Next Article in Journal
One-Step Hydrothermal Synthesis of P25 @ Few Layered MoS2 Nanosheets toward Enhanced Bi-catalytic Activities: Photocatalysis and Electrocatalysis
Next Article in Special Issue
Functional Magnetic Composites Based on Hexaferrites: Correlation of the Composition, Magnetic and High-Frequency Properties
Previous Article in Journal
Reveal the Deformation Mechanism of (110) Silicon from Cryogenic Temperature to Elevated Temperature by Molecular Dynamics Simulation
Previous Article in Special Issue
Biosensing and Delivery of Nucleic Acids Involving Selected Well-Known and Rising Star Functional Nanomaterials
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Nanomaterials
Volume 9
Issue 11
10.3390/nano9111635
nanomaterials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Synthesis of Mn0.5Zn0.5SmxEuxFe1.8−2xO4 Nanoparticles via the Hydrothermal Approach Induced Anti-Cancer and Anti-Bacterial Activities

by
Sultan Akhtar
1,
Suriya Rehman
2,
Munirah A. Almessiere
1,3,
Firdos Alam Khan
4,
Yassine Slimani
1 and
Abdulhadi Baykal
5,*
1
Department of Biophysics, Institute for Research and Medical Consultations (IRMC), Imam Abdulrahman Bin Faisal University, P.0. Box 1982, Dammam 31441, Saudi Arabia
2
Department of Epidemic Disease Research, Institute for Research and Medical Consultations (IRMC), Imam Abdulrahman Bin Faisal University, P.0. Box 1982, Dammam 31441, Saudi Arabia
3
Department of Physics, College of Science, Imam Abdulrahman Bin Faisal University, P.0. Box 1982, Dammam 31441, Saudi Arabia
4
Department of Stem Cell Biology, Institute for Research and Medical Consultations (IRMC), Imam Abdulrahman Bin Faisal University, Post Box No. 1982, Dammam 31441, Saudi Arabia
5
Department of Nano-Medicine Research, Institute for Research and Medical Consultations (IRMC), Imam Abdulrahman Bin Faisal University, P.0. Box 1982, Dammam 31441, Saudi Arabia
*
Author to whom correspondence should be addressed.
Nanomaterials 2019, 9(11), 1635; https://0-doi-org.brum.beds.ac.uk/10.3390/nano9111635
Submission received: 25 October 2019 / Revised: 11 November 2019 / Accepted: 12 November 2019 / Published: 18 November 2019
(This article belongs to the Special Issue Functional Nanomagnetics and Magneto-Optical Nanomaterials)
Browse Figures
Versions Notes

Abstract

:
Manganese metallic nanoparticles are attractive materials for various biological and medical applications. In the present study, we synthesized unique Mn0.5Zn0.5SmxEuxFe1.8−2xO4 (0.01 ≤ x ≤ 0.05) nanoparticles (NPs) by using the hydrothermal approach. The structure and surface morphology of the products were determined by X-ray powder diffraction (XRD), transmission electron and scanning electron microcopies (TEM and SEM), along with energy dispersive X-ray spectroscopy (EDX). We evaluated the impact of Mn0.5Zn0.5SmxEuxFe1.8−2xO4 NPs on both human embryonic stem cells (HEK-293) (normal cells) and human colon carcinoma cells (HCT-116) (cancerous cells). We found that post-48 h of treatment of all products showed a significant decline in the cancer cell population as revealed by microscopically and the (3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide) tetrazolium (MTT) assay. The inhibitory concentration (IC50) values of the products ranged between 0.75 and 2.25 µg/mL. When tested on normal and healthy cells (HEK-293), we found that the treatment of products did not produce any effects on the normal cells, which suggests that all products selectively targeted the cancerous cells. The anti-bacterial properties of the samples were also evaluated by Minimum Inhibitory Concentration (MIC) and Minimum Bactericidal Concentration (MBC) assays, which showed that products also inhibited the bacterial growth.

1. Introduction

In recent years, spinel ferrites have attracted much attention from researchers due to their versatile magnetic properties and wide range of applications. Nanosized ferrites have shown enhanced optical and magnetic properties compared to their bulk counterpart because of better magnetic coupling between the sub-lattices (tetrahedral (Td) or octahedral (Oh)) [1]. Due to improved properties, the nanosized ferrites have been used for a broad range of applications, including: Fundamental research into industrial (sensors, refrigeration, transformers, electrical devices, disk recording, etc.) and medical applications (drug delivery, MRI (magnetic resonance imaging) technology separation, cancer therapy, biosensing, etc.) [2,3,4,5,6,7,8,9,10]. Ferrites are also most frequently used as magnetic absorbing materials owing to their cost effectiveness, excellent magnetic loss, and good stability [8]. Another advantage of nanosized spinel ferrites is that one can tune the magnetic properties by optimizing the size of the nanoparticles. A general structure of spinel ferrites is MFe2O4 (M = manganese, cobalt, zinc, magnesium, etc., Co, Zn, Mg, etc.). In this crystalline structure, anions (oxygen) form face-centered cubic arrangements and metal cations (M2+ and Fe3+) occupy either Td or Oh interstitial sites [11]. From the available ferrites, manganese-based ferrites (MnFe2O4) are considered as more significant because of their high Ms (saturation magnetization) and low loss of power at high frequencies [12]. Manganese ferrites are widely studied owing to their wide range of applications, such as in microwave industries, protecting the barrier against the harm of microwave, satellite communication, microwave dark room, etc. [13]. Furthermore, nanosized ferrites can provide better communication at high frequencies (10 kHz to a few MHz) with great stability because of their high electrical resistivity [13,14]. Recently, Co-Zn-substituted spinel-type ferrites have been studied and found attractive for bio-medical applications because of their suitable room temperature magnetic properties [15,16]. Spinel ferrites have also multiferroic applications. Multiferroic nanostructures have attracted lots of attention by researchers due to their unique benefits compared with bulk multiferroics. The interface between the piezoelectric phase and the ferromagnetic phase is well established and leads to a high magnetoelectric coupling effect by reducing the coupling loss [17,18].
Nanoparticles (NPs) possessed tremendous biological applications [19,20,21,22,23] as they have a dimension of less than 100 nm. There are various types of NPs, like metallic NPs, ceramic NPs, and polymeric NPs, and this classification is based on their size, shape, and property [19,23,24]. Over the past few years, metallic nanoparticles (MNPs) have been used in the field of medicine and pharmaceutical sciences [22,24]. There are many approaches, which have been developed to synthesize diverse and customized MNPs that can be used in experimental medicine, drug design, drug delivery, electrical and electronic engineering, electrochemical sensors, and biochemical sensors [23,24]. There has been an enormous increase in the rate of cancer occurrence around the world, and due to the non-availability of robust treatment, the rate of cancer morality has also been increasing. In this background, there is the need for an alternative approach to tackle this issue. MNPs possess better capabilities to treat the cancer as MNPs have an enhanced reactive surface area, which improves the therapeutic efficacy of the treatment.
To the best of our knowledge, Mn0.5Zn0.5EuxSmxFe1.5−2xO4 (0.01 ≤ x ≤ 0.05) NPs have been synthesized (hydrothermally) and characterized, and its cytotoxicity and antibacterial activity was studied for the first time in this study. In this paper, we synthesized unique Mn0.5Zn0.5EuxSmxFe1.5−2xO4 (0.01 ≤ x ≤ 0.05) NPs using the hydrothermal procedure. Both the spinel structure and nanosized particles were determined via XRD. The cubic morphology of them was proven by SEM, TEM, EDX, and elemental mapping spectroscopy. We evaluated the impact of as-synthesized NPs on two cancer cell lines: HCT-116 (human colorectal carcinoma cells) and HEK-293 (human embryonic kidney cells). The anti-bacterial properties of Mn0.5Zn0.5EuxSmxFe1.5−2xO4 (0.01 ≤ x ≤ 0.05) NPs were also evaluated on Escherichia coli (E. coli) and Staphylococcus aureus (S. aureus) cells using Minimum Inhibitory Concentration (MIC) and Minimum Bactericidal Concentration (MBC), assays and SEM examination.

2. Experimental Procedure

2.1. Synthesis of Spinel Nanoparticles

Manganese (II) nitrate (Mn(NO3)2), zinc (II) nitrate (Zn(NO3)2), iron (III) nitrate hexahydrate (Fe(NO3)3.6H2O), europium(III) nitrate (Eu(NO3)3), and samarium(III) nitrate hexahydrate (Sm(NO3)3·6H2O) were utilized to fabricate Mn0.5Zn0.5EuxSmxFe1.5−2xO4 (0.01 ≤ x ≤ 0.05) NPs via the hydrothermal approach. Specific ratios of metals nitrates were thawed in 50 mL of DI H2O with forceful stirring for 45 min. The pH was attuned at 11 by the addition of sodium hydroxide (NaOH) with stirring for 30 min and then the solution was exposed to an ultrasonic water bath for 40 min. The mixture was transferred to a Teflon-lined vessel, which was heated at 180 °C for 10 h in an oven. The final powder was washed with DI H2O several times and left to dry at 80 °C for 5 h. Structure was confirmed using XRD (Rigaku Benchtop Miniflex XRD analyzer with Cu Kα radiation) over the 2θ range of 20° to 70°. The microstructure was imaged by scanning electron microscope (SEM) and (TEM) (FEI Titan ST) coupled with energy-dispersive X-ray spectroscopy (EDX).

2.2. Anticancer Activities

2.2.1. In Vitro Testing of Cytotoxicity

In the present study, cancer cell line (human colon carcinoma cells-HCT-116) and normal healthy cell line human embryonic kidney cells (HEK-293) were used to evaluate the cytotoxicity. The cells were cultured as per the method described previously [22,24]. In brief, cells were grown in DMEM media, L-glutamine, fetal bovine serum, selenium chloride, and antibiotic penicillin and streptomycin respectively in a CO2 incubator at 37 °C. When cells become 70% to 80% confluence, they were tested for the MTT (3-[4,5-dimethylthiazol-2-yl]-2,5-diphenyl-tetrazolium bromide (Molecules, New Zealand) assay, which was used to examine the impact of nanoparticles on cancer cell viability. Cells were treated with different concentrations (2.0 to 40 µg/mL) of Mn0.5Zn0.5SmxEuxFe1.8−2xO4 (0.01 ≤ x ≤ 0.05) NPs. In the control group, we did not add Mn0.5Zn0.5SmxEuxFe1.8−2xO4 (0.01 ≤ x ≤ 0.05) NPs. After 48 h of treatment, the culture medium was removed and 5.0-µL MTT (Sigma-Aldrich, St. Louis, MO, USA) solution (10 mg/mL) was added to each well and culture plates were incubated for 4 h. Then, culture media was removed and dimethyl sulfoxide (DMSO) was added in each well where MTT developed formazan crystals. Subsequently, culture plates were read under a microplate reader (Bio-Rad Laboratories, Hercules, CA, USA) at 570 nm. The data were analyzed with GraphPad Prism, GraphPad Software by a one-way analysis of variance (ANOVA) and p-values were calculated by Student′s t-test.

2.2.2. Nuclear Staining by DAPI

The cancerous cells were stained with DAPI to examine the impact of Mn0.5Zn0.5SmxEuxFe1.8−2xO4 (0.01 ≤ x ≤ 0.05) NPs on the cell nucleus. In the first group, HCT-116 cells were divided into two types: Group one was the control (without Mn0.5Zn0.5SmEuFe1.8−2xO4 (0.01 ≤ x ≤ 0.05) NPs treatment, and group two was the Mn0.5Zn0.5SmEuFe1.8−2xO4 (0.01 ≤ x ≤ 0.05) NPs-treated groups. Similarly, we also tested HEK-293 cells. They were divided into two groups: One was the control (without NPs treatment), and another one was NPs-treated groups. After 48 h of treatment, both cancerous and normal cells were pre-treated with ice-cold (4%) paraformaldehyde. Then, cells were treated with (0.1%) Triton X-100 in phosphate-buffered saline (PBS) for 5 min for cell membrane permeabilization. Both control and NPs-treated cells were stained with DAPI (1 μg/mL) prepared in PBS for 5 min in a dark environment. Finally, the cells were washed with (0.1%) Triton X-100 prepared in PBS. The nuclear morphology of both control and NPs-treated cells was examined under a confocal scanning microscope (Zeiss, Germany) equipped with a digital camera.

2.3. Antibacterial Activity

2.3.1. Preparation of Test Nanomaterial and Inoculum

The NPs were homogenized and dissolved in sterile LB (Luria Bertaini) at a concentration of 16 to 0.5 mg/mL. For the preparation of the inoculum, test strains, i.e., gram negative (Escherchia coli ATCC35218) and gram positive (Staphylococcus aureus ATCC29213) were grown in LB overnight at 37  °C. The turbidity of the culture broth was adjusted to 106 CFUs/mL using phosphate saline buffer (PBS).

2.3.2. Minimal Inhibitory Concentration (MIC)

The MIC of the products was tested in the concentration ranging from 16 to 0.5 mg/mL, using the broth dilution method. The freshly adjusted bacterial inoculum was added to the prepared NP solution at a cell density of 2.5 × 105 CFU mL−1 and further incubated at 35 ± 2 °C for 24 h with aeration. Untreated bacteria were included in the experiment as the negative control. The MIC was recorded as the lowest concentration of a drug, which visually inhibits 99% of bacterial growth [25].

2.3.3. Minimal Bactericidal Concentration (MBC)

In continuation to the MIC evaluation of the NPs, an aliquot of incubated suspension with no apparent bacterial growth was plated on freshly prepared Mueller Hinton Agar (MHA) plates and further subjected to incubation at 35 ± 2 °C for 24 h. The MBC was recorded as the minimum concentration of a drug that killed 100% or having less than three CFU bacterial cells on the MHA plates [25].

2.3.4. Effects of Mn0.5Zn0.5SmxEuxFe1.8−2xO4 (0.01 ≤ x ≤ 0.05) NPs on the Morphology of Bacteria

The effects of Mn0.5Zn0.5SmxEuxFe1.8−2xO4 (0.01 ≤ x ≤ 0.05) NPs on the morphology of E. coli and S. aureus cells were performed by SEM analysis as previously reported by Rehman et al. 2019 [25]. Precisely, ∼106 CFU/mL of freshly grown bacterial cells treated with NPs (at the concentration obtained as MIC) were incubated with agitation at 37 °C overnight. The untreated bacteria were included in the experiment as a negative control. After the incubation period, cells were harvested by centrifugation at 12,000 rpm for 10 min. The cell pellets were washed using PBS and subsequently fixed with 2.5% glutaraldehyde for primary fixation, which was followed by secondary fixation, i.e., 1% osmium tetroxide. The fixed cells were washed and dehydrated by varying concentrations of a series of ethanol. Later, the cells were placed on the aluminum stubs, followed by drying in a desecrator, and finally coated with gold. Samples were photocaptured and analyzed at an accelerating voltage of 20 kV by SEM.

3. Results and Discussion

3.1. Structural Analysis and Morphological Study

XRD powder patterns of Mn0.5Zn0.5EuxSmxFe1.5−2xO4 (0.01 ≤ x ≤ 0.05) NPs are offered in Figure 1. It is clear that all peaks belonged to a single phase of Mn-Zn spinel ferrite and no other peaks for the extra phase could be observed. This is evidence that the substituted ions were merged successfully into the spinel lattice. The lattice parameters and crystallite size were estimated by full proof refinement [26,27,28]. The lattice parameter “a” was 8.463, 8.434, 8.428, 8.413, and 8.408, respectively. It is obvious that the lattice parameters decreased when the ratio of Sm and Eu ions increased because of the substitutions of some Fe ions by larger ionic radii ions. The average of the crystallite sizes is in the range 7–12 nm. Figure 2 presents the SEM images of Mn0.5Zn0.5EuxSmxFe1.5−2xO4 (x = 0.01, 0.03, and 0.05). All samples exhibited an agglomerated spherical particle. EDX was used to approve the stoichiometric composition spinel ferrite. The TEM of Mn0.5Zn0.5EuxSmxFe1.5−2xO4 (x = 0.03 and 0.05) spinel ferrites displayed a spherical particle, as seen in Figure 3. It is well known that the complex 3d-metal oxides easily allow oxygen excess and/or deficit. Oxygen nonstoichiometry greatly affects the magnetic and magnetoelectric properties of complex oxides. Oxygen nonsctoichiometry changes the oxidation degree of 3d-metalls and magnetic parameters, such as the total magnetic moment and Curie point. The intensity of the exchange interactions decreases with the oxygen vacancy concentration increase. Exchange near the oxygen vacancies is negative according to Goodenough–Kanamori empirical rules [29,30].

3.2. Anti-Proliferative Activities

3.2.1. Cell Proliferation Testing by MTT Assay

Antiproliferative activities of Mn0.5Zn0.5SmxEuxFe1.8−2xO4 (0.01 ≤ x ≤ 0.05) NPs on cancerous cells were done by the MTT assay. After 48 h of treatment, the cytotoxic effects of Mn0.5Zn0.5SmxEuxFe1.8−2xO4 (0.01 ≤ x ≤ 0.05) NPs were observed and we found that Mn0.5Zn0.5SmxEuxFe1.8−2xO4 (0.01 ≤ x ≤ 0.05) NPs showed inhibitory action on HCT-116 cancerous cells. The inhibitory concentration (IC50) values of different compounds were calculated as depicted in Table 1. We also examined the effects of NPs on normal cells (HEK-293) to check whether they produced any cytotoxic effects. We found that NPs did not produce any significant cytotoxic effects on HEK-293 cells after 48 h of treatment.

3.2.2. Nuclear Disintegration by Mn0.5Zn0.5SmxEuxFe1.8−2xO4 (0.01 ≤ x ≤ 0.05) NPs Treatment

The cancer cell nuclear morphology was evaluated by confocal scanning microscopy, which revealed that treatment of NPs showed strong inhibitory action on HCT-116 cells (Figure 4B,C) as compared to control group cells (Figure 4A).
There are several reports where magnetic nanoparticles have shown potential applications in drug delivery and other diagnostic assays [31,32,33,34]. These results suggest that NPs selectively targeted both colon and breast cancerous cells and do not cause any harm to normal and healthy cells. There are reports of involvement of nanoparticles in cancer cell death where nuclear fragmentation and nuclear disintegration were prominent features [35,36,37,38,39,40]. We recommend that Mn0.5Zn0.5SmxEuxFe1.8−2xO4 (0.01 ≤ x ≤ 0.05) NPs possess a selective targeting capability to cancerous cells and could be a potential candidate for cancer treatments.

3.3. Antibacterial Study

3.3.1. Antibacterial Activity (MIC/MBC)

The antibacterial activity of Mn0.5Zn0.5SmxEuxFe1.8−2xO4 (0.01 ≤ x ≤ 0.05) NPs was evaluated by determining the MIC/MBC values. The nanoparticles were tested at the concentration ranging from of 16 to 0.5 mg/mL. For E. coli, the MIC/MBC values obtained were in the range of 8/16, 8/16, 4/8, 2/4, and 2/4 mg/mL for x = 0.01, 0.02, 0.03, 0.04, and 0.05, respectively (Figure 5A). The MIC/MBC values for S. aureus, were also found in the range of 8/16, 8/16, 8/16, 4/8, and 4/8 for x = 0.01, 0.02, 0.03, 0.04, and 0.05 mg/mL, respectively (Figure 5B). The activity of the broth culture was determined as the effectiveness of the content of element Fe (x = n) in the test material. The obtained results demonstrated that the effectiveness of the test material showed little improvement with the increasing ratio of the Fe content, i.e., the minimum MIC/ MBC was obtained by Fe x = 0.05 and 0.06. However, an enhanced activity was found against E. coli as compared to S. aureus; this slight difference could be attributed to the varying cell wall composition among these bacterial strains [41]. In some earlier studies, various metal-substituted NPs, like copper, zinc, nickel, and manganese, were recorded as possessing antibacterial activities [42,43], although the antibacterial activity of the current combination of Mn0.5Zn0.5SmxEuxFe1.8−2xO4 (0.01 ≤ x ≤ 0.05) NPs is the first of its kind to the best of the author′s knowledge.

3.3.2. Effects of Mn0.5Zn0.5SmxEuxFe1.8−2xO4 (0.01 ≤ x ≤ 0.05) NPs on the Morphology of Bacteria

The morphological alteration in E coli and S. aureus cells caused by Mn0.5Zn0.5SmxEuxFe1.8−2xO4 (0.01 ≤ x ≤ 0.05) NPs was further studied by SEM. The untreated (control) cells of both organisms were normal in shape, and intact with a regular and smooth cell surface (Figure 6I). However, cells treated with Mn0.5Zn0.5SmxEuxFe1.8−2xO4 (x ≤ 0.05) NPs were not found intact, i.e., the cells started appearing abnormal in shape with irregularities at the cell surfaces (Figure 6(Ib–If)). During the examination, untreated cells had no obvious visible damage, but the treated cells were observed as moderately damaged to severely damaged, with the increasing ratio of Fe(x=n), i.e., the maximum damage was caused by x = 0.04 and x = 0.05. Furthermore, it was observed that the effect of Mn0.5Zn0.5SmxEuxFe1.8−2xO4 (x ≤ 0.05) NPs on both gram positive and gram negative were somehow similar, although a slightly enhanced activity was observed against E. coli (Figure 6I,II). This difference in activity can be attributed to the varying cell wall composition between the two organisms, which in turn may play an important role in the attachment of Mn0.5Zn0.5SmxEuxFe1.8−2xO4 (x ≤ 0.05) NPs to the bacterial cell surface, and is therefore essential in obtaining enhanced antibacterial activity [44].

4. Conclusions

In the present study, we synthesized five different derivatives of Mn0.5Zn0.5SmxEuxFe1.8−2xO4 (0.01 ≤ x ≤ 0.05) NPs hydrothermally. The structure and surface morphology of Mn0.5Zn0.5SmEuFe1.8−2xO4 spinel hydrothermal NPs were characterized by the XRD, SEM, TEM, and EDX methods, respectively. We examined the impact of Mn0.5Zn0.5SmxEuxFe1.8−2xO4 (0.01 ≤ x ≤ 0.05) NPs on both normal (HEK-293) and cancerous (HCT-116) cells. We found that after 48 h of treatment, Mn0.5Zn0.5SmxEuxFe1.8−2xO4 (0.01 ≤ x ≤ 0.05) NPs showed a significant decline in the cancer cell population. The IC50 value of Mn0.5Zn0.5SmxEuxFe1.8−2xO4 (0.01 ≤ x ≤ 0.05) NPs ranged between 0.75 to 2.25 µg/mL. When tested on normal and healthy cells (HEK-293), we found that the treatment of Mn0.5Zn0.5SmxEuxFe1.8−2xO4 (0.01 ≤ x ≤ 0.05) NPs did not produce any effects on normal cells, which suggests that Mn0.5Zn0.5SmxEuxFe1.8−2xO4 (0.01 ≤ x ≤ 0.05) NPs selectively targeted cancerous cells. The anti-bacterial properties of Mn0.5Zn0.5SmxEuxFe1.8−2xO4 (0.01 ≤ x ≤ 0.05) NPs were also evaluated by MIC and MBC assays. We conclude that Mn0.5Zn0.5SmxEuxFe1.8−2xO4 (0.01 ≤ x ≤ 0.05) NPs produced via the hydrothermal route possess potential anti-cancer and anti-bacterial abilities.

Author Contributions

All authors equally contributed to this study.

Acknowledgments

Authors thank to Institute for Research and Medical Consultations (IRMC), Imam Abdulrahman Bin Faisal University.

Conflicts of Interest

The authors declare no conflicts of interest.

References

  1. Makovec, D.; Kodre, A.; Arcon, I.; Drofenik, M. Structure of manganese zinc ferrite spinel nanoparticles prepared with co-precipitation in reversed microemulsions. J. Nanopart. Res. 2009, 11, 1145–1158. [Google Scholar] [CrossRef]
  2. Manikandan, A.; Vijaya, J.J.; Kennedy, L.J.; Bououdina, M. Microwave combustion synthesis, structural, optical and magnetic properties of Zn1-xSrxFe2O4 nanoparticles. Ceram. Int. 2013, 39, 5909–5917. [Google Scholar] [CrossRef]
  3. Cao, X.; Liu, G.; Wang, Y.; Li, J.; Hong, R. Preparation of octahedral shaped Mn0.8Zn0.2Fe2O4 ferrites via co-precipitation. J. Alloy. Compd. 2010, 497, 10–13. [Google Scholar] [CrossRef]
  4. Nongjai, R.; Khan, S.; Asokan, K.; Ahmed, H.; Khan, I. Magnetic and electrical properties of in doped cobalt ferrite nanoparticles. J. Appl. Phys. 2012, 112, 084321. [Google Scholar] [CrossRef]
  5. Manikandan, A.; Sridhar, R.; Antony, S.A.; Meganathan, C.; Ramakrishna, S. Effects of Mn2+ doping on structural, morphological, optical and catalytic properties of magnetic CoFe2O4 nanoparticles prepared by urea-assisted auto combustion method. Ceram. Int. 2014. [Google Scholar] [CrossRef]
  6. Trukhanov, A.V.; Kostishyn, V.G.; Panina, L.V.; Jabarov, S.H.; Korovushkin, V.V.; Trukhanov, S.V.; Trukhanova, E.L. Magnetic properties and Mössbauer study of gallium doped M-type barium hexaferrites. Ceram. Int. 2017, 43, 12822–12827. [Google Scholar] [CrossRef]
  7. Gupta, S.; Deshpande, S.K.; Sathe, V.G.; Siruguri, V. Effect of scandium substitution on magnetic and transport properties of the M-type barium hexaferrites. J. Alloy. Compd. 2020, 815, 152467. [Google Scholar] [CrossRef]
  8. Liu, P.; Yao, Z.; Zhou, J. Fabrication and microwave absorption of reduced graphene oxide/Ni0.4Zn0.4Co0.2Fe2O4 nanocomposites. Ceram. Int. 2016, 42, 9241–9249. [Google Scholar] [CrossRef]
  9. Trukhanov, A.V.; Trukhanov, S.V.; Kostishyn, V.G.; Panina, L.V.; Korovushkin, V.V.; Turchenko, V.A.; Vinnik, D.A.; Yakovenko, E.S.; Zagorodnii, V.V.; Launetz, V.L.; et al. Correlation of the atomic structure, magnetic properties and microwave characteristics in substituted hexagonal ferrites. J. Magn. Magn. Mater. 2018, 462, 127–135. [Google Scholar] [CrossRef]
  10. Anjum, S.; Seher, A.; Mustafa, Z. Effect of La3+ ions substituted M-type barium hexa-ferrite on magnetic, optical, and dielectric properties. Appl. Phys. A 2019, 125, 664. [Google Scholar] [CrossRef]
  11. Li, J.J.; Yuan, H.M.; Li, G.D.; Liu, Y.J.; Leng, J.S. Cation distribution dependence of magnetic properties of sol-gel prepared MnFe2O4 spinel ferrite nanoparticles. J. Magn. Magn. Mater. 2010, 322, 3396–3400. [Google Scholar] [CrossRef]
  12. Yáñez-Vilar, S.; Sánchez-Andújar, M.; Gómez-Aguirre, C.; Mira, J.; Señarís-Rodríguez, M.A.; Castro-García, S. A simple solvothermal synthesis of MFe2O4 (M=Mn, Co and Ni) nanoparticles. J. Solid State Chem. 2009, 182, 2685–2690. [Google Scholar] [CrossRef]
  13. Ansari, M.M.N.; Khan, S. Structural, electrical and optical properties of sol-gel synthesized cobalt substituted MnFe2O4 nanoparticles. Physica B 2017, 520, 21–27. [Google Scholar] [CrossRef]
  14. Shokrollahi, H.; Janghorban, K. Influence of additives on the magnetic properties, microstructure and densification of Mn–Zn soft ferrites. Mater. Sci. Eng. B 2007, 141, 91–107. [Google Scholar] [CrossRef]
  15. Shokrollahi, H. Magnetic properties and densification of Manganese–Zinc soft ferrites (Mn1-xZnxFe2O4) doped with low melting point oxides. J. Magn. Magn. Mater. 2008, 320, 463–474. [Google Scholar] [CrossRef]
  16. Shen, X.; Xiang, J.; Song, F.; Liu, M. Characterization and magnetic properties of electrospun Co1-xZnxFe2O4 nanofibers. Appl. Phys. A Mater. Sci. Process. 2010, 99, 189–195. [Google Scholar] [CrossRef]
  17. El Bahraoui, T.; Taibi, M.; El-Nagga, A.M.; Slimani Tlemçani, T.; Albassam, A.A.; Abd-Lefdil, M.; Kityk, I.V.; AlZayed, N.S.; Fedorchuk, A.O. Multiferroic Eu doped BiFeO3 microparticle polymer composites as materials for laser induced gratings. Journal Materiasl Science: Materials in Electronics. J. Mater. Sci. Mater. Electron. 2015, 26, 9949–9954. [Google Scholar] [CrossRef]
  18. Zhou, Z.; Sun, N.X. Multiferroic Nanostructures, Composite Magnetoelectrics Materials, Structures, and Applications Woodhead Publishing Series in Electronic and Optical Materials; Elsevier: Amsterdam, Netherlands, 2015; pp. 71–86. [Google Scholar]
  19. Zipare, K.V.; Bndagar, S.S.; Shahane, G.S. Effect of Dy-substituted on structural and magnetic properties of Mn-Zn ferrites nanoparticles. J. Rare Earths. 2018. [Google Scholar] [CrossRef]
  20. Murthy, S.K. Nanoparticles in modern medicine: State of the art and future challenges. Int. J. Nanomed. 2007, 2, 129–141. [Google Scholar]
  21. Halevas, E.G.; Pantazaki, A.A. Copper Nanoparticles as Therapeutic Anticancer Agnents. Nanomed. Nanotechnol. J. 2018, 2, 119. [Google Scholar]
  22. Khan, S.; Ansari, A.; Khan, A.; Abdulla MObeed, O.; Ahmed, R. Invitro evaluation of anticancer and biological activities of synthesized manganese oxide nanoparticles. Med. Chem. Commun. 2016, 7, 1647. [Google Scholar] [CrossRef]
  23. National Nanotechnology Initiative (NNI): Nanotechnology Benefits. 2014. Available online: https://0-pubs-acs-org.brum.beds.ac.uk/doi/abs/10.1021/es0515708 (accessed on 28 March 2014).
  24. Khan, I.; Saeed, K.; Khan, I. Nanoparticles: Properties, applications and toxicities. J. Arabjc. 2017. [Google Scholar] [CrossRef]
  25. Rehman, S.; Asiri, S.M.; Khan, F.A.; Jermy, B.R.; Khan, H.; Akhtar, S.; Jindan, R.A.; Khan, K.M.; Qurashi, A. Biocompatible Tin Oxide Nanoparticles: Synthesis, Antibacterial, Anticandidal and Cytotoxic Activities. Chem. Sel. 2019, 4, 4013–4017. [Google Scholar] [CrossRef]
  26. Almessiere, M.A.; Slimani, Y.; Korkmaz, A.D.; Guner, S.; Sertkol, M.; Shirsath, S.E.; Baykal, A. Structural, optical and magnetic properties of Tm3+ substituted cobalt spinel ferrites synthesized via sonochemical approach. Ultrason. Sonochem. 2019, 54, 1–10. [Google Scholar] [CrossRef] [PubMed]
  27. Slimani, Y.; Almessiere, M.A.; Sertkol, M.; Shirsath, S.E.; Baykal, A.; Nawaz, M.; Akhtar, S.; Ozcelik, B.; Ercan, I. Structural, magnetic, optical properties and cation distribution of nanosized Ni0.3Cu0.3Zn0.4TmxFe2-xO4 (0.0 ≤ x ≤ 0.10) spinel ferrites synthesized by ultrasound irradiation. Ultrason. Sonochem. 2019. [Google Scholar] [CrossRef] [PubMed]
  28. Almessiere, M.A.; Slimani, Y.; Korkmaz, A.D.; Taskhandi, N.; Sertkol, M.; Baykal, A.; Shirsath, S.E.; Ercan, İ.; Ozçelik, B. Sonochemical synthesis of Eu3+ substituted CoFe2O4 nanoparticles and their structural, optical and magnetic properties. Ultrason. Sonochem. 2019, 58, 104621. [Google Scholar] [CrossRef] [PubMed]
  29. Trukhanov, S.V.; Troyanchuk, I.O.; Trukhanov, A.V.; Fita, I.M.; Vasil’ev, A.N.; Maignan, A.; Szymczak, H. Magnetic properties of La0.70Sr0.30MnO2.85 anion-deficient manganite under hydrostatic pressure. JETP Lett. 2006, 83, 33–36. [Google Scholar] [CrossRef]
  30. Shanga, C.; Xia, Z.C.; Zhai, X.Z.; Liu, D.W.; Wang, Y.Q. Percolation like transitions in phase separated manganites La0.5Ca0.5Mn1-xAlxO3-δ. Ceram. Int. 2019, 45, 18632–18639. [Google Scholar] [CrossRef]
  31. Shagholani, H.; Ghoreishi, S.M. Improvement of interaction between PVA and chitosan via magnetite nanoparticles for drug delivery application. Int. J. Biol. Macromol. 2015, 78, 130–136. [Google Scholar] [CrossRef]
  32. Elvia, L.; Joelda, D.; Polyana, T.; Araújo, S.; Sheyla, M.C.M.; Aliaga, K.R.H.G.; Ribeiro, S.M.; Costa, A.C.F.M. Effect of the surface treatment on the structural, morphological, magnetic and biological properties of MFe2O4 iron spinels (M = Cu, Ni, Co, Mn and Fe). Appl. Surf. Sci. 2018, 455, 635–645. [Google Scholar]
  33. Leng, J.; Li, J.; Ren, J.; Deng, L.; Lin, C. Star–block copolymer micellar nanocomposites with Mn, Zn-doped nano-ferrite as superparamagnetic MRI contrast agent for tumor imaging. Mater. Lett. 2015, 152, 185–188. [Google Scholar] [CrossRef]
  34. Aygar, G.; Kaya, M.; Özkan, N.; Kocabiyik, S.; Volkan, M. Preparation of silica coated cobalt ferrite magnetic nanoparticles for the purification of histidine-tagged proteins. J. Phys. Chem. Solids 2015, 87, 64–71. [Google Scholar] [CrossRef]
  35. Shiva, I.; Zhohreh, S.; Mohammad, A.S.; Shahriar, M. Induction of growth arrest in colorectal cancer cells by cold plasma and gold nanoparticles. Arch. Med. Sci. 2015, 11, 1286–1295. [Google Scholar]
  36. Mytych, J.; Lewinska, A.; Zebrowski, J.; Wnuk, M. Gold nanoparticles promote oxidant-mediated activation of NF-κB and 53BP1 recruitment-based adaptive response in human astrocytes. Biomed. Res. Int. 2015, 2015, 304575. [Google Scholar] [CrossRef] [PubMed]
  37. Baharara, J.; Ramezani, T.; Divsalar, A.; Mousavi, M.; Seyedarabi, A. Induction of Apoptosis by Green Synthesized Gold Nanoparticles Through Activation of Caspase-3 and 9 in Human Cervical Cancer Cells. Avicenna J. Med. Biotechnol. 2016, 8, 75–83. [Google Scholar] [PubMed]
  38. Lin-Wei, W.; Ai-Ping, Q.; Wen-Lou, L.; Jia-Mei, C.; Yuan, J.P.; Wu, H.; Li, Y.; Liu, J. Quantum dots-based double imaging combined with organic dye imaging to establish an automatic computerized method for cancer Ki67 measurement. Sci. Rep. 2016, 6, 20564. [Google Scholar]
  39. Khan, F.A.; Akhtar, S.; Almohazey, D.; Alomari, M.; Almofty, S.A. Extracts of Clove (Syzygium aromaticum) Potentiate FMSP-Nanoparticles Induced Cell Death in MCF-7. Cells Int. J Biomater. 2018, 84, 8479439. [Google Scholar] [CrossRef] [Green Version]
  40. Khan, F.A.; Akhtar, S.; Almohazey, D.; Alomari, M.; Almofty, S.A.; Eliassari, A. Fluorescent magnetic submicronic polymer (FMSP) nanoparticles induce cell death in human colorectal carcinoma cells. Artif. Cells Nanomed Biotechnol. 2018, 46, S247–S253. [Google Scholar] [CrossRef]
  41. Rehman, S.; Jermy, B.R.; Akhtar, S.; Borgio, J.F.; Abdul Azeez, S.; Ravinayagam, V.; Al Jindan, R.; Alsalem, Z.H.; Buhameid, A.; Gani, A. Isolation and characterization of a novel thermophile; Bacillus haynesii, applied for the green synthesis of ZnO nanoparticles. Artif. Cellsnanomed. Biotechnol. 2019, 4, 2072–2082. [Google Scholar] [CrossRef] [Green Version]
  42. Elsharif, A.M.; Youssef, T.E.; Al-Jameel, S.S.; Mohamed, H.H.; Ansari, M.A.; Rehman, S.; Akhtar, S. Synthesis of an Activatable Tetra-Substituted Nickel Phthalocyanines-4 (3H)-quinazolinone Conjugate and Its Antibacterial Activity. Adv. Pharmacol. Sci. 2019. [Google Scholar] [CrossRef] [Green Version]
  43. Ansari, M.A.; Baykal, A.; Asiri, S.; Rehman, S. Synthesis and characterization of antibacterial activity of spinel chromium-substituted copper ferrite nanoparticles for biomedical application. J. Inorg. Organomet. Polym. Materials. 2018, 28, 2316–2327. [Google Scholar] [CrossRef]
  44. Bruschi, M.L.; de Toledo, L.D. Pharmaceutical Applications of Iron-Oxide Magnetic Nanoparticles. Magnetochemistry 2019, 5, 50. [Google Scholar] [CrossRef] [Green Version]
Nanomaterials 09 01635 g001 550
Figure 1. XRD powder patterns of Mn0.5Zn0.5EuxSmxFe1.5−2xO4 (0.01 ≤ x ≤ 0.05) NPs.
Figure 1. XRD powder patterns of Mn0.5Zn0.5EuxSmxFe1.5−2xO4 (0.01 ≤ x ≤ 0.05) NPs.
Nanomaterials 09 01635 g001
Nanomaterials 09 01635 g002 550
Figure 2. SEM of Mn0.5Zn0.5EuxSmxFe1.5−2xO4 for x = 0.01, 0.03, and 0.05 and EDX x = 0.03 NPs.
Figure 2. SEM of Mn0.5Zn0.5EuxSmxFe1.5−2xO4 for x = 0.01, 0.03, and 0.05 and EDX x = 0.03 NPs.
Nanomaterials 09 01635 g002
Nanomaterials 09 01635 g003 550
Figure 3. TEM of Mn0.5Zn0.5EuxSmxFe1.5−2xO4 (x = 0.03 and 0.05) NPs.
Figure 3. TEM of Mn0.5Zn0.5EuxSmxFe1.5−2xO4 (x = 0.03 and 0.05) NPs.
Nanomaterials 09 01635 g003
Nanomaterials 09 01635 g004 550
Figure 4. Cancer cells stained with 4′,6-diamidino-2-phenylindole (DAPI). HCT-116 cells treated with Mn0.5Zn0.5SmxEuxFe1.8−2xO4 (0.01 ≤ x ≤ 0.05) NPs for 48 h. (A) is control without treatment, (B) treated with Mn0.5Zn0.5SmxEuxFe1.8−2xO4 NPs for x = 0.01 concentration (2.35 µg/mL), and (C) treated with Mn0.5Zn0.5SmxEuxFe1.8−2xO4 NPs for x = 0.05 concentration (2.33 µg/mL). Arrows in B and C indicate the loss of nuclear staining. 200× magnifications.
Figure 4. Cancer cells stained with 4′,6-diamidino-2-phenylindole (DAPI). HCT-116 cells treated with Mn0.5Zn0.5SmxEuxFe1.8−2xO4 (0.01 ≤ x ≤ 0.05) NPs for 48 h. (A) is control without treatment, (B) treated with Mn0.5Zn0.5SmxEuxFe1.8−2xO4 NPs for x = 0.01 concentration (2.35 µg/mL), and (C) treated with Mn0.5Zn0.5SmxEuxFe1.8−2xO4 NPs for x = 0.05 concentration (2.33 µg/mL). Arrows in B and C indicate the loss of nuclear staining. 200× magnifications.
Nanomaterials 09 01635 g004
Nanomaterials 09 01635 g005 550
Figure 5. MIC/MBC of Mn0.5Zn0.5SmxEuxFe1.8−2xO4 (0.01 ≤ x ≤ 0.05) against (A) E. coli (B) S. aureus.
Figure 5. MIC/MBC of Mn0.5Zn0.5SmxEuxFe1.8−2xO4 (0.01 ≤ x ≤ 0.05) against (A) E. coli (B) S. aureus.
Nanomaterials 09 01635 g005
Nanomaterials 09 01635 g006 550
Figure 6. SEM micrographs of Mn0.5Zn0.5SmxEuxFe1.8−2xO4 (0.01 ≤ x ≤ 0.05) NPs treated (I) E. coli, (II) S. aureus. (a) untreated cells (control), (b) x = 0.01, (c) 0.02, (d) 0.03, (e) 0.04, and (f) 0.05.
Figure 6. SEM micrographs of Mn0.5Zn0.5SmxEuxFe1.8−2xO4 (0.01 ≤ x ≤ 0.05) NPs treated (I) E. coli, (II) S. aureus. (a) untreated cells (control), (b) x = 0.01, (c) 0.02, (d) 0.03, (e) 0.04, and (f) 0.05.
Nanomaterials 09 01635 g006
Table
Table 1. Effect of Mn0.5Zn0.5SmEuFe1.8−2xO4 (0.01 ≤ x ≤ 0.05) NPs on cancerous cells human colon carcinoma cells (HCT-116) and normal cells human embryonic kidney cells (HEK-293).
Table 1. Effect of Mn0.5Zn0.5SmEuFe1.8−2xO4 (0.01 ≤ x ≤ 0.05) NPs on cancerous cells human colon carcinoma cells (HCT-116) and normal cells human embryonic kidney cells (HEK-293).
xIC50 (HCT-116) (µg/mL)IC50 (HEK-293)
0.010.75 µg/mLNo inhibition
0.020.85 µg/mLNo inhibition
0.032.25 µg/mLNo inhibition
0.040.88 µg/mLNo inhibition
0.050.79 µg/mLNo inhibition
Note: IC50 Value [µg/mL] = Inhibitory concentration (IC).

Share and Cite

MDPI and ACS Style

Akhtar, S.; Rehman, S.; Almessiere, M.A.; Khan, F.A.; Slimani, Y.; Baykal, A. Synthesis of Mn0.5Zn0.5SmxEuxFe1.8−2xO4 Nanoparticles via the Hydrothermal Approach Induced Anti-Cancer and Anti-Bacterial Activities. Nanomaterials 2019, 9, 1635. https://0-doi-org.brum.beds.ac.uk/10.3390/nano9111635

AMA Style

Akhtar S, Rehman S, Almessiere MA, Khan FA, Slimani Y, Baykal A. Synthesis of Mn0.5Zn0.5SmxEuxFe1.8−2xO4 Nanoparticles via the Hydrothermal Approach Induced Anti-Cancer and Anti-Bacterial Activities. Nanomaterials. 2019; 9(11):1635. https://0-doi-org.brum.beds.ac.uk/10.3390/nano9111635

Chicago/Turabian Style

Akhtar, Sultan, Suriya Rehman, Munirah A. Almessiere, Firdos Alam Khan, Yassine Slimani, and Abdulhadi Baykal. 2019. "Synthesis of Mn0.5Zn0.5SmxEuxFe1.8−2xO4 Nanoparticles via the Hydrothermal Approach Induced Anti-Cancer and Anti-Bacterial Activities" Nanomaterials 9, no. 11: 1635. https://0-doi-org.brum.beds.ac.uk/10.3390/nano9111635

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop