Nanoscaled Mechanical Properties of Cement Composites Reinforced with Carbon Nanofibers
Next Article in Special Issue
Insight the Luminescence Properties of AlON: Eu, Mg Phosphor under VUV Excitation
Previous Article in Journal
Fatigue Lifetime of Ceramic Matrix Composites at Intermediate Temperature by Acoustic Emission
Previous Article in Special Issue
AC Electroluminescent Processes in Pr3+-Activated (Ba0.4Ca0.6)TiO3 Diphase Polycrystals
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Materials
Volume 10
Issue 6
10.3390/ma10060657
materials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Warm White Light-Emitting Diodes Based on a Novel Orange Cationic Iridium(III) Complex

by
Huaijun Tang
*,
Guoyun Meng
,
Zeyu Chen
,
Kaimin Wang
,
Qiang Zhou
and
Zhengliang Wang
*
Key Laboratory of Comprehensive Utilization of Mineral Resources in Ethnic Regions, Joint Research Centre for International Cross-border Ethnic Regions Biomass Clean Utilization in Yunnan, School of Chemistry & Environment, Yunnan Minzu University, Kunming 650500, China
*
Authors to whom correspondence should be addressed.
Materials 2017, 10(6), 657; https://0-doi-org.brum.beds.ac.uk/10.3390/ma10060657
Submission received: 19 April 2017 / Revised: 21 May 2017 / Accepted: 8 June 2017 / Published: 16 June 2017
(This article belongs to the Special Issue Luminescent Materials 2017)
Browse Figures
Versions Notes

Abstract

:
A novel orange cationic iridium(III) complex [(TPTA)2Ir(dPPOA)]PF6 (TPTA: 3,4,5-triphenyl-4H-1,2,4-triazole, dPPOA: N,N-diphenyl-4-(5-(pyridin-2-yl)-1,3,4-oxadiazol-2-yl)aniline) was synthesized and used as a phosphor in light-emitting diodes (LEDs). [(TPTA)2Ir(dPPOA)]PF6 has high thermal stability with a decomposition temperature (Td) of 375 °C, and its relative emission intensity at 100 °C is 88.8% of that at 25°C. When only [(TPTA)2Ir(dPPOA)]PF6 was used as a phosphor at 6.0 wt % in silicone and excited by a blue GaN (GaN: gallium nitride) chip (450 nm), an orange LED was obtained. A white LED fabricated by a blue GaN chip (450 nm) and only yellow phosphor Y3Al5O12:Ce3+ (YAG:Ce) (1.0 wt % in silicone) emitted cold white light, its CIE (CIE: Commission International de I’Eclairage) value was (0.32, 0.33), color rendering index (CRI) was 72.2, correlated color temperature (CCT) was 6877 K, and luminous efficiency (ηL) was 128.5 lm∙W−1. Such a cold white LED became a neutral white LED when [(TPTA)2Ir(dPPOA)]PF6 was added at 0.5 wt %; its corresponding CIE value was (0.35, 0.33), CRI was 78.4, CCT was 4896 K, and ηL was 85.2 lm∙W−1. It further became a warm white LED when [(TPTA)2Ir(dPPOA)]PF6 was added at 1.0 wt %; its corresponding CIE value was (0.39, 0.36), CRI was 80.2, CCT was 3473 K, and ηL was 46.1 lm∙W−1. The results show that [(TPTA)2Ir(dPPOA)]PF6 is a promising phosphor candidate for fabricating warm white LEDs.

1. Introduction

Due to high efficiency, long lifetime, and energy-saving and environmentally-friendly properties, white light-emitting diodes (WLEDs) have attracted significant attention and are used as the new generation solid-state light sources in general illumination, full-color displays, liquid crystal display backlights and so on [1,2,3,4]. At present, the commercial WLEDs are mainly obtained by the combination of a blue GaN (GaN: gallium nitride) chip (λmax,em ≈ 450 nm)and a yellow-emitting Y3Al5O12:Ce3+ (YAG:Ce) phosphor. YAG:Ce is a blue-light excitable phosphor with high photoluminescence efficiency and good thermal stability [4,5,6]. However, because the main emission of YAG:Ce is in the greenish yellow region, aforementioned commercial WLEDs have low color rendering index (CRI) and high correlated color temperature (CCT). Due to the absence of a red light component in their spectra, the light emitted from such WLEDs is cold white light [7,8,9,10,11,12,13,14,15,16]. Two approaches have been developed to overcome this drawback. In the first approach, a red light component was emitted via some ions (such as Eu3+, Pr3+) being doped in YAG:Ce [7,8,9]; however, the yellow emission was obviously decreased although slightly red light was obtained. In the other approach, some red phosphors were complementally used in aforementioned WLEDs [5,9,10]. Relatively better performances (including CRI, CCT and efficiency etc.) can be obtained via the second approach, because the red phosphors are mainly excited by the blue GaN chip and the emission of YAG:Ce is seldom affected. Hence, the development of new efficient red phosphors for warm WLEDs based on blue chips is very important and urgently needed. Up to now, besides many inorganic phosphors (such as CaSiAlN3:Eu2+ [10], InP/GaP/ZnS quantum dots [11], Mn4+ activated fluorides [5,12,13], and so on), many organic luminescent materials (such as organic metal complexes [14,15,16,17,18], polymers [19] and small-molecule fluorescent dyes [20,21], and so on) have also been used as red luminescent materials in WLEDs.
Up to now, many types of organic metal complexes (e.g., cationic ruthenium(II) complexes, cationic copper(I) complexes, europium(III) complexes, platinum(II) complexes, zinc(II) complexes, etc.) have been used in various luminescent fields. By comparison, as efficient luminescent materials, cationic iridium(III) complexes have some excellent photochemical and photophysical properties, such as high efficiency of 100% theoretical quantum efficiency, good color tenability via various ligands, short triplet state lifetimes, high thermal and photic stability and so on [22,23]. In the past decade and even earlier, cationic iridium(III) complexes have been widely applied in light-emitting electrochemical cells (LECs) [22,23,24], organic light-emitting diodes (OLEDs) [24,25,26], chemical sensors [27], and bioimaging [28] etc.
Recently, cationic iridium(III) complexes have also been used as luminescence conversion materials (i.e., phosphors) in inorganic LEDs [15,18,29,30], and exhibited good performances. In 2013, C.-Y. Sun et al. [29] achieved efficient white-light emission by encapsulating the cation of a yellow-emitting iridium complex [Ir(ppy)2(bpy)]PF6 (ppy: 2-phenylpyridine; bpy: 2,2′-bipyridine) at different ratios in theblue-emitting anionic Cd-based metal–organic frameworks (MOF) cavity. When an optimal concentration (3.5 wt %) of [Ir(ppy)2(bpy)]+ was encapsulated into the host framework and under the excitation of 370 nm ultraviolet light, high-quality white light was obtained with Commission International de I’Eclairage (CIE) coordinates of (0.31, 0.33), a CRI of ca. 80, a CCT of ca. 5900 K, and a quite high quantum yield up to 20.4%. Then high-quality WLEDs were fabricated by using this composite material and ultraviolet chips. In 2016, L. Niklaus et al. [18] fabricated white hybrid light-emitting diodes (WHLEDs) using luminescent rubber-like materials based on a wide palette of compounds including small-molecules, quantum dots, polymers, and coordination complexes. The use of rubbers based on the complex [Ir(ppy)2(tb-bpy)]PF6 (tb-bpy: 4,4′-ditert-butyl-22,2′-bipyridine) outperformed the others in terms of color quality (CRI > 80) and luminous efficiency (>100 lm·W−1) with unprecedented stabilities of more than 1000 h (extrapolated 4000 h) under continuous operation conditions. In one reported work of our research group in 2015 [30], WLEDs fabricated by using cationic iridium(III) complexes [Ir(ppy)2(phen)]PF6 or [Ir(ppy)2(phen)]TiF6 (phen: 1,10-phenanthroline) as luminescence conversion materials showed higher CRI and lower CCT than those of the widely used YAG:Ce. In another reported work of our research group also in 2015 [15], a novel red-emitting cationic iridium(III) complex using 2-(9-(2-ethylhexyl)-9H-carbazol-3-yl)benzo[d]thiazole (CBT) as the main ligand and N,N-diphenyl-4-(5-(pyridin-2-yl)-1,3,4-oxadiazol-2-yl)aniline (dPPOA) as the auxiliary ligand was used as a red phosphor in YAG:Ce based WLEDs with 465 nm-emitting GaN blue chips. The WLED only using YAG:Ce as a phosphor at 1.0 wt % emitted cold white; such WLED can become warm WLEDs when the cationic iridium(III) complex was added over 1.0 wt %.
As a consecutive and upgraded research by us, in this work, another novel orange cationic iridium(III) complex also using dPPOA as auxiliary ligand, but using 3,4,5-triphenyl-4H-1,2,4-triazole (TPTA) instead of CBT as the main ligand was synthesized and also used in YAG:Ce-based WLEDs to obtain warm white light. Donor–acceptor bipolar units have been widely used in organic photoresponse materials for extending absorption range and increasing absorption rate [25,31,32]. Many organic cationic iridium(III) complexes can easily be excited by ultraviolet light, but cannot be effectively excited by blue light (such as the blue light of a GaN chip). In order to make this new complex effectively excited by the blue light of a GaN chip, adonor–acceptor bipolar unit of triphenylamine–oxadiazole was contained in the auxiliary ligand dPPOA; theoretically, the electron-donating or/and electron-withdrawing functional groups on the main ligand will further improve the effect of this donor–acceptor bipolar unit [31,32]. In our previous work [15], CBT containing an electron-donating carbazole group had been successfully used in the cationic iridium(III) complex [Ir(CBT)2(dPPOA)]PF6 for warm WLEDs. This work tried the main ligand TPTA containing an electron-withdrawing 1,2,4-triazole group. In order to achieve higher performance in this new work, besides the replacement of the main ligand in the complex as a new attempt, 450 nm-emitting GaN blue chips with much higher luminous efficiency were also used to replace the 465 nm-emitting GaN blue chips used in previous work [15]. As expected, the cold white light of YAG:Ce-based WLEDs also gradually became warm white light with the increase of the addition of this new cationic iridium(III) complex; at the same time, such WLEDs exhibited encouraging light-emitting performances.

2. Materials and Methods

2.1. General Information

All chemicals and reagents were purchased from chemical reagent companies and used without further purification unless otherwise stated. 1H NMR spectra were recorded on a Bruker AV400 spectrometer (Bruker, Fällanden, Switzerland) operating at 400 MHz; tetramethylsilane (TMS) was used as internal standard. Mass spectra (MS) were obtained on a Bruker amaZon SL liquid chromatography mass spectrometer (LC-MS, Bruker, Karlsruhe, Germany) with an electrospray ionization (ESI) interface using acetonitrile as matrix solvent. Elemental analysis (EA) was performed on a Vario EL III Elemental Analysis Instrument (Elementar, Hanau, Germany). Ultraviolet-visible (UV-vis, Agilent, Palo Alto, CA, USA) absorption spectra were measured on an Agilent 8453 UV-visible Spectroscopy System. Excitation and emission spectra of samples were documented on a Cary Eclipse FL1011M003 (Varian, Palo Alto, CA, USA) spectrofluorometer; the xenon lamp was used as an excitation source, and the temperature of solid samples was controlled by a temperature controller (REX-C110, Kaituo Compressor Parts Co., Ltd, Dongguan, China). Thermogravimetric (TG) analysis was carried out up to 600 °C in N2 atmosphere with a heating speed of 10.0 °C·min−1 on a NETZSCH STA 449F3 thermogravimetric analyzer (NETZSCH, Selb, Germany). The electroluminescent spectra of LEDs were recorded on a high-accuracy array spectrometer (HSP6000, HongPu Optoelectronics Technology Co., Ltd, Hangzhou, China).

2.2. Synthesis

Thecationic iridium(III) complex [(TPTA)2Ir(dPPOA)]PF6 was synthesized by using 3,4,5-triphenyl-4H-1,2,4-triazole (TPTA) and N,N-diphenyl-4-(5-(pyridin-2-yl)-1,3,4-oxadiazol-2-yl)aniline (dPPOA) as ligands, as shown in Figure 1. TPTA and dPPOA were synthesized according to the reported procedures in references [33] and [15] respectively.
Synthesis of the chloro-bridged dimer (TPTA)2Ir(μ-Cl)2Ir(TPTA)2: A mixture of IrCl3·3H2O (1.06 g, 3.0 mmol) and TPTA (1.81 g, 6.10 mmol) in H2O (10 mL) and 2-methoxyethanol (30 mL) was refluxed in Ar atmosphere for 24 h. After being cooled to room temperature, the resultant yellow precipitate was collected on a filter, washed with water and methanol alternately, and then dried in a vacuum. Yield was 75.0% (1.85 g) yellow solid. This dimer product was directly used for the next step without further purification and characterization.
Synthesis of the cationic iridium(III) complex[(TPTA)2Ir(dPPOA)]PF6: The chloro-bridged dimer (TPTA)2Ir(μ-Cl)2Ir(TPTA)2 (0.62 g, 0.38 mmol) and dPPOA (0.30 g, 0.76 mmol) were added into glycol (30 mL) and then kept at 150 °C in Ar atmosphere with stirring for 16 h. After being cooled to room temperature, 10 mL 1.0 mol·L−1 aqueous solution of NH4PF6 was added with stirring, and much orange flocculent precipitate appeared. The precipitate was filtered, washed with water and dried in a vacuum. The crude product was purified by column chromatography on silica gel, eluting with CH2Cl2/MeCN (volume rate, 10:1). Yield was 86.0% (0.86 g) orange solid. 1H NMR (400 MHz, CDCl3, 25 °C, ppm, being shown in Figure S1 as electronic supplementary materials), δ: 8.50 (d, 1H, 3J = 7.6 Hz, ArH), δ: 8.33–8.63 (m, 1H, ArH), δ: 8.16 (d, 1H, 3J = 5.6 Hz, ArH), δ: 7.97–7.99 (m, 2H, ArH), δ: 7.62–7.69 (m, 7H, ArH), δ: 7.47–7.53 (m, 4H, ArH), δ: 7.31–7.39 (m, 11H, ArH), δ: 7.23–7.27 (m, 3H, ArH), δ: 7.14–7.18 (m, 6H, ArH), δ: 7.04–7.06 (m, 2H, ArH), δ: 6.91–7.00 (m, 2H, ArH), δ: 6.75–6.78 (m, 2H, ArH), δ: 6.71 (t, 1H, 3J = 7.6 Hz, ArH), δ: 6.66 (d, 1H, 3J = 7.2 Hz, ArH), δ: 6.44 (t, 2H, 3J = 7.6 Hz, ArH). MS (m/z, ESI+, being shown in Figure S2 as electronic supplementary materials): calc. for C65H46F6IrN10OP, 1320.3, found, 1175.3 [M–PF6]+. Element analysis calculation for C65H46F6IrN10OP: C, 59.13; H, 3.51; N, 10.61%. Found: C, 58.69; H, 3.67; N, 9.91%.

2.3. Fabrication and Measurements of LEDs

Two kinds of LEDs were fabricated and measured in this work. (i) Only [(TPTA)2Ir(dPPOA)]PF6 was blended and stirred homogeneously in silicone atthe mass ratios of 1.0, 2.0, 3.0, 4.0, 5.0 and 6.0 wt %, and then coated on the surface of 450 nm-emitting GaN chips until the reflective cavities were filled up; (ii) YAG:Ce was blended in silicone at a constant mass ratio of 1.0 wt %, and [(TPTA)2Ir(dPPOA)]PF6 was blended together at different mass ratios of 0.0, 0.5, 1.0 and 1.5 wt %. The silicone containing YAG:Ce and [(TPTA)2Ir(dPPOA)]PF6 was also coated on the surface of 450 nm-emitting GaN chips until the reflective cavities were filled up. In the blending process, an analytical balance with the readability of 0.01 mg was used for weighing, 0.10000–0.12000 g viscous silicone was weighed in a little bottle every time, then the quantities of [(TPTA)2Ir(dPPOA)]PF6 and/or YAG:Ce were calculated and weighed. After [(TPTA)2Ir(dPPOA)]PF6 and/or YAG:Ce were added to the silicone, a drop of CH2Cl2 was also added, then the mixture was stirred by hand with a little stainless steel rod for about one minute until all the ingredients were well combined. The LEDs were dried and solidified at 150 °C for 1 h. The LEDs were all operated at 20 mA forward current and 5 V reverse voltage, with their performances measured by an integrating sphere spectroradiometer system (Everfine PMS-50, Everfine Photo-E-Info Co., Ltd., Hangzhou, China).

3. Results and Discussion

3.1. UV-Vis Absorption Spectra

The normalized UV-vis absorption spectrum of [(TPTA)2Ir(dPPOA)]PF6 in CH2Cl2 solution at 1.0 × 10−5 mol∙L−1 together with the emission spectra of the blue GaN chip and YAG:Ce are shown in Figure 2. The strong absorption band between 230 nm and 380 nm can be ascribed to the spin-allowed 1π–π* transition of the ligands; the maximum absorption wavelength (λabs, max) is 267 nm (ε267nm = 5.4 × 104 L·mol−1·cm−1). The weak absorption band from 380 nm extending to the visible region results from the overlapping absorption of the spin-allowed singlet metal-to-ligand charge-transfer (1MLCT), the spin-forbidden triplet metal-to-ligand charge-transfer (3MLCT) and 3π–π* in the ligands [25,34]. The admixture absorption of 3MLCT and 3π–π* with higher-lying 1MLCT is caused by the strong spin-orbit coupling induced by the heavy iridium atom [35,36]. As shown in Figure 2, there is a large overlap between the absorption spectrum of [(TPTA)2Ir(dPPOA)]PF6 and the emission spectrum of the blue GaN chip (λem, max = 450 nm), which suggests that Förster resonance energy transfer (FRET) is able to take place between them easily and [(TPTA)2Ir(dPPOA)]PF6 can be well excited by the blue GaN chip [37]. The overlap between the absorption spectrum of [(TPTA)2Ir(dPPOA)]PF6 and the emission spectrum of YAG:Ce can almost be ignored, which suggests that the emission of YAG:Ce would be seldom affected by [(TPTA)2Ir(dPPOA)]PF6, and [(TPTA)2Ir(dPPOA)]PF6 is a practicable red luminescent additive for YAG:Ce-based WLEDs.

3.2. Photoluminescent Properties

The photoluminescent properties of [(TPTA)2Ir(dPPOA)]PF6 in solution and blended in silicone were investigated and the results are shown in Figure 3. Both excitation (Ex, λem =600 nm) and emission (Em, λex = 450 nm) spectra of [(TPTA)2Ir(dPPOA)]PF6 in silicone showed obvious red shift in comparison with those of [(TPTA)2Ir(dPPOA)]PF6 in CH2Cl2 solution (λem = 581 nm, λex = 450 nm). The red shift should be caused mainly by the increase of the conjugated system of [(TPTA)2Ir(dPPOA)]PF6 in solid silicone, because the steric hindrance and distortion of the phenyls in ligands TPTA and dPPOA are restrained to a certain degree. At the same time, the conjugated system of [(TPTA)2Ir(dPPOA)]PF6 can also be increased by intermolecular π–π stacking in silicone.
In general, sufficient overlap between the excitation spectra of phosphors and the emission spectra of the LED chips is necessary to realize energy transfer from the LED chips to phosphors efficiently. In this work, the excitation spectra of [(TPTA)2Ir(dPPOA)]PF6 in CH2Cl2 solution and blended in silicone lie 225−500 nm and 225−580 nm respectively, and both cover the emission spectra of the 450 nm-emitting blue GaN chip (as shown in Figure 2), which means that [(TPTA)2Ir(dPPOA)]PF6 can be efficiently excited by the blue GaN chip. In particular, there is a maximum wavelength (448 nm) near 450 nm in the excitation spectra of [(TPTA)2Ir(dPPOA)]PF6 blended in silicone, which suggests that the [(TPTA)2Ir(dPPOA)]PF6 can be efficiently excited by the blue light of the GaN chip. The emission spectra of [(TPTA)2Ir(dPPOA)]PF6 mainly lie from 520 nm to 750 nm with the maximum emission wavelengths of 581 nm (in solution) and 600 nm (in silicone) respectively; obviously, considerable red light component was contained in its emission spectra and [(TPTA)2Ir(dPPOA)]PF6 can be used as a phosphor for fabricating warm WLEDs.

3.3. Thermal Stability and Thermal Quenching Properties

The thermal property of [(TPTA)2Ir(dPPOA)]PF6 was characterized by thermogravimetry (TG) in nitrogen atmosphere at a heating speed of 10.0 °C·min−1, and the resultant TG curve is shown in Figure 4. With temperature increasing, the TG curve begins to dip suddenly after about 375 °C, which means that the thermal decomposition happened and 375 °C can be regarded asits thermal decomposition temperature (Td). Such a high decomposition temperature suggests that [(TPTA)2Ir(dPPOA)]PF6 has a high thermal stability and is enough to meet the requirement of its application in LEDs, since LED devices are fabricated and usually work at a temperature below 150 °C [14].
The thermal-quenching property of [(TPTA)2Ir(dPPOA)]PF6 was alsoinvestigatedand the results are shown in Figure 5 and Figure 6. Figure 5 depicts the temperature-dependent photoluminescent spectra (λex = 450 nm) of [(TPTA)2Ir(dPPOA)]PF6 powders. From 25 °C to 200 °C, the light-emitting color of [(TPTA)2Ir(dPPOA)]PF6 exhibited high thermal stability because the profile, wavelength band and the maximum wavelengths (around 601 nm) of its emission spectra at different temperatures were almost unchanged, with the exceptionof the intensity. The relative emission intensity of [(TPTA)2Ir(dPPOA)]PF6 as a function of temperature is shown in Figure 6. Like most phosphors used in LEDs, the emission intensity of [(TPTA)2Ir(dPPOA)]PF6 also decreases with increasing temperature (i.e., thermal quenching) [4,38,39,40]. The relative emission intensities at different temperaturesare descending: 97.2% (at 50 °C), 93.7% (at 75 °C), 88.8% (at 100 °C), 82.3% (at 125 °C), 76.5% (at 150 °C), 68.9% (at 175 °C), 61.9% (at 200 °C). The thermal quenching of luminescent organic metal complexes is usually caused by the aggravating jiggle and wiggle of atoms, and the rotating and stretching vibration of covalent bonds as the temperature increases. The activation energy (Ea) of the thermal quenching can be described by the Arrhenius equation [38,39,40]:
I = I o 1 + A exp ( − E a k B T )
where I represents the emission intensity at any testing temperature (25–200 °C), Io represents the emission intensity at room temperature (25 °C), A is a constant, kB is a Boltzmann constant, and T is any testing temperature. From the Arrhenius equation, the relationship of ln(Io/I − 1) with 1/T can be obtained; the experimental data are well-fitted and shown in Figure 6 (inset); then, the value of Ea for [(TPTA)2Ir(dPPOA)]PF6 was calculated to be 0.2647 eV from the slope value −(Ea/kB). For phosphors used in LEDs, a high Ea value means low thermal quenching. The emission intensity decay rate and Ea value show that [(TPTA)2Ir(dPPOA)]PF6 is an applicable phosphor for LEDs and its thermal quenching is lower than that of many orange or red phosphors reported in recent years [40,41,42].

3.4. Fabrication and Performance of LEDs

At first, in order to understand the luminescent property of [(TPTA)2Ir(dPPOA)]PF6 itself in LEDs, a series of LEDs fabricated using blue GaN (450 nm) as chips and only [(TPTA)2Ir(dPPOA)]PF6 as a phosphor at different blending concentrations were investigated. The emission spectra of such LEDs at 20 mA forward current are shown in Figure 7 and the performances are listed in Table 1. Except for the emission spectrum of the LED using [(TPTA)2Ir(dPPOA)]PF6 at 6.0 wt %, two emission peaks were contained in the emission spectra of the other LEDs. Obviously, the blue emission peaks on the left with the maximum wavelengths around 450 nm were the emission of the blue GaN chips, which were not completely absorbed by [(TPTA)2Ir(dPPOA)]PF6 at low blending concentrations. The broad emission peaks (550–770 nm) on the right with the maximum wavelengths around 615 nm can be ascribed to the emission of [(TPTA)2Ir(dPPOA)]PF6 because they were primarily consistent with the PL spectra of [(TPTA)2Ir(dPPOA)]PF6. The blending concentrations of [(TPTA)2Ir(dPPOA)]PF6 increased from 1.0 wt % to 6.0 wt %, while the emission peaks of blue GaN chips gradually declined and eventually disappeared at 6.0 wt %. On the other hand, the emission peaks of [(TPTA)2Ir(dPPOA)]PF6 gradually increased; at 6.0 wt %, only orange light of [(TPTA)2Ir(dPPOA)]PF6 emitted from the LED; the CIE (Commission Internationale de L’Eclairage) chromaticity coordinates of this LED was (0.62, 0.38), the CRI was 48.0 and the CCT was 1265 K. These results show that [(TPTA)2Ir(dPPOA)]PF6 can be efficiently excited by blue GaN (450 nm) chips, and it is a potential red-light-source phosphor for changing the cold white light of aforementioned YAG:Ce-based WLEDs into warm white light.
In order to demonstrate the application of [(TPTA)2Ir(dPPOA)]PF6 for WLEDs, a series of blue GaN-based WLEDs using YAG:Ce (1.0 wt %) and [(TPTA)2Ir(dPPOA)]PF6 (x wt %, x = 0.0, 0.5, 1.0, 1.5) as phosphors blended in silicone were fabricated and measured. The emission spectra of these WLEDs are shown in Figure 8 and their performances are listed in Table 2. As mentioned previously, the emission peaks of blue GaN chips were also on the left, and their maximum wavelengths were also around 450 nm. On the right, the broad emission peaks from 500 nm to 725 nm were the mixture of emissions from YAG:Ce and [(TPTA)2Ir(dPPOA)]PF6 at different concentrations respectively. Before [(TPTA)2Ir(dPPOA)]PF6 was blended in, the WLED (No. g) only using YAG:Ce as its phosphor exhibited high CCT (6877 K) and low CRI (72.2). After [(TPTA)2Ir(dPPOA)]PF6 wasblended in, the emission peaks on the right showed visible red shift and became broader. When the blending concentrations increased from 0.0 wt % to 1.5 wt %, the maximum wavelengths changed from 554 nm (No. g) to 571 nm (No. h), and then to 582 nm (No. i) and 586 nm (No. j); at the same time, the intensity of the right emission peaks also increased with the increase of the blending concentrations of [(TPTA)2Ir(dPPOA)]PF6. The correlated color temperatures (CCTs) of WLEDs using [(TPTA)2Ir(dPPOA)]PF6 at 0.5 wt % (No. h), 1.0 wt % (No. i) and 1.5 wt % (No. j) were 4896 K, 3473 K and 2864 K respectively; obviously, the CCTs declined in order with the increase of blending concentrations. The CRIs of WLEDs No. h, i and j were 78.4, 80.2 and 75.7 respectively; all of them were higher than the CRI (72.2) of the WLED No. g without [(TPTA)2Ir(dPPOA)]PF6.
The luminous efficiencies of WLEDs No. h, i and j were85.2 lm∙W−1, 46.1 lm∙W−1 and 45.3 lm∙W−1 respectively. In contrast with WLED No. g (128.5 lm∙W−1), the luminous efficiencies decreased due to energy loss in light conversion. Besides some loss of luminous efficiencies when blue light was directly absorbed by [(TPTA)2Ir(dPPOA)]PF6 and transformed into orange light, some of the yellow light emitted from YAG:Ce was also absorbed by [(TPTA)2Ir(dPPOA)]PF6. Consequently, there was also a loss of luminous. Due to some degree of overlap between the excitation spectra of the iridium complex in silicone and the emission spectra of YAG:Ce (Figure 2 and Figure 3), such secondary light energy conversion aggravated the loss of total luminous efficiencies of the LEDs. By comparison with [Ir(CBT)2(dPPOA)]PF6 which was also used as a red-light-source phosphor in warm WLEDs in our previous work [15], the WLEDs using [Ir(CBT)2(dPPOA)]PF6 exhibited lower loss of luminous efficiencies. Thus, the aforementioned secondary light energy conversion between YAG:Ce and the iridium(III) complex can be ignored, mainly because ligand TPTA make wider excitation spectra for [(TPTA)2Ir(dPPOA)]PF6 than that of CBT for [Ir(CBT)2(dPPOA)]PF6. The excitation spectra of [Ir(CBT)2(dPPOA)]PF6 have much lower overlap with the emission spectra of YAG:Ce. Even so, the remaining efficiencies were still encouraging. Moreover, the CRIs of No. h, i and j have been improved, the CCTs of No. h, i and j have been lowered significantly and warmer white lights are obtained. The light emitted from WLED No. h became neutral white light, while the light emitted from WLEDs No. i and j were both warm white light. The CIE chromaticity coordinates of WLEDs No. g, h, i and j were (0.32, 0.33), (0.35, 0.33), (0.39, 0.36) and (0.44, 0.40), respectively. Their CIE chromaticity coordinates and working state photographs are all shown in Figure 9 to visually exhibit the aforementioned changes. In order to further exhibit the changes, the CIE chromaticity coordinates and working state photograph of the orange LED (No. f, only using [(TPTA)2Ir(dPPOA)]PF6 as a phosphor at 6.0 wt %) is also shown in Figure 9, because WLEDs No. h, i and j can be regarded as intermediate devices between WLEDs No. h and orange LED No. f.

4. Conclusions

A novel orange cationic iridium(III) complex [(TPTA)2Ir(dPPOA)]PF6 was synthesized. The [(TPTA)2Ir(dPPOA)]PF6 complex has a high thermal stability with a decomposition temperature of 375 °C, and its relative emission intensity at 100 °C is 88.8% of that at 25 °C. The [(TPTA)2Ir(dPPOA)]PF6 complex can be efficiently excited by blue GaN (450 nm) chips. GaN-based cold white LEDs using only YAG:Ce as a phosphor can become neutral WLEDs and warm WLEDs when [(TPTA)2Ir(dPPOA)]PF6 is added at proper concentrations. The [(TPTA)2Ir(dPPOA)]PF6 complex can effectively improve the red light component for WLEDs, and is a promising phosphor candidate for warm WLEDs.

Supplementary Materials

The following are available online at www.mdpi.com/1996-1944/10/6/657/s1, Figure S1: 1H NMR spectrum of [(TPTA)2Ir(POA)]PF6, Figure S2: MS spectrum of [(TPTA)2Ir(POA)]PF6.

Acknowledgments

This work was supported by National Nature Science Foundation of China (No. 21262046 and 21261027).

Author Contributions

Huaijun Tang, Guoyun Meng, Zeyu Chen and Kaimin Wang performed the experiments; Huaijun Tang, Guoyun Meng and Zhengliang Wang analyzed the data; and Huaijun Tang wrote the initial draft of the manuscript. Huaijun Tang and Zhengliang Wang designed and supervised the project, reviewed and contributed to the final revised manuscript. All authors contributed to the analysis and conclusion, and read the final paper.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Pimputkar, S.; Speck, J.S.; DenBaars, S.P.; Nakamura, S. Prospects for LED lighting. Nat. Photonics 2009, 3, 180–182. [Google Scholar] [CrossRef]
  2. Tsao, J.Y.; Crawford, M.H.; Coltrin, M.E.; Fischer, A.J.; Koleske, D.D.; Subramania, G.S.; Wang, G.T.; Wierer, J.J.; Karlicek, R.F., Jr. Toward smart and ultra-efficient solid-state lighting. Adv. Opt. Mater. 2014, 2, 809–836. [Google Scholar] [CrossRef]
  3. Feezell, D.F.; Speck, J.S.; DenBaars, S.P.; Nakamura, S. Semipolar (20-2-1) InGaN/GaN light-emitting diodes for high-efficiency solid-state lighting. J. Disp. Technol. 2013, 9, 190–198. [Google Scholar] [CrossRef]
  4. Chen, L.; Lin, C.C.; Yeh, C.W.; Liu, R.S. Light converting inorganic phosphors for white light-emitting diodes. Materials 2010, 3, 2172–2195. [Google Scholar] [CrossRef]
  5. Jang, H.S.; Won, Y.-H.; Jeon, D.Y. Improvement of electroluminescent property of blue LED coated with highly luminescent yellow-emitting phosphors. Appl. Phys. B 2009, 95, 715–720. [Google Scholar] [CrossRef]
  6. Zhu, H.; Lin, C.C.; Luo, W.; Shu, S.; Liu, Z.; Liu, Y.; Kong, J.; Ma, E.; Cao, Y.; Liu, R.-S.; et al. Highly efficient non-rare-earth red emitting phosphor for warm white light-emitting diodes. Nat. Commun. 2014, 5, 4312. [Google Scholar] [CrossRef] [PubMed]
  7. Kwak, H.H.; Kim, S.J.; Park, Y.S.; Yoon, H.H.; Park, S.J.; Choi, H.W. Photoluminescence Characteristic of Ce3+-Eu3+ Co-doped Y3Al5O12 Phosphor Prepared by Combustion Method. Mol. Cryst. Liq. Cryst. 2009, 513, 106–113. [Google Scholar] [CrossRef]
  8. Jang, H.S.; Im, W.B.; Lee, D.C.; Jeon, D.Y.; Kim, S.S. Enhancement of red spectral emission intensity of Y3Al5O12:Ce3+ phosphor via Pr Co-doping and Tb substitution for the application to white LEDs. J. Lumin. 2007, 126, 371–377. [Google Scholar] [CrossRef]
  9. Wang, X.; Zhou, G.; Zhang, H.L.; Li, H.; Zhang, Z.; Sun, Z. Luminescent properties of yellowish orange Y3Al5−xSixO12−xNx: Ce phosphors and their applications in warm white light-emitting diodes. J. Alloys Compd. 2012, 519, 149–155. [Google Scholar] [CrossRef]
  10. Lin, C.C.; Zheng, Y.S.; Chen, H.Y.; Ruan, C.H.; Xiao, G.W.; Liu, R.S. Improving optical properties of white LED fabricated by a blue LED chip with yellow/red phosphors. J. Electrochem. Soc. 2010, 157, 900–903. [Google Scholar] [CrossRef]
  11. Kim, S.; Kim, T.; Kang, M.; Kwak, S.K.; Yoo, T.W.; Park, L.S.; Yang, I.; Hwang, S.; Lee, J.E.; Kim, S.K.; et al. Highly luminescent InP/GaP/ZnS nanocrystals and their application to white light-emitting diodes. J. Am. Chem. Soc. 2012, 134, 3804–3809. [Google Scholar] [CrossRef] [PubMed]
  12. Zhou, Q.; Tan, H.; Zhou, Y.; Zhang, Q.; Wang, Z.; Yan, J.; Wu, M. Optical performance of Mn4+ in a new hexa-coordinated fluorozirconate complex of Cs2ZrF6. J. Mater. Chem. C 2016, 4, 7443–7448. [Google Scholar] [CrossRef]
  13. Tan, H.; Rong, M.; Zhou, Y.; Yang, Z.; Wang, Z.; Zhang, Q.; Wang, Q.; Zhou, Q. Luminescence behaviour of Mn4+ ions in seven coordination environments of K3ZrF7. Dalton Trans. 2016, 45, 9654–9660. [Google Scholar] [CrossRef] [PubMed]
  14. Wang, H.; He, P.; Liu, S.; Shi, J.; Gong, M. A europium(III) organic ternary complex applied in fabrication of near UV-based white light-emitting diodes. Appl. Phys. B 2009, 97, 481–487. [Google Scholar] [CrossRef]
  15. Meng, G.; Chen, Z.; Tang, H.; Liu, Y.; Wei, L.; Wang, Z. A novel cationic iridium(III) complex as red phosphor applied in warm white light-emitting diodes. New J. Chem. 2015, 39, 9535–9542. [Google Scholar] [CrossRef]
  16. Luo, Y.; Yan, Q.; Zhang, Z.; Yu, X.; Wu, W.; Su, W.; Zhang, Q. White LED based on poly(N-vinylcarbazole) and lanthanide complexes ternary co-doping system. J. Photochem. Photobiol. A 2009, 206, 102–108. [Google Scholar] [CrossRef]
  17. Xiang, H.-F.; Yu, S.-C.; Che, C.-M.; Lai, P.T. Efficient white and red light emission from GaN/tris-(8-hydroxyquinolato) aluminum/platinum(II) meso-tetrakis(pentafluorophenyl) porphyrin hybrid light-emitting diodes. Appl. Phys. Lett. 2003, 83, 1518–1520. [Google Scholar] [CrossRef]
  18. Niklaus, L.; Dakhil, H.; Kostrzewa, M.; Coto, P.B.; Sonnewald, U.; Wierschem, A.; Costa, R.D. Easy and versatile coating approach for long-living white hybrid light-emitting diodes. Mater. Horiz. 2016, 3, 340–347. [Google Scholar] [CrossRef]
  19. Zhang, C.; Heeger, A.J. Gallium nitride/conjugated polymer hybrid light emitting diodes: Performance and lifetime. J. Appl. Phys. 1998, 84, 1579–1582. [Google Scholar] [CrossRef]
  20. Martino, D.D.; Beverina, L.; Sassi, M.; Brovelli, S.; Tubino, R.; Meinardi, F. Straightforward fabrication of stable white LEDs by embedding of inorganic UV-LEDs into bulk polymerized polymethyl-methacrylate doped with organic dyes. Sci. Rep. 2014, 4, 4400. [Google Scholar] [CrossRef] [PubMed]
  21. Jin, J.-Y.; Kim, H.-G.; Hong, C.-H.; Suh, E.-K.; Lee, Y.-S. White light emission from a blue LED, combined with a sodium salt of fluorescein dye. Synth. Met. 2007, 157, 138–141. [Google Scholar] [CrossRef]
  22. Costa, R.D.; Ortί, E.; Bolink, H.J.; Monti, F.; Accorsi, G.; Armaroli, N. Luminescent ionic transition-metal complexes for light-emitting electrochemical cells. Angew. Chem. Int. Ed. 2012, 51, 8178–8211. [Google Scholar] [CrossRef] [PubMed]
  23. Hu, T.; He, L.; Duan, L.; Qiu, Y. Solid-state light-emitting electrochemical cells based on ionic iridium(III) comp lexes. J. Mater. Chem. 2012, 22, 4206–4215. [Google Scholar] [CrossRef]
  24. Ma, D.; Tsuboi, T.; Qiu, Y.; Duan, L. Recent progress in ionic iridium(III) complexes for organic electronic devices. Adv. Mater. 2017, 29, 1603253. [Google Scholar] [CrossRef] [PubMed]
  25. Tang, H.; Li, Y.; Chen, Q.; Chen, B.; Qiao, Q.; Yang, W.; Wu, H.; Cao, Y. Efficient yellow-green light-emitting cationic iridium complexes based on 1,10-phenanthroline derivatives containing oxadiazol-triphenylamine unit. Dyes Pigments 2014, 100, 79–86. [Google Scholar] [CrossRef]
  26. Tang, H.; Li, Y.; Zhao, B.; Yang, W.; Wu, H.; Cao, Y. Two novel orange cationic iridium(III) complexes with multifunctional ancillary ligands used for polymer light-emitting diodes. Org. Electron. 2012, 13, 3211–3219. [Google Scholar] [CrossRef]
  27. Lo, K.K.-W.; Li, S.P.-Y.; Zhang, K.Y. Development of luminescent iridium(III) polypyridine complexes as chemical and biological probes. New J. Chem. 2011, 35, 265–287. [Google Scholar] [CrossRef]
  28. Yang, Y.; Zhao, Q.; Feng, W.; Li, F. Luminescent chemodosimeters for bioimaging. Chem. Rev. 2013, 113, 192–270. [Google Scholar] [CrossRef] [PubMed]
  29. Sun, C.-Y.; Wang, X.-L.; Zhang, X.; Qin, C.; Li, P.; Su, Z.-M.; Zhu, D.-X.; Shan, G.-G.; Shao, K.-Z.; Wu, H.; et al. Efficient and tunable white-light emission of metal-organic frameworks by iridium-complex encapsulation. Nat. Commun. 2013, 4, 2717. [Google Scholar] [CrossRef] [PubMed]
  30. Yang, H.; Meng, G.; Zhou, Y.; Tang, H.; Zhao, J.; Wang, Z. The photoluminescent properties of new cationic iridium (III) complexes using different anions and their applications in white light-emitting diodes. Materials 2015, 8, 6105–6116. [Google Scholar] [CrossRef]
  31. Dong, H.; Zhu, H.; Meng, Q.; Gong, X.; Hu, W. Organic photoresponse materials and devices. Chem. Soc. Rev. 2012, 41, 1754–1808. [Google Scholar] [CrossRef] [PubMed]
  32. Lin, Y.; Li, Y.; Zhan, X. Small molecule semiconductors for high-efficiency organic photovoltaics. Chem. Soc. Rev. 2012, 41, 4245–4272. [Google Scholar] [CrossRef] [PubMed]
  33. Chen, X.; Liu, R.; Xu, Y.; Zou, G. Tunable protic ionic liquids as solvent-catalysts for improved synthesis of multiply substituted 1,2,4-triazoles from oxadiazoles and organoamines. Tetrahedron 2012, 68, 4813–4819. [Google Scholar] [CrossRef]
  34. Lowry, M.S.; Hudson, W.R.; Pascal, R.A., Jr.; Bernhard, S. Accelerated luminophore discovery through combinatorial synthesis. J. Am. Chem. Soc. 2004, 126, 14129–14135. [Google Scholar] [CrossRef] [PubMed]
  35. Lamansky, S.; Djurovich, P.; Murphy, D.; Abdel-Razzaq, F.; Lee, H.-E.; Adachi, C.; Burrows, P.E.; Forrest, S.R.; Thompson, M.E. Highly phosphorescent bis-cyclometalated iridium complexes: Synthesis, photophysical characterization, and use in organic light emitting diodes. J. Am. Chem. Soc. 2001, 123, 4304–4312. [Google Scholar] [CrossRef] [PubMed]
  36. Wong, W.-Y.; Zhou, G.-J.; Yu, X.-M.; Kwok, H.-S.; Lin, Z.-Y. Efficient organic light-emitting diodes based on sublimable charged iridium phosphorescent emitters. Adv. Funct. Mater. 2007, 17, 315–323. [Google Scholar] [CrossRef]
  37. Sahoo, H. Föster resonance energy transfer—A spectroscopic nanoruler: Principle and applications. J. Photochem. Photobiol. C 2011, 12, 20–30. [Google Scholar] [CrossRef]
  38. Lü, W.; Lv, W.; Zhao, Q.; Jiao, M.; Shao, B.; You, H. A novel efficient Mn4+ activated Ca14Al10Zn6O35 phosphor: Application in red-emitting and white LEDs. Inorg. Chem. 2014, 53, 11985–11990. [Google Scholar] [CrossRef] [PubMed]
  39. Lee, S.-P.; Chan, T.-S.; Chen, T.-M. Novel reddish-orange-emitting BaLa2Si2S8:Eu2+ thiosilicate phosphor for LED lighting. ACS Appl. Mater. Interfaces 2015, 7, 40–44. [Google Scholar] [CrossRef] [PubMed]
  40. Ruan, J.; Xie, R.-J.; Hirosaki, N.; Takeda, T. Nitrogen gas pressure synthesis and photoluminescent properties of orange-red SrAlSi4N7:Eu2+ phosphors for white light-emitting diodes. J. Am. Ceram. Soc. 2011, 94, 536–542. [Google Scholar] [CrossRef]
  41. Li, H.; Zhao, R.; Jia, Y.; Sun, W.; Fu, J.; Jiang, L.; Zhang, S.; Pang, R.; Li, C. Sr1.7Zn0.3CeO4:Eu3+ novel red-emitting phosphors: Synthesis and photoluminescence properties. ACS Appl. Mater. Interfaces 2014, 6, 3163–3169. [Google Scholar] [CrossRef] [PubMed]
  42. Setlur, A.A.; Lyons, R.J.; Murphy, J.E.; Kumar, N.P.; Kishore, M.S. Blue light-emitting diode phosphors based upon oxide, oxyhalide, and halide hosts. ECS J. Solid State Sci. Technol. 2013, 2, R3059–R3070. [Google Scholar] [CrossRef]
Materials 10 00657 g001 550
Figure 1. Synthetic route and chemical structure of [(TPTA)2Ir(dPPOA)]PF6.
Figure 1. Synthetic route and chemical structure of [(TPTA)2Ir(dPPOA)]PF6.
Materials 10 00657 g001
Materials 10 00657 g002 550
Figure 2. Normalized UV-vis absorption spectrum of [(TPTA)2Ir(dPPOA)]PF6 in CH2Cl2 solution at 1.0 × 10−5 mol∙L−1 and emission spectra of the blue GaN chip and YAG:Ce.
Figure 2. Normalized UV-vis absorption spectrum of [(TPTA)2Ir(dPPOA)]PF6 in CH2Cl2 solution at 1.0 × 10−5 mol∙L−1 and emission spectra of the blue GaN chip and YAG:Ce.
Materials 10 00657 g002
Materials 10 00657 g003 550
Figure 3. Normalized excitation (Ex, λem = 581, 600 nm) and emission (Em, λex = 450 nm) spectra of [(TPTA)2Ir(dPPOA)]PF6 in CH2Cl2 solution at 1.0 × 10−5 mol∙L−1 and blended in silicone at 6.0 wt % (coated on quartz plate). Inset: A photograph of [(TPTA)2Ir(dPPOA)]PF6 powders excited by blue light (λex = 450 nm).
Figure 3. Normalized excitation (Ex, λem = 581, 600 nm) and emission (Em, λex = 450 nm) spectra of [(TPTA)2Ir(dPPOA)]PF6 in CH2Cl2 solution at 1.0 × 10−5 mol∙L−1 and blended in silicone at 6.0 wt % (coated on quartz plate). Inset: A photograph of [(TPTA)2Ir(dPPOA)]PF6 powders excited by blue light (λex = 450 nm).
Materials 10 00657 g003
Materials 10 00657 g004 550
Figure 4. Thermogravimetric (TG)curve of [(TPTA)2Ir(dPPOA)]PF6.
Figure 4. Thermogravimetric (TG)curve of [(TPTA)2Ir(dPPOA)]PF6.
Materials 10 00657 g004
Materials 10 00657 g005 550
Figure 5. Temperature-dependent photoluminescent emission spectra of [(TPTA)2Ir(dPPOA)]PF6 powders measured with increasing temperature from 25 °C to 200 °C, λex = 450 nm.
Figure 5. Temperature-dependent photoluminescent emission spectra of [(TPTA)2Ir(dPPOA)]PF6 powders measured with increasing temperature from 25 °C to 200 °C, λex = 450 nm.
Materials 10 00657 g005
Materials 10 00657 g006 550
Figure 6. Relative emission intensity of [(TPTA)2Ir(dPPOA)]PF6 as a function of temperature. The inset represents the ln(Io/I − 1) versus 1/T and the calculated activation energy (Ea) for [(TPTA)2Ir(dPPOA)]PF6.
Figure 6. Relative emission intensity of [(TPTA)2Ir(dPPOA)]PF6 as a function of temperature. The inset represents the ln(Io/I − 1) versus 1/T and the calculated activation energy (Ea) for [(TPTA)2Ir(dPPOA)]PF6.
Materials 10 00657 g006
Materials 10 00657 g007 550
Figure 7. Emission spectra of light-emitting diodes (LEDs) using blue GaN as chips and only [(TPTA)2Ir(dPPOA)]PF6 as a phosphor at different blending concentrations at 20 mA forward current.
Figure 7. Emission spectra of light-emitting diodes (LEDs) using blue GaN as chips and only [(TPTA)2Ir(dPPOA)]PF6 as a phosphor at different blending concentrations at 20 mA forward current.
Materials 10 00657 g007
Materials 10 00657 g008 550
Figure 8. Emission spectra of blue GaN-based white light-emitting diodes (WLEDs) using YAG:Ce (1.0 wt %) and [(TPTA)2Ir(dPPOA)]PF6 (x wt %, x = 0.0, 0.5, 1.0, 1.5) as phosphors blended insilicone at different concentrations.
Figure 8. Emission spectra of blue GaN-based white light-emitting diodes (WLEDs) using YAG:Ce (1.0 wt %) and [(TPTA)2Ir(dPPOA)]PF6 (x wt %, x = 0.0, 0.5, 1.0, 1.5) as phosphors blended insilicone at different concentrations.
Materials 10 00657 g008
Materials 10 00657 g009 550
Figure 9. CIE chromaticity coordinates of blue GaN-based LEDs using YAG:Ce and [(TPTA)2Ir(dPPOA)]PF6 as phosphors at different blending concentrations. (f) only [(TPTA)2Ir(dPPOA)]PF6 at 6.0 wt %; (g) only YAG:Ce at 1.0 wt %; (h) 1.0 wt % YAG:Ce and 0.5 wt % [(TPTA)2Ir(dPPOA)]PF6; (i) 1.0 wt % YAG:Ce and 1.0 wt % [(TPTA)2Ir(dPPOA)]PF6; (j) 1.0 wt % YAG:Ce and 1.5 wt % [(TPTA)2Ir(dPPOA)]PF6. Inset: The photographs of the LEDs No. g, h, i, j and f in working state.
Figure 9. CIE chromaticity coordinates of blue GaN-based LEDs using YAG:Ce and [(TPTA)2Ir(dPPOA)]PF6 as phosphors at different blending concentrations. (f) only [(TPTA)2Ir(dPPOA)]PF6 at 6.0 wt %; (g) only YAG:Ce at 1.0 wt %; (h) 1.0 wt % YAG:Ce and 0.5 wt % [(TPTA)2Ir(dPPOA)]PF6; (i) 1.0 wt % YAG:Ce and 1.0 wt % [(TPTA)2Ir(dPPOA)]PF6; (j) 1.0 wt % YAG:Ce and 1.5 wt % [(TPTA)2Ir(dPPOA)]PF6. Inset: The photographs of the LEDs No. g, h, i, j and f in working state.
Materials 10 00657 g009
Table
Table 1. Performances of blue GaN-based LEDs only using [(TPTA)2Ir(dPPOA)]PF6 as a phosphor at different blending concentrations (at 20 mA forward current).
Table 1. Performances of blue GaN-based LEDs only using [(TPTA)2Ir(dPPOA)]PF6 as a phosphor at different blending concentrations (at 20 mA forward current).
No. of LEDsBlending Concentration (wt %)Luminous Efficiency (lm∙W−1)CRICCT (K)λem, max (nm)CIE (x, y)
a1.018.931.6100,000451, 609(0.31, 0.17)
b2.015.840.72159451, 610(0.37, 0.21)
c3.012.146.61957451, 614(0.41, 0.25)
d4.010.150.21737451, 617(0.45, 0.28)
e5.07.351.61507451, 619(0.55, 0.35)
f6.05.448.01265619(0.62, 0.38)
Table
Table 2. Performances of WLEDs fabricated by using YAG:Ce and [(TPTA)2Ir(dPPOA)]PF6 as phosphors (at 20 mA forward current).
Table 2. Performances of WLEDs fabricated by using YAG:Ce and [(TPTA)2Ir(dPPOA)]PF6 as phosphors (at 20 mA forward current).
No. of LEDsBlending Concentration (wt %)Luminous Efficiency (lm∙W−1)CRICCT (K)λem, max (nm)CIE (x, y)
YAG:CeComplex
g1.00.0128.572.26877449, 556(0.32, 0.33)
h1.00.585.278.44896448, 573(0.35, 0.33)
i1.01.046.180.23473451, 583(0.39, 0.36)
j1.01.545.375.72864450, 586(0.44, 0.40)

Share and Cite

MDPI and ACS Style

Tang, H.; Meng, G.; Chen, Z.; Wang, K.; Zhou, Q.; Wang, Z. Warm White Light-Emitting Diodes Based on a Novel Orange Cationic Iridium(III) Complex. Materials 2017, 10, 657. https://0-doi-org.brum.beds.ac.uk/10.3390/ma10060657

AMA Style

Tang H, Meng G, Chen Z, Wang K, Zhou Q, Wang Z. Warm White Light-Emitting Diodes Based on a Novel Orange Cationic Iridium(III) Complex. Materials. 2017; 10(6):657. https://0-doi-org.brum.beds.ac.uk/10.3390/ma10060657

Chicago/Turabian Style

Tang, Huaijun, Guoyun Meng, Zeyu Chen, Kaimin Wang, Qiang Zhou, and Zhengliang Wang. 2017. "Warm White Light-Emitting Diodes Based on a Novel Orange Cationic Iridium(III) Complex" Materials 10, no. 6: 657. https://0-doi-org.brum.beds.ac.uk/10.3390/ma10060657

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.