNO3), chloroauric acid (HAuCl4), tetrakis(hydroxymethyl)phosphonium chloride (THPC), ascorbic acid (AA), polyvinylpyrrolidone (PVP), phosphate buffer saline (PBS), Tween 20, 4-mercaptophenylboronic acid (4-MPBA), 4-mercaptophenol (4-MPhOH), 4-methylbenzenethiol (4-MBT), thiophenol, 4-glucose, hydrogen peroxide (H2O2), and glucose oxidase (GOx) were purchased from Sigma–Aldrich (USA). Ethanol (EtOH) and aqueous ammonium hydroxide (NH4OH, 27%) were purchased from Daejung (South Korea); and ultrapure water (18.2 MΩ cm) was produced by a Millipore water purification system (EXL water purification; Vivagen Co., Seongnam, Gyeonggi-do, Korea).

2.2. Preparation of SiO2@Au@Ag

The SiO2@Au@Ag NPs were prepared in accordance with the steps outlined in [38]. The SiO2@Au NPs were prepared by incubating 10 mL of Au NP suspension with 2 mL of aminated silica NPs overnight. The colloids were centrifuged and washed thoroughly using EtOH. The NPs were then re-dispersed in 2.0 mL of complete EtOH to obtain 1 mg/mL SiO2@Au NPs in EtOH.
The SiO2@Au@Ag NPs were prepared in an aqueous medium via the reduction and deposition of Ag using ascorbic acid onto SiO2@Au NPs in PVP. Moreover, 200 µL of SiO2@Au (1000 µg/µL) was briefly dispersed in 9.8 mL of water that contained 10 mg of PVP, which was kept still for 30 min. Thereafter, 20 µL of silver nitrate (10 mM) was added to the suspension, followed by the addition of 40 µL of ascorbic acid (10 mM). The suspension was incubated for 15 min to completely reduce the Ag+ ions to Ag0. By repeating the reduction steps, the final AgNO3 concentration of 300 µM was controlled. The SiO2@Au@Ag NPs were obtained by the centrifugation of the suspension at 8500 rpm for 15 min, then the NPs were washed thoroughly using EtOH to remove any excess reagent. The SiO2@Au@Ag NPs were then re-dispersed in 1 mL of absolute EtOH to obtain a 200 µg/mL SiO2@Au@Ag NP suspension.

2.3. Adsorption of 4-MPBA on the Surface of SiO2@Au@Ag

To adsorb 4-MPBA on the surface of SiO2@Au@Ag NPs, 500 µL of 2 mM 4-MPBA solution in EtOH was incubated with 500 µL EtOH contained 20 µg SiO2@Au@Ag NP for 1 h at 25 °C, followed by centrifugation for 15 min at 15,000 rpm to obtain the NP suspension. The prepared NPs were washed thoroughly using PBS containing 0.1% Tween 20 (PBST) to remove any excess reagent. The SiO2@Au@Ag@4-MPBA was then re-dispersed in 100 µL of EtOH, to obtain a 200 µg/mL SiO2@Au@Ag@4-MPBA suspension.

2.4. Behavior of SiO2@Au@Ag@4-MPBA in the Presence of Hydrogen Peroxide

100 µL of PBST containing 20 µg SiO2@Au@Ag@4-MPBA was added incubated with 100 µL of H2O2 at various concentration for 1 h at 25 °C, followed by centrifugation for 15 min at 15,000 rpm to obtain the NP suspension. The prepared NPs were washed thoroughly using PBST to remove any excess reagent. The prepared NPs was then re-dispersed in 100 µL of PBST, to obtain a 200 µg/mL NPs suspension.

2.5. Glucose Detection of SiO2@Au@Ag@4-MPBA

One hundred microliters of PBST containing 20 µg SiO2@Au@Ag@4-MPBA was added, incubated with 100 µL PBST that contained various concentrations of glucose, and 100 µL of GOx for 1 h at 25 °C, followed by centrifugation for 15 min at 15,000 rpm to obtain the NP suspension. The prepared NPs were washed thoroughly using PBST to remove any excess reagent. The prepared NPs was then re-dispersed in 100 µL of PBST, to obtain a 200 µg/mL NPs suspension.

2.6. SERS Measurement

To obtain the surface-enhanced Raman spectra, a micro-Raman system with a 10-mW 532-nm diode-pumped solid-state laser excitation source and an optical microscope (BX41, Olympus, Tokyo, Japan) was utilized. The SERS signals were collected with a back-scattering geometry using an objective lens with a magnification of 10× (0.90 NA, Olympus, Tokyo, Japan). The selected sites were measured randomly, and all the SERS spectra were integrated over a period of 5 s. The size of the laser beam spot was approximately 2.1 μm, and the SERS spectrum was obtained within the wavenumber range of 300–1700 cm−1.

3. Results and Discussion

In this study, SiO2@Au@Ag was first immobilized by 4-MPBA as a Raman reporter and labeling molecule. Then this suspension was added into glucose solution in the presence of the GOx enzyme. GOx enzyme catalyzed and converted glucose to gluconolactone and H2O2. The presence of H2O2 converted 4-MPBA to 4-MPheOH on the surface of SiO2@Au@Au. The variation of SERS signal of 4-MPBA was observed and extrapolated to the concentration of glucose in solution (Figure 1). To prepare SiO2@Au@Ag, silica NPs (~150 nm) were first functionalized by 3-aminopropyltriethoxysilane (APTS) to prepare aminated silica NPs. Simultaneously, colloidal Au NPs (3 nm) were synthesized by THPC and incubated with the aminated silica NPs by to prepare Au NPs seed embedded with SiO2 (SiO2@Au seed NPs), according to the method reported by Pham et al. [37,38,42,43,44]. Subsequently, the Ag NPs on the surface of SiO2@Au seed were grown by reducing a silver precursor (AgNO3) in the presence of ascorbic acid (AA) and polyvinylpyrrolidone (PVP) [37]. The silver ions reduced by AA were selectively grown onto SiO2@Au seed to generate the SiO2@Au@Ag nanostructure. According to a previous study, 4-MPBA was used for specific binding of glucose with the boronic acid motif in 4-MPBA, leading to a significant increase in the absolute intensity of the SERS signal of 4-MPBA. So, we modified the surface of SiO2@Au@Ag by 4-MBPA to generate SiO2@Au@Au@4-MPBA as a specific ligand for glucose. Subsequently, glucose was added in the reaction in the presence of glucose oxidase (GOx). GO catalyzed and converted glucose to glucolactone and hydrogen peroxide (H2O2) in the reaction. H2O2 converts 4-MPBA to 4-mercaptophenol (4-MPhOH).
The characteristics of the SiO2@Au@Ag NPs are first shown in Figure S1. The transmission electron microscopy (TEM) images of the SiO2@Au and SiO2@Au@Ag NPs are shown in Figure S1a. Small-sized Au NPs (3 nm) were immobilized onto the surface of the SiO2 NPs when the colloidal Au NPs were incubated with the amine-functionalized silica NPs for 12 h at 25 °C (Figure S1a-i). After the reduction of AgNO3 in the presence of PVP, the surface of the SiO2@Au NPs contained many Ag NPs (Figure S1a-ii). The UV–Vis spectra of SiO2@Au and SiO2@Au@Ag were investigated, as shown in Figure S1b. The suspension of the SiO2@Au NPs exhibited the maximum peak at ~500–520 nm (Figure S1b-i). A broad band was observed from 320–700 nm, with the maximum peak at ~450 nm, for the suspension of SiO2@Au@Ag NPs (Figure S1b-ii). This indicated the generation of Ag shells, in addition to the creation of hot-spot structures, on the surfaces of the SiO2@Au NPs, thus yielding a continuous spectrum of resonant multi-modes [37,38,42,43].

3.1. Adsorption of 4-MPBA on the Surface of SiO2@Au@Ag

It is believed that 4-MBPA can selectively interact with glucose in solution, so the SERS-active SiO2@Au@Ag were incubated with 4-MPBA solution for 1 h at 25 °C. Figure 2a showed the SERS bands of SiO2@Au@Ag@4-MPBA in ethanol solution. Compared to the SiO2@Au@Au without 4-MPBA (0 µM) and with 100 µM 4-MPBA, we found that the SiO2@Au@Ag in EtOH solution showed SERS bands at 432, 883, 1051, 1097, 1276, and 1455 cm−1, assigned to the SERS bands of the EtOH solution. At 100 µM 4-MPBA, clear and new bands were observed at 417, 473, 1077, 1170, 1484, and 1583 cm−1, indicating that 4-MPBA was successfully immobilized on the surface of SiO2@Au@Ag [18]. The detailed SERS bands of SiO2@Au@Ag@4-MPBA can be seen in Table S1. The SERS intensity of SiO2@Au@Ag@4-MBPA was also examined in the presence of various concentrations of 4-MPBA from 0.1 µM to 100 µM in EtOH solution. The SERS signal of 4-MBPA increased from 0.1 to 10 µM and achieved a saturation at 50 µM. In particular, the intensities of the Raman bands at 1583 cm−1 increased dramatically with 4-MPBA concentration (Figure 2b). Therefore, 50 µM 4-MBPA was chosen for further study.
However, the SERS signal of EtOH was too strong compared to the SERS signal of SiO2@Au@Ag@4-MPBA, which can seriously affect the accuracy of analytical result. Therefore, we re-dispersed the SiO2@Au@Ag@4-MPBA in the PBST pH 7.0 (Figure 3a). Indeed, the SERS bands of 4-MPBA in PBST was clearly observed, compared to those in EtOH. Figure 3a showed that the typical SERS bands of 4-MBPA were dominated by bands at 417 cm−1, 473 cm−1, 824 cm−1, 998 cm−1, 1021 cm−1, 1077 cm−1, 1170 cm−1, 1484 cm−1, and 1583 cm−1. The SERS spectra at 998 cm−1, 1021 cm−1, and 1077 cm−1, which are assigned to the C-C in-plane breathing, C-H in-plane breathing, and C-C in-plane breathing and C-S stretching, respectively (Figure 3a, Table S1). The pair of intense bands at 1586/1573 cm−1 is ascribed to the original and OH--associated forms of C-C stretching. The SERS spectra at 824 and 417 cm−1 were assigned as the C-C out-plane bending and the C-S stretching with weak intensities [18,34,45,46].

3.2. Behavior of SiO2@Au@Ag@4-MPBA in the Presence of Hydrogen Peroxide

First, the SiO2@Au@Ag@4-MPBA were used as a SERS substrate for glucose detection in the range of 1 to 10 mM (Figure S2a). According to the previous report, the boronic acid group of 4-MPBA specifically binds to glucose, leading to a significant increase in the absolute intensity of the SERS signal of 4-MPBA, which was ascribed to the orientation change and the charge transfer effect [17,45]. However, the SERS signal of SiO2@Au@Ag@4-MPBA at pH 7.0 in our study did not show any significantly difference in the range of 1 to 10 mM glucose. Therefore, glucose oxidase enzyme was added to the glucose solution to convert glucose to gluconolactone and hydrogen peroxide to SiO2@Au@Ag@4-MPBA in our study. The behavior of SiO2@Au@Ag@4-MPBA in PBST pH 7.0 containing 1 mg/mL H2O2 was investigated and is shown in Figure 3a.
As mentioned above, we chose the SERS band of 4-MPBA at 417, 1077, and 1583 cm−1 to investigate the variation of SERS band in the presence of H2O2. When SiO2@Au@Ag@4-MPBA was incubated with H2O2, the new bands could be observed clearly at 390 cm−1, 1170 cm−1, and 1597 cm−1. According to previous report, boronated molecules reacts selectively with H2O2 to convert to its corresponding phenol form, so 4-MPBA on the surface of SiO2@Au@Ag can converted to 4-MPheOH or thiophenol [34,46,47]. Thus, we observed the SERS band of both 4-MPheOH and thiophenol in ethanol to compare with 4-MPBA in the presence of H2O2 (Figure S2b). The SERS bands of thiophenol was different from those of 4-PheOH, and 4-MPBA in the presence of H2O2 with dominant bands at 416 cm−1, 996 cm−1, 1018 cm−1, 1069 cm−1, and 1570 cm−1. In contrast, the SERS bands of 4-MPBA in the presence of H2O2 was similar to those of 4-MPheOH with the typical bands at 390 cm−1, 1170 cm−1, and the intense band at 1583/1597 cm−1 (Figure 3a). Based on these results, we concluded that 4-MPBA on the surface of SiO2@Au@Ag was successfully converted to 4-MPheOH in PBST pH 7.0. The effect of H2O2 concentration in the range of 10 pg/mL to 1 mg/mL on the SERS signal of 4-MPBA was also observed in Figure 3b. The bands at 390 cm−1, 1170 cm−1, and 1597 cm−1 increased while the bands at 417 cm−1 and 1583 cm−1 decreased dramatically with the H2O2 concentration. The SERS intensity at 1077 cm−1 was slightly changed. We used the SERS bands of 4-MPBA at 417 cm−1, 1077 cm−1, and 1583 cm−1 as intrinsic internal standards to robust quantitative detection of H2O2 in our study. The results are shown in Figure 3c and Figure S3. Indeed, the increase of H2O2 concentration led to increases of SERS ratio of I390/417, I390/1077, I390/1583, I1170/417, I1170/1077, I1170/1583, I1597/417, I1597/1077, and I1597/1583 (Figure S3). The dramatic increase in SERS ratio was observed in the range of 1 µg/mL to 1000 µg/mL of H2O2. The detection limit of H2O2 based on the SERS ration of I1583/1597 was calculated to be 0.31 µg/mL (3σ/k, where σ is the standard deviation of the blank and k is the slope of the calibration slope).
Next, the effect of experimental conditions for glucose detection on the SERS signal of SiO2@Au@Ag@4-MPBA in the presence of GOx were examined and optimized in Figure 4 and Figures S4–S7.
To reduce the detection time of glucose, we attempted to combine the enzyme reaction and conversion of 4-MPBA to 4-MPheOH into one step, which is termed the “all-in-one” technique. We also conducted the glucose detection in two separate steps: The enzyme reaction followed by the conversion of 4-MPBA to 4-MPheOH, which is termed the “step-by-step” technique. For both techniques, the glucose concentration was fixed at 5 mM using 20 µg SiO2@Au@Ag@4-MPBA for 30 min while the GOx concentration was varied in the range of 10−2–103 µg/mL. The results showed that the SERS signal of the SiO2@Au@Ag@4-MPBA at 5 mM glucose and various concentration of GOx in both the “step-by-step” and “all-in-one” techniques were quite similar (Figure S4). However, the SERS signal of SiO2@Au@Ag@4-MPBA in the “step-by-step” reached saturation earlier than that in the “all-in-one”. As a result, its dynamic linear range was narrower than that of “all-in-one”. Figure 4a showed that in general the SERS signal at I390/1077, and I390/1583 increased with the GOx concentration in the range of 0.1 to 100 µg/mL and achieved the saturation at 100 µg/mL GOx, while the SERS ratio at I390/417 increased with the GOx concentration in the range of 1 to 1000 µg/mL. Thus, 100 µg/mL GOx was utilized for further study.
The incubation time of glucose detection by the SiO2@Au@Ag@4-MPBA was also performed in Figure 4b and Figure S5. The SERS ratio at I390/1077 was saturated at 30 min, and another SERS ratio of the SiO2@Au@Ag@4-MPBA increased with incubation time until 1h. The gradual increase in the SERS signal of SiO2@Au@Ag@4-MPBA in the presence of GOx indicated that the enzyme reaction and conversion of 4-MPBA to 4-MPheOH took place simultaneously for 1h.
In addition, the effect of SiO2@Au@Ag@4-MPBA core-shell amount was observed in the range of 10 to 50 µg. The results can be seen in Figure 4c and Figure S6. It is well known that SERS signal depends on the Raman reporter of nanomaterials [39]. Therefore, when a greater amount of SiO2@Au@Ag@4-MPBA was added, more 4-MPBA were available on the surface of SiO2@Au@Ag, generating numerous detection sites for glucose. However, the SERS signals of the SiO2@Au@Ag@4-MPBA at various core-shell quantities were insignificantly different in our study, indicating that quantities of 4-MPBA molecules of SiO2@Au@Ag at 10 µg were enough to react with all H2O2 generated by 5 mM glucose in the enzyme reaction. However, to ensure that the SiO2@Au@Ag@4-MPBA is sufficient to convert H2O2 generated by higher glucose concentration in diabetes, we decided to use 20 µg SiO2@Au@Ag@4-MPBA for further study.
For Raman measurement, the concentration of SERS substrate is one of the most important factors affecting the SERS signal [39,41,44]. Figure 4d and Figure S7 showed the effect of SiO2@Au@Ag@4-MPBA concentration after glucose incubation in the presence of GOx on the SERS signal of 4-MPBA. In the absence of glucose, the SERS signal of SiO2@Au@Ag@4-MPBA suspension significantly decreased when SiO2@Au@Ag@4-MPBA concentration decreased from 200 µg/mL to 100 µg/mL and the SERS signals were almost unchanged after 100 µg/mL SiO2@Au@Ag@4-MPBA. Meanwhile, the SERS signals of SiO2@Au@Ag@4-MPBA in the presence of 5 mM glucose increased slightly when SiO2@Au@Ag@4-MPBA decreased to 67 µg/mL. After subtracting background signal, the SERS signal achieved the highest value at 67 µg/mL. For concentrations lower than 50 µg/mL, the SERS signal of the glucose-incubated SiO2@Au@Ag@4-MPBA suspension decreased sharply owing to the low diffraction of the suspension.
Based on the above-mentioned results, the highest signal of glucose detection by the SiO2@Au@Ag@4-MPBA in the presence of GOx was achieved at 100 µg/mL GOx with 1-h incubation time using 20 µg SiO2@Au@Ag@4-MPBA and Raman measurement at 67 µg/mL SiO2@Au@Ag@4-MPBA.
After optimizing the detection conditions, the SERS spectra of the SiO2@Au@Ag@4-MPBA suspensions with various glucose concentrations were obtained. Figure 5 described the changes in SERS signal of SiO2@Au@Ag@4-MPBA after reacting with different concentrations of in glucose the range of 0.5 to 8.0 mM with and without 100 µg/mL GOx. The SERS signals of the nanomaterial suspensions at I390/417, I390/1077, I390/1583, I1170/417, I1170/1077, I1170/1583, I1597/417, I1597/1077, and I1597/1583 increased sharply when the glucose concentration was increased from 0.5 mM to 8.0 mM (Figure S8). This implied that H2O2 was produced from GOx in the suspensions by the GOx, and that H2O2 was able to convert 4-MPBA to 4-MPheOH on the surface of SiO2@Au@Ag. When the concentration of glucose increased higher than 6.0 mM, the SERS peak reached saturation. This result was due to complete conversion of 4-MPBA to 4-MPheOH on the surface of SiO2@Au@Ag@4-MPBA. Meanwhile, the SERS signal of SiO2@Au@Ag@4-MPBA in glucose without GOx remained unchanged, indicating that the increase of glucose in the solution did not significantly affect the SERS of 4-MPBA on the surface of SiO2@Au@Ag as mentioned in Figure 2. Therefore, we concluded that the SERS signal of SiO2@Au@Ag@4-MPBA in the glucose solution in the presence of GOx was the result of the combination of the GOx reaction and the conversion of 4-MPBA to 4-MPheOH on the surface of SiO2@Au@Ag.
A linear curve-fitting procedure was utilized for calibration. A significant relationship between the SERS signal ratio and the glucose concentration was found in the experimental data points ranging from 1.0 to 8.0 mM (calibration curve: y = 0.159 x + 0.707, where x is glucose concentration, y is the SERS ration, and R2 = 0.99). The theoretical LOD was 0.15 mM, estimated by the 3sblank criterion. Our result demonstrates that our material can be utilized for glucose detection for diagnosis.
The interference behavior is an important factor for glucose detection since easily oxidizable species, such as ascorbic acid (AA), uric acid (UA), and bovine serum albumin (BSA), at various concentrations and fructose co-exist with glucose in blood samples [48,49,50]. Figure 5b depicted the evaluation of the selectivity of the SiO2@Au@Ag@4-MPBA as a SERS substrate for glucose detection at I390/417 in the presence of interfering species including 50 µM AA, 40 µM UA, 0.5% BSA, 1% BSA, 2% BSA, and 5 µM fructose were evaluated. Additionally, the SERS ration response of the SiO2@Au@Ag@4-MPBA in 5 mM glucose was examined as a reference, and the response SERS ratios at I390/417, I390/1077, I390/1583, I1170/417, I1170/1077, I1170/1583, I1597/417, I1597/1077, and I1597/1583 in 5 mM glucose in the presence of interferences were simultaneously observed in Figure S9. In the presence of 50 µM AA, the SERS ratio of SiO2@Au@Ag@4-MPBA at I390/417 decreased 2% to 98%, while in the presence of 40 µM UA, it decreased to 95% compared to the SERS ratio of 5 mM glucose. The presence of 0.5% BSA caused an insignificant decrease in the SERS ratio at I390/417 to 96%. However the SERS ratio at I390/417 in the presence of 1% BSA or 2% BSA showed a significant decrease to 86 and 82%, respectively, because of the adsorption of BSA on the surface of SiO2@Au@Ag@4-MPBA [51]. The SERS ratio at I390/417 of 5 mM glucose in the presence of 5 µM fructose decreased slightly to 98%. It meant that the detection of glucose by SiO2@Au@Ag@4-MPBA was highly selective. Thereby, the combination of GOx and SiO2@Au@Ag@4-MPBA exhibited excellent selectivity for glucose detection in the presence of interfering species, 50 µM AA, 40 µM UA, 0.5% BSA, and 5 µM fructose with negligible interference to the SERS signal of glucose.
The long-term storage of the SiO2@Au@Ag@4-MPBA was examined in Figure S10. First, 200 µ/mL SiO2@Au@Ag@4-MPBA was synthesized, re-dispersed in EtOH, and stored at 4 °C for one week. The SERS signal of 4-MPBA was measured every day and the SERS signal at 1583 cm−1 was monitored. As showed in Figure S10, the SERS signal was not decreased until seven days, indicating that the surface of SiO2@Au@Ag was not oxidized during storage in EtOH at 4 °C. However, the SERS signal slightly increased after four days, which might be from the partly aggregation of SiO2@Au@Ag.

4. Conclusions

We have developed a new SERS-based boronated nanoprobe of the SiO2@Au@Ag@4-MPBA for quantitative, selective detection of glucose in neutral condition. This work confirmed that 4-MPBA was converted to 4-MPhOH in the presence of H2O2. Moreover, it provided a new calibration curve to evaluate H2O2 species in the range of 1.0 to 1000 µg/mL with LOD as low as 0.3 µg/mL. Moreover, the SiO2@Au@Ag@4-MPBA for glucose detection in the presence of GOx were optimized at 100 µg/mL GOx, 100 µg/mL GOx with 1-h incubation time using 20 µg/mL SiO2@Au@Ag@4-MPBA and measuring Raman signal at 67 µg/mL SiO2@Au@Ag. At the optimized condition, the calibration curve for selective glucose detection in the range of 0.5 to 8.0 mM was successfully developed with an LOD of 0.15 mM. The combination of GOx and our nanostructure also illustrated that our SERS probe can be coupled with other enzymes to greatly expand its applicability to biologically active targets.

Supplementary Materials

The following are available online at https://0-www-mdpi-com.brum.beds.ac.uk/article/10.3390/nano11040948/s1, Figure S1. (a) TEM images and (b) UV-Vis spectra of (i) SiO2@Au (1 mg/mL) and (ii) SiO2@Au@Ag nanostructures (20 µg/mL) synthesized at 2 mg SiO2@NH2 and 300 mM Ag+ concentration. Figure S2. (a) SERS spectra of SiO2@Au@Ag@4-MPBA in PBST containing difference concentration of glucose (0-10 mM). (b) SERS spectra of SiO2@Au@Au in ethanol in the presence of 50 µM 4-mercaptophenylboronic acid, 50 µM 4-mercaptophenylboronic acid + 1000 µg/mL H2O2, 1 mM 4-mercaptophenol, 1 mM thiophenol; Figure S3. Normalized Raman intensity ratio of 20 µg SiO2@Au@Ag@4-MPBA in PBST containing various concentration of H2O2 in the range of 10−6–103 µg/mL at (a) 390/417; (b) 390/1077; (c) 390/1583; (d) 1170/417; (e) 1170/1077; (f) 1170/1583; (g) 1597/417; (h) 1597/1077 and (f) 1597/1583; Figure S4. Normalized Raman intensity ratio of 20 µg SiO2@Au@Ag@4-MPBA in PBST containing 5 mM glucose and difference concentration of glucose oxidase in the range of 10−2–103 µg/mL at (a) 390/417; (b) 390/1077; (c) 390/1583; (d) 1170/417; (e) 1170/1077; (f) 1170/1583; (g) 1597/417; (h) 1597/1077 and (f) 1597/1583; Figure S5. Normalized Raman intensity ratio of 20 µg SiO2@Au@Ag@4-MPBA in PBST containing 5 mM glucose and 100 µg/mL glucose oxidase at different incubation time at (a) 390/417; (b) 390/1077; (c) 390/1583; (d) 1170/417; (e) 1170/1077; (f) 1170/1583; (g) 1597/417; (h) 1597/1077 and (f) 1597/1583; Figure S6. Normalized Raman intensity ratio of SiO2@Au@Ag@4-MPBA using different amount of SiO2@Au@Ag (10–50 µg) in PBST containing 5 mM glucose, 100 µg/mL glucose oxidase for 1 h at (a) 390/417; (b) 390/1077; (c) 390/1583; (d) 1170/417; (e) 1170/1077; (f) 1170/1583; (g) 1597/417; (h) 1597/1077 and (f) 1597/1583; Figure S7. Normalized Raman intensity ratio of 20 µg SiO2@Au@Ag@4-MPBA in PBST containing 5 mM glucose, 100 µg/mL glucose oxidase for 1 h and measure at different concentration of SiO2@Au@Ag at (a) 390/417; (b) 390/1077; (c) 390/1583; (d) 1170/417; (e) 1170/1077; (f) 1170/1583; (g) 1597/417; (h) 1597/1077 and (f) 1597/1583; Figure S8. Glucose detection by SiO2@Au@Au@4-MPBA at optimized condition of 20 µg SiO2@Au@Ag, 100 µg/mL glucose oxidase concentration for 1h and Raman measurement at 67 µg/mL SiO2@Au@Ag in PBST at (a) 390/417; (b) 390/1077; (c) 390/1583; (d) 1170/417; (e) 1170/1077; (f) 1170/1583; (g) 1597/417; (h) 1597/1077 and (f) 1597/1583; Figure S9. Effect of interferences on SERS signal of SiO2@Au@Ag@4-MPBA in 5 mM glucose by SiO2@Au@Au@4-MPBA at optimized condition of 20 µg SiO2@Au@Ag, 100 µg/mL glucose oxidase concentration for 1h and Raman measurement at 67 µg/mL SiO2@Au@Ag in PBST at (a) 390/417; (b) 390/1077; (c) 390/1583; (d) 1170/417; (e) 1170/1077; (f) 1170/1583; (g) 1597/417; (h) 1597/1077 and (f) 1597/1583. Figure S10. Long-term storage of 200 µg/mL SiO2@Au@Ag@4-MPBA at 4 °C in ethanol solution. Table S1. Raman frequencies and assignments of 4-MPBA and 4-MPheOH in EtOH and PBST

Author Contributions

Conceptualization, X.-H.P. and B.-H.J.; methodology, B.S. and X.-H.P.; investigation, B.S. and Y.-H.K.; formal analysis, K.-H.H. and E.H.; software, S.H.L.; writing—original draft preparation, X.-H.P.; writing—review and editing, J.K. and B.-H.J.; supervisor, B.-H.J. All authors have read and agreed to the published version of the manuscript.

Funding

This work was supported by the KU Research Professor Program of Konkuk University and funded by the Ministry of Science and ITC (NRF-2019R1G1A1006488) and by Ministry of Education (NRF-2018R1D1A1B07045708).

Data Availability Statement

Data of the study is included in the main text and/or the supplementary materials.

Acknowledgments

The authors are grateful for the financial support from the NRF of Korea. Further, the author thanks the financial support by Konkuk University.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Rahman, M.M.; Ahammad, A.J.S.; Jin, J.-H.; Ahn, S.J.; Lee, J.-J. A Comprehensive Review of Glucose Biosensors Based on Nanostructured Metal-Oxides. Sensors 2010, 10, 4855–4886. [Google Scholar] [CrossRef] [PubMed]
  2. Reach, G.; Wilson, G.S. Can Continuous Glucose Monitoring Be Used for the Treatment of Diabetes. Anal. Chem. 1992, 64, 381A–386A. [Google Scholar] [CrossRef] [PubMed]
  3. Dutta, A.K.; Maji, S.K.; Biswas, P.; Adhikary, B. New Peroxidase-substrate 3,5-di-tert-butylcatechol for Colorimetric Determination of Blood Glucose in Presence of Prussian Blue-modified Iron Oxide Nanoparticles. Sens. Actuator B Chem. 2013, 177, 676–683. [Google Scholar] [CrossRef]
  4. Chen, H.; Fang, A.; He, L.; Zhang, Y.; Yao, S. Sensitive Fluorescent Detection of H2O2 and Glucose in Human Serum Based on Inner Filter Effect of Squaric Acid-iron(III) on the Fluorescence of Upconversion Nanoparticle. Talanta 2017, 164, 580–587. [Google Scholar] [CrossRef] [PubMed]
  5. Sato, T.; Katayama, K.; Arai, T.; Sako, T.; Tazaki, H. Simultaneous Determination of Serum Mannose and Glucose Concentrations in Dog Serum Using High Performance Liquid Chromatography. Res. Vet. Sci. 2008, 84, 26–29. [Google Scholar] [CrossRef]
  6. Musto, C.J.; Suslick, K.S. Differential Sensing of Sugars by Colorimetric Arrays. Curr. Opin. Chem. Biol. 2010, 14, 758–766. [Google Scholar] [CrossRef] [Green Version]
  7. Deng, J.; Yu, P.; Wang, Y.; Yang, L.; Mao, L. Visualization and Quantification of Neurochemicals with Gold Nanoparticles: Opportunities and Challenges. Adv. Mater. 2014, 26, 6933–6943. [Google Scholar] [CrossRef]
  8. Radhakumary, C.; Sreenivasan, K. Naked Eye Detection of Glucose in Urine Using Glucose Oxidase Immobilized Gold Nanoparticles. Anal. Chem. 2011, 83, 2829–2833. [Google Scholar] [CrossRef]
  9. Jiang, Y.; Zhao, H.; Lin, Y.; Zhu, N.; Ma, Y.; Mao, L. Colorimetric Detection of Glucose in Rat Brain Using Gold Nanoparticles. Angew. Chem. Int. Ed. 2010, 49, 4800–4804. [Google Scholar] [CrossRef] [PubMed]
  10. Li, C.; Hu, J.; Liu, T.; Liu, S. Stimuli-Triggered Off/On Switchable Complexation between a Novel Type of Charge-Generation Polymer (CGP) and Gold Nanoparticles for the Sensitive Colorimetric Detection of Hydrogen Peroxide and Glucose. Macromolecules 2011, 44, 429–431. [Google Scholar] [CrossRef]
  11. Takahashi, S.; Anzai, J.-I. Phenylboronic Acid Monolayer-Modified Electrodes Sensitive to Sugars. Langmuir 2005, 21, 5102–5107. [Google Scholar] [CrossRef]
  12. Li, J.; Wang, Z.; Li, P.; Zong, N.; Li, F. A Sensitive Non-enzyme Sensing Platform for Glucose Based on Boronic Acid–diol Binding. Sens. Actuators B 2012, 161, 832–837. [Google Scholar] [CrossRef]
  13. Gao, P.; Wang, Z.; Yang, L.; Ma, T.; Yang, L.; Guo, Q.; Huang, S. A Glucose-responsive pH-switchable Bioelectrocatalytic Sensor Based on Phenylboronic Acid-diol Specificity. Electrochim. Acta 2015, 151, 370–377. [Google Scholar] [CrossRef]
  14. Zhang, L.; Zhang, Z.-Y.; Liang, R.-P.; Li, Y.-H.; Qiu, J.-D. Boron-Doped Graphene Quantum Dots for Selective Glucose Sensing Based on the “Abnormal” Aggregation-Induced Photoluminescence Enhancement. Anal. Chem. 2014, 86, 4423–4430. [Google Scholar] [CrossRef] [PubMed]
  15. Wannajuk, K.; Jamkatoke, M.; Tuntulani, T.; Tomapatanaget, B. Highly Specific-glucose Fluorescence Sensing Based on Boronic Anthraquinone Derivatives via the GOx Enzymatic Reaction. Tetrahedron 2012, 68, 8899–8904. [Google Scholar] [CrossRef]
  16. Yan, J.; Fang, H.; Wang, B. Boronolectins and Fluorescent Boronolectins: An Examination of the Detailed Chemistry Issues Important for the Design. Med. Res. Rev. 2005, 25, 490–520. [Google Scholar] [CrossRef] [PubMed]
  17. Sun, X.; Stagon, S.; Huang, H.; Chen, J.; Lei, Y. Functionalized Aligned Silver Nanorod Arrays for Glucose Sensing through Surface Enhanced Raman Scattering. RSC Adv. 2014, 4, 23382–23388. [Google Scholar] [CrossRef]
  18. Li, S.; Zhou, Q.; Chu, W.; Zhao, W.; Zheng, J. Surface-enhanced Raman Scattering Behaviour of 4-mercaptophenyl Boronic Acid on Assembled Silver Nanoparticles. Phys. Chem. Chem. Phys. 2015, 17, 17638–17645. [Google Scholar] [CrossRef] [PubMed]
  19. Torul, H.; Ciftci, H.; Dudak, F.C.; Adguzel, Y.; Kulah, H.; Boyac, I.H.; Tamer, U. Glucose Determination Based on a Two Component Self-assembled Monolayer Functionalized Surface-enhanced Raman Spectroscopy (SERS) Probe. Anal. Methods 2014, 6, 5097–5104. [Google Scholar] [CrossRef]
  20. Gupta, V.K.; Atar, N.; Yola, M.L.; Eryılmaz, M.; Torul, H.; Tamer, U.; Boyacı, İ.H.; Üstündağ, Z. A Novel Glucose Biosensor Platform Based on Ag@AuNPs Modified Graphene Oxide Nanocomposite and SERS Application. J. Colloid Interface Sci. 2013, 406, 231–237. [Google Scholar] [CrossRef]
  21. Pham, X.-H.; Shim, S.; Kim, T.-H.; Hahm, E.; Kim, H.-M.; Rho, W.-Y.; Jeong, D.H.; Lee, Y.-S.; Jun, B.-H. Glucose Detection Using 4-mercaptophenyl Boronic Acid-incorporated Silver Nanoparticles-embedded Silica-coated Graphene Oxide as a SERS Substrate. BioChip J. 2017, 11, 46–56. [Google Scholar] [CrossRef]
  22. Sooraj, K.P.; Ranjan, M.; Rao, R.; Mukherjee, S. SERS Based Detection of Glucose with Lower Concentration than Blood Glucose Level Using Plasmonic Nanoparticle Arrays. Appl. Surf. Sci. 2018, 447, 576–581. [Google Scholar] [CrossRef]
  23. Syamala Kiran, M.; Itoh, T.; Yoshida, K.-I.; Kawashima, N.; Biju, V.; Ishikawa, M. Selective Detection of HbA1c Using Surface Enhanced Resonance Raman Spectroscopy. Anal. Chem. 2010, 82, 1342–1348. [Google Scholar] [CrossRef] [PubMed]
  24. Harper, M.M.; McKeating, K.S.; Faulds, K. Recent Developments and Future Directions in SERS for Bioanalysis. Phys. Chem. Chem. Phys. 2013, 15, 5312–5328. [Google Scholar] [CrossRef] [PubMed]
  25. Gong, X.; Bao, Y.; Qiu, C.; Jiang, C. Individual Nanostructured Materials: Fabrication and Surface-enhanced Raman Scattering. Chem. Commun. 2012, 48, 7003–7018. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  26. Wu, D.-Y.; Li, J.-F.; Ren, B.; Tian, Z.-Q. Electrochemical Surface-enhanced Raman Spectroscopy of Nanostructures. Chem. Soc. Rev. 2008, 37, 1025–1041. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  27. Schlücker, S. Surface-Enhanced Raman Spectroscopy: Concepts and Chemical Applications. Angew. Chem. Int. Ed. 2014, 53, 4756–4795. [Google Scholar] [CrossRef] [PubMed]
  28. Shafer-Peltier, K.E.; Haynes, C.L.; Glucksberg, M.R.; Van Duyne, R.P. Toward a Glucose Biosensor Based on Surface-Enhanced Raman Scattering. JACS 2003, 125, 588–593. [Google Scholar] [CrossRef]
  29. Lyandres, O.; Yuen, J.M.; Shah, N.C.; VanDuyne, R.P.; Walsh, J.T.; Glucksberg, M.R. Progress Toward an in vivo Surface-Enhanced Raman Spectroscopy Glucose Sensor. Diabetes Technol. Ther. 2008, 10, 257–265. [Google Scholar] [CrossRef] [Green Version]
  30. Bull, S.D.; Davidson, M.G.; van den Elsen, J.M.H.; Fossey, J.S.; Jenkins, A.T.A.; Jiang, Y.-B.; Kubo, Y.; Marken, F.; Sakurai, K.; Zhao, J.; et al. Exploiting the Reversible Covalent Bonding of Boronic Acids: Recognition, Sensing, and Assembly. Acc. Chem. Res. 2013, 46, 312–326. [Google Scholar] [CrossRef]
  31. Hansen, J.S.; Christensen, J.B.; Petersen, J.F.; Hoeg-Jensen, T.; Norrild, J.C. Arylboronic Acids: A Diabetic Eye on Glucose Sensing. Sens. Actuators B 2012, 161, 45–79. [Google Scholar] [CrossRef]
  32. Nishiyabu, R.; Kubo, Y.; James, T.D.; Fossey, J.S. Boronic Acid Building Blocks: Tools for Sensing and Separation. Chem. Commun. 2011, 47, 1106–1123. [Google Scholar] [CrossRef] [PubMed]
  33. Ye, J.; Chen, Y.; Liu, Z. A Boronate Affinity Sandwich Assay: An Appealing Alternative to Immunoassays for the Determination of Glycoproteins. Angew. Chem. Int. Ed. 2014, 53, 10386–10389. [Google Scholar] [CrossRef] [PubMed]
  34. Gu, X.; Wang, H.; Schultz, Z.D.; Camden, J.P. Sensing Glucose in Urine and Serum and Hydrogen Peroxide in Living Cells by Use of a Novel Boronate Nanoprobe Based on Surface-Enhanced Raman Spectroscopy. Anal. Chem. 2016, 88, 7191–7197. [Google Scholar] [CrossRef] [Green Version]
  35. Hu, S.; Jiang, Y.; Wu, Y.; Guo, X.; Ying, Y.; Wen, Y.; Yang, H. Enzyme-Free Tandem Reaction Strategy for Surface-Enhanced Raman Scattering Detection of Glucose by Using the Composite of Au Nanoparticles and Porphyrin-Based Metal–Organic Framework. ACS Appl. Mater. Interfaces 2020, 12, 55324–55330. [Google Scholar] [CrossRef]
  36. Zhao, M.; Huang, Y.; Peng, Y.; Huang, Z.; Ma, Q.; Zhang, H. Two-dimensional Metal–organic Framework Nanosheets: Synthesis and Applications. Chem. Soc. Rev. 2018, 47, 6267–6295. [Google Scholar] [CrossRef] [PubMed]
  37. Pham, X.-H.; Lee, M.; Shim, S.; Jeong, S.; Kim, H.-M.; Hahm, E.; Lee, S.H.; Lee, Y.-S.; Jeong, D.H.; Jun, B.-H. Highly Sensitive and Reliable SERS Probes Based on Nanogap Control of a Au-Ag Alloy on Silica Nanoparticles. RSC Adv. 2017, 7, 7015–7021. [Google Scholar] [CrossRef] [Green Version]
  38. Shim, S.; Pham, X.-H.; Cha, M.G.; Lee, Y.-S.; Jeong, D.H.; Jun, B.-H. Size Effect of Gold on Ag-coated Au Nanoparticle-embedded Silica Nanospheres. RSC Adv. 2016, 6, 48644–48650. [Google Scholar] [CrossRef]
  39. Bong-Hyun, J.; Gunsung, K.; Sinyoung, J.; Suk, N.M.; Xuan-Hung, P.; Homan, K.; Myung-Haing, C.; Jong-Ho, K.; Yoon-Sik, L.; Hong, J.D. Silica Core-based Surface-enhanced Raman Scattering (SERS) Tag: Advances in Multifunctional SERS Nanoprobes for Bioimaging and Targeting of Biomarkers. Bull. Korean Chem. Soc. 2015, 36, 963–978. [Google Scholar] [CrossRef]
  40. Pham, X.-H.; Hahm, E.; Kim, T.H.; Kim, H.-M.; Lee, S.H.; Lee, Y.-S.; Jeong, D.H.; Jun, B.-H. Enzyme-catalyzed Ag Growth on Au Nanoparticle-assembled Structure for Highly Sensitive Colorimetric Immunoassay. Sci. Rep. 2018, 8, 6290. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  41. Pham, X.-H.; Hahm, E.; Kim, T.H.; Kim, H.-M.; Lee, S.H.; Lee, S.C.; Kang, H.; Lee, H.-Y.; Jeong, D.H.; Choi, H.S.; et al. Enzyme-amplified SERS Immunoassay with Ag-Au Bimetallic SERS Hot Spots. Nano Res. 2020, 13, 3338–3346. [Google Scholar] [CrossRef]
  42. Pham, X.-H.; Hahm, E.; Kang, E.; Ha, Y.N.; Lee, S.H.; Rho, W.-Y.; Lee, Y.-S.; Jeong, D.H.; Jun, B.-H. Gold-silver Bimetallic Nanoparticles with a Raman Labeling Chemical Assembled on Silica Nanoparticles as an Internal-standard-containing Nanoprobe. J. Alloys Compd. 2019, 779, 360–366. [Google Scholar] [CrossRef]
  43. Pham, X.-H.; Hahm, E.; Kang, E.; Son, B.S.; Ha, Y.; Kim, H.-M.; Jeong, D.H.; Jun, B.-H. Control of Silver Coating on Raman Label Incorporated Gold Nanoparticles Assembled Silica Nanoparticles. Int. J. Mol. Sci. 2019, 20, 1258. [Google Scholar] [CrossRef] [Green Version]
  44. Pham, X.-H.; Hahm, E.; Huynh, K.-H.; Son, B.S.; Kim, H.-M.; Jeong, D.H.; Jun, B.-H. 4-Mercaptobenzoic Acid Labeled Gold-Silver-Alloy-Embedded Silica Nanoparticles as an Internal Standard Containing Nanostructures for Sensitive Quantitative Thiram Detection. Int. J. Mol. Sci. 2019, 20, 4841. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  45. Yang, D.; Afroosheh, S.; Lee, J.O.; Cho, H.; Kumar, S.; Siddique, R.H.; Narasimhan, V.; Yoon, Y.-Z.; Zayak, A.T.; Choo, H. Glucose Sensing Using Surface-Enhanced Raman-Mode Constraining. Anal. Chem. 2018, 90, 14269–14278. [Google Scholar] [CrossRef] [Green Version]
  46. Ly, N.H.; Lam, A.T.N.; Dinh Bao, N.; Kwark, Y.-J.; Joo, S.W. Glucose-induced and Fructose-induced Deboronation Reaction of 4-mercaptophenylboronic Acid Assembled on Silver Investigated by Surface-enhanced Raman Scattering. Surf. Interface Anal. 2017, 49, 495–502. [Google Scholar] [CrossRef]
  47. Lippert, A.R.; Van de Bittner, G.C.; Chang, C.J. Boronate Oxidation as a Bioorthogonal Reaction Approach for Studying the Chemistry of Hydrogen Peroxide in Living Systems. Acc. Chem. Res. 2011, 44, 793–804. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  48. Liu, B.; Hu, R.; Deng, J. Characterization of Immobilization of an Enzyme in a Modified Y Zeolite Matrix and Its Application to an Amperometric Glucose Biosensor. Anal. Chem. 1997, 69, 2343–2348. [Google Scholar] [CrossRef] [PubMed]
  49. Laughlin, M.R. Normal Roles for Dietary Fructose in Carbohydrate Metabolism. Nutrients 2014, 6, 3117–3129. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  50. Kawasaki, T.; Akanuma, H.; Yamanouchi, T. Increased Fructose Concentrations in Blood and Urine in Patients with Diabetes. Diabetes Care 2002, 25, 353–357. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  51. Höller, R.P.M.; Jahn, I.J.; Cialla-May, D.; Chanana, M.; Popp, J.; Fery, A.; Kuttner, C. Biomacromolecular-Assembled Nanoclusters: Key Aspects for Robust Colloidal SERS Sensing. ACS Appl. Mater. Interfaces 2020, 12, 57302–57313. [Google Scholar] [CrossRef] [PubMed]
Nanomaterials 11 00948 g001 550
Figure 1. Typical illustration of glucose detection of 4-mercaptophenylboronic acid immobilized-gold-silver core-shell assembled silica nanostructure in the presence of glucose oxidase.
Figure 1. Typical illustration of glucose detection of 4-mercaptophenylboronic acid immobilized-gold-silver core-shell assembled silica nanostructure in the presence of glucose oxidase.
Nanomaterials 11 00948 g001
Nanomaterials 11 00948 g002 550
Figure 2. (a) SERS spectra and (b) normalized SERS intensity plot at 883 cm−1 of SiO2@Au@Ag@4-MPBA at various concentration from 0.1 to 100 µM in ethanol solution.
Figure 2. (a) SERS spectra and (b) normalized SERS intensity plot at 883 cm−1 of SiO2@Au@Ag@4-MPBA at various concentration from 0.1 to 100 µM in ethanol solution.
Nanomaterials 11 00948 g002
Nanomaterials 11 00948 g003 550
Figure 3. (a) SERS spectra and (b) SERS intensity of SiO2@Au@Ag@4-MPBA, and (c) SERS intensity ratio of I390/417, I1170/1077, I1597/1583 toward various concentration of H2O2 from 10 pg/mL to 1 mg/mL in PBST pH 7.0.
Figure 3. (a) SERS spectra and (b) SERS intensity of SiO2@Au@Ag@4-MPBA, and (c) SERS intensity ratio of I390/417, I1170/1077, I1597/1583 toward various concentration of H2O2 from 10 pg/mL to 1 mg/mL in PBST pH 7.0.
Nanomaterials 11 00948 g003
Nanomaterials 11 00948 g004 550
Figure 4. Optimization of glucose detection by SiO2@Au@Au@4-MPBA in all-in-one technique, (a) glucose oxidase concentration, (b) incubation time, (c) SiO2@Au@Ag@4-MBA amount, and (d) dilution of SiO2@Au@Ag for Raman measurement in PBST at I390/417, I390/1077, I390/1583.
Figure 4. Optimization of glucose detection by SiO2@Au@Au@4-MPBA in all-in-one technique, (a) glucose oxidase concentration, (b) incubation time, (c) SiO2@Au@Ag@4-MBA amount, and (d) dilution of SiO2@Au@Ag for Raman measurement in PBST at I390/417, I390/1077, I390/1583.
Nanomaterials 11 00948 g004
Nanomaterials 11 00948 g005 550
Figure 5. (a) SERS signal plot of SiO2@Au@Au@4-MPBA at various glucose concentrations and (b) the effect of interferences on the SERS signal of SiO2@Au@Ag@4-MPBA in 5 mM glucose and 50 µM AA, 40 µM UA, 0.5% BSA, 1% BSA, 2% BSA, and 5 µM fructose by SiO2@Au@Au@4-MPBA in PBST at SERS ratio of 390 and 417. The optimized condition is 20 µg SiO2@Au@Ag, 100 µg/mL glucose oxidase concentration for 1h, and Raman measurement at 67 µg/mL SiO2@Au@Ag.
Figure 5. (a) SERS signal plot of SiO2@Au@Au@4-MPBA at various glucose concentrations and (b) the effect of interferences on the SERS signal of SiO2@Au@Ag@4-MPBA in 5 mM glucose and 50 µM AA, 40 µM UA, 0.5% BSA, 1% BSA, 2% BSA, and 5 µM fructose by SiO2@Au@Au@4-MPBA in PBST at SERS ratio of 390 and 417. The optimized condition is 20 µg SiO2@Au@Ag, 100 µg/mL glucose oxidase concentration for 1h, and Raman measurement at 67 µg/mL SiO2@Au@Ag.
Nanomaterials 11 00948 g005
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Pham, X.-H.; Seong, B.; Hahm, E.; Huynh, K.-H.; Kim, Y.-H.; Kim, J.; Lee, S.H.; Jun, B.-H. Glucose Detection of 4-Mercaptophenylboronic Acid-Immobilized Gold-Silver Core-Shell Assembled Silica Nanostructure by Surface Enhanced Raman Scattering. Nanomaterials 2021, 11, 948. https://0-doi-org.brum.beds.ac.uk/10.3390/nano11040948

AMA Style

Pham X-H, Seong B, Hahm E, Huynh K-H, Kim Y-H, Kim J, Lee SH, Jun B-H. Glucose Detection of 4-Mercaptophenylboronic Acid-Immobilized Gold-Silver Core-Shell Assembled Silica Nanostructure by Surface Enhanced Raman Scattering. Nanomaterials. 2021; 11(4):948. https://0-doi-org.brum.beds.ac.uk/10.3390/nano11040948

Chicago/Turabian Style

Pham, Xuan-Hung, Bomi Seong, Eunil Hahm, Kim-Hung Huynh, Yoon-Hee Kim, Jaehi Kim, Sang Hun Lee, and Bong-Hyun Jun. 2021. "Glucose Detection of 4-Mercaptophenylboronic Acid-Immobilized Gold-Silver Core-Shell Assembled Silica Nanostructure by Surface Enhanced Raman Scattering" Nanomaterials 11, no. 4: 948. https://0-doi-org.brum.beds.ac.uk/10.3390/nano11040948

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop