Next Article in Journal
Synthesis and Biological Evaluation of Amidinourea Derivatives against Herpes Simplex Viruses
Next Article in Special Issue
Molecular and Supramolecular Structures of Triiodides and Polyiodobismuthates of Phenylenediammonium and Its N,N-dimethyl Derivative
Previous Article in Journal
Proteomic Advances in Cereal and Vegetable Crops
Previous Article in Special Issue
Exo⇔Endo Isomerism, MEP/DFT, XRD/HSA-Interactions of 2,5-Dimethoxybenzaldehyde: Thermal, 1BNA-Docking, Optical, and TD-DFT Studies
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Molecules
Volume 26
Issue 16
10.3390/molecules26164926
molecules-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Solution/Ammonolysis Syntheses of Unsupported and Silica-Supported Copper(I) Nitride Nanostructures from Oxidic Precursors

by
Robert Szczęsny
1,2,*,
Tuan K. A. Hoang
1,3,
Liliana Dobrzańska
2 and
Duncan H. Gregory
1,*
1
WestCHEM, School of Chemistry, University of Glasgow, Glasgow G12 8QQ, UK
2
Faculty of Chemistry, Nicolaus Copernicus University in Toruń, Gagarina 7, 87-100 Toruń, Poland
3
Hydro-Québec Research Institute, Hydro-Québec, 1806, Boul. Lionel-Boulet, Varennes, QC J3X 1S1, Canada
*
Authors to whom correspondence should be addressed.
Molecules 2021, 26(16), 4926; https://0-doi-org.brum.beds.ac.uk/10.3390/molecules26164926
Submission received: 6 July 2021 / Revised: 7 August 2021 / Accepted: 11 August 2021 / Published: 14 August 2021
(This article belongs to the Special Issue Inorganic Materials Chemistry)
Browse Figures
Versions Notes

Abstract

:
Herein we describe an alternative strategy to achieve the preparation of nanoscale Cu3N. Copper(II) oxide/hydroxide nanopowder precursors were successfully fabricated by solution methods. Ammonolysis of the oxidic precursors can be achieved essentially pseudomorphically to produce either unsupported or supported nanoparticles of the nitride. Hence, Cu3N particles with diverse morphologies were synthesized from oxygen-containing precursors in two-step processes combining solvothermal and solid−gas ammonolysis stages. The single-phase hydroxochloride precursor, Cu2(OH)3Cl was prepared by solution-state synthesis from CuCl2·2H2O and urea, crystallising with the atacamite structure. Alternative precursors, CuO and Cu(OH)2, were obtained after subsequent treatment of Cu2(OH)3Cl with NaOH solution. Cu3N, in the form of micro- and nanorods, was the sole product formed from ammonolysis using either CuO or Cu(OH)2. Conversely, the ammonolysis of dicopper trihydroxide chloride resulted in two-phase mixtures of Cu3N and the monoamine, Cu(NH3)Cl under similar experimental conditions. Importantly, this pathway is applicable to afford composite materials by incorporating substrates or matrices that are resistant to ammoniation at relatively low temperatures (ca. 300 °C). We present preliminary evidence that Cu3N/SiO2 nanocomposites (up to ca. 5 wt.% Cu3N supported on SiO2) could be prepared from CuCl2·2H2O and urea starting materials following similar reaction steps. Evidence suggests that in this case Cu3N nanoparticles are confined within the porous SiO2 matrix.

Graphical Abstract

1. Introduction

Copper nitride is nontoxic and relatively stable at ambient conditions. It is a semiconductor with high electrical resistivity, low reflectivity, and low thermal stability [1,2,3]. With regard to its potential commercial value and interesting properties, Cu3N has been exploited for applications in optical storage media [4,5,6,7,8], as a component of spintronic systems [9,10], as an electrode material in rechargeable Li- and Na-ion batteries [11,12,13,14] and as a highly active catalyst [15,16,17,18,19]. More specifically, thin films of Cu3N can be utilized in the fabrication of microscopic metal lines, dots, or Cu/Cu3N microscopic structures using electron beam or laser irradiation [7,20,21,22,23,24]. These processes can be implemented effectively by exploiting the inherent thermal instability of copper nitride. Thermal treatment at a moderate temperature decomposes Cu3N into nitrogen and pure metallic copper and the deposited Cu metal unsurprisingly has a significantly higher reflectivity and conductivity than its nitride. Otherwise, the magnetic properties of Cu3N offer applicability in devices as spin valves [7] or can be exploited to examine the spin excitations of antiferromagnetic Mn chains [6]. Cu3N forms a cubic anti-ReO3 type structure (space group Pm-3m) where nitrogen atoms are located at the corners of the primitive unit cell and copper atoms occupy the 3d edge sites. Given the open nature of the structure, in some circumstances, it is possible to insert metal atoms into the interstitial body centre (½,½,½) position [25,26]. According to previous studies, the addition of a transition metal modifies not only the electronic properties of Cu3N but also its magnetic characteristics and, for example, provides a route to magnetic semiconductors [3,27].
Whereas films of copper nitride have primarily been fabricated by physical methods such as reactive RF magnetron sputtering [28,29,30] or pulsed laser deposition (PLD) [31,32], bulk Cu3N was first synthesized by Juza and Rabenau many decades before by heating a CuF2 precursor under gaseous ammonia [33]. The same precursor was utilized by Gregory et al. to prepare gram quantities of copper nitride for powder neutron diffraction studies [34]. A contrasting approach was taken by Zachwieja and Jacobs in 1990 who used nitrate amine “single source” precursors, [Cu(NH3)x]NO3 (2 ≤ x ≤ 3) to prepare Cu3N without the need for ammonia, via a direct thermal decomposition reaction [35]. More recently, however, there has been added interest in the synthesis of different types of Cu3N nanostructures [36,37]. A flurry of different synthesis routes was applied to synthesise nitride nanoparticles, for example by solvothermal methods using copper azide in toluene or THF at moderate temperature [38], by thermal decomposition of Cu(NO3)2 in solutions containing long chain amines as solvents and capping agents [39,40,41], via the reaction of copper(II) acetate with NH3 gas in long-chain alcohol solvents [42] by a one-step process in which copper(II) methoxide reacts with benzylamine [43] or by reduction of Cu(II) to Cu(I) combined with nitridation of Cu(I) by hexamethylenetetramine [44].
Urea (CO(NH2)2) has also been investigated as an alternative—nongaseous—nitrogen source to NH3 [45]. In this work, we utilized CO(NH2)2 for Cu3N fabrication in a two-step process. Urea is soluble in water and its well-known hydrolysis process results in ammonia and carbon dioxide evolution. The thermally induced decomposition of urea in solution causes a relatively slow increase in pH which can be utilized to fabricate nanoparticles [46]. Urea can also play the role of capping and reducing agent in the synthesis of nanoparticles [47]. Moreover, utilizing CO(NH2)2 combined with ethylene glycol (EG) can improve the uniformity of the dispersed precipitate [48].
Generally, the development of facile, inexpensive synthetic methods is especially valuable given the emerging commercial applications of nanomaterials. Synthesis using long-chain amines [39,40,41] is becoming the most-utilized chemical method for the fabrication of Cu3N nanopowders. Implementing this route on a commercial basis is challenging, however, due both to the costs of the required chemicals and to the limits of morphological control that can be exerted [40]. In our approach, we propose important modifications to the classical approach to late transition metal nitride synthesis; namely the reaction of a suitable precursor in gaseous ammonia. Importantly, ammonolysis does not change the initial shape of the nanoparticles and so by using prescribed precursor morphologies, it is possible to exert intricate control over the copper nitride nanostructure. Moreover, ammonolysis can be applied to composite materials including substrates or matrices that are resistant to interaction with NH3 at temperatures of approximately 300 °C or less. We reveal experimental results here that demonstrate that exploiting oxygen-containing inorganic precursors, such as CuO and Cu(OH)2 in ammonolysis reactions, leads to the formation of single-phase Cu3N under a range of experimental conditions. Furthermore, Cu3N composites can be produced in the same way. A range of such experiments illustrates the diversity of Cu3N-based nanomaterials that can be fabricated by this precise two-step approach. In each case, the desired morphology is prescribed by the precursor design in step 1. Simple heating in ammonia then yields Cu3N pseudomorphically in step 2.
In this paper, as an example of this approach, copper(II) chloride dihydrate was used as a precursor for the fabrication of copper(II) oxide and copper(II) hydroxide nanoarchitectures (via synthesis of the hydroxide chloride, Cu2(OH)3Cl). The preparation of copper nitride micro- and nanostructures was then realized by ammonolysing the Cu(OH)2 and CuO nanoparticle precursors. Cu3N/SiO2 nanocomposites comprising Cu3N nanoparticles supported on silica could be assembled using the same precursors in closely related protocols. This is the first time that systematic studies of supported and unsupported Cu3N nanostructures synthesized by this method have been performed. As we demonstrate, the synthetic method can be applied to the growth of different shapes and sizes of nanocrystalline copper nitride, which, despite evidence of negligible porosity when unsupported, can nevertheless display specific surface areas of up to 45 m2 g−1.

2. Results and Discussion

2.1. Synthesis and Ammonolysis Reactions

In a typical synthesis, copper(II) chloride CuCl2·2H2O (3 mmol) was dissolved in a water/EG mixture (28 cm3; v/v, 1:8.3) in a round-bottomed flask to which CO(NH2)2 (17 mmol) was added with constant stirring. The resultant light green solution was heated to 95 °C over a period of 1.5–2.5 h. During the reaction, a green precipitate of Cu2(OH)3Cl formed from a deep blue solution. The final solid product was collected by centrifuging and was washed with water and alcohol several times before dispersing in acetone. A jade-green precipitate of Cu2(OH)3Cl was obtained from the remaining deep navy blue solution after leaving to stand at ambient temperature in air for several days.
To prepare CuO powder, a 0.01 M solution of NaOH was added dropwise into the previously described green Cu2(OH)3Cl powders dispersed in EtOH with constant stirring until a black precipitate formed. A very similar method was used to prepare Cu(OH)2 powder, with the exception that a few drops of NH3 (aq) were added to the Cu2Cl(OH)3 water dispersion prior to adding the 0.01 M NaOH solution. Both the oxide and hydroxide products were centrifuged, washed and then dispersed in acetone. The synthesis route is shown schematically in Figure 1.
As-received SiO2 aerogel is highly hydrophilic, with multiple -OH groups on the surface. The treatment of initial SiO2 with trimethylsilyl chloride was done as described in literature to completely remove the hydrophilicity on the surface [49,50,51]. The Cu3N/SiO2 composite preparation procedure was similarly congruent to the synthesis of the unsupported Cu3N nanoparticles by Cu(OH)2 powder and resulted in a final Cu3N loading of 3.3 or 5.4 wt.% on the SiO2 support. The Cu: urea molar ratio used in this process was 1:5. For a lower final load, the mixture of the CuCl2·2H2O salt, urea and SiO2 in H2O was stirred for 2 h at room temperature before heating. A few drops of 0.5 M NH3 (aq) were then added prior to adding NaOH dropwise until a blue solution was obtained. The resulting suspension was centrifuged, washed with deionized water and acetone before dispersing in acetone.
The ammonolysis experiments were performed in a horizontal tube furnace using NH3 gas (BOC, 99.98%) as the nitriding agent. In each reaction, the dry precursor powder was placed in a ceramic boat (60 mm × 20 mm × 20 mm) and transferred to the centre of the furnace. Reaction temperatures between 240–310 °C were selected (see below) and in all cases, the maximum temperatures were reached in ~45 min. The furnace was allowed to cool naturally under flowing NH3.

2.2. Characterization and Ammonolysis Reaction of Copper(II) Hydroxide Chloride Nanoparticles

In the first step of our investigation, simple copper chloride nanoparticles were synthesized under various conditions. A SEM image of the powders obtained with CuCl2·H2O/CO(NH2)2 and GE/H2O molar ratios of 1:6 and 8.3:1 respectively (A) is presented in Figure 2a. In the case of A, a fine powder was obtained. The morphology and composition of the products were not affected by the gaseous environment (air or argon) in which the reactions were performed. SEM images for powder B fabricated under different conditions (using CuCl2·H2O/CO(NH2)2 and GE/H2O molar ratios of 1:5 and 6.7:1, respectively) revealed that the prepared particles take a cubic form with dimensions of ca. 300–500 nm across (Figure 2b).
The cubes form large spatial systems. Results from PXD and FT-IR experiments for the as-prepared samples (A and B) indicated the presence of Cu2(OH)3Cl. According to the literature, natural copper(II) hydroxide chloride, Cu2(OH)3Cl, exists in nature in four different mineral phases: atacamite, botallackite, paratacamite, and clinoatacamite [52,53]. Figure 3a shows a PXD pattern of the formed product (sample A). All the diffraction peaks could be indexed according to the orthorhombic atacamite structure. For A, indexing yielded a unit cell in the space group Pnma with lattice parameters of a = 6.030(2) Å, b = 9.120(2) Å, c = 6.865(2) Å, which are in good agreement with the reported literature values [54].
The solution synthesis of Cu2(OH)3Cl powders has been previously described using NaOH/H2O2 [55], (NH4)2CO3 [56] or CO(NH2)2 [57]. In the last of these alternatives, the formation of Cu2(OH)3Cl from the hydrothermal reaction of copper(II) chloride and urea involves a hydrolysis−precipitation process. Urea is unstable under heating in aqueous solution and slowly liberates OH− which reacts with Cu2+ and Cl− in the reaction vessel to yield a green precipitate according to reactions:
CO(NH2)2 + 3H2O → 2OH− + 2NH4+ + CO2,
2Cu2+ + 3OH− + Cl− → Cu2(OH)3Cl.
Ammonolysis experiments using A as a precursor were performed at three different reaction temperatures (240, 300 and 330 °C) for 4 h. The SEM images of the products heated under NH3 reveal that the initial particle shape was not completely preserved, with clusters of nanoparticles aggregating to form semiporous “cake-like” structures (Figure 2c). For each reaction temperature used, the composition of the product was identical and according to PXD data, a two-phase product consisting of Cu3N and Cu(NH3)Cl (Figure 3b) was obtained [58]. Phase fractions (wt%) were estimated using profile fitting within the PowderCell software package [59] and, as an example, a sample heated at 330 °C contained approximately 41% Cu3N and 59% Cu(NH3)Cl. IR measurements supported this analysis, with spectra clearly demonstrating the presence of N−H stretching and bending bands from the copper(I) monoamine phase at 3295, 3241 cm−1 (νasNH), 3160 cm−1 (νsNH), 1594 cm−1 (δa(NH3)) and 1240 cm−1 (δs(NH3)) [60]. The presence of copper nitride was also confirmed by a broad IR band at 664 cm−1 [61].

2.3. Characterization and Ammonolysis Reaction of Copper(II) Oxide and Copper(II) Hydroxide Nanoparticles

As shown in the scheme in Figure 1, the reaction of Cu2(OH)3Cl with NaOH resulted in copper(II) oxide, which was obtained as a fine black powder product. The further addition of NH3(aq) led to the transformation of the initial fine powder to the nanoneedles or star-like particles of Cu(OH)2 (Figure 4a–c), depending on the reaction conditions. The identities of the synthesized CuO (see Figure 4d) and Cu(OH)2 powders were confirmed by PXD; all the diffraction peaks in the patterns could be assigned to either CuO (ICDD PDF card No. 05-0661) or Cu(OH)2 (ICDD PDF card No. 72-0140), respectively, and no impurity peaks were observed in either case. A mechanism for the conversion of copper(II) chloride in 0.01 M NaOH has been previously suggested in the literature [62]. SEM analysis in this previous case indicated an initial “etching” of the crystals of the starting material in the basic solution. The growth of needle-like structures on the crystalline surface was observed as the etching continued. The previous authors assumed a mechanism in which NaOH reacts with Cu2(OH)3Cl crystals and Cl− is replaced at the interface with OH− (Equation (3)). Strong deformations of the internal bulk structures occur as a result. Copper(II) hydroxide is known to form needle-like crystals in aqueous solution and “sisal-like” structures subsequently grow along the radical direction.
Cu2(OH)3Cl + OH− → 2Cu(OH)2 + Cl−
In previous studies, CuO formation was realized by thermal treatment of the hydroxide. In our experiment copper(II) oxide occurred directly in solution, probably due to the synergistic effect of using ethanol as a solvent combined with a concentration of NaOH ten times less (influencing the pH accordingly) [63]. The solubility of CO(OH)2 and CuO in the ethanol-water system should also be considered and in the case of aqueous solutions, this difference is relatively large; the solubility of Cu(OH)2 = 1.3 × 10−5 mol L−1 as compared to 2 × 10−7 mol L−1 for CuO [64].
The oxide and hydroxide samples were then heated under gaseous ammonia and the ensuing products were characterized by PXD (Figure 5), SEM (Figure 6) and BET. According to these experiments, the optimal conditions for the synthesis of phase-pure copper nitride are to use a temperature of 300 °C and a heating time of 300 min (Table 1).
Perhaps surprisingly, some experiments resulted in three-phase compositions (e.g., sample 4), with the presence of all three common copper oxidation states (+2, +1 and 0; resulting from dehydration, nitridation and complete reduction, respectively). It is interesting to note that applying the selected precursors under the prescribed conditions led to pseudomorphic transformations from each precursor to copper nitride (Figure 6a,b).
Nitrogen adsorption−desorption experiments performed on different copper nitride samples commonly yield type II isotherms, which are typical for nonporous solids [65]. These adsorption isotherms are essentially linear in the range of P/Po = 0–0.7 and condensation adsorption emerges in the region starting from P/Po~0.8 to 1.0. The specific surface area for the samples obtained from the Cu(OH)2 precursor shows a value of approximately 45 m2 g−1.
The total pore volume, however, was observed to be as low as ~0.15 cm3 g−1, essentially confirming that the material was nonporous. In the case of Cu3N fabricated from a copper oxide precursor, the BET surface area is lower and is manifestly dependent on the precursor synthesis route; CuO powders synthesized from A and B in turn produced copper nitride materials with specific surface areas of 37 m2 g−1 and 4 m2 g−1, respectively. These materials were also nonporous.

2.4. Synthesis of Cu3N/SiO2 Composites

Nanoparticles of binary inorganic copper compounds can provide a very interesting alternative to homogeneous copper complex catalysts for the cycloaddition of terminal alkynes and azides (such as the Huisgen 1,3-dipolar cycloaddition; HDC) and fulfil the requirements of a “click reaction” [66]. With such applications in mind, we were interested in exploring the precursor routes used here in the synthesis of supported Cu3N nanomaterials. To this end, we utilized copper(II) chloride as a precursor for the preparation of copper nitride supported on silica, Cu3N/SiO2. To achieve this, we modified the Cu3N synthesis process such that Cu3N/SiO2 nanocomposites could be achieved in a series of simple steps comprising: (i) silica modification; (ii) incorporation of Cu2(OH)3Cl into silica; (iii) conversion of Cu2(OH)3Cl + silica into a Cu(OH)2/SiO2 nanocomposite and (iv) ammonolysis of the Cu(OH)2/SiO2 precursor to yield Cu3N/SiO2.
The Cu(OH)2/SiO2 nanocomposites were prepared as detailed in the experimental section. Ammonolysis reactions using the Cu(OH)2/SiO2 precursor were performed at 250, 300 and 310 °C (over a period of 4–5 h). After heating under gaseous NH3, the initially blue powders became either grey or light red in colour. Despite the colour change, only amorphous-appearing PXD patterns were observed for, e.g., a sample heated for 4 h at 250 °C (Figure 7a). This may suggest that the Cu3N particles are of submicron dimensions and/or possess no long-range structural order, hence producing no Bragg reflections. Alternatively, the low wt.% loading of Cu3N particles might be constricted inside the internal porosity of the SiO2 matrix (support), rendering them undetectable in the X-ray diffraction patterns.
On ammoniating a nanocomposite sample at 310 °C, PXD showed that the product was the intended Cu3N/SiO2 material (Figure 7b). Only two examples of Cu3N/SiO2 materials exist in the literature [67,68]. The impregnation of SiO2 by a Cu(II) salt in solution followed by deposition–precipitation is an effective way to fabricate oxidic copper-based SiO2 composites [69,70]. We have shown that such combined impregnation−deposition–precipitation approaches work equally well for nitride-SiO2 composites. Our early-stage observations are currently being followed by wider, systematic studies of the ammonolysis of supported materials, which will be reported in due course.
It is useful to consider the absorption behavior of both the silica host and the Cu3N/SiO2 nanocomposite and the resulting implications for the specific surface area of the materials (Figure 8a,b). The pristine SiO2 aerogel exhibits a total adsorption volume of 1125.054 cm3 g−1. Once modified (with trimethyl silyl chloride) the total adsorption of the silica dropped slightly to 1075.616 cm3 g−1. Although this constituted a 4.40% drop in the total sorption capacity, there was otherwise little difference in the adsorption behavior (as perceived from the nitrogen sorption isotherms) of the silica before and after treatment with trimethyl silyl chloride. There were fundamental changes in the internal porosity, however, and when considering the incremental pore volume (Figure 8b), the pore size distribution became narrower and sharper after the treatment (but otherwise remained in the mesoporous range).
By comparison, the Cu3N/SiO2 nanocomposite had a very limited nitrogen adsorption ability, with a total adsorption of 49.345 cm3 g−1. This constitutes a 95.41% drop in the total nitrogen sorption and hence, in relative terms, the pore volume almost disappears. This could be a reflection of the fact that the Cu3N nanoparticles were confined within the modified-SiO2 aerogel, with uniform particle size of the same order of magnitude as the pore size of the host—approximately 21–22 nm.

3. Materials and Methods

3.1. Starting Materials

Copper(II) chloride dihydrate, sodium hydroxide, urea, ammonium hydroxide solution (25% NH3 in H2O) and ethylene glycol (EG) were used as received (Sigma-Aldrich, St. Louis, MO, USA). The silica support material, Aerosil-200 was provided by Evonik free of charge. The silica was modified prior to use by treating with trimethyl silyl chloride (Sigma-Aldrich, St. Louis, MO, USA).

3.2. Materials Characterization

All products were characterized by powder X-ray diffraction (PXD) using either a Philips XPERT Pro θ-2θ (Malvern Panalytical Ltd., Malvern, UK) or a Bruker D8 diffractometer (Bruker AXS, Karlsruhe, Germany) with CuKα or CuKα1 radiation, respectively. Whereas PXD data for the final products were collected directly from powders, PXD data for the precursors were collected from samples dispersed in acetone dropped onto the PXD sample holder. Phase identification was performed by search-match procedures with access to the International Centre for Diffraction Data (ICDD) powder diffraction file (PDF) and by comparison to patterns generated from Inorganic Crystal Structure Database (ICSD) data using PowderCell v.2.3 [59]. Scanning electron microscopy (SEM) was performed by using three instruments: first, a Philips XL 30 environmental (E)SEM equipped with an Oxford Instruments INCA Energy 250 energy dispersive X-ray (EDX) spectrometer (EHT = 20 kV, spot size 5), second, a LEO 1430 VP (LEO Electron Microscopy Ltd., Cambridge, UK) microscope equipped with a Quantax 200 (XFlash 4010 detector, Bruker AXS, Karlsruhe, Germany) EDX spectrometer (HV mode, SE, EHT = 10–20 kV, beam current 100 μA), and finally a Quanta 3D FEG instrument (FEI, Hillsboro, OR, USA) (EHT = 30 kV). The samples were imaged without coating and were placed onto carbon tabs fixed to aluminium SEM stubs. Qualitative analysis of bonding was performed by Fourier transform infrared spectroscopy (FTIR; Shimadzu 8400S spectrometer, Shimadzu Corp., Kyoto, Japan). The surface areas of the synthesized powders were determined by applying BET analysis to nitrogen adsorption−desorption data, which were registered at liquid nitrogen temperature using a Micromeritics Gemini instrument (Norcross, GA, USA).

4. Conclusions

These studies demonstrate that copper nitride powders can be successfully synthesized from a range of oxygen-containing inorganic precursors. With the correct choice of experimental parameters, nitridation is favored over simple reduction. The choice of precursor and synthesis conditions enables the size and morphology of the nitride micro- and nanoparticles to be manipulated. Each of the precursors—Cu2(OH)3Cl, Cu(OH)2 and CuO—can be prepared from a copper(II) chloride starting material by urea hydrolysis in an ethylene glycol/water medium below 100 °C. The first of these precursors, Cu2(OH)3Cl, has limited utility in the preparation of Cu3N, however, since not only is the ammonolysis process not pseudomorphic (thus offering little morphology control), but it also proves challenging to prepare Cu3N without the presence of the copper(I) monoamine, Cu(NH3)Cl.
Alternatively, the Cu2(OH)3Cl precursor can be converted to Cu(OH)2 or CuO in solution by the addition of NaOH/NH4OH. The advantage of these solution syntheses is that CuO nanoparticles can be obtained quickly and without heating, retaining a similar morphology to the copper(II) chloride starting material. Similarly, nanostructured Cu(OH)2 can be obtained from the chloride in solution, forming as needles on the nanoscale. Both CuO and Cu(OH)2 precursors are successful in producing single-phase Cu3N under a range of experimental conditions. At an elevated temperature (of ca. 330 °C and above), the nitride seemingly decomposes, with copper metal as the predominant product. Preliminary observations suggest that mesoporous silica can act as an efficient support for Cu3N. Importantly, modification with trimethylsilyl chloride removes the hydrophilicity from the surface of SiO2 aerogel to enable successful ammoniation of Cu(OH)2/SiO2 composites. Thus, we successfully synthesized Cu3N/modified-SiO2-aerogel nanocomposites and the hydrolysis decomposition of Cu3N by solid-state acidic media was completely excluded.

Author Contributions

Conceptualization, R.S.; methodology, R.S., D.H.G.; investigation, R.S., T.K.A.H.; data analysis, D.H.G., R.S., T.K.A.H., L.D.; writing—original draft preparation, R.S., T.K.A.H., D.H.G., L.D.; writing—review and editing, R.S., D.H.G., L.D., T.K.A.H.; visualization, R.S., T.K.A.H., L.D.; supervision, D.H.G., R.S.; funding acquisition, D.H.G., R.S. All authors have read and agreed to the published version of the manuscript.

Funding

This research was funded by University of Glasgow, the GROWTH (WZROST) project (“Enhancing Educational Potential of Nicolaus Copernicus University in the Disciplines of Mathematical and Natural Sciences”), EPSRC grant ref. EP/I022570/1.

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

Data is contained within the article.

Conflicts of Interest

The authors declare no conflict of interest. The funders had no role in the design of the study; in the collection, analyses, or interpretation of data; in the writing of the manuscript, or in the decision to publish the results.

Sample Availability

The samples are not available from the authors.

References

  1. Ścigała, A.; Szłyk, E.; Dobrzańska, L.; Gregory, D.H.; Szczęsny, R. From binary to multinary copper based nitrides–Unlocking the potential of new applications. Coord. Chem. Rev. 2021, 436, 213791. [Google Scholar] [CrossRef]
  2. Reichert, M.D.; White, M.A.; Thompson, M.J.; Miller, G.J.; Vela, J. Preparation and instability of nanocrystalline cuprous nitride. Inorg. Chem. 2015, 54, 6356–6362. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  3. Szczęsny, R.; Szłyk, E.; Wiśniewski, M.; Hoang, T.K.A.; Gregory, D.H. Facile preparation of copper nitride powders and nanostructured films. J. Mater. Chem. C 2016, 4, 5031–5037. [Google Scholar] [CrossRef] [Green Version]
  4. Ji, Z.; Zhang, Y.; Yuan, Y.; Wang, C. Reactive DC magnetron deposition of copper nitride films for write-once optical recording. Mater. Lett. 2006, 60, 3758–3760. [Google Scholar] [CrossRef]
  5. Cremer, R.; Witthaut, M.; Neuschütz, D.; Trappe, C.; Laurenzis, M.; Winkler, O.; Kurz, H. Deposition and Characterization of Metastable Cu3N Layers for Applications in Optical Data Storage. Mikrochim. Acta 2000, 133, 299–302. [Google Scholar] [CrossRef]
  6. Cui, X.Y.; Soon, A.; Phillips, A.E.; Zheng, R.K.; Liu, Z.W.; Delley, B.; Ringer, S.P.; Stampil, C. First principles study of 3d transition metal doped Cu3N. J. Magn. Magn. Mater. 2012, 324, 3138–3143. [Google Scholar] [CrossRef]
  7. Yue, G.H.; Yan, P.X.; Liu, J.Z.; Wang, M.X.; Li, M.; Yuan, X.M. Copper nitride thin film prepared by reactive radio-frequency magnetron sputtering. J. Appl. Phys. 2005, 98, 103506. [Google Scholar] [CrossRef]
  8. Zhao, Y.; Zhao, J.; Yang, T.; Zhang, J.; Yang, J.; Li, X. Enhanced write-once optical storage capacity of Cu3N film by coupling with an Al2O3 protective layer. Ceram. Int. 2016, 42, 4486–4490. [Google Scholar] [CrossRef]
  9. Hirjibehedin, C.F.; Lutz, C.P.; Heinrich, A.J. Spin coupling in engineered atomic structures. Science 2006, 312, 1021–1024. [Google Scholar] [CrossRef]
  10. Navio, C.; Alvarez, J.; Capitan, M.J.; Camarero, J.; Miranda, R. Thermal stability of Cu and Fe nitrides and their applications for writing locally spin valves. Appl. Phys. Lett. 2009, 94, 263112. [Google Scholar] [CrossRef] [Green Version]
  11. Pereira, N.; Dupont, L.; Tarascon, J.M.; Klein, L.C.; Amatucci, G.G. Electrochemistry of Cu3 N  with lithium: A complex system with parallel processes. J. Electrochem. Soc. 2003, 150, A1273–A1280. [Google Scholar] [CrossRef]
  12. Xianji, L.; Hector, A.L.; Owen, J.R. Evaluation of Cu3N and CuO as negative electrode materials for sodium batteries. J. Phys. Chem. C 2014, 118, 29568–29573. [Google Scholar]
  13. Chen, W.; Zhang, H.; Yang, B.; Li, B.; Li, Z. Characterization of Cu3N/CuO thin films derived from annealed Cu3N for electrode application in Li-ion batteries. Thin Solid Films 2019, 672, 157–164. [Google Scholar] [CrossRef]
  14. Lee, D.; Sun, S.; Kwon, J.; Park, H.; Jang, M.; Park, E.; Son, B.; Jung, Y.; Song, T.; Paik, U. Copper nitride nanowires printed Li with stable cycling for Li metal batteries in carbonate electrolytes. Adv. Mater. 2020, 32, 1905573. [Google Scholar] [CrossRef]
  15. Xi, P.; Xu, Z.; Gao, D.; Chen, F.; Xue, D.; Tao, C.-L.; Chen, Z.-N. Solvothermal synthesis of magnetic copper nitride nanocubes with highly electrocatalytic reduction properties. RSC Adv. 2014, 4, 14206–14209. [Google Scholar] [CrossRef]
  16. Su, C.-Y.; Liu, B.-H.; Lin, T.-J.; Chi, Y.-M.; Kei, C.-C.; Wang, K.-W.; Perng, T.-P. Carbon nanotube-supported Cu3N nanocrystals as a highly active catalyst for oxygen reduction reaction. Mater. Chem. A 2015, 3, 18983–18990. [Google Scholar] [CrossRef]
  17. Yin, Z.; Yu, C.; Zhao, Z.; Guo, X.; Shen, M.; Li, N.; Muzzio, M.; Li, J.; Liu, H.; Lin, H.; et al. Cu3N Nanocubes for Selective Electrochemical Reduction of CO2 to Ethylene. Nano Lett. 2019, 19, 8658–8663. [Google Scholar] [CrossRef] [PubMed]
  18. Wang, Q.; Zhang, Z.; Zhao, X.; Xiao, J.; Manoj, D.; Wei, F.; Xiao, F.; Wang, H.; Wang, S. MOF-derived copper nitride/phosphide heterostructure coated by multi-doped carbon as electrocatalyst for efficient water splitting and neutral-pH hydrogen evolution reaction. ChemElectroChem 2020, 7, 289–298. [Google Scholar] [CrossRef]
  19. Liang, Z.-Q.; Zhuang, T.-T.; Seifitokaldani, A.; Li, J.; Huang, C.-W.; Tan, C.-S.; Li, Y.; De Luna, P.; Dinh, C.T.; Hu, Y.; et al. Copper-on-nitride enhances the stable electrosynthesis of multi-carbon products from CO2. Nat. Commun. 2018, 9, 3828. [Google Scholar] [CrossRef]
  20. Nosaka, T.; Yoshitakea, M.; Okamoto, A.; Ogawa, S.; Nakayama, Y. Thermal decomposition of copper nitride thin films and dots formation by electron beam writing. Appl. Surf. Sci. 2001, 169–170, 358–361. [Google Scholar] [CrossRef]
  21. Maruyama, T.; Morishita, T. Copper nitride and tin nitride thin films for write-once optical recording media. Appl. Phys. Lett. 1996, 69, 890–891. [Google Scholar] [CrossRef] [Green Version]
  22. Li, X.; Liu, Z.; Zuo, A.; Yuan, Z.; Yang, J.; Yao, K. Properties of Al-doped copper nitride films prepared by reactive magnetron sputtering. J. Wuhan Univ. Technol. Mater. Sci. Ed. 2007, 22, 446–449. [Google Scholar] [CrossRef]
  23. Borsa, D.M.; Grachev, S.; Presura, C.; Boerma, D.O. Growth and properties of Cu3N films and Cu3N/γ′-Fe4N bilayers. Appl. Phys. Lett. 2002, 80, 1823–1825. [Google Scholar] [CrossRef] [Green Version]
  24. Du, Y.; Yin, Y.; Wang, J.; Wang, Z.; Li, C.; Baunack, S.; Ma, L.; Schmidt, O.G. Nanoporous copper pattern fabricated by electron beam irradiation on Cu3N film for SERS application. Phys. Status Solidi B 2019, 256, 1800378. [Google Scholar] [CrossRef]
  25. Pierson, J.F.; Horwat, D. Addition of silver in copper nitride films deposited by reactive magnetron sputtering. Script. Mater. 2008, 58, 568–570. [Google Scholar] [CrossRef]
  26. Hahn, U.; Weber, W. Electronic structure and chemical-bonding mechanism of Cu3N, Cui3NPd, and related Cu(I) compounds. Phys. Rev. B 1996, 53, 12684–12693. [Google Scholar] [CrossRef]
  27. Ding, J.-N.; Yuan, N.-Y.; Li, F.; Ding, G.-Q.; Chen, Z.G.; Chen, X.S.; Lu, W. Geometry and stability of CunN (n=1–6), and CunN (n=1–5) clusters. J. Chem. Phys. 2009, 131, 174102. [Google Scholar] [CrossRef] [PubMed]
  28. Liu, Z.Q.; Wang, W.J.; Wang, T.M.; Chao, S.; Zheng, S.K. Thermal stability of copper nitride films prepared by rf magnetron sputtering. Thin Solid Films 1998, 325, 55–59. [Google Scholar] [CrossRef]
  29. Wang, J.; Chen, J.T.; Yuan, X.M.; Wu, Z.G.; Miao, B.B.; Yan, P.X. Copper nitride (Cu3N) thin films deposited by RF magnetron sputtering. J. Cryst. Growth 2006, 286, 407–412. [Google Scholar] [CrossRef]
  30. Wilczopolska, M.; Nowakowska-Langier, K.; Okrasa, S.; Skowronski, L.; Minikayev, R.; Strzelecki, G.W.; Chodun, R.; Zdunek, K. Synthesis of copper nitride layers by the pulsed magnetron sputtering method carried out under various operating conditions. Materials 2021, 14, 2694. [Google Scholar] [CrossRef]
  31. Soto, G.; Díaz, J.A.; de la Cruz, W. Copper nitride films produced by reactive pulsed laser deposition. Mater. Lett. 2003, 57, 4130–4133. [Google Scholar] [CrossRef]
  32. Gallardo-Vega, C.; de la Cruz, W. Study of the structure and electrical properties of the copper nitride thin films deposited by pulsed laser deposition. Appl. Surf. Sci. 2006, 252, 8001–8004. [Google Scholar] [CrossRef]
  33. Juza, R.; Hahn, H. Antisomorphie von Cu3N mit ReO3. Z. Anorg. Allg. Chem. 1939, 241, 172–178. [Google Scholar] [CrossRef]
  34. Paniconi, G.; Stoeva, Z.; Doberstein, H.; Smith, R.I.; Gallagher, B.L.; Gregory, D.H. Structural chemistry of Cu3N powders obtained by ammonolysis reactions. Sol. State Sci. 2007, 9, 907–913. [Google Scholar] [CrossRef]
  35. Zachwieja, U.; Jacobs, H. Ammonothermalsynthese von kupfernitrid, Cu3N. J. Less-Common Met. 1990, 161, 175–184. [Google Scholar] [CrossRef]
  36. Scigala, A.; Szłyk, E.; Rerek, T.; Wiśniewski, M.; Skowronski, L.; Trzcinski, M.; Szczesny, R. Copper nitride nanowire arrays—comparison of synthetic approaches. Materials 2021, 14, 603. [Google Scholar] [CrossRef]
  37. Sithole, R.K.; Machogo, L.F.E.; Moloto, M.J.; Gqoba, S.S.; Mubiayi, K.P.; Van Wyk, J.; Moloto, N. One-step synthesis of Cu3N, Cu2S and Cu9S5 and photocatalytic degradation of methyl orange and methylene blue. J. Photochem. Photobiol. A Chem. 2020, 397, 112577. [Google Scholar] [CrossRef]
  38. Choi, J.; Gillan, E.G. Solvothermal synthesis of nanocrystalline copper nitride from an energetically unstable copper azide precursor. Inorg. Chem. 2005, 44, 7385–7393. [Google Scholar] [CrossRef]
  39. Wu, H.; Chen, W. Copper nitride nanocubes: Size-controlled synthesis and application as cathode catalyst in alkaline fuel cells. J. Am. Chem. Soc. 2011, 133, 15236–15239. [Google Scholar] [CrossRef] [PubMed]
  40. Kadzutu-Sithole, R.; Machogo-Phao, L.F.E.; Kolokoto, T.; Zimuwandeyi, M.; Gqoba, S.S.; Mubiayi, K.P.; Moloto, M.J.; Van Wyk, J.; Moloto, N. Elucidating the effect of precursor decomposition time on the structural and optical properties of copper(I) nitride nanocubes. RSC Adv. 2020, 10, 34231–34246. [Google Scholar] [CrossRef]
  41. Barman, D.; Paul, S.; Ghosh, S.; De, S.K. Cu3N nanocrystals decorated with Au nanoparticles for photocatalytic degradation of organic dyes. ACS Appl. Nano Mater. 2019, 2, 5009–5019. [Google Scholar] [CrossRef]
  42. Nakamura, T.; Hayashi, H.; Hanaoka, T.; Ebina, T. Preparation of copper nitride (Cu3N) nanoparticles in long-chain alcohols at 130–200 °C and nitridation mechanism. Inorg. Chem. 2014, 53, 710–715. [Google Scholar] [CrossRef] [PubMed]
  43. Deshmukh, R.; Zeng, G.; Tervoort, E.; Staniuk, M.; Wood, D.; Niederberger, M. Ultrasmall Cu3N nanoparticles: Surfactant-Free solution-phase synthesis, nitridation mechanism, and application for lithium storage. Chem. Mater. 2015, 27, 8282–8288. [Google Scholar] [CrossRef]
  44. Mondal, S.; Raj, C.R. Copper nitride nanostructure for the electrocatalytic reduction of oxygen: Kinetics and reaction pathway. J. Phys. Chem. C 2018, 122, 18468–18475. [Google Scholar] [CrossRef]
  45. Nakamura, T.; Hayashi, H.; Ebina, T. Preparation of copper nitride nanoparticles using urea as a nitrogen source in a long-chain alcohol. J. Nanoparticle Res. 2014, 16, 2699. [Google Scholar] [CrossRef]
  46. Marinho, J.Z.; Romeiro, F.C.; Lemos, S.C.S.; Motta, F.V.; Riccardi, C.S.; Li, M.S.; Longo, E.; Lima, R.C. Urea-based synthesis of zinc oxide nanostructures at low temperature. J. Nanomater. 2012, 2012, 427172. [Google Scholar] [CrossRef]
  47. Sreekanth, T.V.M.; Nagajyothi, P.C.; Reddy, G.R.; Shim, J.; Yoo, K. Urea assisted ceria nanocubes for efficient removal of malachite green organic dye from aqueous system. Sci. Rep. 2019, 9, 14477. [Google Scholar] [CrossRef] [Green Version]
  48. Hai, C.; Li, S.; Zhou, Y.; Zeng, J.; Ren, X.; Li, X. Roles of ethylene glycol solvent and polymers in preparing uniformly distributed MgO nanoparticles. J. Asian Ceram. Soc. 2017, 5, 176–182. [Google Scholar] [CrossRef] [Green Version]
  49. Gokulakrishnan, N.; Parmentier, J.; Trzpit, M.; Vonna, L.; Paillaud, J.-L.; Soulard, M. Intrusion/extrusion of water into organic grafted SBA-15 silica materials for energy storage. J. Nanosci. Nanotechnol. 2013, 13, 2847–2852. [Google Scholar] [CrossRef]
  50. Capel-Sanchez, M.C.; Barrio, L.; Campos-Martin, J.M.; Fierro, J.L.G. Silylation and surface properties of chemically grafted hydrophobic silica. J. Colloid Interface Sci. 2004, 277, 146–153. [Google Scholar] [CrossRef]
  51. Belyakova, L.A.; Varvarin, A.M. Surfaces properties of silica gels modified with hydrophobic groups. Colloids Surf. A Physicochem. Eng. Asp. 1999, 154, 285–294. [Google Scholar] [CrossRef]
  52. Pollard, A.M.; Thomas, R.G. Synthesis and stabilities of the basic copper(II) chlorides atacamite, paratacamite and botallackite. Mineralog. Mag. 1989, 53, 557–563. [Google Scholar] [CrossRef]
  53. Lee, S.C.; Park, S.-H.; Lee, S.M.; Lee, J.B.; Kim, H.J. Synthesis and H2 uptake of Cu2(OH)3Cl, Cu(OH)2 and CuO nanocrystal aggregate. Catal. Tod. 2007, 120, 358–362. [Google Scholar] [CrossRef]
  54. Anthony, J.W.; Bideaux, R.A.; Bladh, K.W.; Nichols, M.C. Handbook of Mineralogy; Mineralogical Society of America: Chantilly, VA, USA; Available online: http://www.handbookofmineralogy.org/ (accessed on 28 June 2021).
  55. Yang, X.; Zhang, Q.; Gu, W.; Teng, F. Facile self-assembly of uniform Cu2Cl(OH)3 nanoflowers and its photo-Fenton degradation performance for dye wastewater. J. Cryst. Growth 2020, 541, 125681. [Google Scholar] [CrossRef]
  56. Zhu, C.; Chen, C.; Hao, L.Y.; Hu, Y.; Chen, Z.Y. Template-free synthesis of Cu2Cl(OH)3 nanoribbons and use as sacrificial template for CuO nanoribbon. J. Cryst. Growth 2004, 263, 473–479. [Google Scholar] [CrossRef]
  57. Jia, W.; Reitz, E.; Sun, H.; Li, B.; Zhang, H.; Lei, Y. From Cu2(OH)3Cl to nanostructured sisal-like Cu(OH)2 and CuO: Synthesis and characterization. J. Appl. Phys. 2009, 105, 064917. [Google Scholar] [CrossRef]
  58. Margraf, G.; Bats, J.W.; Bolte, M.; Lerner, H.W.; Wagner, M. One- and three-dimensional infinite arrays of Cu(I) ions exhibited by [Cu(NH3)2]Br and [Cu(NH3)Cl] in the solid state. Chem. Commun. 2003, 956–957. [Google Scholar] [CrossRef]
  59. Kraus, W.; Nolze, G. POWDER CELL–A program for the representation and manipulation of crystal structures and calculation of the resulting X-ray powder patterns. J. Appl. Cryst. 1996, 29, 301–303. [Google Scholar] [CrossRef]
  60. Patil, K.C.; Secco, E.A. Metal halide ammines. II. thermal analyses, calorimetry and infrared spectra of fluoride ammines and hydrates of bivalent metals. Can. J. Chem. 1972, 50, 567–573. [Google Scholar] [CrossRef] [Green Version]
  61. Nakamoto, K. Infrared and Raman Spectra of Inorganic and Coordination Compounds. Part B: Applications in Coordination, Organometallic, and Bioinorganic Chemistry, 6th ed.; John Wiley & Sons, Inc.: Hoboken, NJ, USA, 2008. [Google Scholar] [CrossRef]
  62. Park, S.H.; Kim, H.J. Unidirectionally aligned copper hydroxide crystalline nanorods from two-dimensional copper hydroxy nitrate. J. Am. Chem. Soc. 2004, 126, 14368–14369. [Google Scholar] [CrossRef]
  63. Engelbrekt, C.; Malcho, P.; Andersen, J.; Zhang, L.; Ståhl, K.; Li, B.; Hu, J.; Zhang, J. Selective synthesis of clinoatacamite Cu2(OH)3Cl and tenorite CuO nanoparticles by pH control. J. Nanopart. Res. 2014, 16, 2562. [Google Scholar] [CrossRef]
  64. Mahmoud, B.G.; Khairy, M.; Rashwan, F.A.; Foster, C.W.; Banks, C.E. Self-assembly of porous copper oxide hierarchical nanostructures for selective determinations of glucose and ascorbic acid. RSC Adv. 2016, 6, 14474–14482. [Google Scholar] [CrossRef] [Green Version]
  65. Gregg, S.J.; Sing, K.S.W. Adsorption, Surface Area and Porosity, 2nd ed.; Academic Press: London, UK, 1982; pp. 41–110. [Google Scholar]
  66. Lee, B.S.; Yi, M.; Chu, S.Y.; Lee, J.Y.; Kwon, H.R.; Lee, K.R.; Kang, D.; Kim, W.S.; Lim, H.B.; Lee, J.; et al. Copper nitridenanoparticles supported on a superparamagnetic mesoporous microsphere for toxic-free click chemistry. Chem. Commun. 2010, 46, 3935–3937. [Google Scholar] [CrossRef] [PubMed]
  67. Deshmukh, R.; Schubert, U. Synthesis of CuO and Cu3N nanoparticles in and on hollow silica spheres. Eur. J. Inorg. Chem. 2013, 2498–2504. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  68. Zervos, M.; Othonos, A.; Sergides, M.; Pavloudis, T.; Kioseoglou, J. Observation of the direct energy band gaps of defect-tolerant Cu3N by ultrafast pump-probe spectroscopy. J. Phys. Chem. C 2020, 124, 3459–3469. [Google Scholar] [CrossRef]
  69. Li, H.; Ban, L.; Wang, Z.; Meng, P.; Zhang, Y.; Wu, R.; Zhao, Y. Regulation of Cu species in CuO/SiO2 and its structural evolution in ethynylation reaction. Nanomaterials 2019, 9, 842. [Google Scholar] [CrossRef] [Green Version]
  70. Kim, S.; Kang, S.W.; Kim, A.; Yusuf, M.; Park, J.C.; Park, K.H. A highly efficient nano-sized Cu2O/SiO2 egg-shell catalyst for C–C coupling reactions. RSC Adv. 2018, 8, 6200–6205. [Google Scholar] [CrossRef] [Green Version]
Molecules 26 04926 g001 550
Figure 1. Schematic representation of the preparation processes for the respective powders.
Figure 1. Schematic representation of the preparation processes for the respective powders.
Molecules 26 04926 g001
Molecules 26 04926 g002 550
Figure 2. SEM images of as-prepared precursor powders: (a) sample A, (b) sample B and (c,d) sample A after ammonolysis reaction (4 h, 300 °C sample 1b).
Figure 2. SEM images of as-prepared precursor powders: (a) sample A, (b) sample B and (c,d) sample A after ammonolysis reaction (4 h, 300 °C sample 1b).
Molecules 26 04926 g002
Molecules 26 04926 g003 550
Figure 3. PXD patterns of (a) sample A as prepared and (b) sample A after heating in NH3 atmosphere at 300 °C (1b). Sample A could be indexed as single-phase atacamite, while peaks in the pattern from sample 1b could be identified as Cu3N (■) and Cu(NH3)Cl (●).
Figure 3. PXD patterns of (a) sample A as prepared and (b) sample A after heating in NH3 atmosphere at 300 °C (1b). Sample A could be indexed as single-phase atacamite, while peaks in the pattern from sample 1b could be identified as Cu3N (■) and Cu(NH3)Cl (●).
Molecules 26 04926 g003
Molecules 26 04926 g004 550
Figure 4. SEM images of powders: obtained by NaOH/NH3(aq) treatment of the Cu2(OH)3Cl (sample A) (a,b) and Cu2(OH)3Cl (sample B) (c) powders; obtained by NaOH treatment of the Cu2(OH)3Cl (sample B) powder (d).
Figure 4. SEM images of powders: obtained by NaOH/NH3(aq) treatment of the Cu2(OH)3Cl (sample A) (a,b) and Cu2(OH)3Cl (sample B) (c) powders; obtained by NaOH treatment of the Cu2(OH)3Cl (sample B) powder (d).
Molecules 26 04926 g004
Molecules 26 04926 g005 550
Figure 5. X-ray diffraction patterns of: (a) CuO, (b) Cu(OH)2 powders as-made and (c) CuO (2a), (d) Cu(OH)2 (3b) following ammonolysis. Red circles indicate CuO, black triangles indicate Cu(OH)2 and black squares represent Cu3N.
Figure 5. X-ray diffraction patterns of: (a) CuO, (b) Cu(OH)2 powders as-made and (c) CuO (2a), (d) Cu(OH)2 (3b) following ammonolysis. Red circles indicate CuO, black triangles indicate Cu(OH)2 and black squares represent Cu3N.
Molecules 26 04926 g005
Molecules 26 04926 g006 550
Figure 6. SEM images of as-prepared Cu3N powders: (a) sample (2b) (CuO) and (b) sample (3b) (Cu(OH)2) after ammonolysis (4 h, 300 °C). The inset shows a view of the samples magnified 150,000×.
Figure 6. SEM images of as-prepared Cu3N powders: (a) sample (2b) (CuO) and (b) sample (3b) (Cu(OH)2) after ammonolysis (4 h, 300 °C). The inset shows a view of the samples magnified 150,000×.
Molecules 26 04926 g006
Molecules 26 04926 g007 550
Figure 7. PXD patterns of Cu(OH)2/SiO2 composites heated under flowing NH3 gas at: (a) 250 °C (blue) and (b) 300 °C (red). The Miller indices (hkl) for copper(I) nitride, Cu3N, are indicated.
Figure 7. PXD patterns of Cu(OH)2/SiO2 composites heated under flowing NH3 gas at: (a) 250 °C (blue) and (b) 300 °C (red). The Miller indices (hkl) for copper(I) nitride, Cu3N, are indicated.
Molecules 26 04926 g007
Molecules 26 04926 g008 550
Figure 8. (a) BET isotherms and (b) the incremental pore volumes registered for the as-received SiO2 aerogel, modified SiO2 aerogel, and Cu3N/modified SiO2 aerogel samples.
Figure 8. (a) BET isotherms and (b) the incremental pore volumes registered for the as-received SiO2 aerogel, modified SiO2 aerogel, and Cu3N/modified SiO2 aerogel samples.
Molecules 26 04926 g008
Table
Table 1. Experimental conditions for samples prepared by ammonolysis reaction.
Table 1. Experimental conditions for samples prepared by ammonolysis reaction.
Sample
No.		PrecursorTemperature/°CTime/minProduct Phases from
PXD (wt%) *
1aCu2(OH)3Cl240240Cu3N (38) > Cu(NH3)Cl (62)
1bCu2(OH)3Cl300240Cu3N > Cu(NH3)Cl
1cCu2(OH)3Cl330240Cu3N (41) > Cu(NH3)Cl (59)
2aCuO280180Cu3N (69) > CuO (31)
2bCuO310300Cu3N
2cCuO330240Cu3N > Cu
3aCu(OH)2300240Cu3N (77) > CuO (23)
3bCu(OH)2310300Cu3N
3cCu(OH)2330240Cu3N > Cu
4Cu(OH)2310300Cu3N (55)/CuO (33)/Cu (12)
* Phase fractions (wt%) were estimated using profile fitting within the PowderCell software [59]. For some samples the phase composition was not estimated due to the low peak intensity of the corresponding XRD patterns.
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Szczęsny, R.; Hoang, T.K.A.; Dobrzańska, L.; Gregory, D.H. Solution/Ammonolysis Syntheses of Unsupported and Silica-Supported Copper(I) Nitride Nanostructures from Oxidic Precursors. Molecules 2021, 26, 4926. https://0-doi-org.brum.beds.ac.uk/10.3390/molecules26164926

AMA Style

Szczęsny R, Hoang TKA, Dobrzańska L, Gregory DH. Solution/Ammonolysis Syntheses of Unsupported and Silica-Supported Copper(I) Nitride Nanostructures from Oxidic Precursors. Molecules. 2021; 26(16):4926. https://0-doi-org.brum.beds.ac.uk/10.3390/molecules26164926

Chicago/Turabian Style

Szczęsny, Robert, Tuan K. A. Hoang, Liliana Dobrzańska, and Duncan H. Gregory. 2021. "Solution/Ammonolysis Syntheses of Unsupported and Silica-Supported Copper(I) Nitride Nanostructures from Oxidic Precursors" Molecules 26, no. 16: 4926. https://0-doi-org.brum.beds.ac.uk/10.3390/molecules26164926

Article Metrics

Back to TopTop