Next Article in Journal
A Three-Parameter Weibull Distribution Method to Determine the Fracture Property of PMMA Bone Cement
Next Article in Special Issue
Formulation of Modified-Release Bilayer Tablets of Atorvastatin and Ezetimibe: An In-Vitro and In-Vivo Analysis
Previous Article in Journal
Enhancing for Bagasse Enzymolysis via Intercrystalline Swelling of Cellulose Combined with Hydrolysis and Oxidation
Previous Article in Special Issue
A Sustainable Approach to a Cleaner Production of Antimicrobial and Biocompatible Protein Fibers
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Obtaining Ultrafine Dispersions of Silver Particles in Poly(vinyl Alcohol) Matrix Using Mechanical Alloying

by
Deize Basílio dos Santos de Aguiar
1,
Denilson José Marcolino de Aguiar
2,*,
Josiane de Fátima Padilha de Paula
3 and
Osvaldo Mitsuyuki Cintho
4
1
Departamento de Estética e Cosmética, Faculdade Cesumar de Ponta Grossa (Unicesumar), Ponta Grossa 84036–350, PR, Brazil
2
Departamento Acadêmico de Mecânica (DAMEC), Universidade Tecnológica Federal do Paraná—UTFPR, Ponta Grossa 84017–220, PR, Brazil
3
Department of Pharmaceutical Sciences, State University of Ponta Grossa, Ponta Grossa 84030–900, PR, Brazil
4
Departamento de Engenharia de Materiais (DEMA), State University of Ponta Grossa, Ponta Grossa 84030–900, PR, Brazil
*
Author to whom correspondence should be addressed.
Submission received: 2 August 2022 / Revised: 21 August 2022 / Accepted: 22 August 2022 / Published: 30 August 2022

Abstract

:
Mechanical alloying was performed to obtain a composite material with a homogeneous dispersion of silver particles in a poly(vinyl alcohol) (PVA) matrix. Silver is a bactericidal material, and PVA is a widely used biocompatible polymer. Therefore, this mix can lead to a potentially functional biomaterial. This study focuses on the combination of both materials, processed by mechanical alloying, which has a promising application potential. The silver (Ag) used was ultrafine, measuring between 200 and 400 nanometers, produced from silver nitrate (AgNO3) redox. The Attritor high–energy, water–cooled ball mill was used to mill PVA for 4 h, at 600 rpm speed rotation and 38:1 power milling. Mechanical alloying was demonstrated to cause particle refinement in PVA with a timespan of 1 h. A slight additional particle decrease occurred for long–time milling. A milling time of 4 h was used to disperse the silver particles in the polymer matrix homogeneously. Hot pressing films were produced from the obtained dispersion powders. The microstructural features were studied using several material characterization techniques. Antimicrobial Susceptibility Tests (AST), conducted in an in–vitro assay, showed a hydrophilic character of the films and a protection against bacterial growth, making the process a promising path for the production of surface protective polymeric films.

1. Introduction

Nowadays, mechanical alloying is studied in all materials. It ranges from metals and their alloys to obtaining several composite materials involving metals, polymers, and ceramics to produce various commercial application materials of scientific interest. Among the primary purposes of this technique is to obtain: the formation of alloys in solid state; the possibility of obtaining alloys with immiscible elements by other methods; the refinement of grain size to nanometric levels; the decrease or increase in particle size; particle agglomeration; extension of solubility limits; the development of amorphous phases; and the induction of chemical reactions at low temperature, among others [1,2,3]. Mechanical alloying is a solid–state process that consists of adding the materials to be ground, usually dry, together with the grinding balls inside a jar. The intense impact between the material, the spheres, and the jar walls produce a fine powder with a much higher energy than that of other standard grinding processes [1,2]. The application of this technique in polymeric materials is more recent than in other materials, beginning in the late 1980s [4,5]. However, in the last decade, the production of polymer matrix composites in several applications has become widely studied [3,6,7,8,9,10]. The mechanisms acting in the polymer mechanical alloying are somewhat different from other materials. There is the possibility of chain breakage during collisions between the samples and the grinding media, leading to a decrease in molar mass. Nevertheless, breaking bonds in the polymeric chains can also lead to free radicals due to fracture processes, providing new chemical bonds and, thus, mixing immiscible polymers in other ways, forming blends without the solvents used [4,5,11,12,13,14,15]. Furthermore, the crystal structure of semi–crystalline polymers can be altered by milling [6,12].
Commonly, polymer matrix nanocomposites require several processing steps, and the processes are slow. Some of them take days to manufacture [16,17,18,19,20]. The product’s final volume is usually small, limited by the nature of the process. The sol–gel [21] and the solution–based, self–assembly (layer–by–layer) methods are highlighted [22,23,24,25,26]. The sol–gel method synthesizes materials from the sol system transition to a gel system. The term sol defines a colloidal particle dispersion (sizes between 1 and 100 nm). In contrast, the term gel consists of a system formed by the rigid structure of colloidal particles (colloidal gel) or polymeric chains (polymeric gel), immobilizing the liquid phase inside the interstices [21,27]. The solution is the self–assembly (layer–by–layer) technique in a liquid medium, which results in self–structured layers. It consists of the deposition of several layers adhered by the electrostatic attraction between the opposite charges of their constituents. The layers’ deposition is based on physical adsorption, innovating another existing technique based on chemical adsorption [23,24,25,26].
Comparatively, high–energy ball milling is a solid–state method that does not require additional solvents and all production steps can be made in a dry state. In addition, the only limitation to the bulk material’s production quantity is the jar’s volume. However, there are industrial jars capable of grinding large volumes of material in one run, making mechanical alloying an appealing and possibly viable technological path to obtain polymer matrix composites [1,2].
PVA is a synthetic polymer that is thermoplastic, semi–crystalline, non–toxic, biocompatible, biodegradable, hydrophilic, and belons to the polyvinyl ester class. It is commercially available at a low cost, being one of the few water–soluble polymers, depending on the temperature. Its melting temperature is between 180 and 230 °C, depending on the crystallinity degree [28,29,30,31,32,33]. PVA has an excellent ability to form films and hydrogels. In addition, the hydrophilic characteristic of PVA can protect a region from moisture, as it exhibits a high level of absorption of water or biological liquids. Because of this characteristic, PVA can form films with several functionalities, including simulating a natural tissue, enabling numerous applications in biological materials [28,32,33,34]. Silver (Ag) has been used due to its potent antimicrobial activity properties against various types of pathogens, especially in recent times due to the emergence of resistant bacteria [35,36,37,38,39,40,41,42,43,44,45]. Furthermore, when it is combined with PVA, a biocompatible and biodegradable polymer, it is possible to obtain a polymeric film, resistant to microbial contamination, ideal to create films for potential application as biomaterials [34,46,47,48,49]. The originality of this work lies in the use of mechanical alloying in the production of the PVA/Ag composite, which has proved to be a promising processing path. This powder can be easily formed to produce bacterial growth–inhibiting films. Such films can be used both in biocompatible functions and in other applications that require the absence of microorganisms.
The present work is aimed at studying the feasibility of using mechanical alloying to obtain a composite material with an ultrafine dispersion of Ag particles in a PVA matrix using an Attritor mill, with subsequent evaluation of the antimicrobial activity of the obtained materials.

2. Materials and Methods

The materials used in this research were:
  • Silver nitrate (AgNO3)—in powder form, white, supplied by the company Sigma–Aldrich, Saint Louis, MO, USA. It has a silver content of 63.35% and 99.98% purity.
  • Poly(vinyl alcohol) (PVA)—in the form of a white, odorless granular powder, supplied by the Chemical Company, Jamestown, RI, USA, with an approximate molar mass of 72 × 103 g mol−1 and a hydrolysis degree of 88.09%.
  • Sodium hydroxide (NaOH) in powder form, white, supplied by the company Sigma–Aldrich, Saint Louis, MO, USA with an approximate molar mass of 40 g mol−1.
  • Formaldehyde (HCOH) supplied by Dinâmica Química Contemporânea LTDA, Indaiatuba, SP, BRA, with an approximate molar mass of 30.03 g mol−1.
In this research, obtaining Ag was possible by using consecutive oxidation reactions and reduction of silver nitrate [50,51]. Mechanical alloying was used to homogeneously disperse the Ag particles in the polymeric matrix. With the obtained dispersion, films were produced by the widely used hot pressing method [52,53]. The samples were characterized by X-ray diffraction, optical microscopy, scanning electron microscopy by field emission electron gun (SEM–FEG), and differential and infrared exploratory calorimetry (DSC and FTIR) analysis.

2.1. Chemical Reactions to Obtain Silver

Firstly, a 250 mL of sodium hydroxide solution (NaOH) with a concentration of 1 molar was prepared in a volumetric flask. Afterwards, 10 g of white silver nitrate (AgNO3) was weighed in a beaker. The NaOH solution was subsequently added to the beaker with the AgNO3 and kept at 80 °C on a Solab magnetic stirrer with a heating plate (model SL–91) to homogenize the solution and accelerate the reaction for forming black–colored silver oxide (Ag2O), according to Equation (1). After 40 min under the conditions described, the heating plate was switched off. The resulting residue was placed on filter paper, washed in distilled water several times to remove residues from the solution, and dried to perform X-ray diffraction and SEM–FEG analysis of Ag2O. After that, the Ag2O formation experiment was repeated, and about 10 mL of formaldehyde (HCOH) was slowly pipetted for the formation of yellowish silver (Ag) to occur (as it is unpolished), with some metallic shine points according to Equation (2). The resulting residue was also placed on filter paper, successively, and several rounds of rinsing was conducted followed by oven drying to perform an X-ray diffraction and an SEM–FEG analysis of Ag.
The expected reactions were as follows:
2 A g + + 2 N O 3 + 2 N a + + 2 O H   A g 2 O + 2 N a N O 3 + H 2 O
A g 2 O + H C O H + H 2 O 2   A g + C O 2 + 4   H 2 O
The filtering was performed in a device connected to a vacuum pump and later placed in an oven at 40 °C for 24 h for drying purposes. Afterwards, they were photographed, and their visual aspects compared with the as–received sample.

2.2. X-ray Diffraction of Silver Nitrate, Silver Oxide, and Silver

The characterization was performed in a Rigaku Diffractometer, model Ultima IV, using Cu–Kα radiation (0.154 nm). The equipment is installed in the Multi–User Laboratory (C—LABMU) of the State University of Ponta Grossa. The scanning ranges (diffraction angle 2θ) were from 20 to 90° in the step scan mode, with a step of 0.02° and 5 s at each point.

2.3. SEM–FEG of Silver Nitrate, Silver Oxide, Silver, and PVA

The samples were metalized with a gold and palladium alloy to avoid electrical charging before being placed into the microscope. The metalizing equipment used is from Qorum Sputter Coater, model SC7620. An SEM–FEG characterization was performed using Tescan equipment, model Mira. Both equipament are installed in the Multi–User Laboratory (C—LABMU) of the State University of Ponta Grossa. To obtain pure PVA, AgNO3, or composite PVA/Ag images, the SEM–FEG was operated between 3 and 5 kV, although 15 kV for Ag and Ag2O, using secondary electrons in all cases. The low voltage for AgNO3 and the polymer matrix was chosen because higher voltages cause charging and damage to these types of materials, respectively.

2.4. Commercial PVA Mechanical Alloying and SEM–FEG of Samples

The commercial PVA samples were processed with high–energy ball milling in a Union Process Attritor mill, model Attritor 01 HD, installed at the Department of Materials Engineering at the State University of Ponta Grossa. The milling balls used were made of zirconia with a 6.35 mm diameter size. The use of this type of ball instead of steel balls was to minimize contamination with traces of metal. For this same reason, the jar and milling rod used were made of ultra–high molar mass polyethylene, while the rod arms were made of zirconia. Running water at room temperature cooled the mill; thus the heat generated by the grinding action would be dissipated, avoiding possible thermal degradation of the polymer. The milling power adopted in this work was 38:1 for all milling performed. The speed rotation was 600 rpm. The milling parameters are summarized in Table 1 while the PVA milling times are described in Table 2:
After that, SEM–FEG sampling was performed with the same parameters and procedures indicated in the previous item, to verify the influence of milling on the size and morphology of the polymer particles.

2.5. Differential Scanning Calorimetry (DSC) Analysis Processed in an Attritor–Type Mill

The DSC analyses were performed using Setaram equipment, Labsys model, installed in the Multi–User Laboratory (C—LABMU) of the State University of Ponta Grossa, with a thermal analysis capacity of up to 1600 °C. The analysis was conducted in an argon atmosphere with a 20 mL/minute flow in an alumina crucible with approximately 30 mg of material. The heating and cooling rates were 10 °C/minute. The scanning range was from 20 °C to 230 °C, performed in a single cycle. This characterization was intended to verify the influence of different milling times on the melting temperature of the PVA, comparing it with the as–received material, as shown in Table 2.

2.6. Mixing of Several Amounts of PVA and Ag by Mechanical Alloying and Infrared Spectrophotometry Assay with Fourier Transform (FTIR) Analyses of the Mixtures

Some Ag dispersions were prepared in a PVA matrix, where the Ag was obtained by oxidation reactions and reduction of AgNO3. These mixtures were conducted in the same high–energy ball mill used to mill commercially pure PVA. Preliminary experiments were performed, such as milling together the Ag and the PVA from the beginning for 2 and 4 h. Another attempt was made to mill the PVA alone for 1 h, stopping the milling and adding the Ag and milling for another 1 h. Under these conditions, there were still many non–adhered and unsatisfactorily dispersed Ag particles on the polymer matrix. Therefore, all of these parameters were discarded. Based on the preliminary results, DSC and SEM–FEG analyses, the milling time to mixing PVA and Ag chosen was 4 h, while the milling parameters were the same as from Table 1.
The procedure to obtain the Ag dispersion in the matrix was to mill the commercially pure PVA for 2 h, followed by an interruption of the milling and mixing of the Ag with the previously ground PVA, and the finalization of the Ag milling process for another 2 h. In this way, the best relation between the PVA milling time and Ag dispersion in the matrix of the mill operation was achieved.
Milling products with different mass concentrations of Ag weighed on an analytical balance with a mass/mass ratio were elaborated for further characterization and verification of the metal effects in the matrix. The mass fractions used in this work compared with the as–received PVA are shown in Table 3.
After that, the FTIR analysis was conducted using SHIMADZU equipment, model IR Prestige–21, and 64 scans/min, resolution of 4 cm−1, installed in the Multi–User Laboratory (C—LABMU) of the State University of Ponta Grossa. The samples analyzed were as–received PVA (A), pure PVA milled for 4 h (E) from Table 2, and powdered mixture PVA with Ag particles, from Table 3 (E1 to E5).
The powder samples were prepared via cold pressing using a SHIMADZU manual hydraulic press, installed in the Multi–User Laboratory (C—LABMU) of the State University of Ponta Grossa. These disks were set as the sample mixture to be analyzed with potassium bromide (KBr) from the Vetec, each 5 and 195 mg. A reference reading was performed with a pure KBr disk.

2.7. Preparation of Polymeric Films from the PVA/Ag Mixture by Hot Pressing and Characterization by Transmitted Light Optical Microscopy

In this step, for each sample condition, films were made via hot pressing in a Schwing Siwa manual hydraulic press, model 30 tons, installed at the Department of Materials Engineering at the State University of Ponta Grossa. After several tests, the film with a more homogeneous aspect was obtained by processing at a temperature of 220 °C. Then, the press was heated to 220 °C with a thermocouple control. The films were produced with 2 g of material, resulting in a close to circular shape, 3 mm thickness, and 70 mm in diameter. The samples used to prepare films were as–received PVA (A), pure PVA milled for 4 h (E) from Table 2, and powdered mixture PVA with Ag particles, from Table 3 (E1 to E5).
After obtaining the films, they were characterized by transmitted light microscopy to assess the distribution of Ag particles on the PVA surface. The equipment used was an Olympus optical microscope, model BX–51, installed at the Department of Materials Engineering of State University of Ponta Grossa, with a digital camera coupled and controlled by software Image–Pro Plus, version 5.1, from Media Cybernetics Inc., Rockville, MD, USA.

2.8. Characterization of the Fracture Surface of the Films by SEM–FEG

The films produced underwent a process of embrittlement in liquid nitrogen inside a Styrofoam container. This bath was maintained for approximately 5 min to weaken the sample and facilitate fracture, performed with standard pliers. The pieces were then metalized to produce a conductive barrier. Thus, the fracture surfaces along the thickness can be analyzed by SEM–FEG, mainly the distribution of Ag particles.

2.9. Chemical Microanalysis of Particles by Energy Dispersion (EDS)

A chemical microanalysis was conducted using an EDS coupled to the SEM–FEG equipment, device installed in the Multi–User Laboratory (C—LABMU) of the State University of Ponta Grossa. The equipment used was mentioned in the topic above. This analysis was performed to estimate the presence of Ag in the thickness of the fragile film.

2.10. Microbiological Sensitivity Tests on Polymeric Films

The antibiogram, also known as the Antimicrobial Susceptibility Test (AST), is an in–vitro assay that measures the susceptibility or resistance of bacteria to antimicrobials. The method used in this work was susceptibility in a culture plate (90 mm in diameter and 15 mm high) on Müeller Hinton agar. This medium contains proteins and carbohydrates that provide the ideal substrate for developing and growing bacterial strains of interest. This test was conducted to evaluate the antimicrobial activity of polymeric films [42,43,45,46,49,54] and it was performed at Department of Pharmacy and Biochemistry at the State University of Ponta Grossa. The analyzed samples are shown in Table 4.
The tests were conducted using bacterial strains provided by the American Type Culture Collection (ATCC). They are:
Escherichia coli—ATCC 0022;
Staphylococcus aureus—ATCC 0023;
Streptococcus pyogenes—ATCC 0015;
Pseudomonas aeruginosa—ATCC 0016.
The bacterial suspensions were prepared by adding some microorganism colonies in a sterile saline solution. Afterwards, the suspension was read until a turbidity of 1.5, McFarland scale (approximately 108 CFU/mL), was achieved on a Biosystems spectrophotometer, model BTS–330. This procedure was performed individually for each studied bacterium [32,35,37,41,42,44,45,46,47,48,49,50,54,55].
At that moment, each bacterial suspension was sown with the aid of a sterile swab in a culture dish. Then, 6 mm diameter polymeric film discs were deposited and dispersed on the seeded plates. These plates were incubated in a QUIMIS microbiological oven, model Q316M4, at 36 °C for 24 h. Subsequently, the plates were observed to identify the presence or absence of a bacterial inhibition halo in the culture medium. The bacteria growth inhibition halo (H) was measured according to Equation (3) [46], as follows:
H = D d 2
where D is the diameter of the zone of inhibition and d is the diameter of the PVA film disc containing Ag particles.

3. Results and Discussion

3.1. Chemical Reactions of Materials Containing Silver

Changes occurred in the coloring in the transition from as–received material to the oxidation and reduction reactions products. Initially, the as–received ANO3 is white. After the first reaction described in Equation (1), it adopts a black color due to the oxidation of the material, where Ag2O was produced. Finally, after the second reaction described in Equation (2), there was a reduction in the oxide, adopting a yellowish color. Figure 1 illustrates the color change from AgNO3, passing by Ag2O oxidation and then reduction.
Figure 1a–c shows a color change after the reaction steps from the as–received material. Initially, as–received AgNO3 is white (Figure 1a), and after the first reaction described in Equation (1), it adopts a black color due to its oxidation, evidencing Ag2O formation (Figure 1b). Finally, after the second reaction described in Equation (2), the oxide was reduced, adopting a yellowish color due to Ag formation (Figure 1c).

3.2. X-ray Diffraction of Silver Nitrate, Silver Oxide, and Silver

The solids were characterized by X-ray diffraction, with as–received silver nitrate (AgNO3), silver oxide precipitate (Ag2O), and final solid samples silver (Ag). These changes in crystalline structures confirm the peaks of the crystallographic planes of the studied specimens, illustrated in Figure 2.
The summarized values of lattice parameters of the structures are shown in Table 5.
The results of the diffractogram analyses in Figure 2 demonstrate that the proposed reactions occurred. As–received silver nitrate has a crystalline structure with the Miller indices belonging to the orthorhombic system of the Pbca type spatial group. After the first reaction (Equation (1)), there was a change in the crystalline structure, resulting in a material with a crystalline structure with the Miller indices belonging to the simple cubic system, of the spatial group of the type Pn–3m, in the case of silver oxide. The second reaction (Equation (2)) promotes a new change, resulting in a material with a crystalline structure with Miller indices belonging to the face–centered cubic system, of the Fm–3m type spatial group, in the case of Ag. The lattice parameters presented in the Table 4 show these changes.

3.3. SEM–FEG of Silver Nitrate, Silver Oxide, Silver and PVA

As–received materials and precipitates resulting from chemical reactions and samples of materials were also characterized by images obtained by SEM–FEG. The as–received AgNO3, the Ag2O, and Ag chemical reaction results and the as–received PVA are illustrated in Figure 3 from a to d, as follows.
Figure 3 shows that the as–received AgNO3 sample has irregularly shaped particles and variable size distribution; however, close to the millimeter scale. It can also be observed that after the chemical reactions, both the intermediate product, silver oxide, and the product, Ag, have a morphology that resembles spheres and with a more homogeneous size than the initial material. Similarly, it shows that the chemical reactions caused a severe refinement of the particles since they are submicrometric, and several of them are between 200 and 400 nanometers in size. The as–received PVA proved to have an irregular and approximately equiaxial morphology with an approximate size of 1 mm.

3.4. SEM/FEG of Milled PVA

The PVA samples were performed in an Attritor mill with milling parameters described on Table 1 to verify the effects of milling on particle size and shape. Afterwards, the research was conducted using SEM/FEG. Finally, the results of the ground PVA samples were compared with the as–received material (Figure 3d). Figure 4 illustrates the size and morphology of the as–received, and milled PVA particles.
Figure 4 compares the effects of mechanical alloying milling time on the PVA size and morphology, for several conditions in an Attritor–type mill.
A comparison of Figure 3d and Figure 4a–c, shows that the PVA begins to decrease in size with respect to the as–received material from the initial stages of milling. However, after 30 min of milling, not all particles underwent a size reduction process. After 1 h of milling, a greater homogeneity in the size of the particles can be observed. There are no significant differences in size and morphology between using a timespan of 2 h and 4 h of milling. The longest the timespan, the smallest the polymer particles achieved. Another observation made through the detailed image (e) is that for 4 h milling, the PVA particles undergo welding and fracture processes, typical of ductile materials [1,2]. In addition, the approximately equiaxial shape of the as–received material results in the form of thin, flat flakes [1,2]. This type of behavior has been previously reported for other kinds of polymers [6].

3.5. Characterization by Differential Exploratory Calorimetry (DSC) of the Poly(vinyl Alcohol) Ground at Different Times

Figure 5 shows the effect of mechanical alloying in PVA characterized by DSC.
The polymer’s melting temperature was determined by analyzing the heat flow versus the temperature curve. Table 6 contains these values for each processing situation.
Figure 5 shows the effects of the mechanical alloying on the melting temperature of the PVA with respect to the as–received material. DSC can determine first–order transitions that involve enthalpy variation (endothermic and exothermic events), such as melting temperature. The polymer’s melting temperature is measured at the deepest point of the endothermic peak corresponding to temperature [7]. They recall that the physical characteristics of the polymer depend on the degrees of hydrolysis and polymerization [7,28,30,31,56]. It was observed that the milling leads to a decrease in the melting temperature from the as–received sample. However, this decrease is not significant (a difference of approximately 5% between the as–received material and the ground for 16 h). Nevertheless, this comparative effect can still be seen on the peaks around 190 °C in Figure 5, illustrating that the melting temperature of the material ground for 4 h was lower than that of the as–received sample. This effect may be related to the decrease in size and change in the morphology of the PVA particles (a form of thin, flat flakes). Consequently, a greater surface area may favor a faster and more efficient heat exchange, decreasing the polymer’s melting temperature. The PVA melting temperature values listed in Table 6, whether as–received or processed, are within the same range mentioned in the literature [7,28,30,31,56].
Based on the preliminary results described in item 2.6 and characterizations by SEM–FEG and DSC, the selected condition was processing the PVA for 4 h before the manufacture of films by hot pressing. There is a refinement of the material in this processing time and consequently a decrease in its melting temperature. In addition, it does not take too long to achieve well dispersed Ag particles, which justifies the preferred choice.

3.6. Mixing PVA and Silver in an Attritor Mill and Fourier Transformed Infrared (FTIR) Spectra of Powder Mixtures

Figure 6a,b illustrates the result of the mixture of PVA and 10% wt. Ag by mechanical alloying in an Attritor–type mill for 4 h.
When comparing Figure 4c and Figure 6a, it is still possible to observe the presence of flakes, which are circled with a white line. With a more detailed magnification, it is possible to see that the flakes are impregnated with Ag particles.
In Figure 7, the FTIR spectra of the as–received PVA and mechanical alloyed PVA powders with 10% wt. Ag and without Ag can be observed on the same scale.
By analyzing Figure 7, five regions are highlighted in the spectra, corresponding to the interactions of some types of connections at specific FTIR frequencies (cm−1). These five regions are summarized in Table 7.
Figure 7 shows that the PVA sample milled with 10% wt. Ag presents a band near 605 cm−1, indicated in the graph with an arrow, different from the as–received material. This band may suggest a chemical interaction between PVA and Ag particles due to the far–infrared region, meaning stretching and bending vibrations of bonds between metal atoms and both inorganic and organic ligands at frequencies lower than 650 cm−1 [57,58,59].
In Figure 8, each detailed spectrum can be observed separately, in an appropriate scale, for some of the conditions studied (Table 2 and Table 3).
The analysis of the as–received PVA spectrum in Figure 8, showed a narrow band with a maximum peak at 3626 cm−1 representing free O–H bonds from the alcohol functional group. For samples ground from pure PVA and PVA with Ag particles, changes in this bandwidth and amplitude (% transmittance) concerning as–received PVA may be related to the fact that the milling has promoted stretching of the connections between O–H. However, Ag particles did not influence these functional group interactions [7,30,31,56,59,60,61,62,63].
The evidence is the lack of significant differences between milled samples with and without Ag (see Figure 7 in Region I). The maximum peaks were approximately at the frequency of 3300 cm−1. Region II, shown in Figure 7, comprises two situations involving stretching of the C–H bonding. The first situation is related to the symmetrical stretch with a maximum peak at 2937 cm−1. The second situation is associated with the asymmetry of the region with a maximum height of 2910 cm−1. It was noted that this effect occurred in the milled material with and without Ag particles while it was not evidenced in the as–received material. The values of these peaks for all situations studied can be seen in detail in Figure 8.
Region III, shown in Figure 7, with a band between 1735 and 1750 cm−1, which can be seen in greater detail in Figure 8, corresponds to the C=O bonding. The maximum peak is around 1740 cm−1. The origin of this functional group is polyvinyl acetate, which is the raw material for obtaining PVA Region IV, highlighted in Figure 7 and seen in detail for each situation in Figure 8, corresponds to a frequency range from 1200 to 1465 cm−1. Two peaks appear with maximum values of 1237 and 1438 cm−1 as they conform to the C–O–H bond, coupled with the CH2 vibrations of the methylene group.
In Region V, Figure 7 corresponds to the stretching vibration of the C–O bonds of the carbonyl group. Two overlapping peaks appear with maximum heights at 1090 and 1200 cm−1. The details of this region can be observed for all of the situations studied in Figure 8. Transmittance was verified to be 99% on as–received PVA, while in the conditions with milled PVA, the transmittance ranged from 75 to 85%. Therefore, there was no evidence of the influence of Ag levels in this situation, in general, confirmed through the analysis of Figure 8, the difference in peak intensity between the as–received PVA and the PVA milled by mechanical alloying. This effect may be related to the increased surface area or the polymer’s degree of degradation caused by the milling process. However, the observed bands are in the same range of values described in the literature. In addition, no significant difference was found when comparing ground PVA alone with ground PVA with various levels of Ag particles, using the same processing conditions. [7,30,31,56,59,60,61,62,63].

3.7. Films Preparation by Hot Pressing and Characterization by Optical Microscopy

The samples used to prepare films were: as–received PVA (A), pure PVA milled for 4 h (E) from Table 2, and powdered mixture PVA with Ag particles, from Table 3 (E1 to E5). Hot pressing films with 0.3 mm thickness and around 70 mm diameter were made from the powders obtained with 4 h of mechanical alloying in an Attritor mill. Although the information is not objective, nor appealing, the surface quality of the film formed by the previously milled material proved to be abundantly higher than that of the as–received material, comparing the exact parameters of time, temperature, and pressure in the pressing process. Figure 9 illustrates PVA films with 2.5% wt. Ag (a) and 10% wt. Ag (b).
Figure 9, shows, by means of light microscopy, a number of dark spots on the surface of the films that contained Ag. As a result, the distribution of Ag particles on the PVA matrix surface could be understood. The particles are fine and evenly distributed over the entire length of the film for mass fractions up to 2.5% wt. Ag. For the 10% wt. Ag, although the Ag is still well distributed in the film, some larger particles are noted, suggesting agglomeration.

3.8. Characterization of the Fracture Surface of the Films by SEM–FEG

The fragility of the PVA films was conducted in a liquid nitrogen bath, for 5 min, and caused them to break with the aid of pliers. The objective was to verify the distribution of Ag particles and their thickness. As the surface to be observed was rather thin, the analysis was positioned at the edge of the support, fixed with carbon tape, and later metalized with a gold and palladium alloy. The results for the addition of 2.5% wt. Ag and 10% wt. Ag are shown in Figure 10.
In Figure 10, the fracture surface observed (in the thickness of the film) was analyzed by SEM–FEG. The occurrence of shiny and spherical particles, like the Ag images analyzed in Figure 2 is worth noting. Some of these particles are micrometric, probably due to the aggregation of Ag during processing. However, relatively ultrafine particles [64,65] are observed, with a diameter of 200 nanometers. Another observation is that these particles are distributed on the film thickness for all Ag proportions. It is significant to note that the contrast of the images is shallow because the energy of the electron beam is also low (5 kV according to the scale bar). It is appropriate to recall that greater energies would degrade the polymeric material.

3.9. Chemical Microanalysis of the Particle in the Polymeric Film by Energy Dispersive Scanning (EDS)

The EDS detected that the ultrafine particles were Ag, thus averting contamination in the film. The results for all samples were similar. Figure 11 shows an image of agglomerated particles observed in the PVA film with 10% wt. Ag. Table 8 shows its chemical microanalysis.
Figure 11 shows the agglomerated particles observed in the PVA film with 10% wt. Ag. A revision of the chemical microanalysis listed in Table 8, evidences the presence of Ag. The presence of gold and palladium is due to the metallization of the film surface.

3.10. Tests of Microbiological Activity of Polymeric Films

The antimicrobial activity of the films produced was determined by the agar diffusion method, a fast and straightforward technique indicated to verify the activities of the film samples in their different concentrations [32,35,37,41,42,44,45,46,47,48,49,50,55]. Figure 12 illustrates the culture plates on Müller Hinton agar seeded with the bacteria in the following sequence: (a) Pseudomonas aeruginosa; (b) Escherichia coli; (c) Staphylococcus aureus; and (d) Streptococcus pyogenes. The numbers indicated on the plates correspond to pure PVA and PVA films with different concentrations of Ag particles, as described in Table 4.
Figure 12 illustrates the absence of antimicrobial activity observed only in the pure PVA film (condition 1 for all plates), which has also been reported in the literature [49]. There was no bacterial growth on the films in the other conditions (2 to 6). Likewise, no colonies developed either. In addition, from 1% wt. Ag, particles concentration (conditions 3 to 6), an irregularly shaped inhibition halo was formed, like that observed in the literature [60]. The film’s affinity can explain this irregularity with the residual moisture of the culture medium. The polymeric film obtained was highly hydrophilic, which may be due to the dry production process without using additives that decrease the material’s solubility in water [60].
As can be seen from Figure 12a, the PVA film with Ag particles showed inhibition of the growth of strains of P. aeruginosa, one of the most antibiotic–resistant bacteria. An inhibition zone near to 15 mm and an inhibition halo of approximately 4 mm occurred for conditions 3 to 6. Comparing the expected inhibition zone for the composite of PVA and Ag nanoparticles [49], which would measure between 9 and 11 mm, the results are close to those found herein. In this study, the ultrafine Ag particles did not reach the size range to be considered nanometric [64,65], but even so, they showed good antimicrobial activity compared to other studies [41,50,55]. By analyzing Figure 12b–d, there was no bacterial growth on any of the tested films, except in the control one, consisting only of PVA, without incorporating the particles. This information is of paramount importance as it indicates that the material developed may protect against bacterial growth. Thus, it would potentially imply local protection against invasion by microorganisms, a fact demonstrated in the tests performed, making the process a promising path for the production of surface protective polymeric films.

4. Conclusions

Based on the results discussions, it can be concluded that:
X-ray diffraction measurements showed that it was possible to obtain Ag2O from the oxidation of AgNO3 with 1 molar NaOH solution and subsequently obtain Ag by reducing Ag2O with formaldehyde. In addition, SEM–FEG measurements showed that many of these Ag2O and Ag particles were ultrafine, measuring between 200 and 400 nanometers.
It was observed that the mechanical alloying promoted significant refinement and a morphology change in the PVA particles, changing in shape close to the equiaxial of the as–received material to fine flakes after milling. The milling proved to be a promising path to follow for distributing Ag in the PVA matrix in a homogeneous manner throughout the thickness of the polymeric film.
The agar antimicrobial susceptibility test evaluated the films produced. It was observed that there was no inhibition of microbial activity in pure PVA. The inhibition was verified on the surface of all the films that had Ag particles and for all the bacteria tested.

Author Contributions

Conceptualization, D.B.d.S.d.A. and O.M.C.; methodology, D.B.d.S.d.A., D.J.M.d.A., O.M.C. and J.d.F.P.d.P.; formal analysis, D.J.M.d.A. and O.M.C.; investigation, D.B.d.S.d.A.; resources, O.M.C. and J.d.F.P.d.P.; data curation, D.J.M.d.A., O.M.C. and J.d.F.P.d.P.; writing—original draft preparation, D.B.d.S.d.A.; writing—review and editing, D.J.M.d.A.; project administration, O.M.C. All authors have read and agreed to the published version of the manuscript.

Funding

This research was funded by Programa de Demanda Social DS—CAPES (Coordenação de Aperfeiçoamento de Pessoal de Nível Superior).

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

Not applicable.

Acknowledgments

Authors would like to thank CAPES (Coordenação de Aperfeiçoamento de Pessoal de Nível Superior), and Universidade Tecnológica Federal do Paraná (UTFPR)-Ponta Grossa Campus-for financial support.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Suryanarayana, C. Mechanical Alloying: A Novel Technique to Synthesize Advanced Materials. Research 2019, 2019, 4219812. [Google Scholar] [CrossRef] [PubMed]
  2. Suryanarayana, C. Mechanical Alloying and Milling. Prog. Mater. Sci. 2001, 46, 1–184. [Google Scholar] [CrossRef]
  3. Tenorio Gonzalez, F.N.; Barajas Rosales, I.R.; Vera Serna, P.; Sánchez de Jesus, F.; Bolarin Miró, A.M.; Garrido Hernández, A.; Kusý, M. Reducing the Crystallite and Particle Size of SrFe12O19 with PVA by High Energy Ball Milling. J. Alloys Compd. 2019, 771, 464–470. [Google Scholar] [CrossRef]
  4. Smith, A.P.; Shay, J.S.; Spontak, R.J.; Balik, C.M.; Ade, H.; Smith, S.D.; Koch, C.C. High–Energy Mechanical Milling of Poly(Methyl Methacrylate), Polyisoprene and Poly(Ethylene–Alt–Propylene). Polymer 2000, 41, 6271–6283. [Google Scholar] [CrossRef]
  5. Shaw, W.J.D. Current Understanding of Mechanically Alloyed Polymers. Mater. Sci. Forum 1998, 269, 19–30. [Google Scholar] [CrossRef]
  6. Gabriel, M.C.; Mendes, L.B.; de Carvalho, B.M.; Pinheiro, L.A.; Capocchi, J.D.T.; Kubaski, E.T.; Cintho, O.M. High–Energy Mechanical Milling of Ultra–High Molecular Weight Polyethylene (UHMWPE). Mater. Sci. Forum 2010, 660, 325–328. [Google Scholar] [CrossRef]
  7. Abd–Elrahman, M.I. Synthesis of Polyvinyl Alcohol–Zinc Oxide Composite by Mechanical Milling: Thermal and Infrared Studies. Nanoscale Microscale Thermophys. Eng. 2013, 17, 194–203. [Google Scholar] [CrossRef]
  8. Rashidi, S.; Ataie, A. A Comparison Study of Polymer/Cobalt Ferrite Nano–Composites Synthesized by Mechanical Alloying Route. J. Ultrafine Grained Nanostruct. Mater. 2015, 48, 59–67. [Google Scholar] [CrossRef]
  9. Rashidi, S.; Ataie, A. Structural and Magnetic Characteristics of PVA/CoFe2O4 Nano–Composites Prepared via Mechanical Alloying Method. Mater. Res. Bull. 2016, 80, 321–328. [Google Scholar] [CrossRef]
  10. Yang, W.; Xu, J.; Niu, L.; Kang, C.; Ma, B. Effects of High Energy Ball Milling on Mechanical and Interfacial Properties of PBT/Nano–Sb2O3 Composites. J. Adhes. Sci. Technol. 2018, 32, 291–301. [Google Scholar] [CrossRef]
  11. Smith, A.P.; Spontak, R.J.; Ade, H. On the Similarity of Macromolecular Responses to High–Energy Processes: Mechanical Milling vs. Irradiation. Polym. Degrad. Stab. 2001, 72, 519–524. [Google Scholar] [CrossRef]
  12. Bai, C.; Spontak, R.J.; Koch, C.C.; Saw, C.K.; Balik, C.M. Structural Changes in Poly(Ethylene Terephthalate) Induced by Mechanical Milling. Polymer 2000, 41, 7147–7157. [Google Scholar] [CrossRef]
  13. Smith, A.P.; Bai, C.; Ade, H.; Spontak, R.J.; Balik, C.M.; Koch, C.C. X-ray Microscopy of Novel Thermoplastic/Liquid Crystalline Polymer Blends by Mechanical Alloying. Macromol. Rapid Commun. 1998, 19, 557–561. [Google Scholar] [CrossRef]
  14. Koch, C.C.; Smith, A.P.; Bai, C.; Spontak, R.J.; Balik, C.M. Nonequilibrium Processing of Polymeric Materials by Mechanical Attrition. J. Metastable Nanocryst. Mater. 2000, 8, 49–56. [Google Scholar] [CrossRef]
  15. Cavalieri, F.; Padella, F.; Bourbonneux, S. High–Energy Mechanical Alloying of Thermoplastic Polymers in Carbon Dioxide. Polymer 2002, 43, 1155–1161. [Google Scholar] [CrossRef]
  16. Cai, R.; Tao, G.; He, H.; Song, K.; Zuo, H.; Jiang, W.; Wang, Y. One–Step Synthesis of Silver Nanoparticles on Polydopamine–Coated Sericin/Polyvinyl Alcohol Composite Films for Potential Antimicrobial Applications. Molecules 2017, 22, 721. [Google Scholar] [CrossRef] [PubMed]
  17. Wang, W.; Yu, Z.; Alsammarraie, F.K.; Kong, F.; Lin, M.; Mustapha, A. Properties and Antimicrobial Activity of Polyvinyl Alcohol–Modified Bacterial Nanocellulose Packaging Films Incorporated with Silver Nanoparticles. Food Hydrocoll. 2020, 100, 105411. [Google Scholar] [CrossRef]
  18. He, H.; Cai, R.; Wang, Y.; Tao, G.; Guo, P.; Zuo, H.; Chen, L.; Liu, X.; Zhao, P.; Xia, Q. Preparation and Characterization of Silk Sericin/PVA Blend Film with Silver Nanoparticles for Potential Antimicrobial Application. Int. J. Biol. Macromol. 2017, 104, 457–464. [Google Scholar] [CrossRef]
  19. Cobos, M.; De–La–Pinta, I.; Quindós, G.; Fernández, M.J.; Fernández, M.D. One–Step Eco–Friendly Synthesized Silver–Graphene Oxide/Poly(Vinyl Alcohol) Antibacterial Nanocomposites. Carbon 2019, 150, 101–116. [Google Scholar] [CrossRef]
  20. Bryaskova, R.; Pencheva, D.; Kale, G.M.; Lad, U.; Kantardjiev, T. Synthesis, Characterisation and Antibacterial Activity of PVA/TEOS/Ag–Np Hybrid Thin Films. J. Colloid Interface Sci. 2010, 349, 77–85. [Google Scholar] [CrossRef]
  21. Pomogailo, A.D. Polymer Sol–Gel Synthesis of Hybrid Nanocomposites. Colloid J. 2005, 67, 658–677. [Google Scholar] [CrossRef]
  22. Watson, B.; Meng, L.; Fetrow, C.; Qin, Y. Core/Shell Conjugated Polymer/Quantum Dot Composite Nanofibers through Orthogonal Non–Covalent Interactions. Polymer 2016, 8, 408. [Google Scholar] [CrossRef] [PubMed]
  23. Qi, W.; Zhang, X.; Wang, H. Self–Assembled Polymer Nanocomposites for Biomedical Application. Curr. Opin. Colloid Interface Sci. 2018, 35, 36–41. [Google Scholar] [CrossRef]
  24. Chen, G.; Gibson, K.J.; Liu, D.; Rees, H.C.; Lee, J.H.; Xia, W.; Lin, R.; Xin, H.L.; Gang, O.; Weizmann, Y. Regioselective Surface Encoding of Nanoparticles for Programmable Self–Assembly. Nat. Mater. 2019, 18, 169–174. [Google Scholar] [CrossRef] [PubMed]
  25. Quiñones, J.P.; Peniche, H.; Peniche, C. Chitosan Based Self–Assembled Nanoparticles in Drug Delivery. Polymer 2018, 10, 235. [Google Scholar] [CrossRef]
  26. Genix, A.C.; Oberdisse, J. Nanoparticle Self–Assembly: From Interactions in Suspension to Polymer Nanocomposites. Soft Matter 2018, 14, 5161–5179. [Google Scholar] [CrossRef]
  27. Liu, J.; Jiang, W.; Xu, Q.; Zheng, Y. Progress in Antibacterial Hydrogel Dressing. Gels 2022, 8, 503. [Google Scholar] [CrossRef]
  28. Wang, T.; Turhan, M.; Gunasekaran, S. Selected Properties of PH–Sensitive, Biodegradable Chitosan–Poly(Vinyl Alcohol) Hydrogel. Polym. Int. 2004, 53, 911–918. [Google Scholar] [CrossRef]
  29. Sionkowska, A. Current Research on the Blends of Natural and Synthetic Polymers as New Biomaterials: Review. Prog. Polym. Sci. 2011, 36, 1254–1276. [Google Scholar] [CrossRef]
  30. Sudhamani, S.R.; Prasad, M.S.; Udaya Sankar, K. DSC and FTIR Studies on Gellan and Polyvinyl Alcohol (PVA) Blend Films. Food Hydrocoll. 2003, 17, 245–250. [Google Scholar] [CrossRef]
  31. Holland, B.J.; Hay, J.N. The Thermal Degradation of Poly(vinyl alcohol). Polymer 2001, 42, 6775–6783. [Google Scholar] [CrossRef]
  32. Kumar, A.; Han, S.S. PVA–Based Hydrogels for Tissue Engineering: A Review. Int. J. Polym. Mater. Polym. Biomater. 2017, 66, 159–182. [Google Scholar] [CrossRef]
  33. Reddy, M.S.B.; Ponnamma, D.; Choudhary, R.; Sadasivuni, K.K. A Comparative Review of Natural and Synthetic Biopolymer Composite Scaffolds. Polymer 2021, 13, 1105. [Google Scholar] [CrossRef] [PubMed]
  34. Kamoun, E.A.; Chen, X.; Mohy Eldin, M.S.; Kenawy, E.-R.S. Crosslinked Poly(Vinyl Alcohol) Hydrogels for Wound Dressing Applications: A Review of Remarkably Blended Polymers. Arab. J. Chem. 2015, 8, 1–14. [Google Scholar] [CrossRef]
  35. Yin, I.X.; Zhang, J.; Zhao, I.S.; Mei, M.L.; Li, Q.; Chu, C.H. The Antibacterial Mechanism of Silver Nanoparticles and Its Application in Dentistry. Int. J. Nanomed. 2020, 15, 2555–2562. [Google Scholar] [CrossRef] [PubMed]
  36. Jun, B.-H. Silver Nano/Microparticles: Modification and Applications. Int. J. Mol. Sci. 2019, 20, 2609. [Google Scholar] [CrossRef]
  37. Maidaniuc, A.; Miculescu, M.; Voicu, S.I.; Ciocan, L.T.; Niculescu, M.; Corobea, M.C.; Rada, M.E.; Miculescu, F. Effect of Micron Sized Silver Particles Concentration on the Adhesion Induced by Sintering and Antibacterial Properties of Hydroxyapatite Microcomposites. J. Adhes. Sci. Technol. 2016, 30, 1829–1841. [Google Scholar] [CrossRef]
  38. Güzel, R.; Erdal, G. Synthesis of Silver Nanoparticles. In Silver Nanoparticles—Fabrication, Characterization and Applications; InTech: Lahore, Pakistan, 2018; Volume 9, pp. 586–592. [Google Scholar] [CrossRef]
  39. Labouta, H.I.; Schneider, M. Interaction of Inorganic Nanoparticles with the Skin Barrier: Current Status and Critical Review. Nanomed. Nanotechnol. Biol. Med. 2013, 9, 39–54. [Google Scholar] [CrossRef]
  40. Park, M.V.D.Z.; Neigh, A.M.; Vermeulen, J.P.; de la Fonteyne, L.J.J.; Verharen, H.W.; Briedé, J.J.; van Loveren, H.; de Jong, W.H. The Effect of Particle Size on the Cytotoxicity, Inflammation, Developmental Toxicity and Genotoxicity of Silver Nanoparticles. Biomaterials 2011, 32, 9810–9817. [Google Scholar] [CrossRef]
  41. Pal, S.; Tak, Y.K.; Song, J.M. Does the Antibacterial Activity of Silver Nanoparticles Depend on the Shape of the Nanoparticle? A Study of the Gram–Negative Bacterium Escherichia Coli. Appl. Environ. Microbiol. 2007, 73, 1712–1720. [Google Scholar] [CrossRef]
  42. Shahverdi, A.R.; Fakhimi, A.; Shahverdi, H.R.; Minaian, S. Synthesis and Effect of Silver Nanoparticles on the Antibacterial Activity of Different Antibiotics against Staphylococcus Aureus and Escherichia Coli. Nanomed. Nanotechnol. Biol. Med. 2007, 3, 168–171. [Google Scholar] [CrossRef] [PubMed]
  43. Shrivastava, S.; Bera, T.; Roy, A.; Singh, G.; Ramachandrarao, P.; Dash, D. Characterization of Enhanced Antibacterial Effects of Novel Silver Nanoparticles. Nanotechnology 2007, 18, 225103. [Google Scholar] [CrossRef]
  44. Morones, J.R.; Elechiguerra, J.L.; Camacho, A.; Holt, K.; Kouri, J.B.; Ramírez, J.T.; Yacaman, M.J. The Bactericidal Effect of Silver Nanoparticles. Nanotechnology 2005, 16, 2346–2353. [Google Scholar] [CrossRef]
  45. Pompilio, A.; Geminiani, C.; Bosco, D.; Rana, R.; Aceto, A.; Bucciarelli, T.; Scotti, L.; di Bonaventura, G. Electrochemically Synthesized Silver Nanoparticles Are Active against Planktonic and Biofilm Cells of Pseudomonas Aeruginosa and Other Cystic Fibrosis–Associated Bacterial Pathogens. Front. Microbiol. 2018, 9, 1349. [Google Scholar] [CrossRef] [PubMed]
  46. Fan, L.; Zhang, H.; Gao, M.; Zhang, M.; Liu, P.; Liu, X. Cellulose Nanocrystals/Silver Nanoparticles: In–Situ Preparation and Application in PVA Films. Holzforschung 2019, 74, 523–528. [Google Scholar] [CrossRef]
  47. Shahid, M.A.; Ali, A.; Uddin, M.N.; Miah, S.; Islam, S.M.; Mohebbullah, M.; Jamal, M.S.I. Antibacterial Wound Dressing Electrospun Nanofibrous Material from Polyvinyl Alcohol, Honey and Curcumin Longa Extract. J. Ind. Text. 2021, 51, 455–469. [Google Scholar] [CrossRef]
  48. Ali, A.; Shahid, M.A.; Hossain, M.D.; Islam, M.N. Antibacterial Bi–Layered Polyvinyl Alcohol (PVA)–Chitosan Blend Nanofibrous Mat Loaded with Azadirachta Indica (Neem) Extract. Int. J. Biol. Macromol. 2019, 138, 13–20. [Google Scholar] [CrossRef] [PubMed]
  49. Pencheva, D.; Bryaskova, R.; Kantardjiev, T. Polyvinyl Alcohol/Silver Nanoparticles (PVA/AgNps) as a Model for Testing the Biological Activity of Hybrid Materials with Included Silver Nanoparticles. Mater. Sci. Eng. C 2012, 32, 2048–2051. [Google Scholar] [CrossRef]
  50. Mlalila, N.G.; Swai, H.S.; Hilonga, A.; Kadam, D.M. Antimicrobial Dependence of Silver Nanoparticles on Surface Plasmon Resonance Bands against Escherichia coli. Nanotechnol. Sci. Appl. 2017, 10, 1–9. [Google Scholar] [CrossRef] [Green Version]
  51. Mlalila, N.; Swai, H.; Hilonga, A.; Kadam, D. Optimized Preparation of Silver Nanoparticles from Polyethylene Glycol and Formaldehyde. Int. Res. J. Pure Appl. Chem. 2016, 13, 1–9. [Google Scholar] [CrossRef]
  52. Bekhta, P.; Sedliačik, J. Environmentally–Friendly High–Density Polyethylene–Bonded Plywood Panels. Polymer 2019, 11, 1166. [Google Scholar] [CrossRef]
  53. Zhang, L.; Xu, H.; Wang, W. Performance of Straw/Linear Low Density Polyethylene Composite Prepared with Film–Roll Hot Pressing. Polymer 2020, 12, 860. [Google Scholar] [CrossRef]
  54. Dalsgaard, I. Selection of Media for Antimicrobial Susceptibility Testing of Fish Pathogenic Bacteria. Aquaculture 2001, 196, 267–275. [Google Scholar] [CrossRef]
  55. Hajipour, M.J.; Fromm, K.M.; Akbar Ashkarran, A.; Jimenez de Aberasturi, D.; de Larramendi, I.R.; Rojo, T.; Serpooshan, V.; Parak, W.J.; Mahmoudi, M. Antibacterial Properties of Nanoparticles. Trends Biotechnol. 2012, 30, 499–511. [Google Scholar] [CrossRef] [PubMed]
  56. Mansur, H.S.; Sadahira, C.M.; Souza, A.N.; Mansur, A.A.P. FTIR Spectroscopy Characterization of Poly(vinyl alcohol) Hydrogel with Different Hydrolysis Degree and Chemically Crosslinked with Glutaraldehyde. Mater. Sci. Eng. C 2008, 28, 539–548. [Google Scholar] [CrossRef]
  57. Zamiri, R.; Ahangar, H.A.; Zakaria, A.; Zamiri, G.; Shabani, M.; Singh, B.; Ferreira, J.M.F. The Structural and Optical Constants of Ag2S Semiconductor Nanostructure in the Far–Infrared. Chem. Cent. J. 2015, 9, 28. [Google Scholar] [CrossRef]
  58. Kim, Y.Y.; Walsh, D. Metal Sulfide Nanoparticles Synthesized via Enzyme Treatment of Biopolymer Stabilized Nanosuspensionsf. Nanoscale 2010, 2, 240–247. [Google Scholar] [CrossRef]
  59. Salunkhe, A.B.; Khot, V.M.; Thorat, N.D.; Phadatare, M.R.; Sathish, C.I.; Dhawale, D.S.; Pawar, S.H. Polyvinyl Alcohol Functionalized Cobalt Ferrite Nanoparticles for Biomedical Applications. Appl. Surf. Sci. 2013, 264, 598–604. [Google Scholar] [CrossRef]
  60. Li, W.; Wang, J.; Chi, H.; Wei, G.; Zhang, J.; Dai, L. College Preparation and Antibacterial Activity of Polyvinyl Alcohol/Regenerated Silk Fibroin Composite Fibers Containing Ag Nanoparticles. J. Appl. Polym. Sci. 2012, 123, 20–25. [Google Scholar] [CrossRef]
  61. Kumar, S.; Krishnakumar, B.; Sobral, A.J.F.N.; Koh, J. Bio–Based (Chitosan/PVA/ZnO) Nanocomposites Film: Thermally Stable and Photoluminescence Material for Removal of Organic Dye. Carbohydr. Polym. 2019, 205, 559–564. [Google Scholar] [CrossRef]
  62. Paul Sharma, J.; Kumar, P.; Sharma, K.; Kumar, M.; Arora, A.; Kumar Singh, P. Optical and Structural Properties of Drop–Cast PVA/PEG Polyblends. Mater. Today Proc. 2019, 34, 705–709. [Google Scholar] [CrossRef]
  63. Cheng, K.M.; Hung, Y.W.; Chen, C.C.; Liu, C.C.; Young, J.J. Green Synthesis of Chondroitin Sulfate–Capped Silver Nanoparticles: Characterization and Surface Modification. Carbohydr. Polym. 2014, 110, 195–202. [Google Scholar] [CrossRef] [PubMed]
  64. Song, R.; Ponge, D.; Kaspar, R.; Raabe, D. Grain Boundary Characterization and Grain Size Measurement in an Ultrafine–Grained Steel. Z. Fuer Met./Mater. Res. Adv. Tech. 2004, 95, 513–517. [Google Scholar] [CrossRef]
  65. Song, R.; Ponge, D.; Raabe, D. Mechanical Properties of an Ultrafine Grained C–Mn Steel Processed by Warm Deformation and Annealing. Acta Mater. 2005, 53, 4881–4892. [Google Scholar] [CrossRef]
Figure 1. Images of as–received AgNO3 (a); precipitated from Equation (1) Ag2O (b); and precipitated from Equation (2) Ag (c).
Figure 1. Images of as–received AgNO3 (a); precipitated from Equation (1) Ag2O (b); and precipitated from Equation (2) Ag (c).
Polymers 14 03588 g001
Figure 2. Diffractogram from silver nitrate (AgNO3) as–received samples, silver oxide (Ag2O), and silver (Ag).
Figure 2. Diffractogram from silver nitrate (AgNO3) as–received samples, silver oxide (Ag2O), and silver (Ag).
Polymers 14 03588 g002
Figure 3. SEM–FEG images of as–received AgNO3 (a); Ag2O resulting from the oxidation of AgNO3 (b); (Ag) resulting from the reduction Ag2O (c); as–received PVA (d).
Figure 3. SEM–FEG images of as–received AgNO3 (a); Ag2O resulting from the oxidation of AgNO3 (b); (Ag) resulting from the reduction Ag2O (c); as–received PVA (d).
Polymers 14 03588 g003
Figure 4. SEM–FEG of PVA after milling in an Attritor–type mill: (a) PVA milled for 0.5 h; (b) PVA milled for 2 h; (c) PVA milled for 4 h; (d) PVA milled for 16 h; (e) surface detailed image from PVA milled for 4 h.
Figure 4. SEM–FEG of PVA after milling in an Attritor–type mill: (a) PVA milled for 0.5 h; (b) PVA milled for 2 h; (c) PVA milled for 4 h; (d) PVA milled for 16 h; (e) surface detailed image from PVA milled for 4 h.
Polymers 14 03588 g004aPolymers 14 03588 g004b
Figure 5. Differential Exploratory Calorimetry Curve (DSC). PVA in several milling conditions compared to the as–received material.
Figure 5. Differential Exploratory Calorimetry Curve (DSC). PVA in several milling conditions compared to the as–received material.
Polymers 14 03588 g005
Figure 6. SEM–FEG images of composite PVA/Ag obtained by mechanical alloying. In (a), some flakes of PVA are highlighted with white circles, which are impregnated with Ag that can be better observed in (b) with higher magnification.
Figure 6. SEM–FEG images of composite PVA/Ag obtained by mechanical alloying. In (a), some flakes of PVA are highlighted with white circles, which are impregnated with Ag that can be better observed in (b) with higher magnification.
Polymers 14 03588 g006
Figure 7. FTIR spectra of as–received PVA powder samples, PVA mechanical alloyed for 4 h, with 10% wt. Ag and without Ag.
Figure 7. FTIR spectra of as–received PVA powder samples, PVA mechanical alloyed for 4 h, with 10% wt. Ag and without Ag.
Polymers 14 03588 g007
Figure 8. FTIR spectra of as–received PVA and milled powder samples by mechanical alloying with and without Ag in several studied conditions. (A) as–received PVA; (E) Pure PVA milled for 4 h; (E1) PVA + 0.5% wt. Ag milled for 4 h; (E2) PVA + 1% wt. Ag milled for 4 h; (E3) PVA + 2.5% wt. Ag milled for 4 h; (E4) PVA + 5% wt. Ag milled for 4 h; and (E5) PVA + 10% wt. Ag milled for 4 h.
Figure 8. FTIR spectra of as–received PVA and milled powder samples by mechanical alloying with and without Ag in several studied conditions. (A) as–received PVA; (E) Pure PVA milled for 4 h; (E1) PVA + 0.5% wt. Ag milled for 4 h; (E2) PVA + 1% wt. Ag milled for 4 h; (E3) PVA + 2.5% wt. Ag milled for 4 h; (E4) PVA + 5% wt. Ag milled for 4 h; and (E5) PVA + 10% wt. Ag milled for 4 h.
Polymers 14 03588 g008
Figure 9. Optical Microscopy of the films produced from mechanically alloyed powders for 4 h. This is (a) PVA + 2.5% wt. Ag and (b) PVA + 10% wt. Ag.
Figure 9. Optical Microscopy of the films produced from mechanically alloyed powders for 4 h. This is (a) PVA + 2.5% wt. Ag and (b) PVA + 10% wt. Ag.
Polymers 14 03588 g009
Figure 10. SEM–FEG of the film’s fracture surface produced by mechanical alloying powder for 4 h. (a) PVA + 2.5% wt. Ag and (b) PVA + 10% wt. Ag.
Figure 10. SEM–FEG of the film’s fracture surface produced by mechanical alloying powder for 4 h. (a) PVA + 2.5% wt. Ag and (b) PVA + 10% wt. Ag.
Polymers 14 03588 g010
Figure 11. SEM–FEG of agglomerated particles in the PVA film with 10% wt. Ag.
Figure 11. SEM–FEG of agglomerated particles in the PVA film with 10% wt. Ag.
Polymers 14 03588 g011
Figure 12. Photographs of the plates sown after incubation for 24 h in an oven at 36 °C. (a) Pseudomonas aeruginosa; (b) Escherichia coli; (c) Staphylococcus aureus and (d) Streptococcus pyogenes. The numbers correspond to the films under the following conditions: (1) pure PVA; (2) PVA + 0.5% wt. Ag; (3) PVA + 1% wt. Ag; (4) PVA + 2.5% wt. Ag; (5) PVA + 5% wt. Ag; and (6) PVA + 10% wt. Ag. Outer circles represent the inhibition zone, the inner dotted circles represent the polymeric film, and the distance between the inner and outer circles represents the inhibition halo.
Figure 12. Photographs of the plates sown after incubation for 24 h in an oven at 36 °C. (a) Pseudomonas aeruginosa; (b) Escherichia coli; (c) Staphylococcus aureus and (d) Streptococcus pyogenes. The numbers correspond to the films under the following conditions: (1) pure PVA; (2) PVA + 0.5% wt. Ag; (3) PVA + 1% wt. Ag; (4) PVA + 2.5% wt. Ag; (5) PVA + 5% wt. Ag; and (6) PVA + 10% wt. Ag. Outer circles represent the inhibition zone, the inner dotted circles represent the polymeric film, and the distance between the inner and outer circles represents the inhibition halo.
Polymers 14 03588 g012aPolymers 14 03588 g012b
Table 1. Milling Parameters.
Table 1. Milling Parameters.
Ball Size (mm)Milling PowerSpeed Rotation (rpm)Milling Temperature
6.3538:1600Water cooled at room temperature
Table 2. Milling time condition of commercial PVA from the as–received material.
Table 2. Milling time condition of commercial PVA from the as–received material.
SampleCondition
AAs–received
BMilled for 0.5 h
CMilled for 1 h
DMilled for 2 h
EMilled for 4 h
FMilled for 8 h
GMilled for 16 h
Table 3. Weight % fractions of (Ag) and Poly(vinyl alcohol) (PVA).
Table 3. Weight % fractions of (Ag) and Poly(vinyl alcohol) (PVA).
SamplesCondition
AAs–received PVA
E1PVA + 0.5% wt. Ag
E2PVA + 1% wt. Ag
E3PVA + 2.5% wt. Ag
E4PVA + 5% wt. Ag
E5PVA + 10% wt. Ag
Table 4. Samples used to assess the antimicrobial activity of polymeric films.
Table 4. Samples used to assess the antimicrobial activity of polymeric films.
SamplesCondition Films
1As–received PVA
2PVA + 0.5% wt. Ag
3PVA + 1% wt. Ag
4PVA + 2.5% wt. Ag
5PVA + 5% wt. Ag
6PVA + 10% wt. Ag
Table 5. Values of the lattice parameters of silver nitrate (AgNO3), silver oxide (Ag2O), and silver (Ag).
Table 5. Values of the lattice parameters of silver nitrate (AgNO3), silver oxide (Ag2O), and silver (Ag).
SamplesLattices (nm)
abc
AgNO30.6990.7331.013
Ag2O0.4710.4710.471
Ag0.4090.4090.409
Table 6. Melting temperature values obtained by Differential Scanning Calorimetry (DSC) for each sample of PVA.
Table 6. Melting temperature values obtained by Differential Scanning Calorimetry (DSC) for each sample of PVA.
Processing ConditionMelting Point (°C) Measured by DSC
As–received191
Milled for 0.5 h188
Milled for 1 h187
Milled for 2 h187
Milled for 4 h185
Milled for 8 h185
Milled for 16 h182
Table 7. A list of the five regions highlighted in the spectrum illustrated in Figure 7 corresponds to some types of bonding interactions at specific IV–TF frequencies (cm−1).
Table 7. A list of the five regions highlighted in the spectrum illustrated in Figure 7 corresponds to some types of bonding interactions at specific IV–TF frequencies (cm−1).
RegionType of BondingFrequency Ranges (cm−1)
IO–H 3200–3650
IIC–H2800–2900
IIIC = O1700–1750
IVC–O–H e CH2 1230–1465
VC–O1000–1200
Table 8. Chemical elements detected by EDS.
Table 8. Chemical elements detected by EDS.
Chemical Elements
Elements% wt.
Ag92.47
O4.81
Au1.8
Pd0.92
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Aguiar, D.B.d.S.d.; Aguiar, D.J.M.d.; Paula, J.d.F.P.d.; Cintho, O.M. Obtaining Ultrafine Dispersions of Silver Particles in Poly(vinyl Alcohol) Matrix Using Mechanical Alloying. Polymers 2022, 14, 3588. https://0-doi-org.brum.beds.ac.uk/10.3390/polym14173588

AMA Style

Aguiar DBdSd, Aguiar DJMd, Paula JdFPd, Cintho OM. Obtaining Ultrafine Dispersions of Silver Particles in Poly(vinyl Alcohol) Matrix Using Mechanical Alloying. Polymers. 2022; 14(17):3588. https://0-doi-org.brum.beds.ac.uk/10.3390/polym14173588

Chicago/Turabian Style

Aguiar, Deize Basílio dos Santos de, Denilson José Marcolino de Aguiar, Josiane de Fátima Padilha de Paula, and Osvaldo Mitsuyuki Cintho. 2022. "Obtaining Ultrafine Dispersions of Silver Particles in Poly(vinyl Alcohol) Matrix Using Mechanical Alloying" Polymers 14, no. 17: 3588. https://0-doi-org.brum.beds.ac.uk/10.3390/polym14173588

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics