Next Article in Journal
Surface Characterization and Corrosion Behavior of 90/10 Copper-Nickel Alloy in Marine Environment
Previous Article in Journal
Fabrication and Application of Carboxymethyl Cellulose-Carbon Nanotube Aerogels
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Materials
Volume 12
Issue 11
10.3390/ma12111868
materials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Microstructure and Mechanical Properties of Spark Plasma Sintered Si3N4/WC Ceramic Tools

by
Zhenhua Wang
*,
Jiheng Jia
,
Liyan Cao
,
Ning Sun
and
Yulin Wang
*
School of Mechanical Engineering, Nanjing University of Science and Technology, Nanjing 210094, China
*
Authors to whom correspondence should be addressed.
Materials 2019, 12(11), 1868; https://0-doi-org.brum.beds.ac.uk/10.3390/ma12111868
Submission received: 10 May 2019 / Revised: 29 May 2019 / Accepted: 4 June 2019 / Published: 10 June 2019
Browse Figures
Versions Notes

Abstract

:
Silicon nitride (Si3N4) based ceramic tools exhibit good machinability in cutting materials such as gray cast iron, ductile iron, malleable cast iron, and superalloys due to excellent high-temperature mechanical properties. In this paper, high-performance Si3N4-based ceramic tools containing tungsten carbide (WC) and cobalt (Co) were studied. Effects of the WC content and Co content on mechanical properties and a microstructure of Si3N4-based ceramic materials were analyzed. Results showed that Si3N4-based ceramic material containing 10 wt % WC and 1 wt % Co had the best comprehensive mechanical properties at a sintering temperature of 1650 °C and holding time of 6 min, achieving Vickers hardness, fracture toughness, and room temperature bending strength of 16.96 GPa, 7.26 MPa·m1/2, and 1132 MPa, respectively. The microstructure of Si3N4-based ceramic tool material is uniform without obvious abnormal growth. The Si3N4-based ceramic tool was mainly composed of α-Si3N4, β-Si3N4, and WC phases.

1. Introduction

Silicon nitride ceramic materials are widely used in much of the industrial equipment such as cutting tools, gas turbines, thermal insulation materials, and engine parts due to their high strength, high elastic modulus, wear resistance, thermal shock resistance, and creep resistance [1,2,3]. Silicon nitride ceramic cutting tools have good cutting performance in processing the gray cast iron, nodular cast iron, malleable cast iron, and high-temperature alloy. At present, the main factors affecting the cutting performance of silicon nitride ceramic tools are low hardness and fracture toughness. With the aim to improve the hardness and fracture toughness of Si3N4-based ceramic material, scholars had made many efforts such as adding a hard phase, nano-phase, binder phase, and lubricant phase to Si3N4-based ceramic tool materials [4,5].
Adding a high hardness second phase is an important means to improve the hardness and fracture toughness of silicon nitride ceramics. The second phase, which is commonly added to the Si3N4-based composite materials, mainly includes the titanium diboride (TiB2) [6], titanium carbide (TiC) [7,8], titanium nitride (TiN) [9], Ti (C7N3) [10], silicon carbide (SiC) [11], carbon nanostructure [12], and (W, Ti)C [13], and the like. The choice of the second phase is particularly important because it has a great impact on the microstructure and properties of a Si3N4-based composite. Tapasztó et al. [14] prepared the Si3N4-based nanocomposites by hot isostatic pressing sintering (HIP) and spark plasma sintering (SPS) using single- and multi-walled carbon nanotubes (SWCNT and MWCNT), exfoliated graphite (GR), and carbon black (CB) as the reinforcing phases. Their results showed that the comprehensive mechanical properties of the Si3N4-based nanocomposites prepared by the two sintering methods were worse than those of the single-phase silicon nitride ceramics without carbon nanostructures. The Si3N4-based nanocomposites prepared by the hot isostatic pressing, which had good toughness, was mainly composed of the β-Si3N4. The sample prepared by the spark plasma sintering, which had high hardness, was also mainly composed of α-Si3N4. Xu et al. [13] prepared the Si3N4/(W, Ti)C composite ceramic tool materials by microwave sintering, and found that (W, Ti)C inhibited the densification and phase transformation of the Si3N4-based composite ceramics. Besides, they found that when the sintering temperature decreased by 100 °C, the mechanical properties of the Si3N4-based matrix composites increased by 6–9%.
At present, the methods for preparation of Si3N4-based ceramic material are mainly based on the traditional sintering methods such as hot pressing [14,15], hot isostatic pressing [12], air pressure [16], pressureless [17], and reaction sintering [18,19]. In addition, there are new preparation techniques such as spark plasma sintering [20,21,22] and microwave sintering [3,13]. The traditional sintering methods have the disadvantages of high energy consumption and low efficiency, and the microwave sintering is unevenly heated, so a sample is easy to crack, which seriously affects the performance reliability and economic feasibility of the tool. The SPS denotes a new type of material preparation methods which provides high efficiency, has simple operation, low energy consumption, and environmental protection. The SPS technology has the characteristics of hot pressing, plasma activation, and current heating, which make the material obtain high density, uniform microstructure, and fine grains [23]. Therefore, SPS technology was chose to sinter Si3N4-based ceramic.
In addition, the mechanical properties of Si3N4-based ceramic can be significantly improved by appropriate sintering additives and composition ratio. Common sintering aids are oxides, nitrides, and fluorides. These sintering aids play different roles in the preparation of Si3N4-based ceramic. MgO is more significant in reducing the sintering temperature [3]. CeO2 has better wettability with silicon nitride [3]. MgSiN2 can increase the density of Si3N4 ceramic [21]. In our previous study, MgSiN2-Y2O3-CeO2 system was selected as sintering aids to analyze the effects of various components on the mechanical properties and microstructures of Si3N4-based ceramic materials. The results shown that Si3N4-based ceramic materials with 5 wt % MgSiN2, 3 wt % Y2O3, and 1 wt % CeO2 sintering aids had the best mechanical properties [22]. Therefore, the sintering aids of 5 wt % MgSiN2, 3 wt % Y2O3, and 1 wt % CeO2 were selected in this paper.
WC has the advantages of high fracture toughness, good wear resistance, high hardness, and good chemical stability. In addition, in the spark plasma sintering process of ceramic materials, adding an appropriate amount of conductive metal phase (such as Co, Ni, Mo, etc.) can increase the current through the Si3N4-based ceramic material, promote Joule heat generation and increase the α→β Si3N4 phase transformation rate. The wettability between WC and metal Co is good. The WC-Co cemented carbide prepared by spark plasma sintering technology not only has a small grain size, but also greatly improves the mechanical properties [24]. Therefore, WC and Co are selected as the phase to improve the properties of the Si3N4 ceramic tool. Effects of the WC and Co content on the mechanical properties and microstructure of Si3N4-based ceramic material are investigated in the paper.
In this paper, Si3N4-based ceramic material was prepared by adding WC and Co by SPS. The effects of WC and Co content on relative density, microstructure, and mechanical properties of Si3N4/WC ceramic material were investigated. The bending strength of the Si3N4/WC ceramic materials at different temperatures were analyzed to obtain a Si3N4-based ceramic material with excellent comprehensive mechanical properties and to provide support for machining hard materials.

2. Experimental Methods

2.1. Sample Preparation

The raw powders (purity: 99.99%) were purchased from Shanghai Chaoyu New Material Technology Co. Ltd (Shanghai, China). The masses of the α-Si3N4 (700 nm), WC (500 nm), Co (500 nm), MgSiN2 (500 nm), Y2O3 (1 μm), and CeO2 (1 μm) powders were weighed on an electronic balance (WH-BL2003, Weiheng, Guangzhou, China) in proportion, which were then placed in a polyurethane ball mill tank and ball milled in a planetary ball mill (QM-3SP2, Nanda, Nanjing, China) with silicon nitride balls for 48 h. The ratio of powder to ball was 7:1. The mixed powder after ball milling was dried at 120 °C in a vacuum drying oven (DZF-1 type, Keheng, Shanghai, China), and then ground and passed through a 100-mesh sieve. Twenty grams of mixed powder was loaded into a graphite mold having an inner diameter of 20 mm, and a graphite paper coated with boron nitride was placed between the mold and powder for the purpose of more easily demolding after sintering. Subsequently, a graphite mold wrapped with carbon felt was placed in a chamber of a spark plasma sintering system (LABOXTM-650F, Sinter Land Inc., Nagaoka, Japan) for sintering (1650 °C sintering temperature, 100 °C/min heating rate, 50 MPa sintering pressure, and 6 min holding time at Ar). After the sintered body was coarsely grinded, grinded, and polished, the properties were analyzed and characterized.
The experiments with two factors and three levels were conducted at a sintering temperature of 1650 °C while holding for 6 min. The WC content was 5 wt %, 10 wt %, and 15 wt %, and the Co content was 1 wt %, 2 wt %, and 4 wt %, respectively. The total content of the sintering aid was 9 wt % (the specific composition consisted of 5 wt % MgSiN2, 3 wt % Y2O3, and 1 wt % CeO2).

2.2. Performance Testing

The sample density was determined by the Archimedes’ drainage method, and the relative sample density was calculated using the ratio of the measured bulk density to the theoretical density. The Vickers hardness and the fracture toughness of a sample were determined by the indentation method. The load was 196.1 N, and it was maintained for 15 s. The Vickers hardness and fracture toughness were respectively defined by [25]:
H V = 0.001854 × F d 2 ,
K I C = 0.203 ( c / a ) − 3 / 2 a H V ,
where HV denoted the Vickers hardness of a sample (given in GPa), F denoted the load (given in N), d represented the diagonal length of the material indentation (given in mm), KIC was the fracture toughness (given in MPa·m1/2), c denoted a half of the crack length (given in mm), and lastly, a denoted the half-length of the diagonal indentation (given in mm).
Bending strength of the Si3N4-based ceramic material containing 10 wt % WC and 1 wt % Co (named the SW10) at different temperatures (20, 200, 400, 600, and 800 °C) was measured by the method of a 3-points bending test using an electronic universal testing machine (UTM5105-G, Hengsisheng, Jinan, China). The size of bending strength-testing sample was 30 mm × 5 mm × 5 mm (length × width × height). The phase composition of the samples was analyzed by a Bruker D8 X-ray diffractometer (XRD, D8 Advance, Bruker, Leipzig, Germany). The microstructure and elemental composition were examined with a scanning electron microscope (SEM, Quant250FEG, FEI, Hillsboro, OR, USA) equipped with an energy dispersive spectrometer (EDS).

3. Results and Discussion

The relationship between the relative density of Si3N4-based ceramic materials and the WC and Co content was presented in Figure 1, wherein it can be seen that the density of all the sintered samples was above 99%. Generally, the spark plasma sintered Si3N4-based ceramic material could obtain higher density.
Effects WC and Co content on the hardness and fracture toughness of the Si3N4-based ceramic material is presented in Figure 2. As shown in Figure 2, the Vickers hardness of the sample firstly increased, and then decreased with the increase in WC content. The Vickers hardness of the sample decreased with the increase in Co content. The fracture toughness firstly increased and then decreased with the increase in WC content when the Co content was 1 wt % and 4 wt %. However, the fracture toughness increased with the increase in WC content when the Co content was 2 wt %. In summary, the Si3N4-based ceramic material containing 10 wt % WC and 1 wt % Co (named the SW10) achieved the best comprehensive mechanical properties, and the Vickers hardness, fracture toughness were 16.96 GPa and 7.26 MPa·m1/2, respectively. Compared with Si3N4-based ceramic material (91 wt % Si3N4 + 5 wt % MgSiN2 + 3 wt % Y2O3 + 1 wt % CeO2) [22], the Vickers hardness and fracture toughness of SW10 ceramic material were increased by 2.60% and 5.37%, respectively.
SW10 ceramic tools must bear higher cutting temperature during cutting processes. The cutting performance of the cutting tool is better when the cutting tool material has high mechanical properties at a high temperature. In order to study the effect of temperature on the bending strength of SW10, the bending strength of SW10 ceramic materials were analyzed when the material temperature was 20, 200, 400, 600, and 800 °C. The bending strength of the SW10 ceramic material at different temperatures were presented in Figure 3. As shown in Figure 3, the bending strength of SW10 ceramic material reached 1132 MPa at room temperature of 20 °C, and the bending strength reached the value of 566 MPa when the temperature reached 800 °C, which demonstrated excellent high-temperature mechanical properties. The bending strength of the material generally decreased with the increase of temperature.
In Figure 4, the SEM micrographs of the Si3N4-based ceramic having different WC content with the Co content of 1 wt % after being corroded by the molten NaOH were respectively presented. As shown in Figure 4, no obvious abnormal growth was observed in the Si3N4 grains under different conditions; the microstructure was relatively uniform and small, and the aspect ratio of the β-Si3N4 phase was high. Sintering of the Si3N4-based ceramic materials was a dissolution and reprecipitation process [26,27]. The sintering aid formed a low eutectic liquid phase with the SiO2 oxide film on the surface of the silicon nitride ceramic at high temperature. When the temperature exceeded 1500 °C, the α-Si3N4 phase began to convert into β-Si3N4 phase silicon nitride according to the Ostwald ripening mechanism. First, smaller α-Si3N4 grains first dissolved into the liquid phase, and when the liquid phase was saturated, then larger β-Si3N4 grains precipitated. Since the growth rate of the β-Si3N4 grains in different directions was very different, the β-Si3N4 grains tended to grow in preferential orientation to form the rod-like grains [28]. The length-diameter ratio of β-Si3N4 grain was calculated by measuring the lengths and diameters of 50 randomly selected β-Si3N4 grains. Statistical results shown that at the WC content of 5 wt %, 10 wt %, and 15 wt %, the average value of length-diameter ratio of β-Si3N4 was 4.45, 7.81, and 3.26, respectively. Therefore, the average value of length-diameter ratio of β-Si3N4 was largest when the WC content was 10 wt %, which leaded to higher fracture toughness of Si3N4-based ceramic materials containing having 10 wt % WC.
The X-ray diffraction patterns of the Si3N4-based ceramic having different WC contents at the Co content of 1 wt % are presented in Figure 5. The quantitative analysis of α-Si3N4 and β-Si3N4 of the samples was performed using the diffraction intensities of the (1 0 1), (2 0 1), (1 0 2), and (3 0 1) planes for α-Si3N4, and of the (1 1 0), (2 0 0), (1 0 1), and (2 1 0) planes for β-Si3N4 [29]. As Figure 4a and Figure 5 show, the α-Si3N4 grains constituted the majority in the Si3N4-based ceramic material having 5 wt % WC, while there were fewer β-Si3N4 grains and the α→β-Si3N4 conversion rate was 37.91%, As shown in Figure 4b and Figure 5, the number of β-Si3N4 grains in the Si3N4-based ceramic with the WC content of 10 wt % was remarkably increased compared with the Si3N4-based ceramic material having 5 wt % WC, and the α→β-Si3N4 conversion rate was 46.21%. The formation of long columnar grains had an important influence on the fracture toughness of the Si3N4-based ceramic material. As shown in Figure 4b, many well-developed long columnar grains were stacked together forming a spatial network structure. The spindly β-Si3N4 grains were staggered with each other, preventing the crack expansion, and improving the fracture toughness of the material. The columnar β-Si3N4 increased gradually when the WC content increased to 15 wt %, and the conversion rate of α→β-Si3N4 was 47.27%, as shown in Figure 4c and Figure 5. In the non-porous region, some short rod-like β-Si3N4 grains were embedded in the network structure. As shown in Figure 4b,c the β-Si3N4 grain size of the Si3N4-based ceramic material containing 15 wt % WC was larger than the β-Si3N4 grain size of the Si3N4-based ceramic material containing 10 wt % WC. When the WC content was 15%, the porosities were easily formed between the coarse grains of β-Si3N4, which led to a decrease in fracture toughness (as shown in Figure 2). Therefore, higher Vickers hardness and fracture toughness can be obtained at a WC content of 10 wt %.
The SEM micrographs and X-ray diffraction pattern of the corroded surface of Si3N4-based ceramic having different Co content with the WC content of 10 wt % were respectively presented in Figure 6 and Figure 7. As shown in Figure 6 and Figure 7, the amount and length-diameter ratio of β-Si3N4 decreased with the increase of cobalt content, and some larger WC grains were formed. Statistical results shown that at the Co content of 1 wt %, 2 wt %, and 4 wt %, the average value of length-diameter ratio of β-Si3N4 was 7.81, 4.62, and 5.83, respectively.
As Figure 7 showing, the intensity of the β-Si3N4 phase diffraction peak was decreased with the increase in Co content, and the intensity of the α-Si3N4 phase diffraction peak was slightly increased with the increase in Co content. When the Co content is 1 wt %, 2 wt %, and 4 wt %, the conversion rate of α→β-Si3N4 was 46.21%, 35.71%, and 30.28%, respectively. The results showed that the conversion rate of α→β-Si3N4 decreased with the increase of Co content. This was mainly because the WC and Co had good wettability, and when the WC powder was sintered by the spark plasma sintering method under the action of the Co powder, the densification sintering process could be completed at the sintering temperature of 1250 °C [28], and such a temperature was significantly lower than the high densification sintering temperature (1650 °C) of α-Si3N4 under the action of the sintering aid. When the Co content increased, the WC and Co powders in the Si3N4-based ceramic material had more chances to contact with each other, providing more sintering power for the WC pre-sintering. Therefore, the WC grains formed in the initial stage of sintering were uniformly distributed in the Si3N4-based ceramic material, which hindered the conversion of α-Si3N4 to β-Si3N4. Meanwhile, those WC grains might also hinder the overall columnar growth of β-Si3N4. So, higher Vickers hardness and fracture toughness can be obtained at 1 wt % Co when WC content was 10 wt %.

4. Conclusions

In this paper, the high-performance Si3N4-based ceramic material tools containing the WC and Co are prepared by spark plasma sintering to analyze the effect of the WC content and Co content on the phase composition, the conversion rate of α→β-Si3N4, hardness, fracture toughness, and microstructure of the Si3N4-based ceramic material tools. The main conclusions are as follows.
(1)
At the sintering temperature of 1650 °C the Si3N4-based ceramic material containing 10 wt % WC and 1 wt % Co (SW10) achieved the best Vickers hardness and fracture toughness, and the Vickers hardness, fracture toughness, and room temperature bending strength were 16.96 GPa, 7.26 MPa·m1/2, and 1132 MPa respectively, and the α→β phase conversion rate was 46.21%.
(2)
The microstructure image of the Si3N4-based ceramic material showed that there were no abnormally grown grains at the different WC content and Co content, and the microstructure was uniform. The content of β-Si3N4 phase increased with the increase in WC content at the Co content of 1 wt %, but the content of β-Si3N4 phase decreased with the increase in Co content at the WC content of 10 wt %.

Author Contributions

Conceptualization, Z.W.; methodology, Z.W.; validation, Z.W., N.S., Y.W., J.J. and L.C.; investigation, L.C. and J.J.; data curation, N.S. and Y.W.; writing—original draft preparation, L.C. and Z.W.; resources, Z.W.; writing—review and editing, Z.W. and J.J.; supervision, Z.W.; project administration, Z.W.; funding acquisition, Z.W.

Funding

This study was funded by the National Key R&D Program of China (Grant number 2018YFB2002205), National Natural Science Foundation of China (grant number 51775280) and Jiangsu Provincial Six Talent Peaks Project (grant number 2016-HKHT-019).

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Riley, F.L. Silicon nitride and related materials. J. Am. Ceram. Soc. 2000, 83, 245–265. [Google Scholar] [CrossRef]
  2. Miranzo, P.; González-Julián, J.; Osendi, M.I.; Belmonte, M. Enhanced particle rearrangement during liquid phase spark plasma sintering of silicon nitride-based ceramics. Ceram. Int. 2011, 37, 159–166. [Google Scholar] [CrossRef]
  3. Xu, W.; Yin, Z.; Yuan, J.; Wang, Z.; Fang, Y. Effects of sintering additives on mechanical properties and microstructure of Si3N4 ceramics by microwave sintering. Mater. Sci. Eng. A. 2017, 684, 127–134. [Google Scholar] [CrossRef]
  4. Wolfrum, A.K.; Quitzke, C.; Matthey, B.; Herrmann, M.; Michaelis, A. Wear behavior of diamond-silicon nitride composites sintered with FAST/SPS. Wear 2018, 396-397, 171–181. [Google Scholar] [CrossRef]
  5. Liu, C.C.; Huang, J.L. Influence of TiN particles on the wear behaviour of silicon nitride-based composites. J. Mater. Res. 2004, 19, 542–549. [Google Scholar] [CrossRef]
  6. Jones, A.H.; Dobedoe, R.S.; Lewis, M.H. Mechanical properties and tribology of Si3N4-TiB2 ceramic composites produced by hot pressing and hot isostatic pressing. J. Eur. Ceram. Soc. 2001, 21, 969–980. [Google Scholar] [CrossRef]
  7. Ye, C.; Yue, X.; Ru, H.; Long, H.; Gong, X. Effect of addition of micron-sized TiC particles on mechanical properties of Si3N4 matrix composites. J. Alloys Compd. 2017, 709, 165–171. [Google Scholar] [CrossRef]
  8. Zhao, J.; Ai, X.; Lü, Z. Preparation and characterization of Si3N4/TiC nanocomposite ceramics. Mater. Lett. 2006, 60, 2810–2813. [Google Scholar] [CrossRef]
  9. Zou, B.; Huang, C.Z.; Liu, H.L.; Chen, M. Preparation and characterization of Si3N4/TiN nanocomposites ceramic tool materials. J. Mater. Process. Technol. 2009, 209, 4595–4600. [Google Scholar] [CrossRef]
  10. Zou, B.; Huang, C.Z.; Chen, M. Study on the mechanical properties, microstructure and oxidation resistance of Si3N4/Si3N4W/Ti(C7N3) nanocomposites ceramic tool materials. Int. J. Refract. Met. Hard Mater. 2009, 27, 52–60. [Google Scholar] [CrossRef]
  11. Suri, J.; Shaw, L.L. Liquid phase sintering of Si3N4/SiC nanopowders derived from silica fume. Ceram. Int. 2014, 40, 9179–9187. [Google Scholar] [CrossRef]
  12. Tapaszto, O.; Kun, P.; Weber, F.; Gergely, G.; Balazsi, K.; Pfeifer, J.; Balázsi, C. Silicon nitride based nanocomposites produced by two different sintering methods. Ceram. Int. 2011, 37, 3457–3461. [Google Scholar] [CrossRef]
  13. Xu, W.; Yin, Z.; Yuan, J.; Wang, Z.; Liu, Y. Preparation and characterization of Si3N4-based composite ceramic tool materials by microwave sintering. Ceram. Int. 2017, 43, 16248–16257. [Google Scholar] [CrossRef]
  14. Guo, W.M.; Wu, L.X.; Ma, T.; Gu, S.X.; You, Y.; Lin, H.T.; Zhang, G.J. Chemical reactivity of hot-pressed Si3N4-ZrB2 ceramics at 1500–1700 °C. J. Eur. Ceram. Soc. 2015, 35, 2973–2979. [Google Scholar] [CrossRef]
  15. Miyazaki, H.; Hyuga, H.; Yoshizawa, Y.I.; Hirao, K.; Ohji, T. Correlation of wear behavior and indentation fracture resistance in silicon nitride ceramics hot-pressed with alumina and yttria. J. Eur. Ceram. Soc. 2009, 29, 1535–1542. [Google Scholar] [CrossRef]
  16. Liu, S.; Ye, F.; Hu, S.; Yang, H.; Liu, Q.; Zhang, B. A new way of fabricating Si3N4 ceramics by aqueous tape casting and gas pressure sintering. J. Alloys Compd. 2015, 647, 686–692. [Google Scholar] [CrossRef]
  17. Liu, T.T.; Jiang, C.F.; Guo, W. Effect of CeO2 on low temperature pressureless sintering of porous Si3N4 ceramics. J. Rare Earths 2017, 35, 172–176. [Google Scholar] [CrossRef]
  18. Alem, A.; Pugh, M.D.; Drew, R.A.L. Reaction bonded silicon nitride foams: The influence of iron disilicide on microstructure and mechanical strength. Ceram. Int. 2015, 41, 4966–4974. [Google Scholar] [CrossRef]
  19. Logesh, G.; Lodhe, M.; Balasubramanian, M. Effect of temperature and gaseous medium on the evolved microstructures of carbon fiber reinforced reaction bonded silicon nitride composites. Ceram. Int. 2017, 43, 6110–6116. [Google Scholar] [CrossRef]
  20. Khajelakzay, M.; Bakhshi, S.R.; Borhani, G.H.; Ramazani, M. Synthesis and spark plasma sintering of the α-Si3N4 nanopowder. Ceram. Int. 2016, 42, 14867–14872. [Google Scholar] [CrossRef]
  21. Peng, G.H.; Li, X.G.; Liang, M.; Liang, Z.H.; Liu, Q.; Li, W.L. Spark plasma sintered high hardness β-Si3N4 composites with MgSiN2 as additives. Scr. Mater. 2009, 61, 347–350. [Google Scholar] [CrossRef]
  22. Cao, L.; Wang, Z.; Yin, Z.; Liu, K.; Yuan, J. Investigation on mechanical properties and microstructure of silicon nitride ceramics fabricated by spark plasma sintering. Mater. Sci. Eng. A 2018, 731, 595–602. [Google Scholar] [CrossRef]
  23. Ji, B.F.; Tian, C.A.; Xie, J.S. Progress and Trend of Spark Plasma Sintering Technology in China. Guangdong Chem. Ind. 2013, 15, 85–86. [Google Scholar]
  24. Liu, K.; Wang, Z.; Yin, Z.; Cao, L.; Yuan, J. Effect of Co content on microstructure and mechanical properties of ultrafine grained WC-Co cemented carbide sintered by spark plasma sintering. Ceram. Int. 2018, 44, 18711–18718. [Google Scholar] [CrossRef]
  25. Evans, A.G.; Charles, E.A. Fracture toughness determinations by indentation. J. Am. Ceram. Soc. 1976, 59, 371–372. [Google Scholar] [CrossRef]
  26. Greskovich, C. Preparation of High-density Si3N4 by a gas-pressure sintering process. J. Am. Ceram. Soc. 1981, 64, 725–730. [Google Scholar] [CrossRef]
  27. Mitomo, M.; Yang, N.; Kishi, Y.; Bando, Y. Influence of powder characteristics on gas pressure sintering of Si3N4. J. Mater. Sci. 1988, 23, 3413–3419. [Google Scholar] [CrossRef]
  28. Li, L.; Gu, L.; Yuan, W.; Zhang, J. Effect of magnesium titanate content on microstructures, mechanical performances and dielectric properties of Si3N4-based composite ceramics. Ceram. Int. 2017, 43, 9906–9911. [Google Scholar] [CrossRef]
  29. Gazzara, C.P.; Messier, D.R. Determination of phase content of Si3N4 by X-Ray diffraction analysis. Am. Ceram. Soc. Bull. 1977, 56, 777–780. [Google Scholar]
Materials 12 01868 g001 550
Figure 1. Relative density of the Si3N4/WC ceramic tool material at different WC and Co contents.
Figure 1. Relative density of the Si3N4/WC ceramic tool material at different WC and Co contents.
Materials 12 01868 g001
Materials 12 01868 g002 550
Figure 2. Vickers hardness and fracture toughness of the Si3N4/WC ceramic tool at different Co content and WC content.
Figure 2. Vickers hardness and fracture toughness of the Si3N4/WC ceramic tool at different Co content and WC content.
Materials 12 01868 g002
Materials 12 01868 g003 550
Figure 3. Bending strength of the Si3N4-based ceramic material containing 10 wt % WC and 1 wt % Co at different temperatures.
Figure 3. Bending strength of the Si3N4-based ceramic material containing 10 wt % WC and 1 wt % Co at different temperatures.
Materials 12 01868 g003
Materials 12 01868 g004a 550Materials 12 01868 g004b 550
Figure 4. SEM micrograph of the Si3N4-based ceramic with 1 wt % Co after being corroded. (a) 5 wt % WC, (b) 10 wt % WC, and (c) 15 wt % WC.
Figure 4. SEM micrograph of the Si3N4-based ceramic with 1 wt % Co after being corroded. (a) 5 wt % WC, (b) 10 wt % WC, and (c) 15 wt % WC.
Materials 12 01868 g004aMaterials 12 01868 g004b
Materials 12 01868 g005 550
Figure 5. Effect of the WC content on the phase composition of the Si3N4-based ceramic material.
Figure 5. Effect of the WC content on the phase composition of the Si3N4-based ceramic material.
Materials 12 01868 g005
Materials 12 01868 g006 550
Figure 6. SEM micrograph of the Si3N4-based ceramic with 10 wt % WC after being corroded. (a) 1 wt % Co, (b) 2 wt % Co, and (c) 4 wt % Co.
Figure 6. SEM micrograph of the Si3N4-based ceramic with 10 wt % WC after being corroded. (a) 1 wt % Co, (b) 2 wt % Co, and (c) 4 wt % Co.
Materials 12 01868 g006
Materials 12 01868 g007 550
Figure 7. Effect of the Co content on the phase composition of Si3N4-based ceramic material at 10 wt % WC.
Figure 7. Effect of the Co content on the phase composition of Si3N4-based ceramic material at 10 wt % WC.
Materials 12 01868 g007

Share and Cite

MDPI and ACS Style

Wang, Z.; Jia, J.; Cao, L.; Sun, N.; Wang, Y. Microstructure and Mechanical Properties of Spark Plasma Sintered Si3N4/WC Ceramic Tools. Materials 2019, 12, 1868. https://0-doi-org.brum.beds.ac.uk/10.3390/ma12111868

AMA Style

Wang Z, Jia J, Cao L, Sun N, Wang Y. Microstructure and Mechanical Properties of Spark Plasma Sintered Si3N4/WC Ceramic Tools. Materials. 2019; 12(11):1868. https://0-doi-org.brum.beds.ac.uk/10.3390/ma12111868

Chicago/Turabian Style

Wang, Zhenhua, Jiheng Jia, Liyan Cao, Ning Sun, and Yulin Wang. 2019. "Microstructure and Mechanical Properties of Spark Plasma Sintered Si3N4/WC Ceramic Tools" Materials 12, no. 11: 1868. https://0-doi-org.brum.beds.ac.uk/10.3390/ma12111868

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop